The Effect of Low Charge Polycarboxylate on C3A Passivation Monitored by Optical Spectroscopy
(2019)
Tricalcium aluminate (C3A) is less than 10 wt.% of the total cement composition; however, during hydration, the soluble C3A plays an important role in cement setting when mixed with the appropriate amount of sulfate.1 A good understanding about the balance of these components is therefore crucial to follow with the rapid growth of substitution materials and the rising levels of aluminate clinker. The aim of this investigation is the use of optical spectroscopy and in-situ X-ray diffraction utilizing a water-soluble organic dye (dye-S) to monitor early hydration of calcium aluminate (C3A) in the presence of 26 wt.% CaS04.2H2O (G) and PCE polymers with different charge densities (PCE-LC and PCE-HC). Phase characterization and optical evaluation were performed using in-situ X-ray diffraction and steady-state fluorescence and diffuse reflectance spectroscopy. Fluorescence spectroscopy of the reference C3A + dye-S revealed a fast decay in fluorescence intensity. However, in the presence of 26 wt.% G (C3A + dye-S + 26 wt.% G), a gradual increase in fluorescence intensity was observed in the first hours of reaction followed by a plateau that subsequently dropped in intensity after eight hours. The addition of PCE-LC and PCE HC to the mixture exhibited changes in the intensity threshold and overall a higher fluorescence intensity. Dye changes during hydration and structural changes will be further discussed.
The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has enormous influence on the early hydration of cement. C3A as the most reactive phase of Portland cement plays a significant role in early hydration reactions and affects the rheological performance. Therefore, this paper presents experimental results about the influence of delayed addition of PCEs on the Hydration of cement and C3A-gypsum pastes investigated by isothermal heat flow calorimetry. Complementary in-situ XRD was carried out on C3A pastes to analyze hydration and phase changes related to the addition of PCE.
Cement pastes with a delayed addition of PCE showed less Retardation compared to simultaneous addition. The alteration caused by PCE is much more pronounced for C3A-gypsum mixes. With a delayed addition of SP, the hydration of C3A is less retarded or even accelerated. It is obvious that there is less retardation the later the addition of SP. Furthermore, the PCE alter the hydration of C3A when added delayed and exhibit changes in kinetics and hydration rates. XRD results showed that more C3A is dissolved in the presence of PCE. Also, the gypsum depletion occurs earlier in the presence of PCE and even faster with delayed addition. Without PCE AFm starts to form just after the gypsum depletion. However, in the presence of PCE AFm already starts to form at the beginning of the hydration. Due to the faster gypsum depletion in the presence of PCE, also the transformation from ettringite into AFm begins earlier, but takes longer as without SP.
The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has enormous influence on the early hydration of cement. C3A as the most reactive phase of Portland cement plays a significant role in early hydration reactions and affects the rheological performance. Therefore, this talk presents experimental results about the influence of delayed addition of PCEs on the Hydration of alite and C3A-gypsum pastes investigated by isothermal heat flow calorimetry. Complementary in-situ XRD was carried out on C3S and C3A-gypsum pastes to analyze hydration and phase changes related to the addition of PCE. Cement pastes with a delayed addition of PCE showed less retardation compared to simultaneous addition. The alteration caused by PCE is much more pronounced for C3A-gypsum mixes. With a delayed addition of SP, the hydration of C3A is less retarded or even accelerated. It is obvious that there is less retardation the later the addition of SP. Furthermore, the PCE alter the hydration of C3A when added delayed and exhibit changes in kinetics and Hydration rates. XRD results showed that more C3A is dissolved in the presence of PCE. Also, the gypsum depletion occurs earlier in the presence of PCE and even faster with delayed addition. Without PCE AFm starts to form just after the gypsum depletion. However, in the presence of PCE AFm already starts to form at the beginning of the hydration. Due to the faster gypsum depletion in the presence of PCE, also the transformation from ettringite into AFm begins earlier, but takes longer as without SP.