Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Zeitschriftenartikel (23)
- Vortrag (22)
- Posterpräsentation (13)
- Beitrag zu einem Tagungsband (4)
- Dissertation (2)
Sprache
- Englisch (64) (entfernen)
Schlagworte
- Computed tomography (64) (entfernen)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (47)
- 8.5 Röntgenbildgebung (47)
- 9 Komponentensicherheit (6)
- 8.0 Abteilungsleitung und andere (5)
- 5 Werkstofftechnik (3)
- 9.3 Schweißtechnische Fertigungsverfahren (3)
- 9.4 Integrität von Schweißverbindungen (3)
- 5.2 Metallische Hochtemperaturwerkstoffe (2)
- 7 Bauwerkssicherheit (2)
- 7.1 Baustoffe (2)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (22)
Rapid cooling rates and steep temperature gradients are characteristic of additively manufactured parts and important factors for the residual stress formation. This study examined the influence of heat accumulation on the distribution of residual stress in two prisms produced by Laser Powder Bed Fusion (LPBF) of austenitic stainless steel 316L. The layers of the prisms were exposed using two different border fill scan strategies: one scanned from the centre to the perimeter and the other from the perimeter to the centre. The goal was to reveal the effect of different heat inputs on samples featuring the same solidification shrinkage. Residual stress was characterised in one plane perpendicular to the building direction at the mid height using Neutron and Lab X-ray diffraction. Thermography data obtained during the build process were analysed in order to correlate the cooling rates and apparent surface temperatures with the residual stress results. Optical microscopy and micro computed tomography were used to correlate defect populations with the residual stress distribution. The two scanning strategies led to residual stress distributions that were typical for additively manufactured components: compressive stresses in the bulk and tensile stresses at the surface. However, due to the different heat accumulation, the maximum residual stress levels differed. We concluded that solidification shrinkage plays a major role in determining the shape of the residual stress distribution, while the temperature gradient mechanism appears to determine the magnitude of peak residual stresses.
Additive manufacturing (AM) of metals and in particular laser powder bed fusion (LPBF) enables a degree of freedom in design unparalleled by conventional subtractive methods. To ensure that the designed precision is matched by the produced LPBF parts, a full understanding of the interaction between the laser and the feedstock powder is needed. It has been shown that the laser also melts subjacent layers of material underneath. This effect plays a key role when designing small cavities or overhanging structures, because, in these cases, the material underneath is feed-stock powder. In this study, we quantify the extension of the melt pool during laser illumination of powder layers and the defect spatial distribution in a cylindrical specimen. During the LPBF process, several layers were intentionally not exposed to the laser beam at various locations, while the build process was monitored by thermography and optical tomography. The cylinder was finally scanned by X-ray computed tomography (XCT). To correlate the positions of the unmolten layers in the part, a staircase was manufactured around the cylinder for easier registration. The results show that healing among layers occurs if a scan strategy is applied, where the orientation of the hatches is changed for each subsequent layer. They also show that small pores and surface roughness of solidified material below a thick layer of unmolten material (>200 µm) serve as seeding points for larger voids. The orientation of the first two layers fully exposed after a thick layer of unmolten powder shapes the orientation of these voids, created by a lack of fusion.
The low tensile strength of cement-based materials can be improved by the addition of fibres. In a joint research project, an industrial partner designed special coatings for polymer and carbon fibres by integrating surfactants and hydrophilic compounds. Aim of the developed functionalization was to ensure an even coverage of the fibre surfaces and to anchor them chemically in the cement-based matrix. Task of the BAM was to quantify the effect of the improved bond. In a first step a workable mortar adjusted to the strength of the tested fibres was developed and the fibre distribution assessed by light microscopy and computed tomography. To test the new coating for its efficiency to prevent cracking during hardening and to improve the loadbearing behaviour new test setups were developed or existing methods were adjusted.
The experiments showed that the functionalization leads to a reduction of the crack area measured after the exposure of the wet mortar to strong drying conditions in the wind channel. Regarding the Efficiency to mitigate shrinkage cracks the functionalisation turned out to be more efficient for fibres made from polyacrylonitrile (PAN) than for carbon fibres. An improvement of the tensile strength after cracking of the cementitious matrix could only be documented for the coated carbon fibres. It could be quantified, however, only in the three-point bending tests because the fibres turned out to be too brittle for the applied single fibre pull-through test.
The microstructure of an apatite-wollastonite (code name AP40) glass-ceramic is analyzed in this study by combining 2D microscopy, phase analysis, X-ray absorption and synchrotron X-ray refraction computed tomography (XCT and SXRCT, respectively). It is shown that this combination provides a useful toolbox to characterize the global microstructure in a wide scale range, from sub-micrometer to millimeter. The material displays a complex microstructure comprising a glassy matrix with embedded fluorapatite and wollastonite small crystals. In this matrix, large (up to 200 μm) spike-shaped structures are distributed. Such microstructural features are oriented around a central sphere, thereby forming a structure resembling a sea urchin. A unique feature of SXRCT, in contrast to XCT, is that internal interfaces are visualized; this allows one to show the 3D distribution of these urchins with exceptionally good contrast. Furthermore, it is revealed that the spike-shaped structures are not single crystals, but rather composed of sub-micrometric crystals, which are identified as fluorapatite and diopside phases by SEM-EDX analysis.