Wissenschaftliche Artikel der BAM
Carbon Fibre Reinforced Plastics (CFRP) are more and more used in modern civil aircrafts. These days the whole fuselage is made of this material (B787; A350). Due to strict certification standards the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles and the first inter-fibre failure was evaluated non-destructively by accompanying Xray-refraction topography. A tensile testing machine was integrated in a small angle X-ray scattering (SAXS) setup. X-ray refraction topography was performed while the CFRP samples were tensile loaded. This non-destructive technique enables the detection of micro-cracking and inter-fibre failure especially for CFRP. For Glass Fibre Reinforced Plastic (GFRP) X-ray refraction and in-situ loading has already been successfully used. The increase of inner surfaces due to inter fibre failure was measured as a function of the stress state. Fatigue tests were performed at and below the limit of inter-fibre failure strength. State of the art is to assume the failure of the samples under cyclic loading as the fatigue life. Accompanying non-destructive X-ray refraction measurements reflects the damage state and enables to trace its evolution even if the total failure of the specimens does not occur. This investigation technique is of high interest to give the engineer a design value of infinite life which is practically often reached due to knock down factors of certification standards. Finally the infinite life was found for cyclic fatigue loaded CFRP-samples even under high inter fibre transverse and shear loading investigated up to 108 load cycles.
The canister for the permanent storage of spent nuclear fuel used by SKB in Sweden consists of a cast iron insert surrounded by a five centimetre thick shell of copper. It is a safety critical component and in order to secure long-term structural integrity non-destructive methods are used to inspect 100% of the volume of each canister, before it is disposed of in the repository. One of the critical components that requires inspection is a sealing weld, joining the copper tube and the lid. The friction stir weld is inspected using an ultrasonic phased array system. The area of the weld is inspected with several inspection channels with different angles and varying coverage. To make sure that no defects that might occur in the weld are overseen, the reliability of the inspection must be quantified. The reliability of NDT is usually quantified with the probability of detection curves. The influence of the parameters that might influence the POD of the flaws in the weld is investigated analysing the experimental results, as well as with a help of a numerical simulation of the inspection.
Measurement of spontaneous magnetic stray field signals has been reported to be a promising tool for capturing macro-scale information of deformation states, defects and stress concentration zones in a material structure. This paper offers a new method for self-magnetic leakage field detection using a magneto-optical (MO) hand-held microscope. Its sensor has a dynamic field range between ±0.05 and ±2 kA/m and a lateral optical resolution of approx. 10 µm. We examined flat tensile test specimens of metastable austenitic steel AISI 304. Static tensile tests were repeatedly interrupted at various predetermined states of strain and the magnetic information was measured by the MO system. Comparative measurements using a high-precision magnetic field GMR-sensor, verify the outstanding capability of the MO microscope regarding spatial resolution of magnetic fields.
The digital photography has almost completely substituted the film photography. The film replacement is also fast progressing in medical X-ray radiography. This process is slower in NDT and especially in Europe. Reasons for the hesitating change to digital radiography (RT-D) in NDT are the necessary time for adoption of standards and the conservative request for film RT by auditors and NDT managers for applications in large plants and at construction areas. The fast serial inspection for small castings is already almost completely dominated by RT-D due to the cost effective short exposure and interpretation times. Standards were developed in parallel at CEN, ISO, ASTM and ASME. Unfortunately, the standard practices are different and the requirements on image quality and useable hardware are different too. The first standard series on Computed Radiography were developed and published by CEN and ASTM in 2005. Harmonized classification and qualification standards are available but the published practices are different. ASTM has developed the first standards for application of Digital Detector Arrays (DDA) in 2010. The first digital RT ISO standard practice is ISO 17636-2 (2013), which describes the practice for application of DDAs and Imaging Plates for weld inspection. At the first time this standard provides requirements for the selection of suitable hardware. Minimum image quality requirements are specified in analogy to film radiography and 3 Compensation Principles are defined to enable the application of a wider range of digital detectors. A comparison of the different international digital RT standards is given and first experiences with ISO 17636-2 are discussed. New standards on RT wall thickness and corrosion measurements (EN 16407, film and digital) have been developed recently.
In this contribution, we present a dual high-energy X-ray imaging technique for cargo container inspection using the 'spectral high-energy X-ray attenuation method'. This method is based on attenuation of continuous highenergy spectra. The developed experimental technique consists of a betatron as high-energy (up to 7.5 MeV) X-ray source and a matrix detector with high spatial resolution (400 ìm) for digital X-ray imaging. In order to evaluate the material discrimination capability using dual high-energy X-ray imaging, a test specimen is proposed, comprising step wedges of different low and high atomic number (Z) materials. The selected X-ray spectra for the dual-energy experiments correspond to 3 MV and 7.5 MV acceleration potential of the betatron. We evaluated the ratio between low- and high-energy X-ray attenuation coefficients quantitatively based on simulated poly-energetic high-energy X-ray source spectra and the detector sensitivity using the 'analytical Radiographic Testing inspection simulation tool' (aRTist) developed at BAM. The simulated effective attenuation coefficients are compared with corresponding experimental results in order to establish a method for identification of low- and high-Z materials in the container. Finally, important applications of the proposed technique in the context of aviation security are discussed.
Critical parts in aircraft manufacturing such as stringers are very commonly used in modern aircraft structures to resist the compressive loads caused by the aerodynamic effects. They are generally made-up of thin aluminium (Al) metal sheets and are one of the key components in the aircraft wings. Any defects in the stringer leads to weakening of the stiffness of the whole wing structure and consequently, failures may occur. Hence, the structural integrity of the stringers should be evaluated using reliable non-destructive testing (NDT) methods. Due to the complex shaped structure of the stringer, the one-sided access NDT method such as X-ray backscatter technique is more preferable for the non-destructive imaging. In this paper, we present a new X-ray backscatter technique to image the internal sections of the stringer with only a single-sided access. The whole object was inspected by changing the viewing direction of the X-ray backscatter camera. For the first time, the X-ray backscatter measurements were conducted using high-energy (> 0.5MeV) X-rays and proved the applicability of the present technique to inspect thick carbon-fiber laminated components. In order to improve the inspection time and image quality of the backscatter image, we used high-resolution (180ìm) digital detector arrays (DDAs). At the end, important applications of the presented X-ray backscatter technique to the aerospace industry are discussed.