Analytische Chemie
Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (57)
- Posterpräsentation (36)
- Zeitschriftenartikel (27)
- Sonstiges (7)
- Forschungsbericht (7)
- Beitrag zu einem Tagungsband (4)
- Handbuch (4)
- Forschungsdatensatz (2)
- Corrigendum (1)
Referierte Publikation
- nein (145) (entfernen)
Schlagworte
- Nanoparticles (72)
- Electron microscopy (32)
- Nanomaterial (23)
- Particle size distribution (21)
- TiO2 (14)
- EPMA (11)
- SEM/EDX (11)
- Traceability (11)
- Inter-laboratory comparison (10)
- Nanomaterial classification (10)
- VAMAS (10)
- Reference materials (8)
- SEM (8)
- EDS (7)
- Electron probe microanalysis (EPMA) (7)
- Electrospray deposition (6)
- TEM (6)
- Test material (6)
- Thin films (6)
- XPS (6)
- Fe-Ni (5)
- ISO (5)
- NanoDefine (5)
- Shape (5)
- Si-Ge (5)
- Size (5)
- Standardisation (5)
- Thin film analysis (5)
- Core-shell particles (4)
- Nanoparticle size distribution (4)
- Performance check (4)
- Roughness (4)
- Sample preparation (4)
- Scanning electron microscopy (4)
- Titanium oxide (4)
- VSSA (4)
- X-ray spectroscopy (4)
- Auger Electron Spectroscopy (3)
- Auger electron spectroscopy (3)
- BET (3)
- CEN/TC 352 Nanotechnologies (3)
- EDX (3)
- Fluorine (3)
- Functionalization (3)
- Image processing (3)
- Image segmentation (3)
- Iridium oxide (3)
- Microbeam analysis (3)
- Particle sizing techniques (3)
- Perovskite (3)
- Reference material (3)
- Regulation (3)
- Spectroscopic ellipsometry (3)
- ToF-SIMS (3)
- X-ray spectrometer (3)
- XRF (3)
- k-values (3)
- µ-XRF (3)
- 3D (2)
- Anatase (2)
- Automatisation (2)
- Certified reference materials (2)
- Classification (2)
- Convolutional neural networks (2)
- Data (2)
- Definition of nanomaterial (2)
- EBSD (2)
- EC definition (2)
- EC definition of a nanomaterial (2)
- EC definition of nanomaterial (2)
- EC4SafeNano (2)
- EDS-TM002 (2)
- EMPIR (2)
- EU definition of a nanomaterial (2)
- Electron probe microanalysis (2)
- FeNi (2)
- Hydrothermal synthesis (2)
- ISO/TC 229 (2)
- Laser ablation in liquid (2)
- Metrology (2)
- Microanalysis (2)
- Nanomaterials (2)
- Nanopartikel (2)
- Nanoplatelets (2)
- Non-spherical shape (2)
- Porous layers (2)
- Porous thin films (2)
- Pre-standardisation (2)
- SEM/EDS (2)
- SOP (2)
- SiGe (2)
- Solar cells (2)
- Standardization (2)
- Stratagem (2)
- TKD (2)
- Titania (2)
- Titanium dioxide (2)
- Transmission Kikuchi Diffraction (TKD) (2)
- Uncertainties (2)
- thin film analysis (2)
- ACEnano (1)
- AFM (1)
- Advanced materials (1)
- Agglomeration (1)
- Analytical services (1)
- Antigen testing (1)
- Artificial Intelligence (1)
- Atomic fraction (1)
- Au-nanocubes (1)
- Automated Image Analysis (1)
- Automated image analysis (1)
- Bimodal size distribution (1)
- Bipyramidal TiO2 nanoparticles (1)
- Bisphenol A degradation (1)
- Case studies (1)
- Catalogue of services (1)
- Categorisation scheme (1)
- Ceramic (1)
- Characterization (1)
- Characterization method (1)
- Characterization methods (1)
- Characterization techniques (1)
- Confirmatory methods (1)
- Copper alloy (1)
- Correlative Imaging (1)
- Correlative imaging (1)
- EDS Geometrical Detection Efficiency (1)
- EDS Solid Angle (1)
- EDS Spectrometer Test (1)
- EDS X-ray spectrometer (1)
- EDS detector (1)
- EDS net active sensor area (1)
- EDS performance check (1)
- EDS-TM001 (1)
- ESMA (1)
- EU (1)
- EU Definition of nanomaterial (1)
- EU definition (1)
- EU definition of nanomaterial (1)
- EU-Definition (1)
- Electrochemical immunosensor (1)
- Electron Microscopy (1)
- Electron Probe Microanalysis (1)
- Electron micrsocopy (1)
- Electrospray (1)
- Electrspray deposition (1)
- Elektronenmikroskopie (1)
- Elemental composition (1)
- Elementzusammensetzung (1)
- Ellipsometry (1)
- Energy dispersive X-ray spectroscopy (1)
- European Centre (1)
- FIB (1)
- Fenton oxidation (1)
- Few-layered titanium carbide nanosheets (1)
- Fluorescence correction (1)
- Framework (1)
- Gold (1)
- Graphene related 2D materials (1)
- Hard-energy X-ray photoelectron spectroscopy (1)
- High-resolution (1)
- Hyperspectral imaging (1)
- Iinter-laboratory comparison (1)
- Image Segmentation (1)
- Image analysis (1)
- Imaging (1)
- Interlaboratory Comparisons (1)
- Iridium-titanium mixed oxides (1)
- Label-free detection (1)
- Layer analysis (1)
- Layer analytics (1)
- Layer-by-layer deposition (1)
- Light elements (1)
- Machine learning (1)
- MamaLoCA (1)
- MamaLoCa (1)
- Measurement (1)
- Measurement method (1)
- Measurement techniques (1)
- Mesoporous films (1)
- Mesoporous thin films (1)
- Microarray printing (1)
- Microplastic (1)
- Microscopy (1)
- Modelling (1)
- Nano-Charakterisierung (1)
- Nano-Kompetenzzentrum (1)
- Nano-Projekte (1)
- Nano-characterisation (1)
- Nano-safety (1)
- NanoSIMS (1)
- Nanoanalytik (1)
- Nanocatalysts (1)
- Nanocubes (1)
- Nanodefine (1)
- Nanomaterial classfication (1)
- Nanoparticle concentration (1)
- Nanoparticle size (1)
- Nanoplastic (1)
- Nanosafety (1)
- Nanosafety services (1)
- Nanoscale (1)
- Nanotechnology (1)
- Net effective sensor area (1)
- Neural Networks (1)
- Neural networks (1)
- Non-spherical (1)
- Number-weighted median size (1)
- Oberflächenanalytik (1)
- P25 (1)
- PC characterisation (1)
- Particle Characterization (1)
- Particle characterisation (1)
- Particle morphology (1)
- Particle shape (1)
- Particle size (1)
- Particle size analysis (1)
- Particle size and shape distribution (1)
- Pervskite solar cells (1)
- Phase analysis (1)
- Photocatalysis (1)
- Porosity (1)
- Porous film (1)
- Porous layer (1)
- Powder (1)
- Powder X-ray diffraction (1)
- REM (1)
- REM/EDX (1)
- Raman (1)
- Referenzdaten (1)
- Regulatory identification of nanomaterials (1)
- Revision (1)
- SARS-CoV-2 nucleocapsid protein (1)
- SIMS (1)
- STEM-in-SEM (TSEM) (1)
- Screening methods (1)
- Secondary fluorescence (1)
- Secondary fluorescence correction (1)
- Shape control (1)
- Shape-controlled (1)
- Shape-enegineered nanoparticles (1)
- SiO2 (1)
- Silica (1)
- Size and shape distribution (1)
- Size distribution (1)
- Size measurement (1)
- Software (1)
- Solid angle (1)
- Spectrometer check (1)
- Spectrum imaging (1)
- Standard Operation Procedures (1)
- Standardarbeitsanweisung (1)
- Standardisierung (1)
- Standardized check (1)
- Substrates (1)
- Surface characterization (1)
- Surface functionalization (1)
- Surface modification (1)
- TEM grid (1)
- TEM grids (1)
- TOF-SIMS (1)
- TiO2 nanoplatelets (1)
- Tilting (1)
- Titania nanoparticles (1)
- Tools (1)
- Traceable size (1)
- Update 2017 (1)
- VAMAS inter-laboratory comparison (1)
- Volume specific surface area (VSSA) (1)
- WDX (1)
- Wastewater (1)
- X-ray detectors (1)
- X-ray photoelectron spectroscopy (1)
- X-ray spectrometry (1)
- X-ray yields (1)
- X-rays (1)
- XRD (1)
- nPSize (1)
- nanomaterial (1)
- shape control (1)
Organisationseinheit der BAM
- 6 Materialchemie (96)
- 6.1 Oberflächen- und Dünnschichtanalyse (96)
- 1 Analytische Chemie; Referenzmaterialien (11)
- 6.7 Materialsynthese und Design (7)
- 1.2 Biophotonik (5)
- 1.9 Chemische und optische Sensorik (4)
- 5 Werkstofftechnik (3)
- 6.3 Strukturanalytik (3)
- 1.8 Umweltanalytik (2)
- 5.1 Mikrostruktur Design und Degradation (2)
Eingeladener Vortrag
- nein (57)
In this breakout session first, an introduction is given on the planning and organisation of an inter-laboratory comparison (ILC) under the pre-standardisation plattform VAMAS within the newly formed technical working area TWA 45 Micro and Nano Plastics in the Environment. An update with the ILCs on micro- and nanoplastic performed so far is also given. In the third part, the requirements for a reference materials are presented. The needs from the different H2020 micro- and nanoplastic projects are collected and compiled in an ILC matrix for joint activities as the next steps.
In this contribution, two large-area EDS detectors were tested according to the procedure proposed by Procop et al. (2015). In a first step, the optimal working distance (WD) in the two different SEM chambers was determined by moving the sample stage in the Z direction and monitoring the count rates at a magnification of 10,000 and a field of view of 25.6 µm. The WD at which the highest intensity was measured was selected as the optimal position, corresponding to the crossover between the EDS detector optical axis and electron beam optical axis. Next the Cu Kα peak was measured at different relative EDS positions while it was partially removed from the fully inserted position. The spectrum at each location was collected for 10 sec using the highest pulse rate and intermediate current to minimize pile up effects. The ‘inverse squared normalized intensities vs. relative EDS position’ used to extract the true detector – specimen distance shows a non-linear relationship even at the minimal relative positions, which indicates shadowing due to obstruction or use of an unsuitable and/or off-centered collimator. The normalized count rates measured as a function of the EDS distances, results in a too low GCE (too low true solid angles) for both tested detectors. The source of losses of signal was shadowing caused by collimators.
In this contribution, two large-area EDS detectors were tested according to the procedure proposed recently by Procop et al. In a first step, the optimal working distance (WD) in the two different SEM chambers was determined by moving the sample stage in the Z direction and monitoring the count rates from a field of view of 25.6 μm. The WD at which the highest intensity was measured was selected as the optimal position. Next the Cu Kα peak was measured at different relative EDS positions while it was partially removed from the fully inserted position. The spectrum at each location was collected for 10 sec using the highest pulse rate and intermediate current (2.3 nA) to minimize pile up effects (13% dead time). The ‘inverse squared normalized intensities vs. relative EDS position’ used to extract the true detector – specimen distance shows a non-linear relationship even at the minimal relative positions, which indicates shadowing due to obstruction or use of an unsuitable and/or off-centered collimator. The normalized count rates measured as a function of the EDS distances, results in a too low GCE (too low true solid angles) for both tested detectors. The search for sources of losses of signal due to possible shadowing effects is in progress.
The content of the paper is the assessment of the performance of (conventional) measurement techniques (MTs)with respect to the classification of disperse materials according to the EC recommendation for a definition of nanomaterial. This performance essentially refers to the accurate assessment of the number weighted median of (the constituent) particles. All data and conclusions are based on the analytical study conducted as real-world performance testing.
It comprised different types of MTs (imaging, counting, fractionating, spectroscopic and integral) as well as different types of materials. Beside reference materials with well-defined size distribution the study also included several commercial powders (variation of particle composition, morphology, coating, size range and polydispersity). In order to ensure comparability of measurement results, the participants were guided to use uniform protocols in sample preparation, conducting measurements, data analysis and in reporting results. Corresponding documents have been made public, in order to support the reviewing process of the paper, respectively to ensure the reproducibility of data by other users under the same conditions.
The scientific paper relies on a comprehensive set of revised measurement data reported in uniform templates, completely describes the experimental procedures and discusses the MTs’ performance for selected materials in detail. Even more, the study is summarised and evaluated, which leads to recommendations for the use of MTs within a tiered approach of NM characterisation. In addition, the paper critically examines the factors that may affect the outcome of such a comparison among different MTs.
As part of the development of a library of accurate and efficient methods for measurement of nanoparticle properties, we develop and optimize a method for the efficient analysis of nanoparticle size distribution from suspensions via microprinting and digital analysis of electron microscopy (SEM and TEM) images, with the ultimate aim of automated quantitative concentration analysis (calculated from drop volume). A series of different nanoparticle suspensions (gold, latex, and SiO2 in varying sizes and concentrations) were printed onto TEM grids in a 4 x 4 array in the concentration range 7x10^8 to 1x10^11 nanoparticles/mL and imaged with SEM. Concentrations and printing conditions (temperature, relative humidity) were varied in order to minimize the coffee-ring effect.
A femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated by XRD(two instruments operated in different geometries) and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation.
This document is a collection of three JRC Technical Reports that together form the “NanoDefine Methods Manual”, which has been developed within the NanoDefine project ‘Development of an integrated approach based on validated and standardized methods to support the implementation of the EC recommendation for a definition of nanomaterial’, funded by the European Union’s 7th Framework Programme, under grant agreement 604347. The overall goal of the NanoDefine project was to support the implementation of the European Commission Recommendation on the definition of nanomaterial (2011/696/EU). The project has developed an integrated empirical approach, which allows identifying a material as a nano- or not a nanomaterial according to the EC Recommendation. The NanoDefine Methods Manual consists of three parts: Part 1: The NanoDefiner Framework and Tools, which covers the NanoDefiner framework, general information on measurement methods and performance criteria, and tools developed by NanoDefine such as a materials categorisation system, a decision support flow scheme and an e-tool. Part 2: Evaluation of Methods, which discusses the outcome of the evaluation of the nanomaterials characterisation methods for measuring size. Part 3: Standard Operating Procedures (SOPs), which presents the 23 Standard Operating Procedures developed within the NanoDefine project. In this combined document, these three parts are included as stand-alone reports, each having its own abstract, table of contents, page, table and figure numbering, and references.
Worldwide there is a variety of regulatory provisions addressing nanomaterials. The identification as nanomaterial in a regulatory context often has the consequence that specific legal rules apply. In identifying nanomaterials, and to find out whether nanomaterial-specific provisions apply, the external size of particles is globally used as a criterion. For legal certainty, its assessment for regulatory purposes should be based on measurements and methods that are robust, fit for the purpose and ready to be accepted by different stakeholders and authorities. This should help to assure the safety of nanomaterials and at the same time facilitate their international trading. Therefore, we propose a categorisation scheme which is driven by the capabilities of common characterisation techniques for particle size measurement. Categorising materials according to this scheme takes into account the particle properties that are most important for a determination of their size. The categorisation is exemplified for the specific particle number based size metric of the European Commission's recommendation on the definition of nanomaterial, but it is applicable to other metrics as well. Matching the performance profiles of the measurement techniques with the material property profiles (i) allows selecting the most appropriate size determination technique for every type of material considered, (ii) enables proper identification of nanomaterials, and (iii) has the potential to be accepted by regulators, industry and consumers alike. Having such a scheme in place would facilitate the regulatory assessment of nanomaterials in regional legislation as well as in international relations between different regulatory regions assuring the safe trade of nanomaterials.
Copper alloys have found widespread application in various fields. The elemental composition determines the properties of the alloys and consequently their application. Therefore, knowing the composition of a copper alloy is very important.
Metrological institutes like the BAM (German Federal Institute for Materials Research and Testing) offer reference materials that can be used to prove the accuracy of the applied analysis method.
The aim of this application note is to demonstrate how Micro-X-ray fluorescence spectroscopy (Micro-XRF) expediently supplements the analysis of copper alloys by
using Bruker’s micro-focus X-ray source XTrace attached to a scanning electron microscope (SEM) and operating with an energy dispersive spectrometer.
A case study on the TEM analysis of the size and shape distribution of TiO2 bipyramidal nanoparticles prepared on TEM grids was included in the recently published ISO standard ISO 21363. It was agreed to organize at a later stage a second inter-lab comparison with the nanoparticles distributed to the participants as a liquid suspension. Protocols for uniform nanoparticle deposition on suited supports developed and optimized within the EMPIR nPSize project are also prepared to be distributed. For this, we have chosen the VAMAS platform (www.vamas.org) which offers an excellent international infrastructure of laboratories with high competence in nanoparticle measurement. The VAMAS technical working area dedicated to nanoparticle measurement is TWA 34 ‘Nanoparticle populations’. For this type of nanoparticles, the size and shape distributions are the primary parameters to be reported. Due to the good deposition protocols developed, an automated image analysis is enabled (in contrast to the manual analysis of irregular TiO2 nanoparticles.
In parallel with the TiO2 nanoparticle exercise, two spherical SiO2 nanoparticle samples with bi-modal size distributions (nominal relative number concentrations of 1:1 and 10:1) are prepared for a second VAMAS inter-lab comparison. Here, the nanoparticle concentration is the primary parameter to be measured. For the imaging methods it is targeted to measure the relative nanoparticle concentrations of the two modes. For the absolute nanoparticle concentration to be measured by imaging methods it is necessary to control the volume of the liquid suspension deposited on the substrate and to obtain such a homogeneous nanoparticle deposition on the substrate which allows to count (or extrapolate) all the deposited particles.
For test laboratories operating under accreditation schemes like ISO/IEC 17025 (ISO/IEC 17025), as the international reference for testing and calibration laboratories wanting to demonstrate their capacity to deliver reliable results, a periodical control of the critical instrumental parameters of an Energy-Dispersive X-ray Spectrometer (EDS) is required.
This periodical check of an EDS is specified with exact procedures and materials in the ISO 15632:2021 ”Microbeam Analysis – Selected instrumental performance parameters for the specification and checking of energy-dispersive X-ray spectrometers for use in electron probe microanalysis” (ISO 15632). The EDS check can be simplified to the acquisition of only one 10 kV spectrum from a dedicated test material, EDS-TM002, which is made available by BAM since 2009 (https://webshop.bam.de/webshop_en/). The optional BAM software “EDX spectrometer check” is destined to automatically evaluate this spectrum and determine the performance of the EDS in terms of energy resolution and calibration, as well as possible alteration of low-energy efficiency due to detector contamination. Nearly 200 laboratories have the EDS-TM and associated software package in use.
Practical examples based on various types of artifacts occurred in the EDS spectra and a long-term (>10 years) meticulous observation of the own spectrometers will be discussed. Different types of EDS spectrometers are considered, e.g. Si(Li) and SDD, of various window types (AP, the recent one Si3N4 or even windowless), and with different front contact layers (Au and Ni) (Hodoroaba and Procop, 2014). Evaluation of other parameters or effects such as the deadtime at different count rates or pileup effects is also explained with examples.
Scanning Electron Microscopy (SEM) represents the mostly widespread method available in analytical laboratories dedicated to the characterization of physical properties such as morphology of various solid materials from ‘micro-’ down to the nanometre scale. The use of secondary electrons excited by a sharply, nm-focussed primary electron beam enables at any modern SEM to image objects with high in-depth and lateral sensitivity, i.e. with high spatial resolution. Hence, e. g. nanoparticles (NPs) are able to be easily characterized with respect to their individual size and shape, but also to the morphology of their surface.
By preparing the nano-objects on thin membranes as electron transparent samples it is possible to perform electron microscopy in the transmission mode (TEM and TSEM). The corresponding transmission (i.e. mass-thickness) contrast reveals in-depth information, but is also well suited for dimensional measurements in the 2D projection image. Both the surface sensitive mode and the transmission one are meanwhile available at any modern SEM. If an X-ray spectrometer is attached to an electron microscope, it is possible to analyse the characteristic X-rays induced by electron bombardment. Most electron microscopes have attached an energy dispersive X-ray spectrometer (EDX) so that EDX elemental maps can be carried out. Recent technological developments of high throughput EDS detectors and their advantages regarding high-resolution X-ray analysis down to the nm range are reviewed.
High-resolution micrographs (SEM, TSEM, TEM) and corresponding X-ray elemental maps on various representative nanoparticles, but also layered samples prepared in cross-section, will be presented and discussed. The importance of selecting the best suited analysis conditions will be highlighted. Also other, often challenging, topics such as sample preparation and image data processing will be critically addressed by practical examples. Further analytical techniques able to be employed at an electron microscope, like cathodoluminescence (CL) or micro-X-ray fluorescence (µXRF) will be briefly surveyed.
The TiO2 material selected for the present inter-laboratory comparison (ILC) was the bipyramidal anatase UT001 batch synthesized hydrothermally by University of Turin in the frame of the EU/FP7 Project SETNanoMetro and carefully prepared on TEM grids by BAM to be distributed to the ILC participants. A clear measurement protocol including data analysis and reporting (including an xls reporting template) has been also prepared by BAM. 14 of 18 participants have measured and reported results which have been already checked by BAM as being conform to the agreed protocol. After receiving the last results (of 4 participants) the ILC data evaluation will be carried out by BAM in line with agreed ISO/TC229 procedures as for the other case sudies.
In order to ground the debate on the metrics that apply for VSSA determined by adsorption isotherms and to illustrate the consequences of real bimodality for VSSA screening, a bimodal mixture has been selected for systematic investigations. A sample of BaSO4 fine was spiked with 10% g/g of BaSO4 ultrafine. The ultrafine grade is a clear nanomaterial (NM) according to the size criterion with a median Feretmin of 27 nm and the fine grade is clearly a non-NM with a median Feretmin of 249 nm. Because of the number ratio of 300:1, the mixture has to be a NM according to the size criterion. Three independent BET measurements were performed on the mixture by two different labs and resulted in a mean VSSA of 23 m2/cm3 with a standard deviation of 3.3 m2/cm3, which leads to a dminVSSA of 258 nm, and, therefore, would falsely classify the material as a non-NM. This effect was predicted earlier by calculated examples (Roebben et al. 2014) and demonstrates that mixtures of nano- and non-nano multimodal materials very likely lead to false negative classifications. Moreover, the measured VSSA values for the mixture of 23 m²/cm³ are in excellent accord with the value of 24.6 m²/cm³ predicted from the TEM size distributions of the individual materials according to the model described by JRC (Roebben et al. 2014), but are significantly different from the prediction of 309 m²/cm³ obtained from the same TEM size distribution by a particle number weighted approach (Lecloux 2015). The same is true for a 50% g/g mixture. We conclude that the mass-based VSSA approach (Roebben et al. 2014) is equal to the VSSA that is measurable by adsorption isotherms, such as from standardized BET.
A proposal of an inter-laboratory study (ILC) on determination of size and shape distribution of TiO2 nanoparticles (NPs) by transmission electron microscopy is presented. The anatase NPs synthesized in a controllable fashion within the EU/FP7 project SETNanoMetro can be considered as shape-defined (bipyramidal) and are offered to complete the list of case studies already in progress within ISO/TC229/JWG2. The main points of the measurement procedure are presented as well as a proposed procedure to evaluate the size and shape according to the standard operation procedure already developed within SETNanoMetro is discussed. Potential ILC participants and a plan with next step to be carried out are proposed.
Controlled deposition of nanoparticles by electrospray for improved analysis by imaging techniques
(2018)
Of many experimental techniques for measuring particle sizes and size distributions, electron microscopy (EM) is still considered as the gold standard, especially in the nano range (1–100 nm).
Furthermore, high-resolution X-ray spectroscopy (EDX) in conjunction with EM can be applied to individual NPs. Preparation of an EM sample for generic particulate materials is a difficult task. Usually the particles in a suspension are deposited on a support. However, this procedure includes the drying of larger solvent amounts on the substrate itself, and this can affect the spatial distribution of the deposited particles. One possibility to overcome this is the use of an electrospray system, where the suspension of particles is sprayed onto the substrate in charged droplets that are so small that they either dry off on the substrate immediately without affecting the position of particles, or even already during their flight time to the substrate. Additionally, the charging of particles minimizes agglomeration and aggregation, maximizing the collection of the EM grids. The prototype of an electrospray deposition system from RAMEM under its trademark IONER (www.ioner.eu) was tested. Electrospray is theoretically described since a long time, but no dedicated commercial instruments are available for the preparation of TEM grids yet, apart from electrostatic deposition of aerosols.2 Several materials have been sprayed onto TEM grids and the resulting particle distributions were evaluated. Operation parameters such as the sample flow-rate, capillary – substrate distance, electric field strength and sampling period length have been optimized. It was found that the particles deposited by electrospray generally show a much more homogeneous spatial distribution on the substrate and a substantial increase of the number of single particles (suited to automatic analysis).
The EC Recommendation on the definition of nanomaterial1, based solely on size of the constituent particles, foresees development of harmonised measurement methods ensuring ‘consistent results across materials and over time’. The EU/FP7 large research project NanoDefine (http://www.nanodefine.eu) has been exclusively dedicated to support the implementation of this EC Recommendation for the European Union’s legislation. For the first time, measurement techniques able to determine the size of nanoparticles have been evaluated systematically on a well-defined set of quality control materials (spherical, monodisperse) as well as industrial materials of complex shapes and considerable polydispersity. Particularly based on the analytical performance of the measurement techniques as tested on the challenging real-world particulate materials, it was possible to formulate recommendations for use of a new tiered approach consisting of screening and confirmatory techniques. Thus, a consistent framework of guidance for nanomaterial identification according to the EC Definition has been issued in form of the NanoDefiner e-tool (https://labs.inf.fh-dortmund.de/NanoDefiner), with a transparent decision flow scheme and an extensive user manual. Selected examples of analysis and classification as nano-/non-nanomaterials will be given, highlighting the limits of applicability of the available measurement techniques in dependence on sample properties. On some recent relevant developments in sample preparation – as a crucial part for an accurate analysis - will be also reported.
Controlled electrospray deposition of nanoparticles for improved analysis by electron microscopy
(2018)
Of many experimental techniques for measuring particle sizes and size distributions, electron microscopy (EM) is considered as the gold standard, especially in the nano range (1–100 nm). Furthermore, high-resolution X-ray spectroscopy (EDX) in conjunction with EM can be applied to individual NPs. Preparation of an EM sample for generic particulate materials is a difficult task. Usually, the particles in a suspension are deposited on a support. However, this procedure includes the drying of larger solvent amounts on the substrate itself, and this can affect the spatial distribution of the deposited particles. One possibility to overcome this is the use of an electrospray system, where the suspension of particles is sprayed onto the substrate in charged droplets that are so small that they either dry off on the substrate immediately without affecting the position of particles, or even already during their flight time to the substrate. Additionally, the charging of particles minimizes agglomeration and aggregation, maximizing the collection of the EM grids. The prototype of an electrospray deposition system from RAMEM under its trademark IONER (www.ioner.eu) was tested.
Electrospray is theoretically described since a long time, but no dedicated commercial instruments are available for the preparation of TEM grids yet, apart from electrostatic deposition of aerosols. Several materials have been sprayed onto TEM grids and the resulting particle distributions were evaluated. Operation parameters such as the sample flow-rate, capillary – substrate distance, electric field strength and sampling period length have been optimized. It was found that the particles deposited by electrospray generally show a much more homogeneous spatial distribution on the substrate and a substantial increase of the number of single particles (suited to automatic analysis).
The project has received funding from the European Union’s Seventh Programme for research, technological development and demonstration under grant agreement No 604347.
Coming as response to the needs expressed by The European Commission mandating CEN, CENELEC and ETSI to develop European standards for methods that can characterize reliably manufactured nanomaterials, a new European metrology research project ‘nPSize - Improved traceability chain of nanoparticle size measurements’ has received funding for the next three years. The project will develop methods, reference materials and modelling to improve the traceability chain, comparability and compatibility for nanoparticle size measurements to support standardization.
nPSize has selected only those nanoparticle sizing techniques which are able to provide traceable results: electron microscopy (SEM, TSEM and TEM), AFM and SAXS. Metrologists from national metrological or designated institutes (PTB, LNE, LGC, VSL, SMD and BAM) will work together with scientists with know-how in development of new nano reference nanoparticles (CEA, University of Turin, LGC, BAM) and with experts in advanced data processing, e.g. by machine learning (POLLEN). With the support of DIN, the project outcomes will be channelized to standardization bodies such as ISO/TC 229 ‘Nanotechnologies’/JWG 2 ‘Nanoparticle Measurement and Characterization’ (SEM, TSEM and TEM), CEN/TC 352 ‘Nanotechnologies’ (SEM, TSEM and TEM), ISO/TC 201/SC 9 (AFM), ISO/TC 24/SC 4 (SAXS).
Three technical work packages will ensure input for impact to standardization community, nanoparticle manufacturers, instrument manufacturers, and (accredited) service laboratories:
- WP1 Performance and traceability of characterization methods
- WP2 Reference materials - Preparation and Characterization
- WP3 Modelling and development of measurement procedures
Well-defined non-spherical nanoparticles shapes such as cubes, platelets, bipyramids, rods/acicular will be developed, with mono- and polydisperse size distribution, as well as with accurate particle number concentration (by SAXS and isotopically enrichment for ICP-MS).
Physical modelling of the signal for TSEM, SEM, 3D-AFM and SAXS will be used to feed machine learning modeling from a-priori measurement data. Further, data fusion will be developed for hybrid sizing techniques: SEM with TSEM/TEM, SEM/TSEM with AFM, SEM/TSEM with SAXS with the final aim of improving the true shape and size of non-spherical nanoparticles by a better estimation of the measurement uncertainties.
In the second half-time of the project dedicated workshops (focused on method improvement and reference materials development) will be organized to disseminate the gained knowledge to end-users. Further, a data library with relevant tagged measurement data is planned to be organized and made publicly available. Inter-laboratory comparisons based on the newly developed multi-modal nano reference materials will be organized preferably within VAMAS/TWA 34 ‘Nanoparticle populations’.
Extraction of true, 3D shape (and size) of non-spherical nanoparticles (NPs) is associated with errors by conventional 2D electron microscopy using projection images. Significant efforts within the ISO technical committee TC 229 ‘Nanotechnologies’ are aimed at establishing accurate TEM and SEM measurement of NP size and shape as robust, standard procedures. Study groups have been organizing inter-laboratory comparisons on well-selected NP systems according to the market needs, such as aggregated titania nano-powder for which size and shape distribution of primary crystallites of irregular shape must be measured accurately. To be noticed is e. g. the fact that the measurement procedure allows only manual selection of the particles clearly distinguishable for analysis as well as manual definition of the contour of the imaged NPs.
An inter-laboratory exercise on titania NPs (pure anatase, grown by hydrothermal synthesis) of well-defined non-spherical shape, i.e. bipyramidal has been recently started within ISO/TC 229 under similar conditions as for the irregular shaped titania. Overlapped particles were allowed to be considered, as long as they are clearly distinguishable. One decisive NP selection criterion was to analyze only those NPs with a roundness value below 0.7, i.e. the NPs laying on the support foil and, hence, with projection areas clearly deviating from perfect circles (R=1). The overall evaluation (for 15 labs) of the size descriptors (area, Feret, minFeret, perimeter) and shape descriptors (aspect ratio, roundness, compactness, extent) by analysis of variance is just to be finished and included in ISO/WD 21363 Nanotechnologies -- Protocol for particle size distribution by transmission electron microscopy.
The EC Recommendation on the definition of nanomaterial, based solely on size of the constituent particles, foresees development of harmonised measurement methods ensuring ‘consistent results across materials and over time’. The EU/FP7 research project NanoDefine has been exclusively dedicated to support the implementation of this EC Recommendation for the European Union’s legislation. For the first time, measurement techniques able to determine the size of nanoparticles have been evaluated systematically on a well-defined set of quality control materials (spherical, monodisperse) as well as industrial materials of complex shapes and considerable polydispersity.
Particularly based on the analytical performance of the measurement techniques as tested on the challenging real-world particulate materials, it was possible to formulate recommendations for use of a new tiered approach consisting of screening and confirmatory techniques. Thus, a consistent framework of guidance for nanomaterial identification according to the EC Definition has been issued in form of the NanoDefiner e-tool, with a transparent decision flow scheme and an extensive user manual. Selected examples of analysis and classification as nano-/non-nanomaterials will be given, highlighting the limits of applicability of the available measurement techniques in dependence on sample properties. On some recent relevant developments in sample preparation – as a crucial part for an accurate analysis - will be also reported. Further, ISO/TC 229 ‘Nanotechnologies’ activities aiming at establishing accurate TEM and SEM measurement of NP size and shape as robust, traceable, standard procedures are highlighted. With participation of BAM, study groups have been organizing inter-laboratory comparisons on well-selected NP systems according to the market needs, such as aggregated or shape-controlled titania nano-powder for which size and shape distribution of primary particles must be measured accurately.
Many techniques are available for measuring particle size distribution. For ideal materials (spherical particles, well dispersed) it is possible to evaluate the Performance of These methods. The performance of the analytical instrumentation for the purpose of classifying materials according to EC Definition is unknown. In this work the performance of commercially available particle sizing techniques on representative NanoDefine set of real-world testing materials (RTM) and quality control materials (QCM) for the implementation of the Definition is evaluated.
The overall objective of project Improved traceability chain of nanoparticle size measurements is to improve the traceability chain for nanoparticle size measurements. The main impact will be achieved by manifold contributions to standard documents for CEN/TC 352 “Nanotechnologies”, which directly addresses the research needs of CEN, CENELEC and ETSI mandated by EC to develop standards for methods and reference materials to accurately measure the size and size distribution of nanoparticles. This will take place in collaboration with ISO/TC229 ‘Nanotechnologies’, ISO/TC24/SC4 ‘Particle characterization’ and ISO/TC201 ‘Surface analysis’/ SC9 ‘Scanning probe microscopy’.
We discuss the role of the volume specific surface area (VSSA) as determined from the specific surface area measured by the (extended) Brunauer-Emmett-Teller (BET) technique, in the identification process of powdered nano- and non-nanomaterials in line with the EU definition of nanomaterial. Results obtained in the NanoDefine project demonstrate that under appropriate conditions, VSSA can be used as proxy to the number-based particle size distribution. The extent of agreement between nano/non-nano classification by electron microscopy (EM) and classification by VSSA is investigated systematically on a large set of diverse particulate substances, representing most of the cases expected in regulatory practice. Thus, parameters such as particle shape, size polydispersity/multi-modality, and particle (inner or coating) porosity are evaluated. Based on these results, we derive a tiered screening strategy for powders, involving the use of VSSA for the purpose of implementing the definition of nanomaterial, and recommend it for inclusion in a technical guidance for the implementation of the definition.
Extraction of true, 3D shape (and size) of non-spherical nanoparticles (NPs) is associated with errors by conventional 2D electron microscopy using projection images. Significant efforts within the ISO technical committee TC 229 ‘Nanotechnologies’ are aimed at establishing accurate TEM and SEM measurement of NP size and shape as robust, standard procedures. Study groups have been organizing inter-laboratory comparisons on well-selected NP systems according to the market needs, such as aggregated titania nano-powder for which size and shape distribution of primary crystallites of irregular shape must be measured accurately. To be noticed is e. g. the fact that the measurement procedure allows only manual selection of the particles clearly distinguishable for analysis as well as manual definition of the contour of the imaged NPs.
An inter-laboratory exercise on titania NPs (pure anatase, grown by hydrothermal synthesis) of well-defined non-spherical shape, i.e. bipyramidal has been recently started within ISO/TC 229 under similar conditions as for the irregular shaped titania. Overlapped particles were allowed to be considered, as long as they are clearly distinguishable. One decisive NP selection criterion was to analyze only those NPs with a roundness value below 0.7, i.e. the NPs laying on the support foil and, hence, with projection areas clearly deviating from perfect circles (R=1). The overall evaluation (for 15 labs) of the size descriptors (area, Feret, minFeret, perimeter) and shape descriptors (aspect ratio, roundness, compactness, extent) by analysis of variance is just to be finished and included in ISO/WD 21363 Nanotechnologies -- Protocol for particle size distribution by transmission electron microscopy.
The test material EDS-TM001 together with an accompanying software package, “EDX spectrometer check”, have been made available in 2009 by BAM to be employed by EDS (energy dispersive spectrometer) users to check the performance of an EDS attached to the SEM. Particularly for test laboratories operating under accreditation schemes like ISO/IEC 17025, a periodical control of the critical instrumental parameters in end-user laboratories is required. With EDS-TM001 or EDS-TM002 (second generation) test material, this periodical check is simplified to the acquisition of only one 10 kV spectrum. The software “EDX spectrometer check” is destined to evaluate automatically this spectrum and determine the performance of the EDS in terms of energy resolution and calibration as well as possible alteration of low-energy efficiency due to detector contamination. Energy resolution can be compared with the specified values according to the international ISO standard ISO 15632:2012. EDS-TM is a synthetic material consisting of a thick layer of C, Al, Mn, Cu and Zr in a well-defined composition, deposited on a steel (in case of EDS-TM001) or silicon (in case of EDS-TM002) substrate. Meanwhile, more than one hundred laboratories use the EDS-TM001 or EDS-TM002 test material for the periodical check of their EDS. A detailed description of the test material and software together with examples of application was published recently. New results and gained experiences will be presented as well.
When the FWHM of lines appearing in the EDS-TM spectrum are determined, the spectrum background must be subtracted accurately. The applied physical background subtraction procedure is robust and takes into account the transmission of the detector window. While the previous version considers only Moxtek AP windows, the new version includes selection of silicon nitride window and the case of windowless detector. Moreover, the new version allows importing of spectra in Bruker spx format and EMSA/MSA files from EDAX TEAM software.
Gold nanocubes with a monodispersed size distribution (edge = 55 nm) deposited on a silicon wafer. These tiny uniform cubes were produced as reference nanoparticles in the frame of the European project nPSize - Improved traceability chain of nanoparticle size measurements. SEM Image acquired at 10 kV with an in-lens secondary electron detector. Image colored in ImageJ using LUT “Orange hot.” Published in Microscopy and Microanalysis 25(S2) (2019) 2328.
Gold nanocubes with a monodispersed size distribution (edge = 55 nm) deposited on a silicon wafer. These tiny uniform cubes were produced as reference nanoparticles within the EMPIR project nPSize - Improved traceability chain of nanoparticle size measurements. SEM image acquired at 10 kV with an in-lens secondary electron detector. Image colored in ImageJ using LUT “Orange hot.” Published in Microscopy and Microanalysis 25(S2) (2019) 2328.
The progress in activities on Microbeam Analysis under VAMAS/TWA 37 is reviewed. Particularly the liaison with the new projects within the ISO technical committee TC 202 is presented and discussed with respect to the possibility of identifying and launching related VAMAS projects. Need of more promotion for the engagement of more participants from industry and academia at national, European and international level is highlighted. Also, the competition with the other technical working areas (on 'nano' or materials-related) is critically discussed.
Porous materials play an important role in several fields of technology, especially for energy applications like photovoltaics, electrolysis or batteries. The activity of porous films is affected by properties like porosity, film thickness, chemical composition of the material, as well as the crystallinity of the framework. The complex morphology of such porous films constitutes a challenge even for modern analytical techniques and requires new approaches employing the combination/complementation of data of different analytical methods. In this contribution, we characterise thin mesoporous iridium-titanium mixed oxide film properties by electron probe microanalysis (EPMA) with energy-dispersive X-ray spectroscopy (EDS) at an SEM.
Mesoporous iridium oxide - titanium oxide (IrOx-TiOx) films were prepared via dip-coating of a solution containing a triblock-copolymer as structure-directing agent, an iridium precursor as well as a titanium precursor in ethanol. IrOx-TiOx films were synthesized with different amounts of iridium and calcined in air. The SEM micrographs reveal for all films the achievement of a well-ordered mesoporous structure and homogeneous films with thicknesses between 67 nm and 152 nm.
For the determination of film elemental composition and porosity, EPMA can be used as part of a combined SEM/EDS/STRATAGem analysis. Elemental compositions and mass depositions (in μg cm-2) of IrOx-TiOx films were calculated with the thin film analysis Software STRATAGem via k-values measured with SEM/EDS. Pure bulk Ir, TiO2 and Si were measured as references. The average density of the films was obtained from the mass Deposition and the film thickness as measured by cross-section SEM. The porosity was then extracted from the measured average film density divided by a theoretical bulk density. The latter is calculated from the weight fractions of IrOx and TiOx as determined with STRATAGem and the bulk mass densities of IrO2 and TiO2 (rutil) from literature.
The fitting results of the k-values from the STRATAGem software, which are in fair agreement with the measured k-values.
The application of the SEM/EDS/STRATAGem approach for accurate porosity determination on pure mesoporous TiOx films and pure porous IrOx films has been recently demonstrated.
The porosities of pure IrOx, TiOx and mixed IrOx-TiOx films in this study have been determined. The contribution will assess in detail the advantages and limitations of the combined SEM/EDS/STRATAGem analysis for the morphology and porosity of thin metal oxide films. Moreover, the comparison with other measurement techniques and the combination of datasets from multiple measurements will be discussed.
Microbeam analysis data are of continuously improving quality, this owing mainly to developments in instrumentation (hardware and software) and computer performance. The knowledge and skills of the operators must be also kept correspondingly updated. To be deemed as technically competent, the laboratories must be accredited according to an accreditation scheme, mostly following ISO/IEC 17025.
International standards are able to provide requirements, specifications, guidelines or characteristics of methods, instruments or samples with the final goal that these can be used consistently in accredited laboratories. In the field of electron microscopy and microbeam Analysis standardisation and metrology are terms that are encountered rather seldom at major conferences and scientific publications. Several ISO standards already published and used successfully by a large part of the electron microscopy and microbeam analysis community. For example, file formats such as EMSA/MSA for spectral-data exchange or tagged image file format (TIFF) for SEM images; procedures for the specification of X-ray spectrometers, the specification of certified reference materials (CRMs), and for measurement of average grain size by electron backscatter diffraction (EBSD); and guidelines for calibrating image magnification in SEM or TEM. A main task of ISO technical committee TC 202 ‘Microbeam Analysis’ is to identify feasible projects/proposals needed to be developed into new international standards, particularly in respect to recent technology, such the silicon drift detector (SDD).
As far as the metrological aspects are regarded, The International Bureau of Weights and Measures (BIPM) through the Consultative Committee for the Amount of Substance (CCQM) is concerned with the metrological aspect in Chemistry and Biology. In particular, the Surface Analysis Working Group (SAWG) assists in identifying and establishing inter-laboratory work to test the consistency as well as to improve the traceability of spatially resolved chemical surface analysis at the micro and nanoscale. Examples of recent projects on quantitative microbeam analysis at low energies, such as the quantification of light elements such as carbon and nitrogen will be presented.
The significant sources of measurement uncertainty will be emphasized. These are: quality of the unknown and the reference materials used, the quantification model, instrumental parameters like take-off-angle, spectrometer efficiency, and particularly the beam current. The crucial importance of working with uniform and well-defined measurement and data evaluation protocols will be discussed in compliance with the ISO document “Guide to the expression of uncertainty in measurement (GUM)”.
Another international platform where pre-standardisation work can be organised is VAMAS (Versailles Project on Advanced Materials and Standards). International collaborative Projects aim at providing the technical basis for harmonised measurements, testing, specifications, and standards to be further developed at ISO level. One key point of VAMAS activities is constituted by inter-laboratory comparisons for high-quality data. In the field of microbeam analysis, the technical working area (TWA) 37 Quantitative Microstructural Analysis deals with corresponding projects. Good ideas, e.g., on analysis at low energies, are particularly encouraged by directly contacting the author. Support and guidance will be supplied.
Measurement of elemental composition of Fe1-xNix and Si1-xGex alloy thin films by EMPA and µ-XRF
(2019)
It was demonstrated in the past that the electron probe microanalysis (EPMA) can be applied to determine accurately both elemental composition and thickness of thin films by using the dedicated software package for thin film analysis Stratagem. A relatively small number of film materials such as pure metallic films of platinum and nickel, binary alloys of Fe-Ni, and Pt-Ni-Co ternary alloy films has been reported in literature as working successfully. Further, the software can be applied ‘inversely’, i.e., by feeding it with the thickness of the film and using the determined mass coating, one can easily calculate the film density, which for porous layers leads us to the true film porosity.
The present study repeats measurements on an already tested system of Fe-Ni thin films on silicon and reports for the first-time results of analysis on Si-Ge thin films deposited on a non-conductive aluminium oxide substrate. Standard-based and standardless EPMA (with EDS) results were used in combination with Stratagem for the quantification.
Further, X-ray fluorescence analysis (XRF) can be used for the determination of elemental composition and thickness of such films as well. In this case, XRF with a μ-focus X-ray source (μ-XRF) attached to a SEM was applied. For quantification, a fundamental parameter (FP) approach has been used to calculate standard-based and standardless results. Compared to EPMA, XRF has a larger information depth and a higher elemental sensitivity because of a generally lower background.
Both thin film systems have been chosen as samples of an international round robin test (RRT) organised in the frame of standardisation technical committee ISO/TC 201 ‘Surface chemical analysis’, under the lead of KRISS. The main objective of the RRT is to compare the results of atomic fractions of Fe1-xNix and Si1-xGex alloy films obtained by different surface Analysis techniques, such as X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES), and secondary ion mass spectrometry (SIMS) applied in the depth-profiling operation mode.
Five samples of different atomic fractions of each thin film system, i.e., Fe1-xNix and Si1-xGex, have been grown by ion beam sputter deposition on silicon and Al2O3 wafers, respectively. Reference FeNi and SiGe films with well-known elemental composition and thickness have been also supplied for standard-based analysis. The atomic fractions of all the samples including the references have been certified by RBS (Rutherford backscattering spectrometry) and ICP-AES (inductively coupled plasma atomic emission spectroscopy).
The 44th Meeting of the Versailles Project on Advanced Materials and Standards (VAMAS) Steering Committee has just taken place at NIST in Boulder (CO, USA). BAM participates with significant contributions in Technical Working Areas on nanoparticle and surface chemistry characterization, but also has positioned itself to new global material challenges and trends in the developement of advanced materials and their characterization, such as thermal properties, self-healing materials, and micro- and nanoplastic.
The present study addresses the capability of measurement of relative particle number concentration by scanning electron microscopy for model bimodal silica and gold samples prepared in the frame of the European research project “nPSize - Improved traceability chain of nanoparticle size measurements” as candidate reference nanoparticles.
In this paper one refined approach is applied to determine the exact orientation of bipyramidal TiO2 nanoparticles prepared with good dispersion as almost isolated particles on a carbon TEM grid. The advantages of the recently developed high-throughput Transmission Kikuchi Diffraction (TKD) are used to identify quickly and reliably the geometrical orientation of the crystalline TiO2 nanoparticle bipyramids (anatase) on a statistically relevant number of particles.
In this contribution different ways are explored with the aim to generate suitable training data for ‘non-ideal’ samples using various approaches, e.g., computer-generated images or unsupervised learning algorithms such as generative adversarial networks (GANs). We used these data to train simple CNNs to produce segmentation masks of SEM images and tested the trained networks on real SEM images of complex nanoparticle samples. The novel use of CNN for the automated analysis of the size of nanoparticles of complex shape and with a high degree of agglomeration has proved to be a promising tool for the evaluation of particle size distribution on a large number of constituent particles. Further development and validation of the preliminary model, respectively larger training and validation data sets are necessary.
k-values (k-ratio, K-value) is defined as ratio of the X-ray photon intensity I measured for a particular characteristic peak from the unknown sample to the value measured for the same X-ray peak from a reference material of known composition under identical conditions of beam energy, spectrometer efficiency and electron dose.
In this contribution the particle sizing techniques evaluated in NanoDefine are presented together with recommendations for their application/implementation on real-world materials. The experimental evaluation is discussed based on examples on NanoDefine materials. A systematic study on volume specific surface area as derived from BET measurements versus electron microscopy on powdered materials is also presented.
The test material EDS-TM001 together with an accompanying software package, “EDS spectrometer check”, have been made available in 2009 by BAM to be employed by EDS (energy-dispersive X-ray spectrometer) users to check the performance of an EDS with a SEM. With EDS-TM001/002 test material, this periodical check is simplified to the acquisition of only one 10 kV spectrum. The software “EDS spectrometer check” is destined to evaluate automatically this spectrum and determine the EDS performance in terms of energy resolution and calibration, as well as possible alteration of low-energy efficiency due to detector contamination. Energy resolution can be compared with the specified values according to the international ISO standard ISO 15632:2012.
EDS-TM is a synthetic material consisting of a 6 μm thick layer of C, Al, Mn, Cu and Zr deposited on a steel (EDS-TM001) or silicon (EDS-TM002) substrate. The chemical composition of EDS-TM was chosen such as to give nearly equal intensities of the low energy lines in a 10 kV spectrum, thus, making it very sensitive against spectrometer efficiency changes. New results and gained experiences will be presented.
When the FWHM of the X-ray lines in the EDS-TM spectrum are determined, the spectrum Background must be subtracted accurately. The applied physical background subtraction procedure is robust and considers the transmission of the detector window. While the previous version considers only Moxtek AP windows, the new software version includes selection of silicon nitride window and the case of windowless detector.
Porous materials play an important role in several fields of technology, especially for energy applications like photovoltaics, electrolysis or batteries. The activity of thin porous films is affected by properties like porosity, film thickness, chemical composition of the material as well as the homogenous dispersion of the active species within the porous matrix. The complex morphology of such porous films constitutes a challenge even for modern analytical techniques and requires new approaches employing the combination/complementation of data of different analytical methods. In this contribution we characterize thin mesoporous iridium-titanium mixed oxide film properties by complementary analysis of SEM/EDS, ToF-SIMS, NanoSIMS, AES and spectroscopic ellipsometry.
Mesoporous iridium oxide - titanium oxide (IrOx-TiOx) films can be prepared by a well-established Synthesis route via soft-templating. IrOx-TiOx films are very sensitive to the conditions of synthesis. Analysis by SEM and NanoSIMS imaging suggests IrOx-TiOx films with and without a homogenous dispersion of IrOx within the TiOx film matrix under different synthesis conditions.
Auger electron spectroscopy (AES) analysis in the depth-profile mode as well as cross-section line-scan AES measurements of an inhomogeneous IrOx-TiOx film indicate the presence of an IrOx-rich Phase dispersion both at the surface of IrOx-TiOx film as well as within the film.
The contribution will assess in detail the sensitivity of the synthesis conditions and the characterization of the thin metal oxide films. Moreover, the correlation between and comparison to other measurement techniques will be discussed.
New reference material candidates for traceable size measurement of nonspherical nanoparticles
(2019)
Size measurement of nanoparticles (NP) becomes a challenging analytical problem when non-spherical shapes must be traceably measured. However, most industrial NPs have irregular shapes and broad size distribution making it often more complex to follow European regulatory to identify a material as a nanomaterial according to which accurate measurement of the smallest dimension and its size Distribution is necessary.
The European research project nPSize - Improved traceability chain of nanoparticle size measurements aims to fill this gap by developing potential non-spherical reference nanoparticles, measurement procedures and physical modelling to improve the traceability chain, comparability and compatibility for NP size measurements between different methods. Therefore, new model NP with well-controlled shape has been synthesized and are supposed to be systematically characterized using the traceable methods scanning/transmission electron microscopy, atomic force microscopy and small angle X-ray scattering.
Following NP candidates are under investigation with respect to their homogeneity and stability: (i) titania nanoplatelets (10-15 nm thickness x 50-100 nm lateral), (ii) titania bipyramides (~60 nm length x 40 nm width), (iii) titania acicular particles (100 nm length x 15-20 nm width; aspect ratio 5.5/6), (iv) gold nanorods (~10 nm width x 30 nm length), and (v) gold nanocubes (~55 nm x 55 nm x 55 nm). In addition, sample preparation procedures as well as measurement analysis procedures with evaluation of appropriate measurands and descriptors for each material class and method are being developed to support standardization. To underpin the traceability of the size measurement of nonspherical NP, physical modelling of the signals in e.g. electron microscopy techniques will be used and in combination, the implementation of machine learning is aimed to facilitate measurement Analysis procedures, especially regarding the accurate thresholding/segmentation of the NPs.
There are different ways how to prove the quality of the analytical results obtained in a laboratory, e.g. use of validated standard operation procedures, participation in proficiency testing exercises, use of certified reference materials, etc. International standards provide requirements, specifications, Guidelines or characteristics of methods, instruments or samples with the final goal that these can be used consistently in accredited laboratories. In the field of electron microscopy and microbeam analysis standardization and metrology are terms which are encountered rather seldom at major conferences and scientific publications. Nevertheless, spectra formats like EMSA/MSA for spectral-data exchange or tagged image file format (TIFF) for SEM, guidelines for performing quality assurance procedures or for the specification of X-ray spectrometers as well as of certified reference materials (CRMs) in EPMA, or measurement of average grain size by electron backscatter diffraction (EBSD), or guidelines for calibrating image magnification in SEM or TEM are ISO standards already published and used successfully by a large part of the electron microscopy and microbeam analysis community. A main and continuous task of ISO/TC 202 and its subcommittees is to identify and evaluate feasible projects/proposals to be developed into new international standards, particularly with respect to recent but established technology, such the silicon drift detector (SDD) EDS.
An international platform in the frame of which pre-standardization work can be organized is VAMAS (Versailles Project on Advanced Materials and Standards). International collaborative projects involving aim at providing the technical basis for harmonized measurements, testing, specifications, and standards to be further developed at ISO level. One key point of VAMAS activities is constituted by inter-laboratory comparisons for high-quality data. In the field of microbeam analysis, the technical working area (TWA) 37 Quantitative Microstructural Analysis deals with corresponding projects. Good ideas, e.g. on analysis of low-Z materials/elements and at low energies are particularly encouraged by directly contacting the author. Support and already available guidance will be supplied.
The present study reports on measurements on thin Fe-Ni films on silicon and first-time results of analysis on Si-Ge thin films deposited on a non-conductive aluminium oxide Substrate by electron probe microanalysis (EPMA). Standard-based and standardless EPMA (with EDS) results were used in combination with the thin film analysis software Stratagem for the quantification.
Further, X-ray fluorescence analysis (XRF) can be used for the determination of elemental composition and thickness of such films as well. In this case, XRF with a μ-focus X-ray source (μ-XRF) attached to a SEM was applied. For quantification, a fundamental parameter (FP) approach has been used to calculate standard-based and standardless results.
Both thin film systems have been chosen as samples of an international round robin test (RRT) organised in the frame of standardisation technical committee ISO/TC 201 ‘Surface chemical analysis’, under the lead of KRISS. The main objective of the RRT is to compare the results of atomic fractions of Fe1-xNix and Si1-xGex alloy films obtained by different surface Analysis techniques, such as X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES), and secondary ion mass spectrometry (SIMS) applied in the depth-profiling operation mode.
Five samples of different atomic fractions of each thin film system, i.e., Fe1-xNix and Si1-xGex, have been grown by ion beam sputter deposition on silicon and Al2O3 wafers, respectively. Reference FeNi and SiGe films with well-known elemental composition and thickness have been also supplied for standard-based analysis. An excellent agreement has been obtained between the atomic fractions determined by EPMA and µ-XRF with the KRISS certified values.
The characteristics of TiO2 coatings can greatly influence their final performance in large-scale applications. In the present study self-assembly of TiO2 nanoparticles (NPs) in multiple layers was selected as a deposition procedure on various substrates. For this, the main prerequisite constitutes the surface modification of both NPs and substrate with e.g. silane coupling agents. A set of functionalized TiO2 NPs has been produced by reaction with either (3- aminopropyl)triethoxysilane (APTES) or (3-aminopropyl)phosphonic acid (APPA) to functionalize the NP surface with free amino-groups. Then, the complementary functionalized NP set can be obtained from an aliquot of the first one, through the conversion of free surface amino-groups to aldehydes by reaction with glutaraldehyde (GA). Several types of TiO2 NPs differing in size, shape and specific surface area have been functionalized. FTIR, TGA, SEM/EDS, XPS, Auger electron spectroscopy (AES) and ToF-SIMS analyses have been carried out to evaluate the degree of functionalization, all the analytical methods employed demonstrating successful functionalization of TiO2 NP surface with APTES or APPA and GA.
New reference material candidates for traceable size measurement of non-spherical nanoparticles
(2019)
New model nanoparticles with well-controlled shape were synthesized within the EMPIR project nPSize - Improved traceability chain of nanoparticle size measurements. Their systematic characterization takes place by the traceable methods scanning/transmission electron microscopy, atomic force microscopy and small angle X-ray scattering. Following reference nanoparticle candidates are under investigation with respect to their homogeneity and stability: titania nanoplatelets (10-15 nm x 50-100 nm), titania bipyramides (~60 nm x 40 nm), titania acicular particles (100 nm x 15-20 nm; aspect ratio 5.5/6), gold nanorods (~10 nm x 30 nm), and gold nanocubes (~55 nm x 55 nm x 55 nm).
Challenges in Traceable Size Measurement of Non-Spherical, Non-Monodisperse Nanoparticles - nPSize
(2019)
Size measurement of nanoparticles (NP) becomes a challenging analytical problem when non-spherical shapes must be traceably measured. However, most industrial NPs have irregular shapes and broad size distribution making it often more complex to follow European regulatory to identify a material as a nanomaterial according to which accurate measurement of the smallest dimension and its size Distribution is necessary.
The European research project nPSize - Improved traceability chain of nanoparticle size measurements aims to fill this gap by developing potential non-spherical reference nanoparticles, measurement procedures and physical modelling to improve the traceability chain, comparability and compatibility for NP size measurements between different methods. Therefore, new model NP with well-controlled shape has been synthesized and are supposed to be systematically characterized using the traceable methods scanning/transmission electron microscopy, atomic force microscopy and small angle X-ray scattering.
Following NP candidates are under investigation with respect to their homogeneity and stability: (i) titania nanoplatelets (10-15 nm thickness x 50-100 nm lateral), (ii) titania bipyramides (~60 nm length x 40 nm width), (iii) titania acicular particles (100 nm length x 15-20 nm width; aspect ratio 5.5/6), (iv) gold nanorods (~10 nm width x 30 nm length), and (v) gold nanocubes (~55 nm x 55 nm x 55 nm). In addition, sample preparation procedures as well as measurement analysis procedures with evaluation of appropriate measurands and descriptors for each material class and method are being developed to support standardization. To underpin the traceability of the size measurement of nonspherical NP, physical modelling of the signals in e.g. electron microscopy techniques will be used and in combination, the implementation of machine learning is aimed to facilitate measurement Analysis procedures, especially regarding the accurate thresholding/segmentation of the NPs.zeige mehr