Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2020 (48) (entfernen)
Dokumenttyp
- Vortrag (20)
- Sonstiges (18)
- Zeitschriftenartikel (6)
- Dissertation (2)
- Beitrag zu einem Tagungsband (1)
- Forschungsbericht (1)
Schlagworte
- Korrosion (18)
- Corrosion (15)
- Zink (6)
- Coating (5)
- Deckschichtbildung (4)
- Korrosionsprüfung (4)
- Atmosphärische Korrosion (3)
- CCUS (3)
- Crevice corrosion (3)
- Geothermal (3)
- Stainless steel (3)
- Biobrennstoff (2)
- FAME (2)
- Gelartige Elektrolyte (2)
- Heizöl (2)
- Korrosionswechselprüfung (2)
- Lining (2)
- Nomenklatur (2)
- Normung (2)
- Stahl (2)
- Werkstoffprüfung (2)
- gelartige Elektrolyte (2)
- Additive manufacturing (1)
- Alkali-activated materials (1)
- Aluminium (1)
- Atmosphäre (1)
- Auslagerungsversuche (1)
- Batteries (1)
- Beständigkeitsuntersuchungen (1)
- Biofuel (1)
- Bridge (1)
- CO2 pipeline transport (1)
- CO2-corrosion (1)
- Carbon Capture (1)
- Carbon dioxide (1)
- Carbon steel (1)
- Cathodic protection (1)
- Chloridinduzierte Lochkorrosion (1)
- Concrete (1)
- Copper (1)
- Corrosion testing (1)
- Corrosivity (1)
- Critical chloride content (1)
- Disinfectants (1)
- Disinfection (1)
- Drinking water (1)
- Duplex (1)
- Elastomer (1)
- Electrochemical impedance spectroscopy (1)
- Electrochemistry (1)
- Elektrochemie (1)
- Failure (1)
- Failure analysis (1)
- Freibewitterung (1)
- Geothermie (1)
- Grinding (1)
- Heizöl-20% Biodiesel-Blend (1)
- Impurities (1)
- In-situ ED-XRD (1)
- Klimawechseltest (1)
- Korrosionsmonitoring (1)
- Korrosionssensoren (1)
- Lead (1)
- Legierung (1)
- Magnesium (1)
- Magnesium Alloy (1)
- Material properties (1)
- Materials (1)
- Materials behavior (1)
- Metallene Werkstoffe (1)
- Nanoparticle (1)
- Oxyfuel (1)
- Physik (1)
- Pipeline (1)
- Polyaniline (1)
- Polymer (1)
- Polymerwerkstoff (1)
- Polymerwerkstoffe (1)
- Protection (1)
- Resistance (1)
- Saline brine (1)
- Schadnesanalyse (1)
- Schweißen (1)
- Schweißnaht (1)
- Steel (1)
- Steel corrosion (1)
- Steel-concrete interface (1)
- Thermodynamik (1)
- Tunnelbauwerke (1)
- Vorgehensweise (1)
- W-Cl Instandsetzungsprinzip (1)
- Wasserstoff (1)
- Water-bearing (1)
- Werkstoffe (1)
- ZFP (1)
- Zinküberzüge (1)
Organisationseinheit der BAM
- 7.6 Korrosion und Korrosionsschutz (48) (entfernen)
Eingeladener Vortrag
- nein (20)
Im DGMK-Projekt 780 wurde eine forcierte Prüfmethode entwickelt zur Bestimmung der Beständigkeit von metallenen Werkstoffen gegenüber Brennstoffen aus Mitteldestillaten und Gemischen aus Mitteldestillat und paraffinischen Kohlenwasserstoffen, die jeweils Fettsäuremethylester (FAME) als biogene Komponente enthalten. Bei der Prüfmethode werden Proben des Werkstoffes in einem speziellen Prüfmedien ausgelagert. Die Zusammensetzung von zwei Prüfmedien wurde im Vorhaben erarbeitet. Die Prüfmedien decken für den FAME-Anteil einen Bereich von bis zu 20 % (V/V) ab. Die Auslagerung kann bei geringem Aufwand unter Atmosphärendruck durchgeführt werden.
Die Eignung einer Auswahl von metallenen Werkstoffen und Polymerwerkstoffen, die für Versorgungsanlagen für Mitteldestillat relevant sind, wurde durch Auslagerung in folgenden nicht gealterten Brennstoffen bestimmt: Heizöl EL schwefelarm (B0), Heizöl EL schwefelarm mit 20 % (V/V) FAME (B20), FAME (B100) und hydriertes Pflanzenöl (HVO). Die Temperatur bei der Auslagerung betrug 50 °C für die metallenen Werkstoffe und 40 °C und 70 °C für die Polymerwerkstoffe. Die Ergebnisse der Beständigkeitsbewertung wurden in Beständigkeitslisten zusammengefasst. Die mit dem B20 erhaltenen Werkstoffbeständigkeiten gelten generell für Gemische aus Heizöl EL schwefelarm und FAME mit einem FAME-Gehalt bis zu 20 % (V/V). Sie sind auch auf Gemische aus Dieselkraftstoff und FAME mit einem FAME-Gehalt bis 20 %(V/V) übertragbar.
Die forcierte Prüfmethode kann insbesondere KMUs bei der Weiterentwicklung von bestehenden Produkten und der Entwicklung von neuen Produkten als ein kostengünstiger Schnelltest zur Überprüfung der Werkstoff- und Bauteilbeständigkeit gegenüber Mitteldestillaten mit hohem FAME-Anteil dienen. Sie kann für die Hersteller die Sicherheit erhöhen, dass Bauteile die Freigabeprüfungen der Bauaufsicht bestehen, wobei die Freigabe aber nur für Deutschland gültig ist.
Die Erkenntnisse des Forschungsvorhabens können in eine harmonisierte Europäischen Norm für alternative Brenn- und Kraftstoffe einfließen. Diese ist für die Bauteilhersteller die Voraussetzung für die Erschließung des europäischen Marktes.
Polyaniline/Silicon Dioxide Composite-Based Coating for Corrosion Protection in Geothermal Systems
(2020)
Geothermal energy is one of the cleanest renewable alternatives to reduce the dependency on fossil fuel [1, 2]. Despite its promising future, its implementation faces various challenges, one of them being corrosion processes. To implement this energy, hot fluids are pumped from a geothermal well. These hot fluids originate from deep within the earth, so consist of different ionic species and gases in a wide range of temperatures, which lead to their corrosive nature. In terms of geothermal energy resources, Indonesia is at the forefront, with the highest preserved geothermal energy in the world of about 29 GWe and 312 potential geothermal locations [3]. Geothermal wells in Sibayak (North Sumatera), Indonesia, belong to young stratovolcanoes and have operating temperatures varying from 36 °C at the near ground surface to 310 °C at the bottom of the well, which is liquid-dominated with acidic and saline properties [4, 5]. Therefore, this geothermal fluid creates an aggressive environment that is conducive to corrosion of the powerplant infrastructure.
Parts of the geothermal powerplant infrastructure, such as pipelines and heat exchangers, are commonly made of metals, e.g. carbon steel and stainless steel. Consequently, they may undergo corrosion and scaling when exposed to the geothermal fluid, especially for carbon steel. To ensure the safety and longevity of a geothermal powerplant, the infrastructure is constructed of expensive corrosion resistant alloys [6–10], e.g., titanium and Ni-Cr based alloys, or carbon steel which needs to be protected by coatings or inhibitors.
To address the corrosion of carbon steel in the geothermal environment, artificial geothermal water was used to simulate a geothermal well in Sibayak, Indonesia, with pH 4 and a saline composition of 1,500 mg/l Cl-, 20 mg/l SO42-, 15 mg/l HCO3-, 200 mg/l Ca2+, 250 mg/l K+, and 600 mg/l Na+. Carbon steel underwent the most severe corrosion at 150°C in an oxygen-containing solution with a corrosion rate of 0.34 mm/year, which is approximately ten times higher than that in the absence of dissolved oxygen. In all conditions, pitting corrosion was observed, which necessitate a protection strategy on carbon steel. In order to promote a cost effective and locally available option, this work focused on an easily applicable coating which utilized local resources.
Toward developing such protective coating based on the locally available resources in Indonesia which can yield good corrosion resistance and thermal stability in geothermal environment, two additional components, i.e. polyaniline (PANI) and silicon dioxide, were used to modify an alkyd-based commercial coating. The selection of the alkyd-based coating as a matrix focused on the industrial convenience basis, where the coating application procedure should be simple and easy to apply within reasonable costs. The alkyd-based coating underwent severe blistering when exposed to the artificial geothermal water at 70 and 150°C due to the reaction between CaCO3 (as one of its components) and the artificial geothermal water, as well as a possible alkyd hydrolysis in the initial stage of exposure. In the oxygen-free solution, the degradation was controlled by chemical and thermal reactions, whereas in the aerated condition, oxidization at the coating surface further accelerated polymer degradation.
PANI was chosen as one of the anticorrosion pigments which was widely developed over the past decades. To investigate the interaction between PANI and the artificial geothermal water, PANI film was electrochemically deposited on the carbon steel surface and exposed to the artificial geothermal water. Electrochemically synthesized oxalate-doped PANI was protective against corrosion of carbon steel in artificial geothermal water at room temperature. The mechanism involved an exchange of electroactive species within the coating layer, as confirmed by electrochemical impedance spectra. Interaction of ionic species, such as Cl-, Na+, Ca2+ from the artificial geothermal water, with the outer layer of PANI is suggested both at 25°C and 150°C, based on the EDX spectra of the coating surface after exposure to the artificial geothermal water. Thus, the protection mechanism of PANI is not solely based on the physical barrier layer properties, but rather associated with the redox mediated properties of PANI, which selectively allow ionic species intrusion from the electrolyte into the PANI layer. Although PANI is a promising candidate as an anticorrosion coating, its morphological characterization reveals that electrochemically deposited PANI is not stable for an application at 150°C. Therefore, another approach was used to promote better protective behavior of PANI by dispersing chemically synthesized PANI in the alkyd-based coating.
To enhance the thermal stability of the coating, silicon dioxide (SiO2) was added, which was able to prolong the sustainability of coated metals until 28 days compared to the unmodified alkyd-based coating, which underwent a change in color to brown/orange only within 7 days of exposure. This improvement might be associated with the role of SiO2 to proportionate the thermal expansion coefficient of the coating system to be compatible with that of carbon steel. Although the coating is thermally enhanced, the electrolyte might still intrude through the coating resulting in the change of coating color after 28 days of exposure in the artificial geothermal water. When PANI was added, the coating system provided an active corrosion protection on the carbon steel surface. The chemical and morphological characterization of the PANI-alkyd and SiO2-alkyd coating system showed that coatings were improved, and no blisters were observed, albeit the degradation continued. Based on the results of exposure tests, the combined coating system was further investigated.
The combinational coating of PANI/SiO2-alkyd was used with 2 wt% of PANI and 15 wt% of SiO2. Electrochemical tests indicated cathodic protection at 150°C, as the Ecorr of PANI/SiO2 remained approximately 400 mV lower than the carbon steel potential. The impedance spectra of the combinational coating of PANI/SiO2 showed a continuous decrease in the absolute impedance value over time. A significant decrease was observed within one day of exposure, followed by a slow gradual decrease, which might be associated with water absorption in the coating. FTIR spectra revealed that several peaks associated with the organic portion of the coatings were reduced after the specimens were exposed for 6 months. However, the absorption peaks related to the inorganic portion of the coatings remained stable until 6 months. Morphological characterization of the combinational coating of PANI/SiO2 showed that there were no blisters or significant discoloration of coatings after long-term exposure for 6 months in artificial geothermal water at 150°C, indicating that the chemical degradation does not significantly affect the functionality of the coating. This clearly shows the durability of PANI/SiO2 coating in the geothermal condition, suggesting that this coating can be used for such geothermal application. However, further testing of this coating should be conducted in a real geothermal environment on-site to ensure safety and viability.
Risiko der Wasserstoffentwicklung an martensitischen Schraubankern unter baupraktischen Bedingungen
(2020)
Die vorliegende Untersuchung beschäftigt sich mit der Fragestellung ob unter praxisrelevanten Bedingungen die Entstehung von Wasserstoff an vollmartensitischen Schraubankern möglich ist. Im Gegensatz zu austenitischen Werkstoffen besteht bei martensitischen Werkstoffen bei Gegenwart von Wasserstoff stets die Möglichkeit einer wasser-stoffinduzierten Versprödung des Materials. Hierfür wurde ein in der Praxis häufig anzutreffendes Szenario gewählt, das ein galvanisches Element, bestehend aus nichtrostenden Schraubankern (in diesem Fall martensitischen) und einer verzinkten Ankerplatte an einem Betonkörper, umfasst. Zum Nachweis einer Wasserstoffentwicklung wird der Elementstrom zwischen den Bauteilen sowie das Korrosionspotential erfasst. Die Ergebnisse der Versuche zeigen, dass über eine zeitlich begrenzte Dauer eine starke kathodische Polarisation der martensitischen Schraubanker durch die korrosive Auflösung des Zinks erfolgt. Als Folge kommt es zur Wasserzersetzung im Phasengrenzbereich der Schraubanker und zur Entstehung von atomarem Wasserstoff. Das berechnete Gasvolumen des entstandenen Wasserstoffs an den Stahlankern wurde bestimmt und lag im Mittel bei 11,14 ± 1,94 ml. Eine Diffusion des an der Stahloberfläche adsorbierten Wasserstoffs in den martensitischen Werkstoff ist somit theoretisch möglich und impliziert eine mögliche Gefährdung durch wasserstoffinduzierte Rissbildung und spontanem Versagen unter Belastung.
Aufgrund der stark korrosiven Atmosphäre in Tunnelbauwerken kommt es aufgrund von Reinigungs- und Sanierungsmaßnahmen an Ein- und Anbauteilen aus nichtrostendem Stahl häufig zu wartungsbedingten Verkehrsbeeinflussungen und Tunnelsperrungen. Bislang ist nur eine kleine Gruppe rostfreier Edelstähle für die Verwendung in Tunnelbauwerken zugelassen. Im Sinne einer mittel- bis langfristigen Reduktion von Wartungsarbeiten besteht jedoch großes Interesse, die Einsatzmöglichkeiten alternativer nichtrostender Stähle zu erhöhen. Ziel ist die Qualifizierung ferritischer-austenitischer Stähle.
Erste Untersuchungen nach 2 Jahren Auslagerung zeigten bisher vielversprechende Ergebnisse.
Im Vorhaben wurde eine forcierte Prüfmethode zur Bestimmung der Beständigkeit von metallenen Werkstoffen gegenüber Brennstoffen aus Mitteldestillaten und Gemischen aus Mitteldestillat und paraffinischen Kohlenwasserstoffen, die jeweils Fettsäuremethylester (FAME) als biogene Komponente enthalten, entwickelt. Bei der Prüfmethode werden Prüfkörper des jeweiligen Werkstoffes in speziellen Prüfmedien ausgelagert. Die Zusammensetzung von zwei Prüfmedien wurde im Vorhaben erarbeitet. Diese Prüfmedien erfassen die Effekte der Alterung des FAME, die zu erwarten sind, wenn der Brennstoff länger als 2 Jahre im Feld lagert. Sie decken den Bereich bis 20 % (V/V) FAME-Anteil ab. Die Auslagerung kann bei geringem Aufwand unter Atmosphärendruck durchgeführt werden.
Die Eignung einer Auswahl von metallenen Werkstoffen und Polymerwerkstoffen, die für Versorgungsanlagen für Mitteldestillat relevant sind, wurde durch Auslagerung in folgenden nicht gealterten Brennstoffen bestimmt: Heizöl EL schwefelarm (B0), Heizöl EL schwefelarm mit 20 % (V/V) FAME (B20), FAME (B100) und hydriertes Pflanzenöl (HVO). Die Werkstoffe wurden auch in einem 1 Jahr gealterten B20 und einem 8 Jahre gealtertem B10 ausgelagert. Die Temperatur bei der Auslagerung betrug 50 °C für die metallenen Werkstoffe und 40 °C und 70 °C für die Polymerwerkstoffe. Die Ergebnisse der Beständigkeitsbewertung wurden in Beständigkeitslisten zusammengefasst. Die mit B20 erhaltenen Bewertungen gelten generell für Gemische aus Heizöl EL schwefelarm und FAME mit einem FAME-Gehalt bis 20 % (V/V). Sie sind auch auf Gemische aus Dieselkraftstoff und FAME mit einem FAME-Gehalt bis 20 %(V/V) übertragbar.
Die forcierte Prüfmethode kann insbesondere KMUs bei der Weiterentwicklung von bestehenden Produkten und der Entwicklung von neuen Produkten als ein kostengünstiger Schnelltest zur Überprüfung der Werkstoff- und Bauteilbeständigkeit gegenüber Mitteldestillaten mit hohem FAME-Anteil dienen. Sie kann für die Hersteller die Sicherheit erhöhen, dass Bauteile die Freigabeprüfungen der Bauaufsicht bestehen, wobei die Freigabe jedoch nur für Deutschland gültig ist.
Die Erkenntnisse des Forschungsvorhabens können in eine harmonisierte Europäische Norm für alternative Brenn- und Kraftstoffe einfließen. Diese ist für die Bauteilhersteller die Voraussetzung für die Erschließung des europäischen Marktes.
Die Werkstoffklasse der Nichteisenmetalle gewinnt wegen ihrer unzähligen Anwendungsmöglichkeiten nicht nur im Maschinen‐ und Anlagenbau eine immer größere technische und wirtschaftliche Bedeutung, sodass es unabdingbar ist, insbesondere Studierenden der Material‐ und Werkstoffwissenschaften und des Maschinenbaus, den aktuellen Wissensstand auf diesem Gebiet zu vermitteln. Mit dieser Neuerscheinung veröffentlicht der Wiley‐VCH‐Verlag ein solches Lehrbuch. Kompakt und übersichtlich machen die beiden Autoren den Leser in 10 Kapiteln auf verständliche Art mit dieser Thematik vertraut. Dabei kommt ihnen ihre durch langjährige Lehrtätigkeit erworbene didaktische Erfahrung sehr zugute.
Alles in allem bietet dieses Lehrbuch durch seinen von den Natur‐, über Material‐ zu Ingenieurwissenschaften weitgespannten Bogen einen interessanten und übersichtlichen Einstieg in die Welt der am häufigsten verwendeten Nichteisenmetalle, wobei es keinen Anspruch auf Vollständigkeit erhebt.
Indonesien gilt aufgrund seiner vielen Vulkane als einer der Hotspots für Geothermie. Doch Salz und Hitze setzen den Geothermie‐Anlagen zu und gefährden ihre Sicherheit und Wirtschaftlichkeit. Ein Team an der BAM hat günstigen, lokal verfügbaren Baustahl jetzt so beschichtet, dass ein nachhaltiger und sicherer Betrieb der Geothermie‐Kraftwerke möglich ist ‐ auch unter Extrembedingungen.
Das BAM‐Team will das Beschichtungssystem nun den Anwendern in Indonesien zur Verfügung stellen, damit es unter Realbedingungen in einem Geothermie‐Kraftwerk getestet werden kann. Der Schutz vor Korrosion ist mitentscheidend, weil sie die Lebensdauer dieser Kraftwerke bestimmt. Unsere Arbeit könnte die Effizienz der Energieproduktion mit Geothermie wesentlich verbessern.
This book introduces to aspects to be considered when dealing with coatings and linings. Philip A. Schweitzer covers and compares a variety of specific coatings and their applications. In 18 chapters he divided the content into two main parts: linings and coatings.
All professionals involved in design and maintenance processes get by this book a compact survey of necessary considerations which needs to be done when applying surface protection measures. The literature references at the end of some chapters support the readers finding additional information about the special topic, mainly written by the author himself. Since this newly issued paperback edition is a 1:1 re‐print of the 2001 hardcover version, neither current publications are referenced, nor revisions were made.
The corrosion resistance of aluminium surfaces is closely linked to the surfacecstate after a grinding process. For years, iron‐containing abrasive materials were suspected to lead to increased corrosion susceptibility after processing of aluminium surfaces. To prove a possible correlation between the iron content of an abrasive and the corrosion behaviour of aluminium components, scientific investigations and experimentally practical corrosion tests are necessary.
For the current investigation, specimens of a technical Al‐Si alloy from the same batch were used. The test specimens were mechanically ground with various resin‐bonded model abrasives containing different iron contents. The performed corrosion tests did not reveal a negative influence of the different iron‐containing abrasives on the corrosion behaviour of the Al–Si alloy.
However, the most sensitive measuring method (electrochemical noise)
showed differences in the surface activity depending on the type of abrasive.