Influence of the of dealumination and porosity on the acid sites of natural zeolite clinoptilolite
(2016)
Heavy feedstock from crude and bio oil is a widely available and renewable resource for production of fuel and starting materials for other organic valuables by cracking or hydrocracking. Catalytic processing of heavy feedstock can meet the increased demand of energy up to a great extent. It requires the application of acidic catalysts like zeolites. However, the used synthetic catalysts are difficult to recover and reuse and are mostly spent.
The use of natural zeolite as spent catalysts may open new perspectives in the chemical use of heavy feed feedstock by chemical conversion. Natural zeolites are not expensive, widely available and environment friendly. Clinoptilolite is the most abundant natural zeolite. Clinoptilolite has a crystalline structure with a defined micropore system of medium size showing unique ion exchange and sorption properties. However, it is catalytically active only in the H-form. Also certain porosity is required for improvement of the accessibility of active sites.
This paper deals with the tuning of acid properties and of the mesoporosity of the clinoptilolite by variation of the Si/Al framework ratio, extra-framework aluminum and modification of the porosity by specific acid and water vapor treatment. The preparation of hierarchical pore structures containing interconnected micro-meso-macropores is an important factor influencing the catalytic performance.
The obtained materials have been characterized by XRD, TEM, FTIR, Raman, TG/DSC. The chemical composition has been determined by ICP-AES. The porosity have been investigated by nitrogen adsorption desorption measurements. The acidity has been measured by Ammonia-TPD. The extent of dealumination, stability of the clinoptilolite against acid treatment and the change in the nature of acid sites and their local structure has been studied by solid state 29Si and 27Al MAS NMR spectroscopy in detail. The catalytic activity has been investigated in the acetalization of benzaldehyde with 1,3-butanediol. The impact of the porosity, change of the Si/Al ratio as well as present Al species on catalytic properties will be discussed.
Natural zeolite clinoptilolite CLIN with a framework ratio of Si/Al ≥ 4 containing mainly potassium and calcium ions in its internal channel system was used as a starting material. The acidic HCLIN catalysts were prepared under soft conditions avoiding the use of environmental less benign mineral acids. The starting material was ion exchanged using a 0.2 M aqueous ammonium nitrate solution at a temperature 80 ◦C for 2 h. The obtained NH4CLIN was converted into the acid HCLIN catalyst by calcination at 300–600 ◦C. The obtained samples were characterized by XRD, FTIR, SEM/TEM, AAS, and EDX element mapping. The state of aluminium and silicon was studied by 27Al- and 29SiMAS NMR spectroscopy. The textural properties of the catalysts were investigated by nitrogen adsorption and desorption measurements. The Brønsted acidity of the HCLIN catalysts was studied by temperature-programmed decomposition of the exchanged ammonium ions releasing ammonia as well as 1H MAS NMR, {1H–27Al} Trapdor, and {1H–27Al}
Redor experiments. The strongly agglomerated samples were crystalline and thermally stable up to >500 ◦C. Although a part of the clinoptilolite framework is maintained up to 600 ◦C, a loss of crystallinity is already observed starting from 450 ◦C. The specific surface areas of the starting CLIN and ammonium exchanged NH4CLIN are low with ca. 26 m2/g. The pores are nearly blocked by the exchangeable cations located in the zeolite pores. The thermal decomposition of the ammonium ions by calcination at 400 ◦C causes an opening of the pore entrances and a markable increase in the specific micropore area and micropore volume to ca. 163 m2/g and 0.07 cm3/g, respectively. It decreases with further rising calcination temperature indicating some structural loss. The catalysts show a broad distribution of Brønsted acid sites (BS) ranging from weak to strong sites as indicated the
thermal decomposition of exchanged ammonium ions (TPDA). The ammonium ion decomposition leaving BS, i.e., H+ located at Al–O–Si framework bridges, starts at ≥250 ◦C. A part of the Brønsted sites is lost after calcination specifically at 500 ◦C. It is related to the formation of penta-coordinated aluminium at the expense of tetrahedral framework aluminium. The Brønsted sites are partially recreated after repeated ammonium ion exchange. The catalytic performance of the acidic HCLIN
catalysts was tested in the etherification of glycerol as a green renewable resource with different C1 -C4 alcohols. The catalysts are highly active in the etherification of glycerol, especially with alcohols containing the branched, tertiary alkyl groups. Highest activity is observed with the soft activated catalyst HCLIN300 (300 ◦C, temperature holding time: 1 min). A total of 78% conversion of glycerol to mono and di ether were achieved with tert-butanol at 140 ◦C after 4 h of reaction.
The mono- and di-ether selectivity were 75% and 25%, respectively. The catalyst can be reused.