Electron backscatter diffraction and energy-dispersive X-ray spectrometry were used to investigate the intermixed interface produced during laser cladding of a Co-Cr-Mo alloy on a steel substrate. A multi-component system and rapid solidification conditions together lead to a complex microstructure at the interface. The solidification of the cladding starts with the formation of an interface layer, which is about 75µm in thickness and consists of randomly oriented equiaxed grains of Co-Cr-Fe solid solution and martensite. Orientation analysis of the grains in the interface layer revealed that some grains have a special orientation relationship with the former austenite grains in the heat affected zone but the cladding is not formed by epitaxial growth on the substrate. Intermixing of the materials at the interface is providing a strong bond between the substrate and the cladding. For a grain from the interface layer to emerge as columnar grain in the cladding, it was determined that its <001> crystallographic direction is not supposed to deviate more than 25° from the sample normal direction.
Optical and scanning electron microscopy, as well as electron microprobe analysis and electron backscatter diffraction, have been used to study diffusion processes that occur in a diffusion pair that consistsof a single-crystal CMSX-10 nickel-base superalloy and polycrystalline nickel, at temperatures of 1050–1250°C. It has been found that, in this system, the distributions of γ-stabilizing elements (Cr, Co, W, and Re) are described by the Boltzmann solution for diffusion between two semiinfinite plates of a binary alloy. The processing of these distributions has shown that the diffusion coefficients of Cr, Co, W, and Re in the multicomponent system are close to those in binary alloys of these elements with Ni. The diffusion redistribution of the elements leads to the dissolution of the γ′ phase in the nickel-base superalloy, growth of nickel grains toward the superalloy constituent of the diffusion pair, and the formation of porosity on both sides of the migrating interface, which is determined from a crystal misorientation of the alloy single crystal and nickel grains.