The detection of cracks before the failure is highly significant when it comes to safety-relevant structures. Crack detection in metallic samples at high surface temperature is one of the challenging situation in manufacturing industries.
Laser thermography has already proved its detection capability of surface cracks in metallic samples at room temperature. In this work a continuous wave (CW) laser use to generate a laser, which is using to scan the metal surface with notch.
The corresponding heat distribution on the surface monitored using infrared thermal (IR) camera. A simplified 3D model for laser thermography is developed and validated with experimental results. A dedicated image processing algorithm developed to improve the detectability of the cracks. To understand the dependency of surface temperature, laser power, laser scanning speed etc. in defect detection, we carried out parametric studies with our validated model. Here we Report the capability of laser thermography in crack detection at elevated temperature.
Data fusion for multi-sensor nondestructive detection of surface cracks in ferromagnetic materials
(2018)
Fatigue cracking is a dangerous and cost-intensive phenomenon that requires early detection. But at high test sensitivity, the abundance of false indications limits the reliability of conventional materials testing. This thesis exploits the diversity of physical principles that different nondestructive surface inspection methods offer, by applying data fusion techniques to increase the reliability of defect detection. The first main contribution are novel approaches for the fusion of NDT images. These surface scans are obtained from state-of-the-art inspection procedures in Eddy Current Testing, Thermal Testing and Magnetic Flux Leakage Testing. The implemented image fusion strategy demonstrates that simple algebraic fusion rules are sufficient for high performance, given adequate signal normalization. Data fusion reduces the rate of false positives is reduced by a factor of six over the best individual sensor at a 10 μm deep groove. Moreover, the utility of state-of-the-art image representations, like the Shearlet domain, are explored. However, the theoretical advantages of such directional transforms are not attained in practice with the given data. Nevertheless, the benefit of fusion over single-sensor inspection is confirmed a second time. Furthermore, this work proposes novel techniques for fusion at a high level of signal abstraction. A kernel-based approach is introduced to integrate spatially scattered detection hypotheses. This method explicitly deals with registration errors that are unavoidable in practice. Surface discontinuities as shallow as 30 μm are reliably found by fusion, whereas the best individual sensor requires depths of 40–50 μm for successful detection. The experiment is replicated on a similar second test specimen. Practical guidelines are given at the end of the thesis, and the need for a data sharing initiative is stressed to promote future research on this topic.
Crack detection in steel bars at high surface temperatures is a critical problem in any manufacturing industry. Surface breaking cracks are the major problems during the billet casting. Many NDT techniques are proven its capability in crack detection at room temperature. Here, we are demonstrating the possibility of exposure of cracks using laser line thermography at higher surface temperatures (up to 600 °C). A continuous-wave (CW) laser is used to excite the sample kept at higher surface temperatures. The temperature distribution over the sample due to the laser line scanning is captured using a temperature calibrated infrared (IR) thermal camera. The response of the sample temperature in crack detection is investigated using a validated FE model. The impact of the oxide layer in crack detection is investigated by using two types of samples; one without any oxide layer and the second is with the oxide layer. The influence of laser power in the detection of defects at high temperatures is studied. 3D numerical models were developed for the cases; when the sample is with oxide layer and without any oxide layer for a better understanding of physics. The surface temperature rise due to laser heating is higher for the scaled sample compared to the no-scale sample. The presence of the oxide layer above the parent metal will reduce the reflectivity of the surface. Lower reflectivity will lead to increased absorption of incident energy so that the surface temperature rise will be higher than the surface with no scale. Thermal contrast linearly depends on laser power, which means higher laser power will increase the defect detectability even at a higher surface temperature.