Due to the penetration of harmful chlorides into concrete, e.g. from de-icing salt, damage processes such as chloride-related pitting corrosion can occur if critical values are exceeded. In this study, multiphase materials such as chloride-contaminated concrete are examined in detail. A direct comparison is made by analyzing the spectroscopic information of simultaneously measured atomic and molecular emissions with laser-induced breakdown spectroscopy (LIBS). In addition, the influence on the calibration is examined on the basis of the combined spectral information of both reaction paths of the penetrated chlorides. The calibration models of univariate and multivariate methods were validated using reference samples with wet chemical analysis. The results are applied to a concrete sample of a parking deck, which was also analyzed by potentiometric wet chemistry. In order to account for the heterogeneity of concrete, spatially (200 μm) and spectroscopically (0.1 nm) resolved LIBS measurements were performed using a fully automated laboratory system. Simultaneous measurements with three spectrometers allow the analysis of the emission processes of several elements such as Cl, Ca, O, Si and Mg as well as the newly formed molecules CaO and CaCl. The evaluation of the molecular emission in combination with atomic lines extends the analytical performance, since different concrete phases such as aggregates and cement matrix can be better represented. The measurements were carried out in ambient air and with helium purge gas. The limit of detection (LOD) achieved for a combined evaluation of atomic and molecular emission was determined to be 0.028 wt%.
The effect of particle grain sizes in different cement-based mixtures on the laser-induced plasma evolution is studied using two experimental methods: (i) temporal and spatial evolution of the laser-induced shock wave is investigated using shadowgraphy and two-dimensional plasma imaging, and (ii) temporal and spatial distribution of elements in the plasma is investigated using two-dimensional spectral imaging. This study is motivated by the interest in applying laser-induced breakdown spectroscopy (LIBS) for chemical analysis of concrete, and subsequently obtain information related to damage assessment of structures like bridges and parking decks. The distribution of grain sizes is of major interest in civil engineering as for making concrete different aggregate grain sizes defined by a sieving curve (64mm to 0.125 mm) are needed. Aggregates up to a size of 180 μm can be excluded from the data set, therefore only the amount of small aggregates with a grain size below 180 μm must be considered with LIBS. All components of the concrete with a grain size smaller than 0.125mm are related to the flour grain content. Tested samples consisted of dry and hardened cement paste (water-cement ratio w/z=0.5), which served as a reference. Aggregate mixtures were made by adding flour grains (size 40 μm) and silica fume (size 0.1 μm) in different ratios to cement: 10%, 30%, 50% and 60%, all combined to the remaining percentage of dry or hydrated cement. The visualization results show that a dependance in the evolution of the plasma as a function of sample grain size can be detected only in the initial stages of the plasma formation, that is, at the initial 3 μs of the plasma life. Spectral information reveals the elemental distribution of the silicon and calcium in plasma, in both neutral and ionized form. Here also, a significant effect is observed in the first 1 μs of the plasma lifetime.