Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Posterpräsentation (60) (entfernen)
Referierte Publikation
- nein (60)
Schlagworte
- Additive manufacturing (15)
- Additive Manufacturing (11)
- Computed tomography (11)
- Laser powder bed fusion (7)
- Computed Tomography (6)
- Residual stress (6)
- X-ray refraction (6)
- Microstructure (4)
- AlSi10Mg (3)
- Laser Powder Bed Fusion (3)
Organisationseinheit der BAM
- 8.5 Röntgenbildgebung (60) (entfernen)
The understanding of process-microstructure-property-performance (PMPP) relationships in additive manufacturing (AM) of metals is highly necessary to achieve wide-spread industrial application and replace conventionally manufactured parts, especially regarding safety-relevant applications. To achieve this understanding, reliable data and knowledge regarding material’s microstructure-property relationships (e.g. the role of defects) is needed, since it represents the base for future more targeted process optimizations and more reliable calculations of performance. However, producing reliable material data and assessing the AM material behaviour is not an easy task: big challenges are e.g. the actual lack of standard testing methods for AM materials and the occasional difficulties in finding one-to-one comparable material data for the conventional counterpart.
This work aims to contribute to end this lack of reliable material data and knowledge for the low cycle fatigue behaviour of the most used titanium alloy in aerospace applications (Ti-6Al-4V). For this purpose, two sets of test specimens were investigated. The first set was manufactured from cylindrical rods produced by an optimized DED-L process and the second was manufactured from a hot formed round bar. The test specimens were cyclically loaded until failure in the low-cycle-fatigue (LCF) regime. The tests were carried out according to ISO 12106 between 0.3 to 1.0 % axial strain amplitude from room temperature up to 400°C. The LCF behaviour is described and compared between materials and with literature values based on cyclic deformation curves and strain-based fatigue life curves. Besides, the parameters of Manson-Coffin-Basquin relationship were calculated. The microstructures (initial and after failure) and fracture surfaces were comparative characterized. Thereby, the focus lied on understanding the role of grain morphology and defects on the failure mechanisms and fatigue lifetimes. For this latter characterization, optical microscopy (OM), scanning electron microscopy (SEM) and micro computed tomography (µCT) were used.
The subsurface residual stress in laser powder bed fused 316L structures was analyzed using X-ray diffraction (XRD) and layer removal. The influence of varying structure thicknesses was investigated. In this study the importance of combining surface roughness measurements with XRD was shown. Moreover, a clear relation between the structure thickness and the subsurface residual stress profiles was observed.
Fibre-Matrix-Debonding in glass fibre reinforced dental posts can play an important role for their mechanical performance and long term stability… We show that synchrotron X-ray refraction radiography (SXRR) allows analysis of large samples (up to several millimetres) without compromising the detectability of sub micrometer defects.
Als bildgebendes und zerstörungsfreies Verfahren eignet sich die Röntgen-Computertomographie (CT) insbesondere bei der Untersuchung von Kunst- und Kulturgütern. Die für Werkstoffprüfung und Materialanalyse konzipierten CT-Anlagen bieten dank hoher Röntgenleistung die Möglichkeit zusätzlich zu Holz, Keramiken und Kunststoffen auch stark schwächende Materialien, wie bspw. Metalle, zu durchdringen. Für eine hohe räumliche Auflösung im unteren Mikrometerbereich (2-200µm) sorgen entsprechend ausgelegte CT-Anlagen. In der Bundesanstalt für Materialforschung und -prüfung (BAM) stehen mehrere solcher CT-Anlagen für unterschiedliche Fragestellungen sowie Probengrößen und - materialien zur Verfügung. Einige Beispiele aus den vergangenen Arbeiten der BAM veranschaulichen das große Potential dieser Untersuchungsmethode.
Da bei einer CT-Messung in der Regel das gesamte Untersuchungsobjekt erfasst und in ein digitales Volumenmodell überführt wird, eröffnet sich für Archäologen und Restoratoren die Möglichkeit Untersuchungen hinsichtlich Materialzusammensetzung, Erhaltungszustand und Herstellungstechnik am virtuellen Objekt vorzunehmen, ohne die Originalsubstanz zu beeinträchtigen. Gegenüber der klassischen Radiografie, bei der nur eine zweidimensionale Abbildung erreicht wird, bietet die CT-Untersuchung die Möglichkeit innenliegende Strukturen dreidimensional zu erfassen. Die notwendige Bestimmung der Objektoberfläche erlaubt zudem die Erstellung eines Oberflächenmodells des untersuchten Gegenstandes. Damit lassen sich unter anderem mechanische Simulationen (Belastung, Durchbiegung, Durchströmung) durchführen. Der erzeugte Datensatz kann somit auch zur Herstellung eines Replikats im 3D-Druckverfahren genutzt werden. Anhand der Untersuchung der Mandoline von Smorsone wird gezeigt, wie eine CT-Messung durchgeführt wird und wie in dem anschließend rekonstruierten 3D-Datensatz mittels Koordinatenmesstechnik Maße (Abstände, Wandstärken, Winkel) exakt ermittelt werden können.
The Influence of the Temperature Gradient on the Distribution of Residual Stresses in AM AISI 316L
(2019)
Steep temperature gradients and solidification shrinkage are the main contributors to the formation of residual stresses in additively manufactured metallic parts produced by laser beam melting. The aim of this work was to determine the influence of the temperature gradient.
Diffraction results show a similar pattern for both specimens, indicating the shrinkage to be more dominant for the distribution of residual stresses than the temperature gradient. Thermography results imply that a higher energy input result in higher compressive residual stresses in the bulk.
µCT is used to validate the capability of online monitoring for in-situ detection of defects during the L-PBF build process, which is a focus of the TF project ProMoAM.
Our first experiments show that online monitoring using thermography and optical tomography cameras are able to detect defects in the built part. But further research is needed to understand root cause of the correlation.
Rapid cooling rates and steep temperature gradients are characteristic of additively manufactured parts and important factors for the residual stress formation. This study examined the influence of heat accumulation on the distribution of residual stress in two prisms produced by Laser Powder Bed Fusion (LPBF) of austenitic stainless steel 316L. The layers of the prisms were exposed using two different border fill scan strategies: one scanned from the centre to the perimeter and the other from the perimeter to the centre. The goal was to reveal the effect of different heat inputs on samples featuring the same solidification shrinkage. Residual stress was characterised in one plane perpendicular to the building direction at the mid height using Neutron and Lab X-ray diffraction. Thermography data obtained during the build process were analysed in order to correlate the cooling rates and apparent surface temperatures with the residual stress results. Optical microscopy and micro computed tomography were used to correlate defect populations with the residual stress distribution. The two scanning strategies led to residual stress distributions that were typical for additively manufactured components: compressive stresses in the bulk and tensile stresses at the surface. However, due to the different heat accumulation, the maximum residual stress levels differed. We concluded that solidification shrinkage plays a major role in determining the shape of the residual stress distribution, while the temperature gradient mechanism appears to determine the magnitude of peak residual stresses.
The layer-by-layer Additive Manufacturing (AM) by means of Selective Laser Melting (SLM) offers many prospects regarding the design of a part used in aeroplane components and gas turbines. However, structural deviations from the nominal morphology are unavoidable. The cooling of the finished part leads to shrinkage and a high surface roughness is induced by attached powder particles affecting the part volume too.
The integrity and load-bearing capacity of a SLM produced lattice structure (see Fig.1) has been investigated by means of in-situ X-ray computed tomography during compression. The lattice structure was compressed by 10 % in height with an applied maximum force of 5 kN. Additionally, a single strut has been investigated ex-situ as a component of the lattice structure. With the higher resolution achieved on the single strut, the pore distribution (size and location) as well as the surface roughness were assessed. One of the main results coming from the in-situ analysis was that the nodes were identified as the weakest points in the lattice structure.
In this work, the structural integrity of LBM fabricated IN625 small cylinders (d = 1 mm, h = 6 mm) was investigated regarding the porosity and the surface roughness by means of computed tomography. The measurements were carried out on a GE v|tome|x L 300/180 with a reconstructed voxel size of 2 µm. The pores were analyzed for size, shape and spatial distribution. The correlation between compactness C and spatial distribution showed that elongated pores (C < 0.2) appear exclusively within a distance of 80 µm to the sample surface. The reconstructed surface was digitally meshed and unwrapped to evaluate the mean roughness Ra. Since the gravity correlates linearly with the sine of the build angle, the influence of gravity on porosity and surface roughness was determined.
Ziel der Untersuchung: Evaluation der Eignung der Refraktions-Tomographie zur Analyse von Alterungserscheinungen innerhalb von adhäsiv verankerten Materialien vor und nach künstlicher Probenalterung.
Material und Methode: Vier humane mittlere Oberkieferfrontzähne wurden wurzelkanalbehandelt und ausgedehnte Klasse IV Defekte der Krone mit einer Aufbaufüllung aus dualhärtendem Komposit (Rebilda DC, VOCO) und einem Glasfaserstift (Rebilda Post, VOCO) restauriert. Alle Proben wurden feucht gelagert und in einer Synchrotron-Einrichtung (BAMline, BESSY II, HZB) mit einer Pixelgröße von 4,08 µm gescannt. Für diese Synchrotron-Refraktions-Tomographie (SXRCT) muss zunächst der Analysatorkristall (AK) zu einer Bragg-Reflexion (Beugung) angeregt werden, um eine SXRCT durchzuführen. Die SXRCT wird mit einer Transmissions-Tomographie (ohne AK) verrechnet. Darauf folgte eine künstliche Probenalterung mit 400.000 Kau- und 3.000 Thermozyklen (50N, 5-55°C). Anschließend wurden die Proben ein weiteres Mal gescannt. Die Datensätze beider SXRCT wurden mittels des „filtered back projection“ Algorithmus rekonstruiert, mit einer Bildanalyse-Software aufeinander registriert und ausgewertet. Hierdurch konnten die Veränderungen initialer Schädigungen analysiert werden.
Ergebnisse: Alle 4 Proben zeigten in den Scans Veränderungen des inneren Gefüges und an Grenzflächen nach Belastung. Es zeigten sich Ansammlungen von Wasser innerhalb eingeschlossener Hohlräume, subkritisches Risswachstum, Ausdehnung des Komposit und Quellung des Glasfaserstiftes um 0,4%. In den SXRCT Aufnahmen waren außerdem Dentintubuli, die bei Auflösungen von 4,08 µm sonst nicht deutlich sichtbar sind darstellbar. Dadurch konnte Eindringen von Wasser in die Tubuli im Anschluss an die Alterung belegt werden.
Zusammenfassung: SXRCT bietet die Möglichkeit, trotz einer vergleichbar geringen Auflösung, kleinste Strukturen und Veränderungen abzubilden. Dies ermöglicht unter anderem die detaillierte Analyse relativ großer Proben, wie eines vollständigen Zahnes in einem Scanvorgang.