The impact of high additions of vegetable oil (12 vol%) on the mechanical and microstructural properties of metakaolin-slag-based alkali-activated materials (AAMs) was studied. The addition of oil resulted in a slight decrease in initial polymerization kinetics but did not affect the final degree of reaction. AAM-oil-composite-mortars exhibited approximately ∼30% lower compressive strength primarily due to the entrainment of air voids. Newly formed soap phases significantly reduced the volume of small capillary and gel pores (pore radii <15 nm), leading to a decrease in specific inner surface area by a factor of up to 15. The porosity modification induced by the oil addition greatly enhanced the resistance of AAMs against sulfuric acid attack, shifting the dominant processes from diffusion and cracks to framework-dissolution controlled by the inherent phase stabilities. Following the immersion in sulfuric acid (pHstat = 2) for 8 weeks, the depth of corroded layer decreased by 70% and no cracks due to expansive phases were observed. These promising findings suggest that the incorporation of vegetable oil in AAMs has the potential to address durability concerns associated with diffusion-based corrosion processes, thereby expanding the range of future applications.
Additive manufacturing (AM) of alkali-activated materials is a promising method for producing ceramic precursors, construction elements and other parts. A recently introduced AM process is laser-induced slip casting of lithium aluminate/microsilica slurries, which yields parts with excellent mechanical strengths. To clarify the underlying mechanisms, μ-Raman spectroscopy was applied to parts produced by the process, and the dissolution and hydration of lithium aluminate was studied inter alia using conventional and in-situ X-ray diffraction. The results show that significant dissolution of lithium aluminate occurs, particularly at increased temperatures during laser interaction, which leads to an increase of pH and precipitation of an akopovaite-like Li-Al-CO3 layered double hydroxide. The increase of the pH is likely to induce dissolution of the microsilica and possibly formation of a hydrous lithium aluminosilicate gel. These observations explain the strength evolution of the studied parts and can also aid the development and improvement of related AM methods.