3D coherence scanning interferometry (CSI) is an optical, non-contact and rapide measurement technique using a defined bandwidth of white light at normal incidence. Based on this operational principle, white light interference microscopy (WLIM) provides three-dimensional surface topometry data up to a resolution of 0.4 μm lateral and 0.1 nm vertical. Three operating modi, i.e. surface, films and advanced films, enable measurements of step heights, roughness, wear volume, cone angle, surface pattern and layer thickness of transparent coatings.
The determination of layer thickness by WLIM requires the knowledge of optical constants, i.e.the refractive index n and the extinction coefficient k. For technical surfaces, data base values - if available at all - have to be determined or validated by spectroscopic ellipsometry (SE). From this oblique incidence technique both optical constants and layer thickness can be derived based on a model for at least semi-transparent coatings. For different layer thicknesses, a
comparison is made between WLIM and SE. Measurement uncertainty is
discussed for both topometric features and layer thickness for different use cases.
Traceability to SI system is ensured by certified standards (PTB/NIST) within a DAkkS DIN EN ISO/IEC 17025:2018 accredited lab.
3D coherence scanning interferometry (CSI) is anoptical, non-contact and rapide measurement technique using a defined bandwidth of white light at normal incidence. White light interference microscopy (WLIM) providest here-dimensional surface topometry data up to a resolution of 0.4 µm lateral and 0.1 nm vertical. Three operating modi, surface, films and advanced films, enable measurements of step heights, roughness, wear volume, cone angle, surface pattern and layer thickness. Traceability to SI system is ensured by certified standards (PTB/NIST) within a DAkkS DIN EN ISO/IEC 17025:2018 accredited lab.
Porous materials play an important role in several fields of technology, especially for energy applications like photovoltaics, electrolysis or batteries. The activity of porous films is affected by properties like porosity, film thickness, chemical composition of the material as well as the crystallinity of the framework. The complex morphology of such porous films constitutes a challenge even for modern analytical techniques and requires new approaches employing the combination/complementation of data of different analytical methods. In this contribution we characterize thin mesoporous iridium-titanium mixed oxide film properties by Electron Probe Microanalysis (EPMA) with energy dispersive X-ray spectroscopy (EDS) at an SEM.
Ellipsometry has become a powerful measurement tool in semiconductor industry since the sixties of the last century.
Early standardization activities focused exclusively on SiO2/Si (ASTM F 576-01, SEMI 3624). The first generic standard dealing with ellipsometry is DIN 50989-1:2018 Ellipsometry – Part 1: Principles. Standardization is a prerequisite for accreditation according to DIN EN ISO/IEC 17025 and the evaluation of uncertainty budgets.
Porous materials play an important role in several fields of technology, especially for energy applications like photovoltaics, electrolysis or batteries. The activity of porous films is affected by properties like porosity, film thickness, chemical composition of the material, as well as the crystallinity of the framework. The complex morphology of such porous films constitutes a challenge even for modern analytical techniques and requires new approaches employing the combination/complementation of data of different analytical methods. In this contribution, we characterise thin mesoporous iridium-titanium mixed oxide film properties by electron probe microanalysis (EPMA) with energy-dispersive X-ray spectroscopy (EDS) at an SEM.
Mesoporous iridium oxide - titanium oxide (IrOx-TiOx) films were prepared via dip-coating of a solution containing a triblock-copolymer as structure-directing agent, an iridium precursor as well as a titanium precursor in ethanol. IrOx-TiOx films were synthesized with different amounts of iridium and calcined in air. The SEM micrographs reveal for all films the achievement of a well-ordered mesoporous structure and homogeneous films with thicknesses between 67 nm and 152 nm.
For the determination of film elemental composition and porosity, EPMA can be used as part of a combined SEM/EDS/STRATAGem analysis. Elemental compositions and mass depositions (in μg cm-2) of IrOx-TiOx films were calculated with the thin film analysis Software STRATAGem via k-values measured with SEM/EDS. Pure bulk Ir, TiO2 and Si were measured as references. The average density of the films was obtained from the mass Deposition and the film thickness as measured by cross-section SEM. The porosity was then extracted from the measured average film density divided by a theoretical bulk density. The latter is calculated from the weight fractions of IrOx and TiOx as determined with STRATAGem and the bulk mass densities of IrO2 and TiO2 (rutil) from literature.
The fitting results of the k-values from the STRATAGem software, which are in fair agreement with the measured k-values.
The application of the SEM/EDS/STRATAGem approach for accurate porosity determination on pure mesoporous TiOx films and pure porous IrOx films has been recently demonstrated.
The porosities of pure IrOx, TiOx and mixed IrOx-TiOx films in this study have been determined. The contribution will assess in detail the advantages and limitations of the combined SEM/EDS/STRATAGem analysis for the morphology and porosity of thin metal oxide films. Moreover, the comparison with other measurement techniques and the combination of datasets from multiple measurements will be discussed.
Ziel des Projektes HARFE (Haftfestigkeit Reproduzierbarkeit Festigkeit) war es, eine Er-höhung der Haft- bzw. Klebfestigkeit auf Niedrigenergie-Polymeren (PE, PP, PTFE) zu erreichen. SENTECH realisierte dazu plasmachemische Oberflächenaktivierungen mit O2 und die Abscheidung von Aluminiumoxidschichten (Al2O3) mittels Atomic Layer Deposition (ALD), wobei die Ellipsometrie zum in-situ Monitoring der ALD-Prozesse diente. Die BAM charakterisierte die modifizierten Oberflächen bezüglich der Oberflächenenergie (OFE) und bestimmte die Verbund- bzw. Klebfestigkeit mittels der Zentrifugentechnologie
For the determination of porosity of Ir oxide thin films, electron probe microanalysis (EPMA) can be used as part of a combined SEM/EDS/STRATAGem analysis. The mass deposition (in μg cm-2) of films was calculated with the analysis software STRATAGem via k-values measured with EDS. The average density of coated films was obtained from the mass deposition and the film thickness as measured by the cross-section SEM. The porosity was calculated by dividing the average film density by the bulk (theoretical) density of the film material.
Film porosities were counterchecked by spectroscopic ellipsometry (SE) using the Bruggeman effective medium approximation (BEMA).
The results obtained by both analytical approaches/methods used, SEM/EDS/STRATAGem and SE were in good agreement.
A femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated by XRD and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation.
Thin mesoporous metal oxide films are versatile and attractive candidates for several energy applications like photovoltaics, electrolysis or batteries. Due to their high surface area and ordered pore structure, mesoporous metal oxides demonstrate higher activities. The performance of the porous films is affected by properties like size and shape of the mesopores as well as the crystallinity of the framework. The exact determination and metrological evaluation of the complex morphology of thin mesoporous films requires a new analytical approach employing to combined data of different analytical methods. In this contribution we present a novel evaluation procedure for spectroscopic ellipsometry (SE) to analyse thin mesoporous iridium oxide films.
Mesoporous iridium oxide films were prepared via dip-coating of a solution containing a triblock-copolymer as structure directing agent and an iridium precursor in ethanol. Deposited films were calcined in air at temperatures between 300 and 600 °C. Their morphology was studied with SEM and an electron probe microanalysis (EPMA)and correlated via SE with a Bruggeman effective medium approximation (BEMA). The developed SE model described the film thickness as well as the porosity.
Figure 1a shows a top-view SEM image of mesoporous IrO2 film calcined at 375 °C. The image reveals that the films exhibit a well-ordered mesopore structure with an average pore diameter of 16 nm and a periodic distance between pore centres of 24 nm (FFT inset). Figure 1b is a parity plot of film thicknesses determined by cross-section SEM versus SE of IrO2 film samples prepared at different calcination temperatures. The porosity from the SE model is in good agreement to the porosity values obtained by EPMA.
The contribution will assess in detail the novel approach to analyse the morphology and porosity of thin metal oxide films with spectroscopic ellipsometry. Moreover, the advantages of the new developed approach will be discussed as well as combination of datasets from multiple measurements to development new methods for innovative energy technologies.
Ellipsometry is well known as a highly sensitive and reproducible surface analysis technique. However, in a context of metrological applications, the most important property of a measurement process is accuracy, relying on statistical precision, (reproducibility) and trueness (in an absolute sense versus a given standard). The latter is much more difficult to achieve. In this presentation, we discuss the possibility of establishing ellipsometry in a diverse metrological landscape by means of defining standard procedures and best practice methodologies for the measurement and for calibration purposes. The most important task of this approach is to determine the model-inherent uncertainty, originating from parameter coupling. We achieve this by means of sensitivity analysis of the parameters resulting from the fit process. We discuss the definition of reference materials by which accuracy can be made available for ellipsometry, passed along between ellipsometry laboratories and for other measurement techniques. The determination of uncertainty is presented in this work for a number of examples involving difficult analysis models employed for samples from different production environments. We present a standardization initiative with the goal to disseminate this work into an international standard alongside an inter-laboratory study comparing the results for complex samples gained by laboratories with different instrumentation. We also present the results gained within EURAMET projects focused on the metrology of materials with strong non-idealities used in photovoltaics and other energy technology.