Large, ink-bottle-shaped pores in mesocellular foams (MCFs) are desired for various applications requiring enhanced mass transfer or the immobilization of larger compounds. Hence, the cylindrical pores of COK-12, an ordered mesoporous silica structurally comparable to SBA-15 but synthesized at room-temperature at quasi-neutral pH, are chemically swollen into ink-bottle pores. Therefore, p-xylene is used as a more sustainable swelling agent compared to popular alternatives. Its high boiling point allows for an additional thermal aging step to amplify the mesostructure enlargement without needing additional chemicals. For COK-12, the MCFs obtained at room temperature reach an unprecedented plateau for the modal mesopore cell and window diameter of 19.9 and 5.5 nm, respectively, with an underlying broad pore size distribution and distorted hexagonal lattice up to 14.5 nm, involving hexagonal and spherical structures. The combined chemical and thermal swelling resulted in the selective enlargement of the window diameter to more than 200% and a slightly increased cell diameter, pore size distribution, and hexagonal lattice distortion in comparison to the room temperature synthesis. Such materials are thought to be promising alternatives to SBA-15-based MCFs, often utilizing toxic catalysts during synthesis. The presented results pave the way for enhanced adsorptive, catalytic, and drug delivery performances for COK-12-based materials.
The continuously increasing use of plastics is supposed to result in a rising exposure of MNPs to humans. Available data on human health risks of microplastics after oral uptake increased immensely in the past years and indicates very likely only low risks after oral consumption. Concerning nanoplastics, uptake, transport and potential adverse effects after oral uptake are less well understood. This study aims to investigate differences between microplastic particles and particles in the submicron- and nanoscaled size derived from food-relevant polymers with a particle size range consistent with higher potential for cellular uptake, fate, and effects when applied to human intestinal and liver cells. This work includes the development of cellular and subcellular detection methods for synthetic polymeric particles in the micro- and nanometer-range, using Scanning Electron Microscopy, Small-Angle X-ray and Dynamic Light Scattering methods, Asymmetric Flow Field Flow Fractionation, octanol-water fractionation, fluorescence microscopy and flow cytometry. Polylactic acid (250 nm and 2 μm (polydisperse)), melamine formaldehyde (366 nm) and polymethylmethacrylate (25 nm) were thoroughly characterized. The submicro- and nanoplastic test particles showed an increased uptake and transport quantity through intestinal cells. Both types of particles resulted in observed differences of uptake behavior, most likely influenced by different lipophilicity, which varied between the polymeric test materials. Toxic effects were detected after 24 h only in overload situations for the particles in the submicrometer range. This study provides further evidence for gastrointestinal uptake of submicro- and nanoplastics and points towards differences regarding bioavailability between microplastics and smaller plastic particles that may result following the ingestion of contaminated food and beverages. Furthermore, the results reinforce the importance for studying nanoplastics of different materials of varying size, surface properties, polymer composition and hydrophobicity.
This paper reports a systematic study into the effect of different biomass-derived precursors on the structure and porosity of carbons prepared via catalytic graphitization. Glucose, starch and cellulose are combined with iron nitrate and heated under a nitrogen atmosphere to produce Fe3C nanoparticles, which catalyze the conversion of amorphous carbon to graphitic nanostructures. The choice of organic precursor provides a means of controlling the catalyst particle size, which has a direct effect on the porosity of the material. Cellulose and glucose produce mesoporous carbons, while starch produces a mixture of micro- and mesopores under the same conditions and proceeds via a much slower graphitization step, generating a mixture of graphitic nanostructures and turbostratic carbon. Porous carbons are critical to energy applications such as batteries and electrocatalytic processes. For These applications, a simple and sustainable route to those carbons is essential. Therefore, the ability to control the precise structure of a biomass-derived carbon simply through the choice of precursor will enable the production of a new generation of energy materials.