In this talk, the evolution of the demand for engineering applications of neutrons at the ILL in the last 10 years is presented. It is shown that small angle neutron scattering and diffraction are highly demanded by the materials science community. Further development in the field is foreseen, with the use of in-situ (furnace, tension/compression rig, humidity cells, etc.) techniques to associate to the neutron techniques.
The Influence of the Temperature Gradient on the Distribution of Residual Stresses in AM AISI 316L
(2019)
Steep temperature gradients and solidification shrinkage are the main contributors to the formation of residual stresses in additively manufactured metallic parts produced by laser beam melting. The aim of this work was to determine the influence of the temperature gradient.
Diffraction results show a similar pattern for both specimens, indicating the shrinkage to be more dominant for the distribution of residual stresses than the temperature gradient. Thermography results imply that a higher energy input result in higher compressive residual stresses in the bulk.
The evolution of the internal strains during in situ tension and compression tests has been
measured in an MgY2Zn1 alloy containing long-period stacking ordered (LPSO) phase using
neutron diffraction. The alloy was extruded at two different temperatures to study the influence
of the microstructure and texture of the magnesium and the LPSO phases on the deformation
mechanisms. The alloy extruded at 623 K (350 °C) exhibits a strong fiber texture with the basal
plane parallel to the extrusion direction due to the presence of areas of coarse non-recrystallised
grains. However, at 723 K (450 °C), the magnesium phase is fully recrystallised with grains
randomly oriented. On the other hand, at the two extrusion temperatures, the LPSO phase
orients their basal plane parallel to the extrusion direction. Yield stress is always slightly higher
in compression than in tension. Independently on the stress sign and the extrusion temperature,
the beginning of plasticity is controlled by the activation of the basal slip system in the dynamic
recrystallized grains. Therefore, the elongated fiber-shaped LPSO phase which behaves as the
reinforcement in a metal matrix composite is responsible for this tension–compression asymmetry.
The combination of tomographic, microstructural data with other experimental techniques and with modeling is paramount, if we want to extract the maximum amount of information on material and component properties. In particular, quantitative image analysis, statistical approaches, direct discretization of tomographic reconstructions represent concrete possibilities to extend the power of the tomographic 3D representation to insights into the material and component performance. This logic thread equally holds for industrial and academic research, and valorizes expensive experiments such as those carried out at synchrotron sources, which cannot be daily repeated.
I will show a few examples of possible use of X-ray tomographic data for quantitative assessment of damage evolution and microstructural properties, as well as for non-destructive testing. Examples of micro-structured inhomogeneous materials will be given, such as Composites, Ceramics, Concrete, and Additively manufactured parts. I will also show how X-ray refraction computed tomography (CT) can be highly complementary to classic absorption CT, being sensitive to internal interfaces.
Additionally, I will present a new technique in our portfolio, Neutron Diffraction, which is extremely well suited to the study of internal stresses, both residual and under external load.
Quantitative image analysis, statistical approaches, direct discretization of tomographic reconstructions represent concrete possibilities to extend the power of the tomographic 3D representation to insights into the material and component performance. I will show a few examples of possible use of X-ray tomographic data for quantitative assessment of damage evolution and microstructural properties, as well as for non-destructive testing, with particular focus on additively manufactured materials. I will also show how X-ray refraction computed tomography (CT) and Neutron diffraction can be highly complementary to classic absorption CT, being sensitive to internal interfaces and residual stress analysis, respectively.
Internal damage of an AlSi12CuMgNi alloy reinforced with planar random short fibres has been investigated after compression. This damage strongly influences the load partition between matrix and reinforcement. For fibres perpendicular to the applied load, breakage and interconnected cracks appear in significantly higher volume fraction than with fibres parallel to load.