The bond between polymer fibers and the surrounding cementitious matrix is essential for the development of concrete reinforcement. The single fiber pull-out test (SFPT) is the standard characterization technique for testing the bond strength. However, the different phases of debonding cannot be distinguished by the SFPT. This study investigates the debonding of different polymer fibers from the surrounding cementitious matrix with a modified SFPT and proposes methods to change the SFPT setup to generate more valuable information on the debonding mechanism. The SFPT was equipped with linear variable differential transformers (LVDT), digital image correlation (DIC) and acoustic emission (AE) analysis. The results demonstrate that the modified SFPT allows a better understanding of the different phases of debonding during fiber pull-out. Furthermore, bond strength values calculated by different methods reveal that the chemical bond of the investigated polymers is not different as reported by previous studies. Deformation measurements performed using LVDTs and DIC are suitable measuring techniques to characterize the debonding mechanism in SFPT. A correlation between recorded AE and debonding phases was not found.
problem. One reason is the sensitivity to stress corrosion cracking of the prestressing steel. Failure of prestressing wires can result in collapse of the entire structure without premature indication by transverse bending cracks or considerable deformation. The response of a structure to significant number of prestressing wire breaks was studied on a bridge in Brandenburg, Germany. Two thirds of the prestressing wires in concentrated tendons of two girders were cut before the bridge was demolished. Acoustic Emission Analysis was used to detect the wire breaks. Thus, the number of wire breaks was correlated with results of other measurement techniques, in particular strain measurements on the girders. In preparation of the measurements, the acoustic properties of the bridge were determined and the suitability of Schmidt hammer impacts as an acoustic reference source was validated.
Ein großer Teil unserer Brücken wurden in den 1950er bis 1970er Jahren als Spannbetonbrücken gebaut. Mit der damals noch relativ jungen Technologie entstanden elegante, teilweise gewagte Bauwerke mit großen Spannweiten, welche die Vorteile der Materialien Stahl und Beton geschickt kombinieren. Die Standsicherheit einiger dieser Brücken ist heute gefährdet. Die Ursachen liegen in der enorm gewachsenen Belastung durch Schwerverkehr, teilweise ungenügender Wartung und in konstruktiven und Materialschwächen, die der mangelnden Erfahrung mit der Technologie in der Bauzeit geschuldet sind. Ein neuralgischer Punkt der Bauwerke sind die in den Beton integrierten Spannglieder.
Infolge von Korrosion und Ermüdung können Elemente der Spannglieder reißen, wodurch die für das Tragwerk notwendige Spannung und somit die Tragfähigkeit reduziert werden. Nicht bei allen Brücken kündigen sichtbare Risse im Beton oder auffällige Verformungen den Tragfähigkeitsverlust bzw. das finale Versagen rechtzeitig an.
Die Schallemissionsanalyse ist die derzeit einzige Methode, das Reißen einzelner Spannstähle zuverlässig und mit wirtschaftlich vertretbarem Aufwand zu detektieren. Trotzdem es schon einige Spannbetonbauwerke gibt, die mit Schallemissionsanalyse überwacht werden, ist das Verfahren noch wenig bekannt.
Außerdem fehlen technische Richtlinien, was die Ausschreibung und Vergabe von entsprechenden Aufträgen und die Bewertung der Angebote sehr erschwert. Um sowohl Baulastträger als auch Dienstleistungsanbieter in den Vergabeverfahren und im Betrieb der Monitoringsysteme zu unterstützen, hat sich eine Gruppe von Experten aus den Bereichen Bauingenieurwesen und Schallemission zum Entwurf einer Richtlinie „Detektion von Spanndrahtbrüchen mit Schallemission“ zusammengefunden. Mit diesem Beitrag wird die Richtlinie vorgestellt, deren Bearbeitung bis zur SCHALL 23 abgeschlossen sein soll.
Alkali-silica reaction (ASR) is a chemical reaction within concrete which can lead over time to cracking and spalling. Due to the complexity of the problem, it still causes damage to concrete constructions worldwide.
The publication aims to illustrate the interdisciplinary research of the German Federal Institute for Materials Research and Testing (BAM) within the last 20 years, considering all aspects of ASR topics from the macro to the micro level. First, methods for characterization and assessment of ASR risks and reaction products used at BAM are explained and classified in the international context. Subsequently the added value of the research approach by combining different, preferably nondestructive, methods across all scales is explained using specific examples from a variety of research projects. Aspects covered range from the development of new test-setups to assess aggregate reactivity, to analysis of microstructure and reaction products using microscopical, spectroscopical and X-ray methods, to the development of a testing methodology for existing concrete pavements including in-depth analysis of the visual damage indicator and the de-icing salt input using innovative testing techniques. Finally, research regarding a novel avoidance strategy that makes use of internal hydrophobization of the concrete mix is presented.
The fatigue process of concrete under compressive cyclic loading is still not completely explored. The corresponding damage processes within the material structure are especially not entirely investigated. The application of acoustic measurement methods enables a better insight into the processes of the fatigue in concrete. Normal strength concrete was investigated under compressive cyclic loading with regard to the fatigue process by using acoustic methods in combination with other nondestructive measurement methods. Acoustic emission and ultrasonic signal measurements were applied together with measurements of strains, elastic modulus, and static strength. It was possible to determine the anisotropic character of the fatigue damage caused by uniaxial loading based on the ultrasonic measurements. Furthermore, it was observed that the fatigue damage seems to consist not exclusively of load parallel oriented crack structures. Rather, crack structures perpendicular to the load as well as local compacting are likely components of the fatigue damage. Additionally, the ultrasonic velocity appears to be a good indicator for fatigue damage beside the elastic modulus. It can be concluded that acoustic methods allow an observation of the fatigue process in concrete and a better understanding, especially in combination with further measurement methods.
Bending beams and slabs are typical examples for structural elements used for reinforced concrete structures such as bridge girders, T-beams and bridge decks. Their strength related failure modes at maximum loading can be divided into bending and shear failure. The failure of beams loaded in bending can occur with or without indication. Therefore, conventional design concepts aim on failure modes with sufficient indication (e.g. large deflections or cracks), as it occurs in the case of secondary flexural compression failure. These indicating factors can also be used for Structural Health Monitoring (SHM) of civil infrastructure systems (e.g. bridges) to identify structural changes. In this context, non-destructive testing (NDT) methods offer different techniques for measuring deflections or crack formation and opening. However, profound knowledge on the determining failure modes of bending beams and their detection by NDT methods is required for the reliable application of SHM. Different NDT methods have been used in this study for analysing the load-bearing behaviour of a reinforced concrete beam in bending. The different measuring techniques are briefly described and their applicability is discussed by means of experimental results. For this purpose, the load-bearing behaviour of a reinforced concrete beam having a span of 2.75 m was investigated in a four-point bending flexural test at laboratory scale. The focus is on the characterization of determining failure modes by optical NDT and the comparison with classical measuring techniques (e.g. deformation measurements by displacement transducers). The bending beam was equipped with two single-mode (SM) sensor fibres. One fibre served as Distributed Optical Fibre Sensor (DOFS), whereas the other fibre contained Fibre Bragg Grating (FBG) sensors. In addition, optical deformation measurements using Digital Image Correlation (DIC) and Stereophotogrammetry (SP) were conducted.
Alkali-activated materials are ideal for the repair of concrete structures in harsh environmental conditions due to their high durability in chemically aggressive environments. However, slag-based mortars, in particular, are prone to shrinkage and associated cracks. In this respect, the application of steel fibres is one solution to reduce the formation of shrinkage induced cracks and to improve post cracking behaviour of these mortars. This study investigated the influence of two different types of steel fibres on the tensile properties of two alkali-activated mortars. Direct tensile tests and single fibre pull-outs were performed to analyse the determining failure modes both on macro and micro scale. Mechanical testing was accompanied by non-destructive testing methods such as digital image correlation and acoustic emission for a detailed analysis of the fracture process.
Die Brücken im Netz der Bundesverkehrswege sind überwiegend in einem ausreichenden bis guten Zustand. Allerdings steigt der Unterhalts- und Sanierungsaufwand aufgrund des inzwischen hohen Alters vieler Brücken sowie des ständig wachsenden Schwerlastverkehrs. Techniken zur Einschätzung der verbleibenden Lebensdauer von Brücken sowie zur dauerhaften Beobachtung des Tragverhaltens bzw. des Erfolges von Sanierungsmaßnahmen werden daher für den sicheren und wirtschaftlichen Betrieb dringend benötigt. Zur Evaluierung dafür geeigneter holistischer Ansätze wurde in der BAM das Projekt BLEIB - Bewertung, Lebensdauerprognose und Instandsetzung von Brückenbauwerken - ins Leben gerufen.
Ein zentrales Ergebnis des Projektes ist eine extern vorgespannte Stahlbetonbrücke als Zweifeldträger mit einer Gesamtlänge von 24 m, die für den Test verschiedenster Sensorsysteme, zur Validierung numerischer Modelle und zur Erprobung von Sanierungs- und Verstärkungsmaßnahmen entwickelt wurde. Für die Simulation unterschiedlicher Schädigungsgrade kann die Vorspannung der Brücke variiert werden. Die Brücke wird mit beweglichen Gewichten belastet und über einen Shaker zum Schwingen angeregt.
Das Brückenmodell wurde bewusst geschädigt, indem die Vorspannung der Struktur erstmalig schrittweise bis auf null reduziert wurde. Unter der Eigenlast verformte sich die Brücke, wodurch eine Rissbildung im Beton einsetzte. Die Zugspannung, die zuvor durch die Vorspannung aufgenommen wurde, übernahm Schritt für Schritt der Beton. Als die Zugspannungen die relativ geringe Zugfestigkeit des Betons überstiegen, begann dieser zu reißen und die schlaffe Bewehrung der Struktur nahm die Spannungen auf. Dieser Versuch wurde unter anderem von Schallemissionsmessungen begleitet. Der Rissbildungsprozess konnte damit, bei gleichzeitiger Aufzeichnung der Vorspannung, früh detektiert und die Risse geortet werden. Die Ergebnisse korrelieren gut mit den Ergebnissen der stereophotogrammetrischen Verformungsmessungen der Struktur.
The susceptibility of concrete structures due to alkali–silica reaction (ASR) can be assessed by means of ASR concrete prism testing at 60 °C, according to RILEM AAR 4.1. There, expansion of concrete prisms indicates alkali-reactivity of the examined concrete mix. This work applies in situ expansion measurement to accelerated concrete prism testing. Automated measuring facilitates both storage without the usually necessary interruptions for manual measurement and acquisition of quasi-continuousexpansion data. A comparative experimental programme showed that conventional testing resulted in stronger expansion and leaching of alkalis than automated testing. Experimental simulation of interruptions, typically associated with manual measurements in conventional testing, could prove the influence of these cooling–heating cycles. Two phenomenological approaches, frequently used for describing reaction kinetics of ASR by linking it to expansion results from ASR-testing, were validated with continuous expansion data of three types of aggregate. Experimental expansion depicted s-shaped curves similar to them of the modelling approaches. However, strong swelling recorded in the beginning of the test was not covered by the model curves. Auxiliary measurement of acoustic emissions and ultrasonic velocity helped characterising mechanisms such as hydration and cracking, which also influence prism expansion. The proposed modification of the measurement procedure provides an extended basis to analyse expansion mechanisms. Regarding data for validation of ASR-expansion models, continuous expansion results are preferable to conventional test results.