Wissenschaftliche Artikel der BAM
We report on calibration standards of nanoparticles meeting the definition of a nanomaterial given by the European Commission (EU 2011) which are relevant for the characterisation methods applied in the NanoDefine project. We found that the Impact of nanoparticles is outstanding in the scientific literature. A number of 270.000 paper titles on nanoparticles are listed in the Web of Science data base. But surprisingly, the availability of suitable certified standard reference materials is scarce. Only a few sources were found. For example, BAM provides the database Nanoscaled Reference Materials at http://www.nano-refmat.bam.de/en/ in cooperation with the ISO/TC 229 Nanotechnologies. In addition, two publications from 2013 on nanoscale reference materials are available. Candidates of nano-(certified) reference materials from other ongoing or just finished FP6 and FP7 nano-metrology projects have been extracted from the Compendium of Projects in the European NanoSafety Cluster (Compendium NSC, 2013). Recommendations for selection of representative test materials and calibration standards for NanoDefine internal tasks, respectively, are also given.
Starch is one of the most common and easily obtained natural polymers, making it attractive as a potential bio-based alternative to synthetic polymers. This study shows that a simple quaternary ammonium salt combined with urea or glycols forms effective modifiers that produce flexible plastics with good mechanical properties that are comparable to some polyolefin plastics. The processing conditions are shown to significantly affect the structure of the polymer which has a concomitant effect upon the mechanical and physical properties of the resulting plastic. Using a glycerol based modifier results in a totally sustainable and biodegradable material which can be injection moulded.
The synthesis of the polymorphic cocrystal caffeine:anthranilic acid was investigated to obtain a better understanding of the processes leading to the formation of different polymorphic forms. In the case of these cocrystal polymorphs synthesized by liquid-assisted grinding a distinct influence of the dipole moment of the solvent was found. A pre-coordination between the solvent molecules and the caffeine:anthranilic acid cocrystal could be identified in the formation of form II. In the case of form II the solvent can be regarded as a catalyst. The formation pathway of each polymorph was evaluated using synchrotron X-ray diffraction.
The mechanochemical synthesis of two model compounds, a metal organic framework ([Bi(1,4-bdc)2]*(Im) (bdc = benzene dicarboxylate, Im = imidazole cation)) and a cocrystal (Carbamazepine:Indometacin 1:1) were followed ex situ by combined analytical methods. Powder X-ray diffraction (XRD) and Raman spectroscopy data were evaluated for the synthesis of the metal organic framework. XRD measurements and REM images were analysed for the synthesis of the cocrystal. The measurements revealed that both model compounds were synthesised within minutes. The metal organic framework [Bi(1,4-bdc)2]*(Im) is synthesised via an intermediate structure. The cocrystal Carbamazepine:Indometacin 1:1 is formed within few seconds and afterwards the crystallite size decreases extremely.
Two metal organic structures composed of the ligands benzene-1,4-dicarboxylate and pyridine-2,5-dicarboxylate and bismuth cations are presented: (H2Im)[Bi(1,4-bdc)2] (1) and [Bi(pydc)(NO3)2(H2O)2]*H2O (2) (bdc = benzenedicarboxylate, H2Im = imidazole cation, pydc = pyridinedicarboxylate). Both compounds were synthesised via grinding and the crystal structure of compound (2) was solved based on its powder diffraction pattern. Compound 1 crystallises isostructurally to the dimethyl ammonium containing compound (dma)[(Bi(1,4-bdc)2]. Raman spectroscopy and Extended X-ray absorption fine structure (EXAFS)
measurements provided additional information about the two mechanochemically synthesised metal organic compounds.
The vibrational density of states of a series of homologous triphenylene-based discotic liquid crystals HATn (n = 5, 6, 8, 10, 12) depending on the length of the aliphatic side chain is investigated by means of inelastic neutron scattering. All studied materials have a plastic crystalline phase at low temperatures, followed by a hexagonally ordered liquid crystalline phase at higher temperatures and a quasi isotropic phase at the highest temperatures. The X-ray scattering pattern for the plastic crystalline phase of all materials shows a sharp Bragg reflection corresponding to the intercolumnar distance in the lower q-range and a peak at circa 17 nm-1 related to intracolumnar distances between the cores perpendicular to the columns as well as a broad amorphous halo related to the disordered structure of the methylene groups in the side chains in the higher q-range. The intercolumnar distance increases linearly with increasing chain length for the hexagonal columnar ordered liquid crystalline phase. A similar behaviour is assumed for the plastic crystalline phase. Besides n = 8 all materials under study exhibit a Boson peak. With increasing chain length, the frequency of the Boson peak decreases and its intensity increases. This can be explained by a self-organized confinement model. The peaks for n = 10, 12 are much narrower than for n = 5, 6 which might imply the transformation from a rigid system to a softer one with increasing chain length. Moreover the results can also be discussed in the framework of a transition from an uncorrelated to a correlated disorder with increasing n where n = 8 might be speculatively considered as a transitional state.