A comparative analysis is performed by XPS, HAXPES and SEM of industrial functionalised graphene powder of different morphology. The chemical analysis carried out by XPS, which probing depth is around 10nm, and HAXPES, which can reach up to 30nm probing depth. By combining these two techniques is possible to get a rough, non-destructive depth profiling of the sample's surface. The results show a higher concentration of the functionlisation elements on the surface of the sample and the influence of the morphology on the functionalisation process and the C/O ratio.
Experience gained at BAM within the European project ISGScope on the accurate measureemnt of graphene oxide flakes by electron microscopy is presented. Particularly, factors such as the type of solvent, substrate temperature, but also proper, gentle measurement parameters and image analysis conditions towards automation are highlighted. The measurement procedures in develeopment are being prepared to launch an inter-laboratory comparison under VAMAS (TWA41) as preparatory guidance for future standardisation at ISO.
Nanosafety is becoming increasingly important as nanomaterials are widely used in industrial processes and consumer products. For nanotoxicity measurements prior sterilization of the samples is necessary, but as structure activity relationships are made with properties of pristine particles, the question arises, if the sterilization process has an impact on the physico-chemical properties of nanoparticles and thus on the biological behavior.
This question will be addressed in this talk. For this purpose, results from SEM and EDS measurements are combined with those of a novel lab-based HAXPES spectrometer in order to obtain a more complete picture. At the end, an influence of sterilization will be evident, which indicates a restructuring of the nanoparticles owing to sterilization.
Before industrial grade graphene could reach comparable quality to the controlled laboratory scale material, many challenges must be overcome. In order to bridge the gap between lab-scale and industrial-scale production is necessary to develop processes, equipment and measurement procedures to control the material features. One of the most crucial reasons of graphene’s limited commercialization is the lack of standard procedures to properly characterize and define the material chemical and structural properties down to the nanometer level. This leads to many issues regarding material synthesis repeatability, inappropriateness choice of measurands and measurement reproducibility which heavily affect the consistency of the material performance. For example, among all the different industrially produced real-world graphene, it is crucial to determine how many layers of graphene build the material. Products that are built by more than 10 layers should be more correctly referred as nanosized graphite, a problem that is often regarded as the “fake graphene” issue.
In our study, a comparative analysis is performed on two different series (G5 and G6) of industrial graphene powders, each series produced with four types of functionalization: raw graphene, oxygen-functionalized, nitrogen-functionalized and fluorine-functionalized. All the 8 sample variants were analyzed from a chemical and morphological point of view in the form of powders prepared as slightly pressed in metallic sample holders.
The results of the comparative chemical analyses XPS and EDS show a good agreement in the concentration values for all the elements present in the samples, despite the different analysis volumes addressed by the two techniques. For this reason, the samples can be considered homogeneous in both lateral and vertical direction.
A clear influence of the morphology on the composition is evident. Therefore, such correlative measurements of morphology and composition are necessary for a comprehensive characterization of industrial graphene flakes. Protocols for reliable characterization of industrial graphene flakes are in progress.