Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Zeitschriftenartikel (152)
- Vortrag (144)
- Posterpräsentation (60)
- Beitrag zu einem Tagungsband (16)
- Dissertation (3)
- Buchkapitel (2)
- Forschungsbericht (1)
- Forschungsdatensatz (1)
Schlagworte
- Additive manufacturing (91)
- Additive Manufacturing (57)
- Residual stress (51)
- Computed tomography (49)
- Laser powder bed fusion (29)
- X-ray refraction (27)
- Neutron diffraction (25)
- Residual Stress (22)
- Microstructure (20)
- Computed Tomography (19)
Organisationseinheit der BAM
- 8.5 Röntgenbildgebung (379) (entfernen)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (144)
The in situ analysis of the damage evolution in a metal Matrix composite (MMC) using synchrotron X-ray refraction radiography (SXRR) is presented. The investigated material is an Al alloy (6061)/10 vol% Al2O3 MMC after T6 heat treatment.
In an interrupted tensile test the gauge section of dog bone-shaped specimens is imaged in different states of tensile loading. On the basis of the SXRR images, the relative change of the specific surface (proportional to the amount of damage) in the course of tensile loading was analyzed. It could be shown that the damage can be detected by SXRR already at a stage of tensile loading, in which no Observation of damage is possible with radiographic absorption-based imaging methods.
Moreover, the quantitative analysis of the SXRR images reveals that the amount of damage increases homogeneously by an average of 25% with respect to the Initial state. To corroborate the experimental findings, the damage distribution was imaged in 3D after the final tensile loading by synchrotron X-ray refraction computed tomography (SXRCT) and absorption-based synchrotron X-ray computed tomography (SXCT). It could be evidenced that defects and damages cause pronounced indications in the SXRCT images.
Microstructural changes in porous cordierite for diesel particulate filter applications caused by machining were characterized using microtensile testing and X-ray computed tomography (XCT). Young’s modulus was determined on ~215-380 m thick machined samples by digital image correlation. Results show a decrease of Young’s modulus due to machining of the thin samples. Explanation of this phenomenon was provided by XCT: the presence of debris due to machining and the variation of porosity due to removal of the outer layers were quantified and correlated with the introduction of further microcracking.
The present work offers an explanation for the variation of the power-law stress exponent, n, with the stress r normalized to the shear modulus G in aluminum alloys. The approach is based on the assumption that the dislocation structure generated with deformation has a fractal nature. It fully explains the evolution of n with r/G even beyond the so-called power law breakdown region. Creep data from commercially pure Al99.8%, Al-3.85%Mg, and ingot AA6061 alloy tested at different temperatures and stresses are used to validate the proposed ideas. Finally, it is also shown that the fractal description of the dislocation structure agrees well with current knowledge.
Additive Manufacturing (AM) enables the unique capability of building highly complex parts with integrated functional design. One particular advantageous design feature is known as lattice structures, which provide opportunities for innovative applications in the high-temperature regime of gas turbines. Generally, manufacturing of these structures is already known to be achievable with AM, however proof of structural integrity and geometrical accuracy is not yet reliably established.
In this investigation, a systematic design-follows-complexity approach is utilized to pursue a holistic assessment of Ni based high temperature lattice. As the major element of lattice structures, single struts of different build orientations are investigated at first. This approach includes the application of Computed Tomography (CT), which allows for a non destructive assessment of quality criteria such as porosity and inner geometries as well as the parts’ metrology at a micrometre scale. The applied laboratory CT benefits from high magnification factors around 100 and voxel sizes down to a thousandth of the specimens’ diameter.
Preliminary results show a correlation between the inclination angle and the struts’ quality, which indicate a dependency of geometrical accuracy and structural properties to the AM process setup. Consequently, lattice structures require the development of reliable manufacturing to produce dependable characteristics.
While there is large potential for use of lattice structures in gas turbine and high temperature applications, the results indicate the strong need for an increased understanding of manufacturing and design as well as of the validation methods for these complex lattice structures.
The layer-by-layer Additive Manufacturing (AM) by means of Selective Laser Melting (SLM) offers many prospects regarding the design of a part used in aeroplane components and gas turbines. However, structural deviations from the nominal morphology are unavoidable. The cooling of the finished part leads to shrinkage and a high surface roughness is induced by attached powder particles affecting the part volume too.
The integrity and load-bearing capacity of a SLM produced lattice structure has been investigated by means of in-situ X-ray computed tomography during compression. The lattice structure was compressed by 10 % in height with an applied maximum force of 5 kN. Additionally, a single strut has been investigated ex-situ as a component of the lattice structure. With the higher resolution achieved on the single strut, the pore distribution (size and location) as well as the surface roughness were assessed. The particle and pore size distribution of the raw powder have been investigated, too. One of the main results coming from the in-situ analysis was that the nodes were identified as the weakest points in the lattice structure.
The layer-by-layer Additive Manufacturing (AM) by means of Selective Laser Melting (SLM) offers many prospects regarding the design of a part used in aeroplane components and gas turbines. However, structural deviations from the nominal morphology are unavoidable. The cooling of the finished part leads to shrinkage and a high surface roughness is induced by attached powder particles affecting the part volume too.
The integrity and load-bearing capacity of a SLM produced lattice structure (see Fig.1) has been investigated by means of in-situ X-ray computed tomography during compression. The lattice structure was compressed by 10 % in height with an applied maximum force of 5 kN. Additionally, a single strut has been investigated ex-situ as a component of the lattice structure. With the higher resolution achieved on the single strut, the pore distribution (size and location) as well as the surface roughness were assessed. One of the main results coming from the in-situ analysis was that the nodes were identified as the weakest points in the lattice structure.
During Rutherford cable production the wires are plastically deformed and their initially round shape is distorted. Using X-ray absorption tomography we have determined the 3D shape of an unreacted Nb3Sn 11 T dipole Rutherford cable, and of a reacted and impregnated Nb3Sn cable double stack. State-of-theart image processing was applied to correct for tomographic artefacts caused by the large cable aspect ratio, for the segmentation of the individual wires and subelement bundles inside the wires, and for the calculation of the wire cross sectional area and shape variations. The 11 T dipole cable cross section oscillates by 2% with a frequency of 1.24 mm (1/80 of the transposition pitch length of the 40 wire cable). A comparatively stronger cross sectional area variation is observed in the individual wires at the thin edge of the keystoned cable where the wire aspect ratio is largest.
Thermoelectric properties of doubly substituted La0.95Sr0.05Co1-xCrxO3 (0 ≤ x ≤ 0.5) ceramics
(2018)
Dense La0.95Sr0.05Co1-xCrxO3 (0 ≤ x ≤ 0.5) ceramics were synthesized by solid-state reaction and conventional sintering. Room-temperature crystal structure and microstructure were investigated and the thermoelectric properties were measured in the temperature range 323 K – 1020 K. All compositions are single phase with rhombohedral structure, and the lattice parameter of La0.95Sr0.05Co1-xCrxO3 increases with increasing Cr content.
La0.95Sr0.05Co1-xCrxO3 is a p-type small polaron conductor. The charge carrier concentration is determined by both substitution of La3+ with Sr2+ and thermally-activated charge disproportionation of Co3+ and / or Cr3+. Above 550 K, the substitution of Co with Cr increases the Seebeck coefficient and reduces the electrical conductivity. Below 550 K, the trend of Seebeck coefficient with Cr content is not clear due to the thermally activated charge disproportionation. At low temperature, the electrical conductivity shows a minimum with Cr content of x = 0.4, as a result of trapped polarons in the Cr sites. By substituting Co with Cr, the power factor below 800 K is reduced and that above 800 K is improved.
The thermal conductivity is effectively reduced by doping Cr. The highest ZT value of 0.053 at 373 K is achieved for x = 0, but it decreases rapidly with increasing temperature. Substitution of Co with Cr can effectively improve the ZT values at high temperatures. In the temperature range 700 K – 1000 K, ZT increases with increasing Cr content, the highest being 0.04 at 1000 K for the composition with x = 0.5, more than 4 times the value of the La0.95Sr0.05CoO3 compound.
Two metal matrix composites, both consisting of a near-eutectic cast AlSi12CuMgNi alloy, one reinforced with 15%vol. Al2O3 short fibers and the other with 7%vol. Al2O3 short fibers + 15%vol. SiC particles were studied. Distribution, orientation, and volume fraction of the different phases was determined by means of synchrotron computed tomography. The load partitioning between phases was investigated by in-situ neutron diffraction compression tests. The internal damage of the eutectic Si phase and Al2O3 fibers after ex-situ compression tests was directly observed in CT reconstructed volumes. Significant debonding between Al-matrix and SiC particles was found. Those observations allowed rationalizing the load transfer among the constituent phases of two different composites. Finally, based on the Maxwell scheme, a micro-mechanical model was utilized for the composite with one and two ceramic reinforcements. The model rationalizes the experimental data, and predicts the evolution of principal stresses in each phase.
Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in the bulk of IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.