Analytische Chemie
Filtern
Erscheinungsjahr
- 2023 (45) (entfernen)
Dokumenttyp
Sprache
- Englisch (44)
- Mehrsprachig (1)
Referierte Publikation
- ja (45) (entfernen)
Schlagworte
- Machine learning (5)
- Concrete (3)
- LIBS (3)
- Non-destructive testing (3)
- Additive manufacturing (2)
- Artificial neural networks (2)
- Automatic segmentation (2)
- BOFDA (2)
- Defect detection (2)
- Dice score (2)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (45) (entfernen)
Paper des Monats
- ja (5)
An observation of the fracture process in front of the crack tip inside a dentin sample by means of ex-situ X-ray computed tomography after uniaxial compression at different deformation values was carried out in this work. This ex-situ approach allowed the microstructure and fracturing process of human dentin to be observed during loading. No cracks are observed up to the middle part of the irreversible deformation in the samples at least visible at 0.4μm resolution. First cracks appeared before the mechanical stress reached the compression strength. The growth of the cracks is realized by connecting the main cracks with satellite cracks that lie ahead of the main crack tip and parallel its trajectory. When under the stress load the deformation in the sample exceeds the deformation at the compression strength of dentin, an appearance of micro-cracks in front of the main cracks is observed. The micro-cracks are inclined (~60°) to the trajectory of the main cracks. The further growth of the main cracks is not realized due to the junction with the micro-cracks; we assume that the micro-cracks dissipate the energy of the main crack and suppressed its growth. These micro-cracks serve as additional stress accommodations, therefore the samples do not break apart after the compression test, as it is usually observed under bending and tension tests.
In this work, the thermal properties of ternary Li₃ₓCo₇₋₄ₓSb₂₊ₓO₁₂ solid solutions are studied for different concentrations in the range 0 ≤ x ≤ 0.7. Samples are elaborated at four different sintering temperatures: 1100, 1150, 1200 and 1250 °C. The effect of increasing the content of Li⁺ and Sb⁵⁺, accompanied by the reduction of Co²⁺, on the thermal properties is studied. It is shown that a thermal diffusivity gap, which is more pronounced for low values of x, can be triggered at a certain threshold sintering temperature (around 1150 °C in this study). This effect is explained by the increase of contact area between adjacent grains. Nevertheless, this effect is found to be less pronounced in the thermal conductivity. Moreover, a new framework for heat diffusion in solids is presented that establishes that both the heat flux and the thermal energy (or heat) satisfy a diffusion equation and therefore highlights the importance of thermal diffusivity in transient heat conduction phenomena.
A novel DAS setup based on geometric phases in coherent heterodyne detection is applied for the first time to the characterisation of the Earth’s subsurface. In addition, an optimisation of the proposed setup in terms of its spatial resolution is also presented for the first time. The surface waves are generated by strong blasts of 25 kg of explosives at a dedicated test site. A 10 km dark fiber link in the vicinity of the test site connected to the test setup records the resulting strain signals. The spike-free and low-noise strain data thus obtained minimize post-processing requirements, making the setup a candidate for real-time seismic monitoring. An analysis of the dispersion characteristics of the generated surface waves is performed using a recently reported optimised seismic interferometric technique. Based on the dispersion characteristics, the shear wave velocities of the surface waves as a function of the depth profile of the Earth’s crust are determined using an optimised evolutionary algorithm.
Human factors (HFs) are a frequently mentioned topic when talking about the reliability of non-destructive testing (NDT). However, probability of detection (POD), the commonly used measure of NDT reliability, only looks at the technical capability of an NDT system to detect a defect.
After several decades of research on the influence of HFs on NDT reliability, there is still no commonly accepted approach to rendering HFs visible in reliability assessment. This paper provides an overview of possible quantitative and qualitative methods for integrating HFs into the reliability assessment. It is concluded that reliability assessment is best carried out using both quantifiable and non-quantifiable approaches to HFs.
It is shown that preconditioning of experimental X‐ray computed tomography (XCT) data is critical to achieve high‐precision segmentation scores. The challenging experimental XCT datasets and deep convolutional neural networks (DCNNs) are used that are trained with low‐resemblance synthetic XCT data. The material used is a 6‐phase Al–Si metal matrix composite‐reinforced with ceramic fibers and particles. To achieve generalization, in our past studies, specific data augmentation techniques were proposed for the synthetic XCT training data. In addition, two toolsets are devised: (1) special 3D DCNN architecture (3D Triple_UNet), slicing the experimental XCT data from multiple views (MultiView Forwarding), the i.S.Sy.Da.T.A. iterative segmentation algorithm, and (2) nonlocal means (NLM) conditioning (filtering) for the experimental XCT data. This results in good segmentation Dice scores across all phases compared to more standard approaches (i.e., standard UNet architecture, single view slicing, standard single training, and NLM conditioning). Herein, the NLM filter is replaced with the deep conditioning framework BAM SynthCOND introduced in a previous publication, which can be trained with synthetic XCT data. This leads to a significant segmentation precision increase for all phases. The proposed methods are potentially applicable to other materials and imaging techniques.
Gas source localization (GSL) helps mitigate the impact of industrial accidents and natural disasters. While GSL may be dangerous and time-consuming when performed by humans, swarms of agile and inexpensive nano aerial robots may increase the safety and efficiency of gas source localizations. Since the small payloads of nano aerial robots limit the sensing and computing resources, strategies adapted from biological swarms, such as colonies of social insects, are used to coordinate robot swarms. Most swarm GSL strategies are based on the assumption that the maxima of gas concentrations are sufficiently close to the gas sources. However, prior studies have indicated that the occurrence of “bouts”, a metric for the intermittency of gas distributions, may advantageously be used as a more accurate gas source proximity indicator. This paper presents a swarm GSL strategy employing bouts as source proximity indicators and a bio-inspired pheromone system for communication. Nano aerial robots, deployed in this study, act as agents and emit pheromone markers in an artificial environment upon detecting bouts. Leveraging the concept of artificial potential fields, the agents switch between exploiting the knowledge of the swarm by following pheromone gradients and exploring the search space by targeting a random point. The agents are repelled by each other and by walls to avoid collisions. The swarm GSL strategy is implemented into three nano aerial robots and validated in a real-world experiment in an indoor environment with a single gas source. The results indicate that the the swarm GSL strategy presented in this paper is capable of GSL in indoor environments and that the intermittency of gas distributions is a better source proximity indicator than the mean concentration.
High energy X-ray synchrotron diffraction is used to investigate the elastic anisotropy of the nickel-based superalloy IN718 produced by laser powder bed fusion (PBF-LB). This material is characterized by a columnar grain morphology with some crystallographic texture. The material is subjected to elastic loading to determine the diffraction elastic constants (DECs). Furthermore, the single-crystal elastic constants (SCEC) are refined from these experiments using different micromechanical models. The results show that each micromechanical model predicts a specific set of SCEC that well describes the elastic anisotropy of PBF-LB/IN718.
Laser powder bed fusion is one of the most promising additive manufacturing techniques for printing complex-shaped metal components. However, the formation of subsurface porosity poses a significant risk to the service lifetime of the printed parts. In-situ monitoring offers the possibility to detect porosity already during manufacturing. Thereby, process feedback control or a manual process interruption to cut financial losses is enabled.
Short-wave infrared thermography can monitor the thermal history of manufactured parts which is closely connected to the probability of porosity formation. Artificial intelligence methods are increasingly used for porosity prediction from the obtained large amounts of complex monitoring data. In this study, we aim to identify the potential and the challenges of deep-learning-assisted porosity prediction based on thermographic in-situ monitoring.
Therefore, the porosity prediction task is studied in detail using an exemplary dataset from the manufacturing of two Haynes282 cuboid components. Our trained 1D convolutional neural network model shows high performance (R² score of 0.90) for the prediction of local porosity in discrete sub-volumes with dimensions of (700 x 700 x 40) μm³.
It could be demonstrated that the regressor correctly predicts layer-wise porosity changes but presumably has limited capability to predict differences in local porosity. Furthermore, there is a need to study the significance of the used thermogram feature inputs to streamline the model and to adjust the monitoring hardware. Moreover, we identified multiple sources of data uncertainty resulting from the in-situ monitoring setup, the registration with the ground truth X-ray-computed tomography data and the used pre-processing workflow that might influence the model’s performance detrimentally.
In this study, the wavefield radiated from a building to its surroundings is identified and extracted from M4.6 earthquake recordings collected by sensors installed in a building and on the nearby athletic field in Matera (Italy) using a new approach for soil-structure interaction assessment. The proposed approach for earthquake data analysis combines in an innovative way two methods already used in seismology and engineering seismology: deconvolution and polarization analysis. The approach enables the identification, reconstruction, and characterization of the wavefield radiated from a vibrating building into its surroundings, and the estimation of the amount of energy associated with it. The approach consists of four steps: estimation of the resonant frequencies of the building, deconvolution of the earthquake recordings from a building and its surroundings, identification of the seismic phases, reconstruction of the signal transmitted from the building to its surroundings, and estimation of its energy, and polarization analysis. Analysis of recordings of the M4.6 event highlighted that the motion related to the wavefield radiated from the building to the ground was mostly linearly polarized in the radial and transverse planes, while a clear ellipticity was observed only in the horizontal plane. The wavefield radiated from the building might be dominated by unconventionally polarized surface waves, i.e., quasi-Rayleigh waves or a combination of quasi-Rayleigh and quasi-Love waves. The results indicated that the energy transmitted from the analyzed vibrating building to its surroundings was significant and decreased the ground motion shaking due to the out-of-phase motion.