The motivation of this work is to produce thin films perovskite solar cells with constant high light conversion efficiency over time. Loss of efficiency may be caused by structural and/or chemical alterations of the complex layered system. As these changes might take place either in the bulk and/or on the surface of the stratified material, analytical tools addressing both key issues are selected and combined. SEM/EDS combined with XPS were chosen as appropriate methodical approach to characterise perovskite laboratory cells in depth and complementary on top, before and after light exposure. The layered perovskite system investigated here is based on glass covered with fluorine doped tin oxide (FTO), followed by three porous thin films of TiO2, ZrO2 and a thick monolithic carbon. The TiO2 film is subdivided into a dense layer covered by a porous one constituted of nanoparticles with a truncated bipyramidal shape. This layered system serves as the matrix for the perovskite. After infiltration of perovskite solution and annealing, EDS
spectral maps on cross-sections of the specimen have been measured. The distribution of relevant
elements – Si, Sn, Ti, Zr and C – correlates conclusively with layers visible in the acquired SEM images. Lead and iodine are distributed throughout the porous layers C, ZrO2 and TiO2. Specimens were exposed to ambient daylight for 7 weeks. In a SEM micrograph taken of the cross-section of a sample after illumination, the glass substrate and all layers FTO, TiO2, ZrO2 as well as C are clearly identified. EDS data have been acquired under the same measurement conditions as before the illumination. It was found that several weeks of ambient daylight did not change significantly the qualitative elemental composition of lead and iodine throughout the solar cell system. It was confirmed with EDS that nanoparticles identified in high-resolution SEM micrographs contain mainly Pb and I, indicating these to be the perovskite
crystals. However, a time-dependent compositional and chemical altering was observed with XPS for the near-surface region of the outermost ~10 nm after 2 months of illumination.
Manufacturing of new perovskite layered solar cells with constant high light conversion efficiency over time may be hampered by the loss of efficiency caused by structural and/or chemical alterations of the complex layered system. SEM/EDX combined with XPS were chosen as an appropriate methodical approach to characterize perovskite laboratory cells in depth and at surface, before and after light exposure. The layered perovskite system investigated here is based on glass covered with fluorine doped tin oxide (FTO), followed by thin films of TiO2, ZrO2 and a thick monolithic carbon. TiO2 film is subdivided into a dense layer covered by porous one constituted of nanoparticles (NPs) of truncated bipyramidal shape. This layered system serves as the matrix for the perovskite. EDX spectral maps on cross-sections of specimen have shown that Pb and I are distributed homogeneously throughout the porous layers C, ZrO2 and TiO2. SEM/EDX data show that 20 weeks of ambient daylight did not change significantly the indepth distribution of the elemental composition of Pb and I throughout the entire solar cell system. It was confirmed with EDX that NPs identified in high-resolution SEM micrographs contain mainly Pb and I, indicating these to be the perovskite crystals. However, a compositional and chemical altering began in the near-surface region of the outermost ~10 nm after 2 months of illumination which was observed with XPS.
Self-assembly of TiO2 nanoparticles in multiple layers by layer-by-layer deposition has been selected of different deposition procedures usually applied for fabrication of TiO2 thin films with defined and homogeneous thickness on supports of interest for the large-scale applications. The substrates tested were: conductive (FTO) glass, silica glass and titanium alloy. The selected film fabrication technique consists of the deposition of alternating layers of oppositely charged, i.e. functionalized, TiO2 nanoparticle layers with wash steps in between. The controlled assembly of TiO2 nanoparticles on the supports surface requires both a proper functionalization of the supports to promote the adhesion of the TiO2 film to the substrates and proper functionalization of TiO2 nanoparticles to allow attachment to substrate and subsequent reaction between different NP layers. The current study focusses on the analytical control of the functionalization of the substrates with 3-Aminopropyltriethoxysilane (APTS) and glutaraldehyde (GA) by means of surface sensitive methods, XPS, Auger Electron Spectroscopy (AES) and ToF-SIMS. Chemical composition of surface of functionalized substrates shows differences in the degree and type of modification in dependence on substrate.
Loss in efficiency of perovskite solar cells may be caused by structural and/or chemical alterations of the complex layered system. As these changes might take place either in the bulk and/or on the surface of the stratified material, analytical tools addressing both key issues are selected and combined. SEM/EDX combined with XPS were chosen as appropriate methodical approach to characterise perovskite laboratory cells in depth and complementary on top, before and after light exposure. The layered perovskite system investigated here is based on glass covered with fluorine doped tin oxide (FTO), followed by three porous thin films of TiO2, ZrO2 and a thick monolithic carbon. The TiO2 film is subdivided into a dense layer covered by a porous one constituted of nanoparticles with a truncated bipyramidal shape. This layered system serves as the matrix for the perovskite. After infiltration of perovskite solution and annealing, EDX
spectral maps on cross-sections of the specimen have been measured. The distribution of relevant
elements – Si, Sn, Ti, Zr and C – correlates conclusively with layers visible in the acquired SEM images. Lead and iodine are distributed throughout the porous layers C, ZrO2 and TiO2. In a SEM micrograph taken of the cross-section of a sample after illumination, the glass substrate and all layers FTO, TiO2, ZrO2 as well as C are clearly identified. By EDX it was found that several weeks of ambient daylight did not change significantly the qualitative elemental composition of lead and iodine throughout the solar cell system. It was confirmed with EDX that nanoparticles identified in high-resolution SEM micrographs contain mainly Pb and I, indicating these to be the perovskite
crystals. However, a time-dependent compositional and chemical altering was observed with XPS for the near-surface region of the outermost ~10 nm after two months of illumination.
Organic surface modification and analysis of TiO2 nanoparticles for self-assembly in multiple layers
(2017)
Parameters of TiO2 coatings can greatly influence their final performance in largescale applications such as photocatalytic measurements, orthopedic and/or dental prostheses, cell cultures, and dye-sensitized solar cells. From different film deposition procedures, self-assembly of TiO2 NPs in multiple layers was selected for systematic characterization. EDX, AES and ToF-SIMS analysis have been carried out in order to evaluate the functionalization of several types of TiO2 NPs differing in size, shape and surface area.
CCQM key comparison K-129 for the quantitative analysis of Cu(In,Ga)Se2 (CIGS) films has been performed by the Surface Analysis Working Group (SAWG) of the Consultative Committee for Amount of Substance (CCQM). The objective of this key comparison is to compare the equivalency of the National Metrology Institutes (NMIs) and Designated Institutes (DIs) for the measurement of mole fractions of Cu, In, Ga and Se in a thin CIGS film. The measurand of this key comparison is the average mole fractions of Cu, In, Ga and Se of a test CIGS alloy film in the unit of mole fraction (mol/mol). Mole fraction with the metrological unit of mol/mol can be practically converted to atomic fraction with the unit of at%.
In this key comparison, a CIGS film with certified mole fractions was supplied as a reference specimen to determine the relative sensitivity factors (RSFs) of Cu, In, Ga and Se. The mole fractions of the reference specimen were certified by isotope dilution - inductively coupled plasma/mass spectrometry (ID-ICP/MS) and are traceable to the SI. A total number counting (TNC) method was recommended as a method to determine the signal intensities of the constituent elements acquired in the depth profiles by Secondary Ion Mass Spectrometry (SIMS), X-ray Photoelectron Spectroscopy (XPS) and Auger Electron Spectroscopy (AES). Seven NMIs and one DI participated in this key comparison. The mole fractions of the CIGS films were measured by depth profiling based-SIMS, AES and XPS. The mole fractions were also measured by non-destructive X-Ray Fluorescence (XRF) Analysis and Electron Probe Micro Analysis (EPMA) with Energy Dispersive X-ray Spectrometry (EDX).
In this key comparison, the average degrees of equivalence uncertainties for Cu, In, Ga and Se are 0.0093 mol/mol, 0.0123 mol/mol, 0.0047 mol/mol and 0.0228 mol/mol, respectively. These values are much smaller than that of Fe in a Fe-Ni alloy film in CCQM K-67 (0.0330 mol/mol). This means that the quantification of multi-element alloy films is possible by depth profiling analysis using the TNC method.
Core–shell nanoparticles (CSNPs) have become indispensable in various industrial applications. However, their real internal structure usually deviates from an ideal core–shell structure. To control how the particles perform with regard to their specific applications, characterization techniques are required that can distinguish an ideal from a nonideal morphology. In this work, we investigated poly(tetrafluoroethylene)–poly(methyl methacrylate) (PTFE–PMMA) and poly(tetrafluoroethylene)–polystyrene (PTFE–PS) polymer CSNPs with a constant core diameter (45 nm) but varying shell thicknesses (4–50 nm). As confirmed by transmission scanning electron microscopy (T-SEM), the shell completely covers the core for the PTFE–PMMA nanoparticles, while the encapsulation of the core by the shell material is incomplete for the PTFE–PS nanoparticles. X-ray photoelectron spectroscopy (XPS) was applied to determine the shell thickness of the nanoparticles. The software SESSA v2.0 was used to analyze the intensities of the elastic peaks, and the QUASES software package was employed to evaluate the shape of the inelastic background in the XPS survey spectra. For the first time, nanoparticle shell thicknesses are presented, which are exclusively based on the analysis of the XPS inelastic background. Furthermore, principal component analysis (PCA)-assisted time-of-flight secondary-ion mass spectrometry (ToF-SIMS) of the PTFE–PS nanoparticle sample set revealed a systematic variation among the samples and, thus, confirmed the incomplete encapsulation of the core by the shell material. As opposed to that, no variation is observed in the PCA score plots of the PTFE–PMMA nanoparticle sample set. Consequently, the complete coverage of the core by the shell material is proved by ToF-SIMS with a certainty that cannot be achieved by XPS and T-SEM.
Low-cost, high-efficient catalysts for water splitting can be potentially fulfilled by developing earthabundant metal oxides. In this work, surface galvanic formation of Co-OH on K0.45MnO2 (KMO) was achieved via the redox reaction of hydrated Co2+ with crystalline Mn4+. The synthesis method takes place at ambient temperature without using any surfactant agent or organic solvent, providing a clean, green route for the design of highly efficient catalysts. The redox reaction resulted in the formation of ultrathin Co-OH nanoflakes with high electrochemical surface area. X-ray absorption spectroscopy (XAS) and X-ray photoelectron spectroscopy (XPS) analysis confirmed the changes in the oxidation state of the bulk and
surface species on the Co-OH nanoflakes supported on the KMO. The effect of the anions, such as chloride, nitrate and sulfate, on the preparation of the catalyst was evaluated by electrochemical and spectrochemical means. XPS and Time of flight secondary ion mass spectrometry (ToF-SIMS) analysis demonstrated that the layer of CoOxHy deposited on the KMO and its electronic structure strongly depend on the anion of the precursor used during the synthesis of the catalyst. In particular, it was found that Cl- favors the formation of Co-OH, changing the rate-determining step of the reaction, which enhances the catalytic activity towards the OER, producing the most active OER catalyst in alkaline media.
Loss in efficiency of perovskite solar cells may be caused by structural and/or chemical alterations of the complex layered system. SEM/EDX combined with XPS were chosen as appropriate methodical approach to characterise perovskite laboratory cells in depth and complementary on top, before and after light exposure. The layered perovskite system investigated here is based on glass covered with fluorine doped tin oxide (FTO), followed by three porous thin films of TiO2, ZrO2 and a thick monolithic carbon. This layered system serves as the matrix for the perovskite. After infiltration of perovskite solution and annealing, EDX spectral maps on cross-sections of the specimen have been measured. The distribution of relevant elements – Si, Sn, Ti, Zr and C – correlates conclusively with layers visible in the acquired SEM images. Lead and iodine are distributed throughout the porous layers C, ZrO2 and TiO2. By EDX it was found that several weeks of ambient daylight did not change significantly the qualitative elemental composition of lead and iodine throughout the solar cell system. It was confirmed with EDX that nanoparticles identified in high-resolution SEM micrographs contain mainly Pb and I, indicating these to be the perovskite
crystals. However, a time-dependent compositional and chemical altering was observed with XPS for the near-surface region of the outermost ~10 nm after two months of illumination.
Manufacturing of new perovskite layered solar cells with constant high light conversion Efficiency over time may be hampered by the loss of efficiency caused by structural and/or chemical alterations of the complex layered system. SEM/EDX combined with XPS were chosen as an appropriate methodical approach to characterize perovskite laboratory cells in depth and at surface, before and after light exposure. The layered perovskite system investigated here is based on glass covered with fluorine doped tin oxide, followed by thin films of TiO2, ZrO2, and a thick monolithic carbon. TiO2 film is subdivided into a dense layer covered by porous one constituted of nanoparticles of truncated bipyramidal shape. This layered system serves as the matrix for the perovskite. EDX spectral maps on cross sections of specimen have shown that Pb and I are distributed homogeneously throughout the porous layers C, ZrO2, and TiO2. SEM/EDX data show that 20 weeks of ambient daylight did not change significantly the in‐depth distribution of the elemental composition of Pb and I throughout the entire solar cell system. It was confirmed with EDX that nanoparticles identified in high‐resolution SEM micrographs contain mainly Pb and I, indicating these to be the perovskite crystals. However, a compositional and chemical altering began in the near‐surface region of the outermost ~10 nm after 2 months of illumination which was observed with XPS.