The corrosivity of atmospheres in Europe has changed significantly in recent decades. For the Federal Republic of Germany, no current values for the corrosion rate based on 1‐year atmospheric exposure of standard specimens can be found in the scientific literature after 2000. This paper presents results from a field exposure study in the Berlin metropolitan area and Helgoland in 2016. Based on standard specimens, values for the corrosion rate and the corresponding atmospheric corrosivity category are determined for open exposure and indirect weathering in a ventilated enclosure as sheltering after 1 year of exposure. The results prove that determined corrosivity categories are material‐specific. Sheltered exposure is a typical atmospheric situation for many building components. It allows statements on the effect of the concentration of airborne substances on the corrosivity beyond the normative requirements.
Novel agar-based test electrolytes are used to perform electrochemical corrosion investigations on ZnFe and ZnNi binary as well as ZnFeMo ternary zinc coatings. The objectives of the electrochemical investigations include the characterization of the corrosion behavior, the description of the protective effect of the coatings as well as the investigation of the layer formation and degradation under artificial aging. ZnFe and ZnFeMo coatings are applied with varying iron content as well as an additional passivation layer, respectively, to study the effect on corrosion resistance. The results show that the protective effect of the coatings is not negatively influenced by different iron contents or the addition of molybdenum. Additional passivation of the ZnFe-containing coatings by means of a passivating agent leads to a significant improvement in the protective effect. Artificial aging leads to slight degradation of the additional passivation layer whereas coatings without post-treatment enhance their protective effect by the formation of corrosion product layers.
Although zinc and zinc coatings have been widely used for corrosion protection for decades new zinc coatings are constantly being developed. Characterizing the corrosion protectiveness of these new coatings, however, should not be underestimated. While exposure tests are time intensive, cyclic tests can only be used for a very limited field of application. Thus, electrochemical measurements provide both an efficient and an effective alternative. Conventional aqueous bulk electrolytes influence the surface layers of a tested zinc coating and are therefore not reliable. Gel electrolytes, however, have evolved over the last few years, are minimally invasive and provide reliable results.
This work describes experiments with gel electrolytes made of agar. Unlike previous work, it proposes a composition of gel electrolyte for minimally invasive description of the protective power of naturally formed oxide layers on zinc and zinc coatings. Therefore, as a first part, the gel electrolyte made of agar is verified as a method for zinc and zinc-coated samples. Afterwards, this paper introduces the corrosion product layer resistance RL as a promising parameter to evaluate the protective power of zinc coatings. Results are verified with EIS and FTIR measurements. An example on a representative zinc coating demonstrates the practical application.
The corrosion resistance of aluminium surfaces is closely linked to the surfacecstate after a grinding process. For years, iron‐containing abrasive materials were suspected to lead to increased corrosion susceptibility after processing of aluminium surfaces. To prove a possible correlation between the iron content of an abrasive and the corrosion behaviour of aluminium components, scientific investigations and experimentally practical corrosion tests are necessary.
For the current investigation, specimens of a technical Al‐Si alloy from the same batch were used. The test specimens were mechanically ground with various resin‐bonded model abrasives containing different iron contents. The performed corrosion tests did not reveal a negative influence of the different iron‐containing abrasives on the corrosion behaviour of the Al–Si alloy.
However, the most sensitive measuring method (electrochemical noise)
showed differences in the surface activity depending on the type of abrasive.
Investigation of the salinization in marine and offshore environment - test methods and challenges
(2019)
Salinization and contamination of metal surfaces by chloride-containing aerosols is of great importance with regard to corrosion phenomena in the maritime sector and in offshore applications. Especially Offshore Wind Turbines are exposed to extreme corrosive conditions due to high chloride concentrations in the atmosphere and the resulting high chloride deposition rates. It is of great importance to evaluate to what extent salinization of the surface influences the corrosion protection of coatings and pitting occurrence on stainless steels under atmospheric conditions to evaluate the durability of metallic building structures in offshore and marine environments. The evaluation of the scientific literature and regulatory guidelines has shown that there are still many open questions regarding the contamination of metal surfaces by chlorides. This contribution will discuss how salinization of metal surfaces is evaluated and monitored according to current standards and guidelines. Future challenges concerning test methods and the application of evaluated salinization values and deposition rates will be discussed.
The paper presents a new method for the determination and evaluation of tafel factors using gel-type electrolytes and electrochemical frequency modulation technique (EFM). This relatively new electrochemical method offers the possibility to determine both polarization resistances and tafel factors within one measurement and in short measuring intervals. Starting from a comprehensive parameter study it is shown that a direct relationship between the two values exists that can be described mathematically. This contribution presents the determined tafel factors for the system gel-type electrolyte/zinc and discusses their applicability and their limits.
Limitations are encountered regarding the electrolyte when studying atmospheric corrosion reactions on materials that form protective layers on their surface or tend to passivate. For example, the reconstruction of a thin wet film, as well as the interpretation of electrochemical measurements in so-called bulk solutions (a "mass" of electrolyte), often proves to be difficult in view of corrosion behavior under atmospheric conditions. A new approach to this problem in corrosion research includes the use of gel-type electrolytes as an alternative to bulk electrolytes. Gel-type electrolytes form a thin wet film on the surface of the material, whereby the naturally formed protective layer is affected similar to atmospheric conditions and can be examined in an almost non-destructive way. Through electrochemical instrumentation specific values such as polarization resistances and corrosion currents can be determined providing information on kinetics of surface layer formation and stability of surface layers formed under the influence of a thin wet film. Thus, new test methods can be developed that supply a better understanding of corrosion processes in specific atmospheres.
In this article different zinc coatings and aluminium alloys were investigated, their naturally formed protective layers were electrochemically characterized and corrosion relevant values were determined by using a gel pad based on polysaccharide. Corrosion relevant values allowed the differentiation of various coating systems and could describe the current protective effect provided by the coating. It is shown that gel-type electrolytes influence protective layers and coatings considerably less than corresponding bulk electrolytes and that an atmospheric wet film is approached by these test conditions. From the results it is evident that gel-type electrolytes represent a viable and promising field in corrosion research.