Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Zeitschriftenartikel (2)
- Beitrag zu einem Tagungsband (1)
- Dissertation (1)
- Vortrag (1)
Schlagworte
- Pressure vessel (3)
- Composite (2)
- Degradation (2)
- Modal analysis (2)
- Acoustic emission analysis (1)
- Additive manufacturing (1)
- Aging (1)
- Alterung (1)
- Carbon (1)
- Composite material (1)
- Distributed fiber optic sensing (1)
- Druckbehälter (1)
- Eigenspannung (1)
- Faserverbund (1)
- Fibre reinforced plastics (1)
- Hybrid composite pressure vessel (1)
- Komposit (1)
- Photopolymer (1)
- Porous materials (1)
- Residual stress (1)
- Structural health monitoring (1)
- Transport limitations (1)
Organisationseinheit der BAM
- 3.5 Sicherheit von Gasspeichern (5) (entfernen)
Eingeladener Vortrag
- nein (1)
Degradation and damage analysis of composite pressure vessels via experimental modal analysis
(2023)
For mobile gas storage systems, the application of type IV pressure vessels is state of the art. Type IV tanks consist of an inner polymer liner fully wrapped with fibre-reinforced plastic (FRP). Because of the complex fabric of the FRP as well as a difficulty estimable interaction behaviour between the single components under load, there are still no satisfying non-destructive testing methods to assess the current state of failure nor to estimate the level of degradation accurately and economically. At BAM division 3.5, analysing the ageing process of mobile composite pressure vessels is a major task to ensure safe usage over the whole lifetime. In this context, key aspects of our ongoing research activities are the invention of new test procedures and the development of accurate lifetime prediction models. In order to determine the level of degradation or damage, one meaningful non-destructive approach is to analyse the structural dynamic behaviour via an experimental modal analysis (EMA). Over the last few years, different types and sizes of composite pressure vessels have been tested in several research projects. The presented paper gives an insight into how to extract and interpret modal parameters and how to fit them to the results of residual strength tests.
Degradation and damage analysis of composite pressure vessels via experimental modal analysis
(2023)
For mobile gas storage systems, the application of type IV pressure vessels is state of the art. Type IV tanks consist of an inner polymer liner fully wrapped with fibre-reinforced plastic (FRP). Because of the complex fabric of the FRP as well as a difficulty estimable interaction behaviour between the single components under load, there are still no satisfying non-destructive testing methods to assess the current state of failure nor to estimate the level of degradation accurately and economically. At BAM division 3.5, analysing the ageing process of mobile composite pressure vessels is a major task to ensure safe usage over the whole lifetime. In this context, key aspects of our ongoing research activities are the invention of new test procedures and the development of accurate lifetime prediction models. In order to determine the level of degradation or damage, one meaningful non-destructive approach is to analyse the structural dynamic behaviour via an experimental modal analysis (EMA). Over the last few years, different types and sizes of composite pressure vessels have been tested in several research projects. The presented paper gives an insight into how to extract and interpret modal parameters and how to fit them to the results of residual strength tests.
Photopolymer derived carbon grows in popularity, yet the range in available feature sizes is limited. Here we focus on expanding the field to low surface to volume ratio (SVR) structures. We describe a high temperature acrylic photopolymerizable precursor with FTIR and DSC and develop a thermal inert-gas treatment for producing architected carbon in the mm scale with SVR of 1.38 x10-3 μm-1. Based on TGA and MS, we distinguish two thermal regimes with activation energies of ~79 and 169 kJ mol-1, which we reason with mechanisms during the polymer’s morphologic conversion between 300 - 500 °C. The temperature range of the major dimensional shrinkage (300-440 °C, 50%) does not match the range of the largest alteration in elemental composition (440-600 °C, O/C 0.25-0.087%). The insights lead to an optimized thermal treatment with an initial ramp (2 °C min-1 to 350 °C), isothermal hold (14h), post hold ramp (0.5 °C min-1 to 440 °C) and final ramp (10 °C min-1 to 1000 °C). The resulting carbon structures are dimensionally stable, non-porous at the μm scale, and comprise an unprecedented variation in feature sizes (from mm to μm scale). The findings shall advance architected carbon to industrially relevant scales.
Bei der Auslegung von Druckbehältern kommen, auf Grund ihrer hohen spezifischen Festigkeit, vermehrt Faserverbundwerkstoffe zum Einsatz. Durch eine hohe Streuung von Material- und Produktionsparametern sowie unterschiedlichster Belastungsszenarien gestaltet sich jedoch Aussagen über die Lebensdauer sowie eine Festlegung sinnvoller Prüffristen als schwierig. Im Fokus der Untersuchungen steht ein Behälterdesign mit metallischem Liner und einem kohlenstofffaserverstärkten Kunststoffverbund, wobei die Lebensdauer maßgeblich durch den im Metall vorherrschenden Eigenspannungszustand bestimmt wird. Mit Hilfe einer alterungsbegleitenden Eigenspannungsanalyse werden Eigenspannungsveränderungen erfasst und in einem erarbeiteten Betriebsfestigkeitsmodell berücksichtigt. Durch eine Nachstellung verschiedener Belastungsszenarien kann gezeigt werden, dass durch die Berücksichtigung einer veränderlichen Eigenspannung die Anzahl ertragbarer Lastwechsel bis zum Versagen sowie damit verbundene Überlebenswahrscheinlichkeiten mit einer erhöhten Genauigkeit abgeschätzt werden können.
We present the results of distributed fiber optic strain sensing for condition monitoring of a hybrid type IV composite fully wrapped pressure vessel using multilayer integrated optical fibers. Distributed strain sensing was performed for a total number of 252,000 load cycles until burst of the vessel. During this ageing test material fatigue could be monitored and spatially localized. Critical material changes were detected 17,000 cycles before material failure. Results have been validated by acoustic emission analysis.