New Ca- and Sr-based coordination polymers (CPs) were mechanochemically synthesized by milling metal hydroxide samples (M = Ca, Sr) with tetrafluorophthalic acid (H2oBDC-F4) and isophthalic acid (H2mBDC). [Ca(oBDC-F4)(H2O)2] (1) exhibits a small surface area which is slightly increased after removing the crystal water. On the other hand, the hydrated sample of the nonfluorinated [Sr(mBDC)(H2O)3.4] (2) reveals a small BET surface area which remains unchanged even after the release of crystal water via thermal treatment. The new compounds 1 and 2 are similar to their Sr- and Ca-analogs, respectively. These findings are confirmed by thermal analysis, MAS NMR, and ATR-IR measurements, in addition to the Le Bail refinements for the measured powder X-ray data of 1 and 2. Ca- and Sr-CPs based on perfluorinated dicarboxylic systems and their nonfluorinated analogs diverse in structural and chemical properties depending on the geometries of the organic linkers and the presence of fluorine atoms. The fluorinations of organic ligands lead to the formation of fluorinated CPs with higher dimensionalities compared to their nonfluorinated counterparts. Conversely, the thermal stabilities of the latter are higher than those of the fluorinated CPs.
A series of new Ba-based coordination polymers (CPs) were mechanochemically synthesized by milling Ba-hydroxide samples with perfluorinated and fluorine-free benzene-dicarboxylic acids, including tetrafluoroisophthalic acid (H2mBDC-F4), tetrafluorophthalic acid (H2oBDC-F4), isophthalic acid (H2mBDC) and phthalic acid (H2oBDC). The new fluorinated CPs: [Ba(mBDC-F4)$0.5H2O] (1) and [Ba(oBDC-F4)·1.5H2O] (2) are compared to their nonfluorinated counterparts: [Ba(mBDC)·2.5H2O] (3), and [Ba(oBDC)·1H2O] (4). These materials are thoroughly characterized using powder X-ray diffraction. The products obtained by milling are all hydrated but vary in their water contents. Compositions and local structures are investigated by elemental analysis, thermal analysis, MAS NMR and attenuated total reflectioninfrared spectroscopy. These materials exhibit high thermal stabilities but small surface areas that remain unchanged even after thermal treatments.
Ca-, Sr-, and Ba-Based coordination polymers (CPs) were prepared mechanochemically by milling metal-hydroxide samples with anthranilic acid (oABAH). {[Ca(oABA)2(H2O)3]}n consists of one-dimensional polymeric chains that are further connected by a hydrogen-bonding network. {[Sr(oABA)2(H2O)2]·H2O}n is a one-dimensional CP in which water molecules bridge Sr2+ ions and increase the dimensionality by building an extended network. {[Ba(oABA)2(H2O)]}n crystallizes as a two-dimensional CP comprising one bridging water molecule. The cation radii influence the inorganic connectivity and dimensionality of the resulting crystal structures. The crystal structures were refined from powder X-ray diffraction data using the Rietveld method. The local coordination environments were studied via extended X-ray absorption fine structure (EXAFS) measurements. The compounds were further characterized using comprehensive analytical methods such as elemental analysis, thermal analysis, MAS NMR, imaging, and dynamic vapor sorption (DVS) measurements. Compounds 1, 2, and 3 exhibit small surface areas which decrease further after thermal annealing experiments. All compounds exhibit a phase transformation upon heating, which is only reversible in 3.