9.0 Abteilungsleitung und andere
Filtern
Dokumenttyp
- Vortrag (131)
- Zeitschriftenartikel (51)
- Beitrag zu einem Tagungsband (26)
- Posterpräsentation (9)
- Buchkapitel (2)
- Forschungsbericht (2)
- Tagungsband (Herausgeberschaft für den kompletten Band) (1)
- Dissertation (1)
- Sonstiges (1)
Schlagworte
- Hydrogen (48)
- Welding (35)
- Wasserstoff (28)
- Schweißen (20)
- Diffusion (16)
- Hydrogen assisted cracking (15)
- Creep-resistant steel (14)
- High-entropy alloy (12)
- High Entropy Alloy (11)
- Mechanical properties (10)
Organisationseinheit der BAM
- 9.0 Abteilungsleitung und andere (224) (entfernen)
Paper des Monats
- ja (7)
Zur Umsetzung der wasserstoffbasierten Energiewende ist eine zuverlässige Transportinfrastruktur unverzichtbar. Hierfür ist die Nutzung großer Teile des vorhandenen Erdgasnetzes vorgesehen. Im Rahmen von Reparatur- und Wartungsarbeiten ist das Schweißen im Betrieb an Erdgaspipelines Stand der Technik. In Verbindung mit Wasserstoff wirft diese Technik jedoch Fragen der Materialverträglichkeit auf. Das im Vortrag vorgestellte Projekt H2SuD leistet Beiträge zur Aufklärung des Einflusses von Reparaturschweißprozessen auf die Wasserstoffaufnahme und Degradation im Betrieb befindlicher H2 Gasleitungen. Ein Schwerpunkt des Vortrages liegt auf der im Projekt erarbeiteten Prüfmethode für Modellversuche, mit denen der Einfluss von Schweißen im Betrieb an Pipelines auf die Wasserstoffaufnahme getestet wird. Die Durchführung erster Versuche und dabei erzielte Ergebnisse werden präsentiert.
Mikrolegierungselemente wie Nb und Ti sind entscheidend für die erwünschte mechanische Festigkeit von vergüteten Feinkornbaustählen mit einer Nennstreckgrenze von ≥ 690 MPa. Aktuelle Spezifikationen geben lediglich Obergrenzen für die chemische Zusammensetzung vor, allerdings können geringfügige Abweichungen erhebliche Auswirkungen auf die mechanischen Eigenschaften haben. Die Vorhersage der Schweißbarkeit und Integrität von Schweißverbindungen stellt aufgrund der variierenden Zusammensetzung und Mikrostrukturen Herausforderungen dar. Unerwünschte Effekte wie Erweichung der Wärmeeinflusszone (WEZ) oder Verfestigung können auftreten. Um dies zu untersuchen, wurden verschiedene Mikrolegierungsrouten mit variierenden Ti- und Nb-Gehalten an Laborschmelzen erforscht. Die Basis jeder Route entsprach der üblichen S690QL in Zusammensetzung und Wärmebehandlung. Dreilagenschweißungen wurden mittels Metallaktivgasschweißens (MAG) durchgeführt, um kritische Gefügebereiche zu identifizieren. Die Analyse konzentrierte sich auf Phasenumwandlungen während der Abkühlung und metallurgisches Ausscheidungsverhalten. Die mechanischen Eigenschaften der Schweißnähte wurden durch Zugversuche ermittelt. Die Ergebnisse zeigen einen bedeutenden Einfluss der Mikrolegierungsroute und Schweißwärmezufuhr auf die Ausscheidungskinetik, trotz insgesamt guter Schweißbarkeit der Werkstoffe.
Mikrolegierungselemente, wie Nb und Ti, sind für die signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zusammensetzung geben dabei nur obere Grenzwerte für die Hersteller vor. Weiterhin wirken sich bereits kleine Abweichungen in der Legierungsroute teilweise drastisch auf die mechanischen Eigenschaften aus. Somit wird eine adäquate Vorhersage der Schweißeignung und der Integrität der Schweißverbindung aufgrund der variierenden Mikrogefüge erschwert bis unmöglich. Unerwünschte Nebeneffekte sind die mögliche Erweichung der Wärmeeinflusszone (WEZ) als auch der gegenteilige Effekt der Aufhärtung. Vor diesem Hintergrund werden erstmals systematisch die unterschiedlichen Mikrolegierungsrouten mit variierenden Ti und Nb-Gehalten an Versuchsschmelzen untersucht. Die Stahlgüte S690QL bildet dabei die Grundlage der chemischen Zusammensetzung sowie der entsprechenden Wärmebehandlung. Zur Untersuchung der jeweiligen Schweißeignung wurden Dreilagen-Schweißungen mittels moderner MAG-Hochleistungsschweißprozesse durchgeführt und kritische Gefügebereiche mit hoher Erweichung/Aufhärtung identifiziert. Der Fokus der analytischen Betrachtungen lag hier auf der Identifikation der Phasenumwandlungen beim Abkühlen und auf dem metallurgischen Ausscheidungsverhalten. Zusätzlich wurden isotherme und nicht-isotherme Phasenberechnungen mit der Software Thermo-Calc durchgeführt. Mechanisch-technologische Untersuchungen zur Kerbschlagzähigkeit mittels Kerbschlagbiegeversuchen durchgeführt wurden, bestätigen dabei die Ergebnisse der thermodynamischen Simulation bezüglich des Ausscheidungsverhaltens während der Temperatur-Zeit Schweißzyklen. Daraus lässt sich der Einfluss der Wärmeeinwirkung beim Schweißen auf die Gefügeausbildung in der WEZ und der korrespondierenden mechanischen Eigenschaften qualitativ beschreiben.
Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods, or jackets. These components are typically constructed using submerged arc welding (SAW) with high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen-assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicates the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam/layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with over 20 passes and a seam length of 1000 mm. Additional welded stiffeners simulated the effect of a high restraint, to achieve critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of up to 48 h after the completion welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modeling allowed the qualitative estimation of the hydrogen diffusion in the weld. No noticeable HAC occurrence was identified and confirms the high cracking resistance of the investigated material. Finally, the applicability of the MWT concept should be critically discussed.
Steelmaking slag is a by-product of steel production, of which 4.5 Mt were produced in 2020 in Germany alone. It is mainly used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical cycle, used as fertiliser or landfilled.
With this use, iron oxides still contained in steelmaking slag are lost. In addition, the possibility of producing higher-grade products from steelmaking slag is foregone. In recent decades, many researchers have investigated the production of Portland cement clinker and crude iron from basic oxygen furnace slags (BOFS) via a reductive treatment. Carbothermal treatment of liquid BOFS causes a reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. Simultaneously, the chemical composition of the reduced slag is adapted to that of Portland cement clinker.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as a reducing agent. The resulting low-iron mineral product has a similar chemical composition to Portland cement clinker and was rich in the tricalcium silicate solid solution alite (Ca3SiO5). Based on its chemical and mineralogical composition, similar to that of Portland cement clinker, the reduced BOFS has the potential to react comparably. In our study, the reduced BOFS produced less hydration heat than OPC, and its hydraulic reaction was delayed. However, adding gypsum has shown to accelerate the hydration rate of the reduced BOFS compared to that known from the calcium silicates of Portland cement clinker.
Further research to improve the hydraulic properties of the reduced slag is essential. If successful, producing a hydraulic binder and crude iron from BOFS has economic and ecological benefits for both the cement and steel industries.
Mikrolegierungselemente, wie Nb und Ti, sind für die signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zu-sammensetzung geben dabei nur obere Grenzwerte für die Hersteller vor. Weiterhin wirken sich bereits kleine Abweichungen in der Legierungsroute teilweise drastisch auf die mechanischen Eigenschaften aus. Somit wird eine adäquate Vorhersage der Schweißeignung und der Integrität der Schweißverbindung aufgrund der variierenden Mikrogefüge erschwert bis unmöglich.
Die Nb-mikrolegierte Güte weist im Vergleich zur Ti-mikrolegierten Güte eine bessere Anlassbeständigkeit auf. Eine divergente Phasenverteilung in den äußeren Zonen der WEZ der Fülllagen erklärt die unterschiedliche Härteverteilung in der WEZ der drei untersuchten Legierungen und die markanten Unterschiede der Kerbschlagzähigkeit. Die quasistatischen Querzugversuche mittels DIC zeigten ein divergentes lokales Dehnungsverhalten auf. Die Ti-mikrolegierte Stahlsorte zeigt ein signifikanten lokales Dehnungsverhalten in der WEZ, wobei hier sich aufgrund der hohen metallurgischen Kerbwirkung Makrostützeffekte während des plastischen Fließens in der WEZ auftreten.
Offshore-Windenergieanlagen erfordern Gründungskonzepte aus unterpulver-(UP-)geschweißten Dickblechen (bspw. der Güte S420ML). Während der Schweißfertigung kann eine zeitverzögerte wasserstoffunterstützte Kaltrissbildung auftreten, deren Bewertung aufgrund der Bauteilgröße von Offshore-Strukturen sehr komplex ist. Deswegen wurde eine bauteilähnliche Geometrie (Mock-Up) entwickelt, um reale Steifigkeitsverhältnisse auf den Labormaßstab zu übertragen. Zusätzliche Versteifungen simulieren die Wirkung einer Einspannung bzw. Schrumpfbehinderung der Schweißnaht. Über die Verwendung von Schweißpulvern mit definierter Feuchte wurden zudem ein Extremszenario der Wasserstoffaufnahme simuliert. Entsprechend der vorgegebenen Mindestwartezeit für die ZfP von bis zu 48 h wurde die Schweißnaht zerstörungsfrei mit Phased-Array-Ultraschall-Prüfung (PAUT) geprüft und die Eigenspannungen über Röntgendiffraktometrie (XRD) bestimmt. Zusätzlich wurde die Wasserstoffverteilung in der Schweißverbindung numerisch simuliert. Außer zulässigen Defekten (wie Poren), wurde keine verzögerte Kaltrissbildung in den Mock-Ups festgestellt, was auf hohe Rissbeständigkeit hindeutet.
Offshore-Windenergieanlagen erfordern Gründungskonzepte aus unterpulver-(UP-)geschweißten Dickblechen (bspw. der Güte S420ML). Während der Schweißfertigung kann eine zeitverzögerte wasserstoffunterstützte Kaltrissbildung auftreten, deren Bewertung aufgrund der Bauteilgröße von Offshore-Strukturen sehr komplex ist. Deswegen wurde eine bauteilähnliche Geometrie (Mock-Up) entwickelt, um reale Steifigkeitsverhältnisse auf den Labormaßstab zu übertragen. Zusätzliche Versteifungen simulieren die Wirkung einer Einspannung bzw. Schrumpfbehinderung der Schweißnaht. Über die Verwendung von Schweißpulvern mit definierter Feuchte wurden zudem ein Extremszenario der Wasserstoffaufnahme simuliert. Entsprechend der vorgegebenen Mindestwartezeit für die ZfP von bis zu 48 h wurde die Schweißnaht zerstörungsfrei mit Phased-Array-Ultraschall-Prüfung (PAUT) geprüft und die Eigenspannungen über Röntgendiffraktometrie (XRD) bestimmt. Zusätzlich wurde die Wasserstoffverteilung in der Schweißverbindung numerisch simuliert. Außer zulässigen Defekten (wie Poren), wurde keine verzögerte Kaltrissbildung in den Mock-Ups festgestellt, was auf hohe Rissbeständigkeit hindeutet.
Hydrogen and its derivatives (e.g. ammonia) are considered as a suitable energy carrier in the future supply of renewable energy. Hydrogen transportation systems require pipes, valves and fittings, among other components. In this sense, austenitic stainless steels are commonly used structural materials for pure hydrogen applications. Stable austenitic alloys, like AISI 316L, are often assumed to be practically unsusceptible to hydrogen embrittlement. At the same time, a number of studies show the influence of hydrogen even in 316L under some circumstances. Some other studies state that this embrittlement could be avoided by using steel grades with a higher nickel equivalent which contributes to a more stable austenitic phase. Nonetheless, 316L is widely used in hydrogen atmospheres since many years because of lower costs and positive practical experience. For these reasons, not only 316L but also 304 could be further utilized by identifying the exact constraints.
With increasing demand for components regarding hydrogen applications, additive manufacturing technologies are getting increasingly important complementary to conventional manufacturing. In the context of additive manufacturing, 316L is a common material as well. The manufacturing process offers great advantages due to higher freedoms in design and the possibility for customized components in small batches. For example, valves with improved flow characteristics and reduced component weight can be produced. Nevertheless, there is still lack of experience and experimental results concerning additively manufactured parts under hydrogen service. Therefore, the influence on the material properties for additively manufactured parts in hydrogen environments needs to be further investigated.
In the present work, slow strain rate testing (SSRT) has been applied using hollow specimens. This testing procedure allows to perform practicable and faster in-situ tests in comparison to tests in autoclaves and investigate the influence of hydrogen on the mechanical properties.
Conventional AISI 304 and 316L specimens as well as additively manufactured 316L specimens were tested at room temperature and a pressure of 200 bar. Elongation at fracture and relative reduction of area (RRA) have been used to evaluate the influence of hydrogen. It is shown that the influence of hydrogen is more pronounced in 304 than in 316L. Furthermore, potentially influencing factors such as surface roughness, microstructure and porosity are discussed.