Ground penetrating radar (GPR) was used to characterize the frequency-dependent dielectric relaxation phenomena in ordinary Portland cement (OPC) hydration in concrete changing from fresh to hardened state. The study was experimented by measuring the changes of GPR A-scan waveforms over a period of 90 days, and processed the waveforms with short-time Fourier transform (STFT) in joint time-frequency analysis (JTFA) domain rather than a conventional time or frequency domain alone. The signals of the direct wave traveled at the concrete surface and the reflected wave from an embedded steel bar were transformed with STFT, in which the changes of peak frequency over ages were tracked. The peak frequencies were found to increase with ages and the patterns were found to match closely with primarily the well-known OPC hydration process and secondarily, the evaporation effect. The close match is contributed to the simultaneous effects converting free to bound water over time, on both conventional OPC hydration and dielectric relaxation mechanisms.
The changes in the sonic surface wave velocity of concrete under stress were investigated in this paper. Surface wave velocities at
sonic frequency range were measured on a prismatic concrete specimen undergoing several cycles of uniaxial compression. The
loading was applied (or removed) gradually in predefined small steps (stress-controlled). The surface wave velocity was measured
at every load step during both loading and unloading phases. Acoustic Emission (AE) test was conducted simultaneously to
monitor the microcracking activities at different levels of loading. It was found that the sonic surface wave velocity is highly stress
dependent and the velocity-stress relationship follows a particular trend. The observed trend could be explained by a combination
of acoustoelasticity and microcracking theories, each valid over a certain range of applied stresses. Having measured the velocities
while unloading, when the material suffers no further damage, the effect of stress and damage could be differentiated. The slope
of the velocity-stress curves over the elastic region was calculated for different load cycles. This quantity was normalized to yield a
dimensionless nonlinear parameter. This parameter generally increases with the level of induced damage in concrete.