The analysis of the chemical composition of cement-based materials like concrete is a crucial task in civil engineering. Concrete is a multi-phase material made of cement, water, aggregates, additives and admixtures. During the damage assessment of concrete structures, the external ingress of harmful species like chlorine, alkalis or sulfates needs to be determined. In order to provide a fast and precise analysis of concrete the application of LIBS offers unique possibilities as the technique can detect all elements at air atmosphere.
To determine the condition of concrete, the information about the chemical composition, the ingress of harmful species as well as the evaluation of characteristic values like the used cement type or the type of aggregates are needed. This work presents the two-dimensional evaluation of concrete samples using LIBS and multivariate data analysis of atomic and molecular emission. For the evaluation of the main components different classification methods will be applied to identify the heterogeneity of the samples. With respect to their specific phase, different species will be quantified using multivariate regression (PLS) and important figures of merit will be presented. All results will be verified using Standard procedure of wet chemistry (XRF, potentiometric titration and ICP-OES).
The propagation of ultrasonic waves in concrete is affected by its micro- and macro-structure, geometry and properties as well as external influences as stress, temperature or moisture. In addition, age and degradation have a strong influence. Therefore, Ultrasound has been used to monitor concrete samples and structures since decades. However, early applications using conventional techniques as time-of flight or changes in amplitudes have been limited to detect changes in a late stage close to serviceability or ultimate load states.
Around 2000, several new, more sensitive techniques adopted from geophysics or other field of material sciences have been introduced to research in ultrasonic monitoring of concrete. The most discussed methodologies are coda wave interferometry, a technique which allows to detect very subtle changes from repeated ultrasonic measurements. Nonlinear acoustic techniques help to identify e. g. cracks even in an inhomogeneous background. Both techniques can be combined.
This paper reviews methods and results achieved so far on the laboratory scale and with full scale models the directions for future research and application is given as well.
The propagation of ultrasonic waves in concrete is affected by its micro- and macro-structure, geometry and properties as well as external influences as stress, temperature or moisture. In addition, age and degradation have a strong influence. Therefore, Ultrasound has been used to monitor concrete samples and structures since decades. However, early applications using conventional techniques as time-of flight or changes in amplitudes have been limited to detect changes in a late stage close to serviceability or ultimate load states.
Around 2000, several new, more sensitive techniques adopted from geophysics or other field of material sciences have been introduced to research in ultrasonic monitoring of concrete. The most discussed methodologies are coda wave interferometry, a technique which allows to detect very subtle changes from repeated ultrasonic measurements. Nonlinear acoustic techniques help to identify e. g. cracks even in an inhomogeneous background. Both techniques can be combined.
This paper reviews methods and results achieved so far on the laboratory scale and with full scale models the directions for future research and application is given as well.
Ultrasonic non-destructive testing methods have found various applications in quality assurance and condition assessment of nuclear concrete structures. This includes but is not limited to the localization of construction features (thickness measurements, reinforcement, tendon ducts, and others) and damage detection (e. g. corrosion or cracks). However, there are still limitations, e. g. limited penetration depth and resolution, issues when testing hybrid steel/concrete structures as well as absence of standards and regulations.
This presentation will show progress in some of these issues and will focus on advanced instrumentation and validation of ultrasonic NDT for concrete structures.
Ultrasonic echo testing has been limited to a penetration depth of less than one meter in reinforced concrete. The development of the LAUS (Large Aperture Ultrasonic System), using a large array of ultrasonic transducers and wider offsets between transmitter and receiver, allows to reach up to 5 m in reinforced concrete and 9 m in unreinforced concrete. This capability has been demonstrated by collecting data from an engineered salt concrete barrier in an underground nuclear waste storage facility. Due to an increasingly competitive environment, commercial manufacturers will continue to develop equipment with enhanced penetration and/or increased resolution.
To quantify the capabilities and reliability of ultrasonic tests, validation mockups with engineered flaws are required. EPRI and BAM have built a large-scale mockup at a test site close to Berlin (BAM-TTS, Horstwalde) using a design which is repeated at other places. This presentation will also cover the methods deployed on engineered flaws and the repeatability of the test results.
Ultrasonic transmission measurements are used to monitor concrete elements mostly on a laboratory scale since decades. Recently, coda wave interferometry, a technique adapted from seismology, has been introduced to civil engineering experiments. It can be used to reveal subtle changes in concrete samples and even large construction elements without having a transducer directly at the location where the change is taking place. The methodology works best with embedded transducers to avoid coupling issues or excessive environmental influence. These transducers can be used for newly built and existing structures. Recently, large concrete beams have been equipped with a network of transducers and loaded until failure. Using code wave interferometry, it was possible to visualize stress fields and damaged areas. This paper gives an overview of the state of the art, recent results achieved at BAM and a task list for further results and development.
Ultrasonic transmission measurements are used to monitor concrete elements mostly on a laboratory scale since decades. Recently, coda wave interferometry, a technique adapted from seismology, has been introduced to civil engineering experiments. It can be used to reveal subtle changes in concrete samples and even large construction elements without having a transducer directly at the location where the change is taking place. The methodology works best with embedded transducers to avoid coupling issues or excessive environmental influence. These transducers can be used for newly built and existing structures. Recently, large concrete beams have been equipped with a network of transducers and loaded until failure. Using code wave interferometry, it was possible to visualize stress fields and damaged areas. This paper gives an overview of the state of the art, recent results achieved at BAM and a task list for further results and development.