Attenuation of ultrasonic signals in concrete has the potential to carry much information about the microstructure of the material. In this work a series of concrete specimens of varying porosities and pore size distributions were internally imaged with x-ray computed tomography (CT), and then subsequently examined with throughtransmission ultrasound. The CT images were used to quantify both capillary porosity of cement paste as well as internal interfaces that are likely to produce elastic wave scattering. Ultrasound signals were represented as a diffusion process such that absorption and scattering attenuation could be isolated. As implemented, the diffusion model was a poor predictor of capillary porosity, while diffusivity was a reasonable predictor of scattering interfaces. Diffusivity was found to scale extremely well with small scale porosity, which made it a good predictor of compressive strength.
With a goal to improve our understanding of the relationships between microstructural features and ultrasonic signal behavior, concrete specimens of varying water-to-cement ratio were imaged using X-ray computed tomography (CT), and subsequently subjected to ultrasonic testing. From the CT scans, measurements were made of cement paste density and number of interfaces. Ultrasonic signals produced using a through-transmission configuration were analyzed and fit to a diffusion model to separate absorption from scattering attenuation. The results showed that at the frequencies tested, ultrasonic dissipation rate correlated weakly with paste density, while diffusivity correlated well with number of interfaces, but only if entrained air is considered separately. Cement paste density was found to be very well predicted by diffusivity, leading to a clear power-law relationship between diffusivity and compressive strength.