Quantification of impact damages in CFRP and GFRP structures with thermography and ultrasonics
(2018)
The extent of damage caused by impacts in fibre reinforced composites depends on the energy of the impacts, on the velocity and the shape of the impacting body, on the material and structure of the composite and on the geometry of the structure. Here, mainly the thickness of the component is essential. The non-destructive evaluation of these damages can be carried out using both ultrasound and active thermography methods. A comparison of the detection sensitivity of these methods for the different damages is carried out in this paper depending on the fibre composite material used (CFRP and GFRP), the thickness of the material and the impact energy. The NDT methods used after the damage are supplemented by thermographic measurements with high temporal resolution, which were already recorded during the impact.
Additively manufactured test specimens made of polyamide 12 (PA 12) by Laser Sintering (LS) as well as of acrylnitril-butadien-styrol (ABS) by Fused Layer Modeling (FLM), were tested with active thermography. For this, two different excitation methods (flash and impulse excitation) were used and compared, regarding the suitability for the detection of constructed and imprinted defects. To increase the quality of the thermograms, data processing methods like thermal signal reconstruction (TSR) and Fourier-Transformation were applied. Furthermore, the long-term stability of the probes towards environmental stress, like UV-radiation, heat, water contact and frost is being investigated in the presented project with artificial weathering tests.
Amongst various other NDT methods, within the EMRP-project
‘VITCEA’ active thermography is validated for testing of CFRP and
GFRP structures constructed for energy application. In this
contribution, the optical and thermal properties of CFRP and GFRP
reference defect artefact (RDA) and natural defects artefact (NDA)
test specimens are characterized. Different excitation techniques
and techniques for data analysis are compared for optimizing the
number of detected defects.
A round robin test on flash thermography was organized within the scope of a standardization research project. This test gives information on reliability, comparability and efficiency of different testing situations. Data recorded on metal and CFRP test specimens with flat bottom holes (FBH) were analysed by evaluating the detectability and by calculating the signal-to-noise ratio (SNR) of the defect signatures as a function of defect parameters. For the investigation of the influence of material properties on the spatial resolution as well as on penetration depth, test specimens made of steel and copper with crossed notches and a notch ramp were constructed and investigated. Here, the minimum resolvable notch distance and the maximum detectable depth of the ramp were analysed.
Active thermography is well suited for the detection of delaminations and cracks in façade elements like plaster and tiles. Not only artificial heating but also solar heating can be used if the adjustment of the façade and the weather conditions are suitable. Optical methods like laser scanners, photogrammetric methods and crack tracking sensors are providing geometrical 3D data which can be used for a 3D mapping of thermograms and for providing data with higher geometrical resolution. Thus, by the combination and fusion of these data, a comprehensive mapping and monitoring of damages of façade systems is possible.
Carbon-fiber reinforced composites are becoming more and more important in the production of light-weight structures, e.g., in the automotive and aerospace industry. Thermography is often used for non-destructive testing of These products, especially to detect delaminations between different layers of the composite.
In this presentation, we aim at methods for defect reconstruction from thermographic measurements of such carbon-fiber reinforced composites. The reconstruction results shall not only allow to locate defects, but also give a quantitative characterization of the defect properties. We discuss the simulation of the measurement process using finite element methods, as well as the experimental validation on flat bottom holes.
Especially in pulse thermography, thin boundary layers with steep temperature gradients occurring at the heated surface need to be resolved. Here we use the combination of a 1D analytical solution combined with numerical solution of the remaining defect equation. We use the simulations to identify material Parameters from the measurements.
Finally, fast heuristics for reconstructing defect geometries are applied to the acquired data, and compared for their accuracy and utility in detecting different defects like back surface defects or delaminations.