Wissenschaftliche Artikel der BAM
Filtern
Dokumenttyp
Referierte Publikation
- nein (35) (entfernen)
Schlagworte
- Simulation (6)
- Additive manufacturing (4)
- Röntgen-Refraktion (4)
- Neutron imaging (3)
- Computed Tomography (2)
- Computed tomography (2)
- Computertomografie (2)
- Computertomographie (2)
- Verbundwerkstoffe (2)
- X-ray computed tomography (2)
Organisationseinheit der BAM
- 8.5 Röntgenbildgebung (35) (entfernen)
Time-dependent in situ measurement of atmospheric corrosion rates of duplex stainless steel wires
(2018)
Corrosion rates of strained grade UNS S32202 (2202) and UNS S32205 (2205) duplex stainless steel wires have been measured, in situ, using time-lapse X-ray computed tomography. Exposures to chloride-containing (MgCl2) atmospheric environments at 50 °C (12–15 M Cl− and pH ~5) with different mechanical elastic and elastic/plastic loads were carried out over a period of 21 months. The corrosion rates for grade 2202 increased over time, showing selective dissolution with shallow corrosion sites, coalescing along the surface of the wire. Corrosion rates of grade 2205 decreased over time, showing both selective and pitting corrosion with more localised attack, growing preferentially in depth. The nucleation of stress corrosion cracking was observed in both wires.
The ability to track electrode degradation, both spatially and temporally, is fundamental to understand performance loss during operation of lithium batteries. X-ray computed tomography can be used to follow structural and morphological changes in electrodes; however, the direct detection of electrochemical processes related to metallic lithium is difficult due to the low sensitivity to the element. In this work, 4-dimensional neutron computed tomography, which shows high contrast for lithium, is used to directly quantify the lithium diffusion process in spirally wound Li/SOCl2 primary cells. The neutron dataset enables the quantification of the lithium transport from the anode and the accumulation inside the SOCl2 cathode to be locally resolved. Complementarity between the collected neutron and X-ray computed tomographies is shown and by applying both methods in concert we have observed lithium diffusion blocking by the LiCl protection layer and identified all cell components which are difficult to distinguish using one of the methods alone.
Regardless of the experimental care practiced in acquiring X-ray computed tomography (XCT) data, artifacts might still exist, such as noise and blur. This is typical for fast XCT data acquisitions (e.g., in-situ investigations), or low-dose XCT. Such artifacts can complicate subsequent analysis of the data. Digital filters can moderately cure extensive artifacts. The selection of filter type, intensity, and order of application is not always straight forward. To tackle these problems, a complete sequential multilevel, multi-scale framework: BAM SynthCOND, employing newly designed deep convolutional neural networks (DCNNs), was formulated. Although data conditioning with neural networks is not uncommon, the main complication is that completely artifact-free XCT data for training do not exist. Thus, training data were acquired from an in-house developed library (BAM SynthMAT) capable of generating synthetic XCT material microstructures. Some novel DCNN architectures were introduced (2D/3D ACEnet_Denoise, 2D/3D ACEnet_Deblur) along with the concept of Assertive Contrast Enhancement (ACE) training, which boosts the performance of neural networks trained with continuous loss functions. The proposed methodology accomplished very good generalization from low resemblance synthetic training data. Indeed, denoising, sharpening (deblurring), and even ring artifact removal performance were achieved on experimental post-CT scans of challenging multiphase Al-Si Metal Matrix Composite (MMC) microstructures. The conditioning efficiencies were: 92% for combined denoising/sharpening, 99% for standalone denoising, and 95% for standalone sharpening. The results proved to be independent of the artifact intensity. We believe that the novel concepts and methodology developed in this work can be directly applied on the CT projections prior to reconstruction, or easily be extended to other imaging techniques such as: Microscopy, Neutron Tomography, Ultrasonics, etc.
A systematic, nature-inspired chemical engineering approach is employed to solve the issue of flooding in electrochemical devices. The mechanism of passive water transport utilized by lizards living in arid environments is leveraged to design flow-fields with a microchannel structure on their surface, through which capillary pressure rapidly removes the water generated in the electrochemical device. This water management strategy is implemented in proton exchange membrane fuel cells (PEMFCs) with a lunginspired flow-field, which ensures uniform distribution of reactants across the catalyst layer. Jointly, this nature-inspired approach results in flood-free, stable operation at 100% RH and a B60% increase in current (B1.9 A cm-2) and peak power density (B650 mW cm−2) compared to current PEMFCs with a flood-prone, serpentine flow-field (B0.8 A cm-2 and 280 mW cm-2, respectively). This significant advance allows for PEMFC operation at fully humidified conditions.
Sandwich-Schalenstrukturen in situ charakterisiert mit Thermographie und Felddehnungsmessungen
(2018)
An der BAM wurde ein Schalenprüfstand entwickelt, mit dem typische Sandwichschalenstrukturen unter simulierter Betriebsbeanspruchung belastet werden können. Im mechanischen Ermüdungsversuch wurden in situ die Entstehung von Schäden in Schalenprüfkörpern mit Test-Imperfektionen mittels der passiven Thermographie und Felddehnungsmessungen verfolgt. Damit konnten der Zeitpunkt, der Schadensursprung und der Schadensfortschritt zerstörungsfrei bestimmt werden. Zudem wurden vergleichend Schalenprüfkörper mit Luftultraschall und der Röntgen-Laminographie untersucht. Im Rahmen eines BMWi-Forschungsvorhabens wurden die Schädigungsmechanismen evaluiert und Empfehlungen für die Praxis der Fertigung von Rotorblättern abgeleitet. In diesem Beitrag wird sich auf die Darstellung der ZfP-Verfahren und der ZfP-Ergebnisse konzentriert.
Metastable austenitic stainless steel (304L) samples with a rectangular cross-section were plastically deformed in torsion during which they experienced multiaxial stresses that led to a complex martensitic phase distribution owing to the transformation induced plasticity effect. A three-dimensional characterization of the phase distributions in these cm-sized samples was carried out by wavelength-selective neutron tomography. It was found that quantitatively correct results are obtained as long as the samples do not exhibit any considerable preferential grain orientation. Optical microscopy, electron backscatter diffraction, and finite element modeling were used to verify and explain the results obtained by neutron tomography. Altogether, neutron tomography was shown to extend the range of microstructure characterization methods towards the meso- and macroscale.
The quality of components made by laser beam melting (LBM) additive manufacturing is naturally influenced by the quality of the powder bed. A packing density <1 and porosity inside the powder particles lead to intrinsic voids in the powder bed. Since the packing density is determined by the particle size and shape distribution, the determination of these properties is of significant interest to assess the printing process. In this work, the size and shape distribution, the amount of the particle’s intrinsic porosity, as well as the packing density of micrometric powder used for LBM, have been investigated by means of synchrotron X-ray computed tomography (CT). Two different powder batches were investigated: Ti–6Al–4V produced by plasma atomization and stainless steel 316L produced by gas atomization. Plasma atomization particles were observed to be more spherical in terms of the mean anisotropy compared to particles produced by gas atomization. The two kinds of particles were comparable in size according to the equivalent diameter. The packing density was lower (i.e., the powder bed contained more voids in between particles) for the Ti–6Al–4V particles. The comparison of the tomographic results with laser diffraction, as another particle size measurement technique, proved to be in agreement.
Sacrifice Few to Save Many: Fire Protective Interlayers in Carbon- Fiber-Reinforced Laminates
(2024)
The fire protection of carbon-fiber-reinforced polymer (CFRP) laminates often relies on flame-retardant coatings, but in some applications, their efficacy may diminish upon direct fire exposure due to rapid pyrolysis. This study introduces an innovative approach by integrating protective interlayers within the laminate structure to enhance the fire resistance. Various materials, including ceramic composite WHIPOX, titanium foil, poly(etherimide) (PEI) foil, basalt fibers, rubber mat, and hemp fibers, were selected as protective interlayers. These interlayers were strategically placed within the laminate layout to form a sacrificial barrier, safeguarding the integrity of the composite. Bench-scale fire resistance tests were conducted, where fire (180 kW/m2) was applied directly to the one side of the specimen by a burner while a compressive load was applied at the same time. Results indicate significant prolongation of time to failure for CFRP laminates with protective interlayers, which is up to 10 times longer. This innovative approach represents a potential advance in fire protection strategies for CFRP laminates, offering improved resilience against fire-induced structural failure.
Most knowledge about the structure, function, and evolution of early compound eyes is based on investigations in trilobites. However, these studies dealt mainly with the cuticular lenses and little was known about internal anatomy. Only recently some data on crystalline cones and retinula cells were reported for a Cambrian trilobite species. Here, we describe internal eye structures of two other trilobite genera. The Ordovician Asaphus sp. reveals preserved crystalline cones situated underneath the cuticular lenses. The same is true for the Devonian species Archegonus (Waribole) warsteinensis, which in addition shows the fine structure of the rhabdom in the retinula cells. These results suggest that an apposition eye with a crystalline cone is ancestral for Trilobita. The overall similarity of trilobite eyes to those of myriapods, crustaceans, and hexapods corroborates views of a phylogenetic position of trilobites in the stem lineage of Mandibulata.
Al-Si alloys produced by Laser Powder Bed Fusion (L-PBF) techniques allow the fabrication of lightweight free-shape components that find space in aerospace, automotive, biomedical and military applications. Due to the high cooling rates occurring during the building process, L-PBF AlSi10Mg alloys exhibit an ultra-fine microstructure that leads to superior mechanical properties in the as-built condition compared to conventional cast Al-Si materials. Nevertheless, L-PBF processing induces high thermal gradients, leading to deleterious residual stress levels that must be considered to avoid part distortion and unpredicted failures. In order to relax detrimental residual stress and to increase the ductility, post-processing stress relief treatments are generally performed. In as-built condition the hypoeutectic AlSi10Mg microstructure consist of fine α-Al cells containing uniformly dispersed silicon nanoparticles, which are, in addition, surrounded by a eutectic Si network. Above 260°C the silicon interconnectivity starts to breakdown into spheroidized particles and to coarsen. At the same time, the heating residual stresses are relieved.
The objective of the contribution is to investigate, under different heat treatment conditions, the evolution of microstructure and residual stresses in view of optimizing the fatigue performance of the alloy. To this purpose various heat treatments in a range of temperatures between 265°C and 300°C for a duration between 15 minutes and 2 hours are performed. The microstructure modifications are analysed using a scanning electron microscope and the residual stress state is measured by laboratory X-ray diffraction.