Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Zeitschriftenartikel (157)
- Vortrag (145)
- Beitrag zu einem Tagungsband (69)
- Posterpräsentation (25)
- Sonstiges (22)
- Buchkapitel (8)
- Forschungsdatensatz (5)
- Tagungsband (Herausgeberschaft für den kompletten Band) (2)
- Beitrag zu einem Sammelband (1)
- Dissertation (1)
Sprache
- Englisch (436) (entfernen)
Schlagworte
- Corrosion (98)
- Geothermal (24)
- Cement (22)
- Durability (18)
- Stainless steel (17)
- Coating (15)
- Concrete (14)
- Polyaniline (14)
- Rheology (14)
- CCUS (13)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (436) (entfernen)
Paper des Monats
- ja (2)
Eingeladener Vortrag
- nein (144)
In the late 1980s, a new type of corrosion appeared in drinking water installations where galvanized steel pipes failed forming a deep groove with no corrosion at the other surfaces. The reason was discussed quite fiercely between failure analysts and material suppliers. In the end the discussion lead to the solution: inductive welded pipes of a certain sulphur content were prone to selective corrosion. The history of the arguments is discussed using old communications between Wilhelm Schwenk and Wolfgang Stichel, who later published the results in a paper unfortunately only I german.
Thus the knowledge got lost and new cases based on the same material problems are observed in application of so-called C-Steel piping systems. Failure cases are shown.
Compared with most common construction materials, fiber reinforced cementitious materials are well known to exhibit better physical, working and mechanical properties. In this study, three fibers were selected: polypropylene fiber (PPF) and polyvinyl alcohol fiber (PVAF), which represented synthetic fibers, and sisal fiber (SF), which represented natural fibers. Effects of these fibers on the flowability, rheological properties, and adsorption behavior of the cement paste with polycarboxylate superplasticizer (PCE) were investigated. Furthermore, the above experimental results were verified by measuring the contact angle of the fiber with water and PCE solution and the apparent morphology of the fiber. Results revealed that the addition of fibers significantly reduces the fluidity of the cement paste, while the yield stress and plastic viscosity of the cement paste increase with the addition of fibers. From the contact angle and scanning electron microscope, the surface of SF was relatively rough, and the contact angle of SF with water or PCE solution was the smallest. It can be concluded that the plant fiber has a significant influence on the fluidity and rheology of cement paste.
Nowadays, various polymeric materials are used in E&E applications with sufficient flame retardance by adding rather different flame retardants. It doesn’t matter whether cables are used outdoor or are installed indoor as building products, the weathering exposures such as UV radiation, humidity and variation in temperature occur and influence the flame-retardant property. Recently, the lifetime of the flame retardance itself becomes an increasingly important factor. In this work, several devices were used to perform accelerated artificial ageing simulating different environment exposures.
The comprehensive and global understanding of the durability of flame retardance in dependence on the weathering or ageing conditions is still a matter of discussion. Therefore, the weathering resistance of various halogen-free fire-retarded polymers was investigated in this work. Polymeric systems with different kinds of fire retardants were chosen, including various fire retardant mechanisms. Ethylene Vinyl Acetate (EVA) blends with high amounts of inorganic flame retardant such as aluminum hydroxide (ATH), boehmite and synergists, which mainly dilutes the polymer resin work as heat sink and cooling agent, and enhance residue formation was examined. Thermoplastic Polyurethane (TPU) was modified with melamine cyanurate (MC), which mainly acts by changed melt flow and dripping behavior as well as fuel dilution. Additionally, aluminum diethylphosphinate and boehmite are induced as assistant flame retardant. Furthermore, glass fiber reinforced Polyamide 66 (PA) was investigated containing different kinds of aluminum diethylphosphinate based flame retardant mixtures, which acts by flame inhibition and additional char formation.
The degradation of the surface was analyzed after the different weathering conditions. Most of the specimens exhibited an intensive material degradation at the top surface accompanied by a distinct discoloration, e.g. getting darker or showing yellowing. The weathering of the EVA samples lead to numerous cracks (already) after 4000 h. The corresponding changes in the chemical structure was investigated by ATR FT-IR for all materials.
The flammability was investigated by cone calorimeter, UL-94 burning chamber, and oxygen index (LOI) using plate and bar specimens. The flame retardance of most of the materials studied degrades only slightly or were rather stable for the investigated exposure times. Interestingly, also some opposite results were found. EVA modified by different inorganic flame retardants such as ATH achieved higher LOI after exposing in the humidity chamber and the accelerated oxidation under water in the autoclaves. It is suggested that the particle size of ATH and boehmite plays an important role, when these flame retardants agglomerate at the surface during accelerated weathering.
Both materials, EVA and TPU, were also investigated as cable jackets. While EVA modified with inorganic flame retardants exhibits low-smoke and non-dripping fire behavior, TPU flame-retarded with MC yields cables with pronounced melt-dripping. Cone calorimeter tests were carried out using cable rafts of the size of 100 mm * 100 mm as well as our self-made cable module test, which simulates the vertical full-scale test of a bundle of cables at the bench-scale. Both methods were used to investigate the weathering resistance of the flame retardance in cables. The results of the cable module test for the flame-retarded EVA cables were only slightly affected even when a long time hydrothermal ageing was carried out. This is because of inorganic residue which just delays the fire growth but does not extinguish. However, for the flame-retarded TPU cable jackets, the cable module test exhibited an accelerated fire spread and a melt-dripping behavior which was promoted by weathering exposure.
Water migration in one-side heated concrete: 4D in-situ CT monitoring of the moisture-clog-effect
(2019)
Explosive spalling due to fire exposure in concrete structures can lead severe damage and, in the worst case, to premature component failure. For this reason, an in situ investigation of water Migration in concrete due to surface heating was undertaken.
During these experiments, a miniaturized concrete specimen within a confining and insulating double-hull was subjected to surface heating during simultaneous X-ray computed tomography (CT) scanning. Through the use of subtraction-based Image analysis techniques, it was possible to observe and quantify not only drying within areas of the concrete matrix close to the heated surface, but also the migration of moisture to both pore and matrix regions deeper within the specimen. It was also discovered that the correction of CT images for specimen deformation using DVC and variable detector performance using calibrated image filters significantly improved the quality of the results. This clearly demonstrates the potential of X-ray CT for evaluation of other rapid-density-change phenomena in concrete and other building materials.
Water Migration in One-Side Heated Concrete: 4D In-Situ CT Monitoring of the Moisture-Clog-Effect
(2018)
In order to study damage in concrete exposed to fire, a series of continuous X-ray computed tomography (CT) measurements were performed on a concrete sample heated, in-situ, on one side. The water migration relative to time and 3D space and, in particular, the dynamic condensation and vaporization of water droplets in the pores was quantified. This approach shows significant potential for further investigation of fire-related concrete damage.
Viscosity modifying agents: Key components of advanced cement-based materials with adapted rheology
(2022)
Viscosity modifying agents (VMAs) are essential ingredients for the production of flowable cement-based materials. This paper presents an overview of commonly used VMAs and attempts to shed some light on the underlying physics at the origin of their mechanisms of action. The main molecular parameters of VMA controlling the rheological properties of the cement pore solution are highlighted. As the mechanisms of action of VMAs in cement-based materials are closely related to their affinity with the surface of cement particles, the adsorption of the main VMA types is discussed. The effect of VMAs on flow properties and stability of cement-based materials is presented for VMAs added without any superplasticizer, and then in systems incorporating both VMAs and superplasticizers. Finally, the effect of VMAs in enhancing concrete properties to secure adequate performance of different construction applications, and perspectives for future developments of novel cement-based materials made with VMAs are showcased.
Polymers with intrinsic microporosity are promising candidates for the active separation layer in gas separation membranes. Here, by means of inelastic neutron scattering, the vibrational density of states (VDOS) and the molecular mobility were investigated for PIM-1, the prototypical polymer with intrinsic microporosity. The results are compared to data measured for a more conventional high-performance polyimide used in gas separation membranes (Matrimid).
The measured data show the characteristic low frequency excess contribution to the VDOS above the Debye sound wave level, generally known as the Boson peak in glass-forming materials. In comparison to the Boson peak of Matrimid, that of PIM-1 is shifted to lower frequencies. This shift is discussed considering the microporous, sponge-like structure of PIM-1 as providing a higher compressibility at the molecular scale than for conventional polymers.
Elastic fixed window scans were measured on a neutron backscattering spectrometer to have an overview about the molecular dynamics at a time scale of ca. 1 ns. The temperature dependence of the estimated mean squared displacement shows a step-like increase in the temperature range from 100 K to 250 K indicating the onset of some molecular mobility. The nature of this motional process was analyzed in detail by quasielastic neutron scattering where the data are discussed with regard to both the q- and the temperature dependence.
Utilisation of alkali-sensitive aggregates for concrete pavements by internal hydrophobisation
(2021)
In order to avoid the increased ASR damage to concrete pavements in the German motorway network in the future, the ARS 04/2013 introduced mandatory suitability tests to exclude alkali-sensitive aggregates in new construction measures. This resulted in a significant reduction of suitable aggregates. Against this background, borderline alkali-sensitive aggregates are to be made usable by adding an internal water repellent agent during concrete casting. The ASR avoidance strategy is based on the significant reduction of the penetration of water and de-icing salt solution into the concrete pavement. Laboratory tests show that, with a suitable active ingredient, the ASR damage process can be significantly reduced with internal hydrophobisation. The disadvantage is that this is associated with a deterioration of the mechanical properties and the resistance to freeze-thaw with de-icing salt. The aim of the ongoing research is to reduce these disadvantages through targeted modification of the hydrophobising agent and air-entraining agent.