Green Intelligent Building
Filtern
Erscheinungsjahr
- 2024 (4)
Dokumenttyp
- Vortrag (2)
- Zeitschriftenartikel (1)
- Beitrag zu einem Tagungsband (1)
Sprache
- Englisch (4)
Referierte Publikation
- nein (4) (entfernen)
Schlagworte
- 3D concrete printing (1)
- AFm phases (1)
- Alkali-activated materials (1)
- Alkali-activated slags (1)
- Automatization (1)
- Brown Coal Fly Ash (1)
- Chloride binding (1)
- Chloride sorption isotherms (1)
- Concrete (1)
- Design (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (2)
Concretes produced from salt aggregate and hybrid alkaline cements, an alkali-activated slag/fly ash blend, or a Portland cement were exposed to a magnesium chloride-rich saline solution ([Mg2+] = 3.6 m, [Cl−] = 8.3 m), representing a solution formed after contact of surface water with evaporite rock (rock salt) in a nuclear waste repository. The hydration and deterioration of the concretes were studied with X-ray diffraction, thermogravimetric analysis, pH mapping and permeability measurements. The results show that calcium silicate hydrate (C-S-H) or sodium-substituted calcium aluminium silicate hydrate (C-N-A-S-H) and Friedel's salt were the major reaction products in the concretes prior to exposure to the saline solution. During exposure to the saline solution, increasing amounts of C-S-H/C-N-A-S-H dissolved, and gypsum and a secondary AFm phase formed. The durability of the concretes improved with increasing amounts of Portland clinker in the cements, due to the associated differences in permeability and chemical resistance. Nevertheless, a massive increase of permeability occurred for all concretes, likely caused by crack formation due to the formation of gypsum from anhydrite in the salt aggregate. Thus, the behavior of the concretes differed from, and was more complex than, the behavior of plain cement pastes.
3D concrete printing is an innovative new construction technology offering the potential to enable an efficient production of individual structures with less consumption of resources. The technology will mainly shape the future construction philosophy, automate the build process and help reaching the climate goals in civil engineering. From the design of a structure to the printed component, many individual steps based on different software are required which must be repeated for each new or changed structure. First, the geometry of the structure is created in a CAD program. Second, the print path is defined in a slicer software creating the machine code for the printer (G-Code). Finally, the structure can be printed. Furthermore, a numerical model of the printed structure is necessary for process optimization and control. In that way the number of test prints can be reduced, costs can be saved, and the component behavior can be predicted. For those purposes, an automated workflow allowing to run all steps or individual steps without interacting with each individual software program is required. Furthermore, changes in parameters or the exchange of parts (using a different design or different printer) must be possible in a simple manner. In the presented work, such an automated workflow based on the example of a parametrized wall element for extrusion-based concrete printing is developed. The investigated wall structure is parametrized using the global geometry parameters: height, width, thickness, radius, kind of infill structure (honey-comb, zig-zag) and number of repeated infills. All above mentioned steps are implemented via python interfaces using pydoit as workflow tool. General interfaces with prescribed input and output files are defined allowing adaptations for different software and tools. The described workflow is tested by performing a test series investigating the influence of the in-fill structure on the mechanical properties of the test walls.
Chloride binding by the hydrate phases of cementitious materials influences the rate of chloride ingress into these materials and, thus, the time at which chloride reaches the steel reinforcement in concrete structures. A particularly important role in this context is played by layered double hydroxides (LDHs), including AFm phases. Chloride binding isotherms of individual LDH/AFm phases would be required as input for computational models of chloride ingress, but such isotherms are only available for a few AFm phases, and in addition the available data are partly conflicting.
The present study, conducted in the context of RILEM TC 283-CAM ‘Chloride transport in alkali-activated materials’, significantly extends the available database by determining the chloride binding isotherms of LDH/AFm phases (monosulfate, strätlingite, hydrotalcite, and meixnerite), and of alkali-activated slags (AAS) produced with four different activators (Na2SiO3, Na2O∙1.87SiO2, Na2CO3, and Na2SO4), in NaOH/NaCl solutions at various liquid/solid ratios. Selected solids after chloride binding were analysed by X-ray diffraction, and thermodynamic modelling was applied to simulate the phase changes occurring during chloride binding by the AFm phases.
The chloride binding isotherms of LDH/AFm phases depended strongly on the liquid/solid ratio during the experiments, resolving apparent contradictions of the previously available data. The dependency on liquid/solid ratio must be attributed to kinetic restrictions, which are, however, currently poorly understood. Chloride binding by AAS pastes was generally higher than for Portland cement pastes and was only moderately influenced by the employed activator. A steep increase of the chloride binding by AAS occurred at free chloride concentrations above approx. 1.0 M, which is possibly related to chloride binding by the C-(N-)A-S-H gel in the AAS.
Portland cement is one of the principal sources of anthropomorphic CO2 emissions. It is estimated that cement production contributes up to 10% of greenhouse gas emissions and annual cement production over 4 billion tons. This has led to the development of a range of alkali activated materials (AAM), the most common precursor materials being class F fly ash and blast furnace slag. At present Class C Fly Ash is not widely utilized as an AAM due to the chemical composition and activation requirements. However, initial research on high Calcium German Class C Fly Ash suggests that the material may have potential for application as an AAM. This paper reports the development of ambient cured alkali activated mortar optimised by varying the alkali modulus and w/b ratio. The evolution of the mechanical and microstructural properties is reported over the initial 28 day period. Compressive strength in excess of 10 MPa at 7 days and 15 MPa at 28 days was achieved at ambient temperature. Similar strengths were observed for both 10% and 15% dosage but as dosage increases the optimal Alkali Modulus reduces.