Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
Sprache
- Englisch (8) (entfernen)
Schlagworte
- Fatigue (4)
- Concrete (2)
- Damage evolution (2)
- High-cycle (2)
- High-strength concrete (2)
- Photogrammetry (2)
- Size effect (2)
- Ultrasonic testing (2)
- Acoustic emission testing (1)
- Compressive Cyclic loading (1)
Organisationseinheit der BAM
Severe mechanical fatigue conditions for worldwide proliferating windfarms are a Major challenge for high-performance concrete in towers, connecting joints and foundations of wind turbines. High-performance concrete offers potential for the application in offshore windfarms, not only regarding its good mechanical, but also chemical resistivity due to low diffusivity in the highly densified microstructure. For a more reliable fatigue assessment, monitoring based on nondestructive testing can be a valuable complement to design rules. Both approaches demand reliable experimental data, information about scalability and the development of standardized testing methods. This article presents results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung), which is a part of a joint national project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject implemented by BAM examines the fatigue behavior in dependence of size and slenderness for varying concrete strength at different stress levels. Besides fatigue strength, nondestructive testing is carried out additionally.
Methods used are strain measurement and ultrasonic testing. The change of strain, stiffness and ultrasonic pulse velocity in the fatigue process is discussed. Results disclose a deeper insight into the damage process under cyclic loading of high-performance concrete and contribute to improve nondestructive monitoring.
The worldwide spread of windfarms brings new challenges, especially for concrete structures as a part of towers, connecting joints and foundations of wind turbines. High-cyclic loadings in such structures lead to a high relevance of the subject of fatigue. A proper assessment of the fatigue strength of concrete demands therefore a basis of reliable experimental data and the development of standardized testing methods. This article presents first results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung) which is a part of a joint project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject investigates the effects of size and slenderness of the specimens on the fatigue behaviour of high strength concrete at different stress levels. Not only the fatigue strength, but also the fatigue process itself is monitored by means of several measurement methods. Strain measurements are used to calculate the load dependent elastic modulus in the fatigue hysteresis as indicators for fatigue development. Furthermore, the application of non-destructive methods like acoustic emission analysis and ultrasonic measurement in laboratory tests gives a deeper insight into damage processes under cyclic loading. The results shall be used to improve design rules for concrete members under fatigue load and to develop or improve non-destructive techniques for in-service structural health monitoring.
Within a current research project which is funded by the German Research Foundation (DFG) the influence of the size and the geometry of specimens on the spalling result in fire tests is going to be investigated at Bundesanstalt für Materialforschung und -prüfung (BAM). This paper describes some preliminary results and a newly developed test setup. The novel setup enables the efficient and precise quantification of spalling by using a special photogrammetric measurement system.
Industrial wastes (bottom ash, crushed concrete fines, filter residue, paper ash and lignite fly ash) have potential for use in building materials, for instance as raw materials for clinker production, as supplementary cementitious materials (SCMs) or mineral additions in concrete. The properties of the products are dependent on the reactivity of the waste materials used, which can be classified as inert, latent hydraulic or pozzolanic. In this study, waste materials were first characterised. This was followed by theoretical considerations of the mentioned application options. Experiments were limited to evaluation of potential as SCMs and, for this purpose, activity index measurements and calorimetric and thermogravimetric analyses were performed. Finally, the synergetic effects of various waste materials were considered. Paper ash (calcium oxide source) and filter residue (amorphous silicon dioxide source) showed the best prospects for use as cementitious material components.
The current knowledge about fatigue behavior of concrete is still incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Therefore, the process of fatigue itself under cyclic compressive loading was investigated in a systematic and comprehensive way. The aim of this investigation was to obtain a deeper insight and to provide a better understanding of the damage process occurring within the material during fatigue loading. Concrete cylinders were tested with a number of cycles to failure between 106 and 107. To investigate macroscopic and microscopic changes in the material, various methods of non-destructive and destructive testing were used. One main result was, in contrast to other authors, that the investigated changes in macroscopic material behavior could not be explained only by a development of micro-cracks. The results indicated rather, that the related changes in the fatigue behavior are mainly a result of viscous processes in the hardened cement paste, similar to the processes of creep. Based on the experimental results a description of the possible processes was derived which take place in the material structure during fatigue loading and also leads to the observed macroscopic changes in the material behavior. In this context, the results have shown that in case of isotropic material behavior a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain-relationship caused by fatigue.
Fatigue is of relevance not only for metals but also for concrete. The current knowledge about fatigue behaviour of concrete is, however, incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Some macroscopic effects of this process are well known but the governing material changes behind them are still less studied. The focus of the present contribution lay on a systematic and comprehensive investigation of the fatigue process under cyclic compressive loading. The aim was to obtain a deeper insight and to provide a better understanding of the damage process in the material. Cylindrical specimens were tested with a number of cycles to failure between 106 and 107. Various methods of non-destructive and destructive testing were used to investigate macroscopic and microscopic changes in the material. One main result was that the changes in the macroscopic material behaviour could not be explained only by the development of micro cracks. The results indicated that the related changes in the fatigue behaviour originate rather from viscous processes in the cement stone, similar to the process of creep. A sound description of the possible processes was derived from the obtained experimental results which concerns material structure during fatigue loading. It has been shown that in case of isotropic material behaviour a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain relationship caused by fatigue.
The modeling and prediction of the behavior of reinforced concrete under impact load is still an engineering challenge. The scientific community has put a lot of effort into the development of this knowledge, especially after the unfortunate events of 09/11 in Manhattan. The main concern is with nuclear power plants and how to design structures that can withstand such extreme situations. An experimental investigation has been carried out to collect fundamental data and to develop a deeper understanding of the effect of impact damage on the load capacity of concrete plates. The paper presents the process on the definition of procedures and the first results of an experimental investigation on the damage and residual load capacity of reinforced concrete plates after impact load. Two types of reinforced concrete plates measuring 1.5 x 1.5 x 0.3 m were subjected to the impact of a flat-nose hard projectile. The two types were casted with the same reinforcement and 80 or 40 MPa concrete. After the impact, the plates go through planar tomography, visual inspection and an ultimate load capacity test. The results showed that the planar tomography can be used for the assessment of internal damage on concrete plates, as long as the number of scans in each direction is more than four. The visual inspection gave a good. The formation of cone cracking after the impact load showed the highest influence on the remaining load capacity of the concrete plates. More plates will be tested to confirm the indications at different damage conditions.
Self-compacting concrete typically contains a higher content of powder materials than normal concrete. Furthermore it is assumed that the use of superplasticizers yields a more homogenous microstructure in the hardened paste. Both aspects generate a very dense microstructure, which can be assumed to cause material behaviour that differs from than normal concrete when it is exposed to elevated temperatures. However, the paste volumes in SCC can vary significantly based on the mixture composition. At a low paste volumes SCC can be very similar to normal concrete at hardened state while it can vary greatly at higher paste volumes. Since the high temperature behaviour of concrete is strongly affected by the different physical behaviour of the paste and the aggregates, it is likely that the high temperature behaviour is consequently strongly affected by the ratio of these mixture components. In the present study different SCC mixtures were observed with similar mechanical properties, but with significantly differing paste to aggregate ratios. Based on observations of the heat evolution at the fire exposed surface and at different depths inside the specimens as well as based on photogrammetric observations of the spalled dimensions, the results indicate that with increasing paste volumes the heat conductivity is reduced and as a result concrete with higher paste to aggregate ratios shows less spalling.