Wissenschaftliche Artikel der BAM
Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (2086)
- Beitrag zu einem Tagungsband (386)
- Forschungsbericht (19)
- Beitrag zu einem Sammelband (10)
- Sonstiges (10)
- Buchkapitel (9)
- Corrigendum (3)
- Tagungsband (Herausgeberschaft für den kompletten Band) (2)
- Dissertation (1)
- Zeitschriftenheft (Herausgeberschaft für das komplette Heft) (1)
Sprache
- Englisch (2290)
- Deutsch (233)
- Mehrsprachig (3)
- Portugiesisch (1)
Schlagworte
- Additive manufacturing (69)
- Fluorescence (56)
- Nanoparticles (48)
- Concrete (47)
- SAXS (46)
- Ultrasound (38)
- Corrosion (37)
- MALDI-TOF MS (36)
- Quantum yield (36)
- Non-destructive testing (34)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (448)
- 6 Materialchemie (442)
- 1 Analytische Chemie; Referenzmaterialien (362)
- 7 Bauwerkssicherheit (228)
- 5 Werkstofftechnik (218)
- 9 Komponentensicherheit (215)
- 4 Material und Umwelt (197)
- 6.3 Strukturanalytik (168)
- 8.5 Röntgenbildgebung (139)
- 6.1 Oberflächen- und Dünnschichtanalyse (102)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (101)
- 8.0 Abteilungsleitung und andere (100)
- 5.1 Mikrostruktur Design und Degradation (80)
- 9.3 Schweißtechnische Fertigungsverfahren (79)
- 1.2 Biophotonik (74)
- 6.6 Physik und chemische Analytik der Polymere (70)
- 9.4 Integrität von Schweißverbindungen (69)
- 8.4 Akustische und elektromagnetische Verfahren (66)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (65)
- 6.2 Material- und Oberflächentechnologien (63)
- 1.1 Anorganische Spurenanalytik (61)
- 7.4 Baustofftechnologie (61)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (57)
- 1.4 Prozessanalytik (56)
- 4.1 Biologische Materialschädigung und Referenzorganismen (56)
- 1.7 Organische Spuren- und Lebensmittelanalytik (55)
- 3 Gefahrgutumschließungen; Energiespeicher (54)
- 1.5 Proteinanalytik (52)
- 6.0 Abteilungsleitung und andere (51)
- 8.6 Faseroptische Sensorik (50)
- 1.8 Umweltanalytik (43)
- 4.3 Schadstofftransfer und Umwelttechnologien (42)
- 5.2 Metallische Hochtemperaturwerkstoffe (42)
- 7.2 Ingenieurbau (40)
- 1.9 Chemische und optische Sensorik (38)
- 5.4 Multimateriale Fertigungsprozesse (38)
- 9.0 Abteilungsleitung und andere (35)
- 9.2 Versuchsanlagen und Prüftechnik (32)
- 4.2 Material-Mikrobiom Wechselwirkungen (31)
- 5.3 Polymere Verbundwerkstoffe (29)
- 2 Prozess- und Anlagensicherheit (28)
- 4.0 Abteilungsleitung und andere (28)
- 4.5 Kunst- und Kulturgutanalyse (28)
- 5.5 Materialmodellierung (27)
- 5.6 Glas (27)
- S Qualitätsinfrastruktur (27)
- 2.1 Sicherheit von Energieträgern (26)
- 7.6 Korrosion und Korrosionsschutz (26)
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (24)
- 9.5 Tribologie und Verschleißschutz (23)
- 9.6 Additive Fertigung metallischer Komponenten (23)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (22)
- VP Vizepräsident (22)
- VP.1 eScience (22)
- 7.1 Baustoffe (21)
- 1.3 Instrumentelle Analytik (19)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (17)
- 5.0 Abteilungsleitung und andere (17)
- 1.6 Anorganische Referenzmaterialien (16)
- S.2 Digitalisierung der Qualitätsinfrastruktur (16)
- 7.7 Modellierung und Simulation (15)
- 1.0 Abteilungsleitung und andere (13)
- 7.0 Abteilungsleitung und andere (13)
- P Präsident (11)
- 3.2 Gefahrguttanks und Unfallmechanik (10)
- 3.5 Sicherheit von Gasspeichern (10)
- P.0 Präsident und andere (10)
- 6.7 Materialsynthese und Design (9)
- 7.3 Brandingenieurwesen (9)
- 6.4 Materialinformatik (8)
- 3.4 Sicherheit von Lagerbehältern (7)
- S.3 Ökodesign und Energieverbrauchskennzeichnung (7)
- 3.6 Elektrochemische Energiematerialien (6)
- S.1 Qualität im Prüfwesen (5)
- 3.0 Abteilungsleitung und andere (4)
- 8.3 Thermografische Verfahren (4)
- 4.6 Molekulare und angewandte Entomologie (3)
- 2.0 Abteilungsleitung und andere (2)
- 2.2 Prozesssimulation (2)
- 2.3 Einstufung von Gefahrstoffen und -gütern (1)
- 2.5 Konformitätsbewertung Explosivstoffe/Pyrotechnik (1)
- 3.3 Sicherheit von Transportbehältern (1)
- KM Kommunikation, Marketing (1)
- PST Präsidiale Stabsstelle (1)
- VP.2 Informationstechnik (1)
Paper des Monats
- ja (68)
The obvious benefits derived from the increasing use of engineered nano-, new, and advanced materials and associated products have to be weighed out by a governance process against their possible risks. Differences in risk perception (beliefs about potential harm) among stakeholders, in particular nonscientists, and low transparency of the underlying decision processes can lead to a lack of support and acceptance of nano-, new, and other advanced material enabled products. To integrate scientific outcomes with stakeholders needs, this work develops a new approach comprising a nine-level, stepwise categorization and guidance system entitled “Knowledge, Information, and Data Readiness Levels” (KaRLs), analogous to the NASA Technology Readiness Levels. The KaRL system assesses the type, extent, and usability of the available data, information, and knowledge and integrates the participation of relevant and interested stakeholders in a cocreation/codesign process to improve current risk assessment, communication, and governance. The novelty of the new system is to communicate and share all available and relevant elements on material related risks in a user/stakeholder-friendly, transparent, flexible, and holistic way and so stimulate reflection, awareness, communication, and a deeper understanding that ultimately enables the discursive process that is needed for the sustainable risk governance of new materials.
Nickel alloys are cost intensive materials and generally classified as difficult-to-cut material. However, machining of these materials is needed especially in case of alloy 36 (1.3912), which is commonly used in mould construction for the production of fibre-reinforced composites. With regard to repair, modification and manufacturing of such components, additive manufacturing offers significant economic advantages. Nevertheless, subsequent machining steps are needed to achieve the final component contour and defined surface conditions. Dependent on the material and machining process conditions, detrimental tensile residual stresses may be the result on the machined surface, having negative impact on the component performance and safety. In this investigation, machining experiments were carried out on wire arc additive manufactured components made of alloy 36, varying the cutting speed and the feed rate. In addition, the conventional milling process (CM) was compared with a modern, hybrid machining process, the ultrasonic-assisted milling (US). The cutting forces and the surface-near residual stresses were analysed using X-ray diffraction. A significant improvement of the machinability as well as the surface integrity by using the ultrasonic assistance was observed, especially at low cutting speeds. The CM induced mainly tensile residual stresses, the US mainly compressive residual stresses.
The dataset contains raw data gathered with the ultrasonic pulse-echo method on concrete specimens. The surfaces of the measuring objects were automatically scanned point by point. Pulse-echo measurements were performed at each of these measuring points. The test specimens represent two typical testing tasks in construction industry: the detection of objects and the determination of dimensions to describe the geometry of components. By automating the measurement process, the different test scenarios are examined with a high repeatability, precision and measuring point density. Longitu- dinal and transversal waves were used and the geometrical aperture of the testing system was varied. The low-frequency probes operate in a range of up to approximately 150 kHz. In addition to the specification of the geometrical dimensions of the individual probes, the directivity pattern and the sound field characteristics are provided. The raw data are stored in a universally readable format. The length of each time signal (A-scan) is two milliseconds and the sampling rate is two mega-samples per second. The provided data can be used for comparative studies in signal analysis, imag- ing and interpretation as well as for evaluation pur- poses in different, practically relevant testing scenarios.
The prediction of porosity is a crucial task for metal based additive manufacturing techniques such as laser powder bed fusion. Short wave infrared thermography as an in-situ monitoring tool enables the measurement of the surface radiosity during the laser exposure. Based on the thermogram data, the thermal history of the component can be reconstructed which is closely related to the resulting mechanical properties and to the formation of porosity in the part. In this study, we present a novel framework for the local prediction of porosity based on extracted features from thermogram data. The framework consists of a data pre-processing workflow and a supervised deep learning classifier architecture. The data pre-processing
workflow generates samples from thermogram feature data by including feature information from multiple subsequent layers.
Thereby, the prediction of the occurrence of complex process phenomena such as keyhole pores is enabled. A custom convolutional neural network model is used for classification. Themodel is trained and tested on a dataset from thermographic in-situ monitoring of the manufacturing of an AISI 316L stainless steel test component. The impact of the pre-processing parameters and the local void distribution on the classification performance is studied in detail. The presented model achieves an accuracy of 0.96 and an f1-Score of 0.86 for predicting keyhole porosity in small sub-volumes with a dimension of (700 × 700 × 50) μm3. Furthermore, we show that pre-processing parameters such as the porosity threshold for sample
labeling and the number of included subsequent layers are influential for the model performance. Moreover, the model prediction is shown to be sensitive to local porosity changes although it is trained on binary labeled data that disregards the actual sample porosity.
Photopolymer derived carbon grows in popularity, yet the range in available feature sizes is limited. Here we focus on expanding the field to low surface to volume ratio (SVR) structures. We describe a high temperature acrylic photopolymerizable precursor with FTIR and DSC and develop a thermal inert-gas treatment for producing architected carbon in the mm scale with SVR of 1.38 x10-3 μm-1. Based on TGA and MS, we distinguish two thermal regimes with activation energies of ~79 and 169 kJ mol-1, which we reason with mechanisms during the polymer’s morphologic conversion between 300 - 500 °C. The temperature range of the major dimensional shrinkage (300-440 °C, 50%) does not match the range of the largest alteration in elemental composition (440-600 °C, O/C 0.25-0.087%). The insights lead to an optimized thermal treatment with an initial ramp (2 °C min-1 to 350 °C), isothermal hold (14h), post hold ramp (0.5 °C min-1 to 440 °C) and final ramp (10 °C min-1 to 1000 °C). The resulting carbon structures are dimensionally stable, non-porous at the μm scale, and comprise an unprecedented variation in feature sizes (from mm to μm scale). The findings shall advance architected carbon to industrially relevant scales.
The corner echo is a well-known effect in ultrasonic testing, which allows detection of surface breaking cracks with predominantly perpendicular orientation to the surface as, for example, corrosion cracks in metal pipes or shafts. This echo is formed by two planes, the surface of the crack and the surface which the crack breaks. It can also be classified as a half-skip method, since a reflection of the pulse occurs on the backwall before the reflection at the defect takes place. In combination with the diffraction from the crack tip, the corner echo also allows crack sizing. As shown in this paper, the corner reflection can be used in civil engineering for nondestructive inspection of concrete. Commercially available low frequency ultrasonic arrays with dry point contact sources generate SH transversal waves with sufficient divergence of the sound field in order to detect corner reflections. Ultrasonic line-scans and area-scans were acquired with a linear array on flat concrete specimens, and the data were reconstructed by the Synthetic aperture focusing technique. If the angles and the area of reconstruction are chosen accordingly, the corner echo reflection can be distinguished from other ultrasonic information. The corner echo can thus be used as a method for deciding whether a crack is a partial-depth crack or a full-depth crack and thus for obtaining a statement about crack depth. This paper presents corresponding experimental results obtained on concrete specimens with artificial test defects and cracks induced under controlled conditions.
Two test series were examined using nondestructive measuring methods by six independent laboratories before determining their compressive strength. The nondestructive test methods used were the rebound hammer and ultrasonic pulse velocity measurement. Two types of geometries were investigated: drilled cores and cubes. The measurement procedure for each of these datasets is conditioned to the geometry and is therefore different.
The first series consists of 20 drilled cores (approximately diameter/height = 10 cm/20 cm) from the 55-year-old Lahntal Viaduct near Limburg, Germany. After preparation in the first laboratory, the lateral surface of the drilled cores was tested with the rebound hammer using a given pattern. Every laboratory tested every drilled core at different locations.
Ultrasonic measurements in transmission were performed repeatedly at predefined points on the flat surfaces of the specimen.
The second series consisted of 25 newly manufactured concrete cubes of a mix with a target concrete strength class of C30/37. The edge length was 15 cm. Each laboratory received five specimens of this test series. Thus, contrary to the first series, each specimen was tested by only one laboratory. Two side faces of each cube were tested with the rebound hammer. In addition, ultrasonic measurements were performed by one laboratory. The time of flight was measured between the tested side faces of the rebound hammer at different positions.
For both series, rebound hammers were used to determine the R-value as well as the Q-value. The rebound hammer models within the laboratories were always the same, while they differed between the laboratories. The ultrasonic measurements took place with different measurement systems and couplants. Finally, both specimen series were tested destructively for compressive strength.
The dataset contains the raw data summarized in tabular form. In addition, relevant calculated data are included in some cases. For the ultrasonic measurements, the time of flight has already been converted into the ultrasonic velocity. Besides, in addition to the raw data of the compressive strength test (force, weight, and geometry values), the calculated compressive strengths and densities are also provided.
The glass transition behavior of thin films of poly(bisphenol A carbonate) (PBAC) was studied employing ellipsometry. The glass transition temperature increases with the reduction of the film thickness. This result is attributed to the formation of an adsorbed layer with a reduced mobility compared to bulk PBAC. Therefore, for the first time, the growth kinetics of the adsorbed layer of PBAC was investigated, prepared by leaching samples from a 200 nm thin film which were annealed for several times at three different temperatures. The thickness of each prepared adsorbed layer was measured by multiple scans using atomic force microscopy (AFM). Additionally, an unannealed sample was measured. Comparison of the measurements of the unannealed and the annealed samples provides proof of a pre-growth regime for all annealing temperatures which was not observed for other polymers. For the lowest annealing temperature after the pre-growth stage only a growth regime with a linear time dependence is observed. For higher annealing temperatures the growth kinetics changes from a linear to a logarithmic growth regime at a critical time. At the longest annealing times the films showed signs of dewetting where segments of the adsorbed film were removed from the substrate (dewetting by desorption). The dependence of the surface roughness of the PBAC surface on annealing time also confirmed that the films annealed at highest temperatures for the longest times desorbed from the substrate.
The interaction of microcroplastics (MP) with dissolved organic matter, especially humic substances, is of great importance in understanding the behavior of microplastics in aquatic ecosystems. Surface modification by humic substances plays an essential role in transport and interaction of MP with abiotic and biotic components. Previous studies on the interaction between MP and humic substances were largely based on a model compound, humic acid (Sigma-Aldrich). In our work, we therefore investigated the interaction of natural organic matter (NOM) sampled from a German surface water with low-density polyethylene particles (LDPE). Highpressure size exclusion chromatography (HPSEC) and UV/vis absorption and fluorescence spectroscopy were used to characterize the incubation solutions after modifications due to the presence of LDPE, and Raman spectroscopy was used to characterize the incubated microplastics. While the studies of the solutions generally showed only very small effects, Raman spectroscopic studies allowed clear evidence of the binding of humic fractions to MP. The comparison of the incubation of NOM and a lignite fulvic acid which also was tested further showed that specific signatures of the humic substances used could be detected by Raman spectroscopy. This provides an elegant opportunity to conduct broader studies on this issue in the future.
Using digital twins for decision making is a very promising concept which combines simulation models with corresponding experimental sensor data in order to support maintenance decisions or to investigate the reliability. The quality of the prognosis strongly depends on both the data quality and the quality of the digital twin. The latter comprises both the modeling assumptions as well as the correct parameters of these models. This article discusses the challenges when applying this concept to realmeasurement data for a demonstrator bridge in the lab, including the data management, the iterative development of the simulation model as well as the identification/updating procedure using Bayesian inference with a potentially large number of parameters. The investigated scenarios include both the iterative identification of the structural model parameters as well as scenarios related to a damage identification. In addition, the article aims at providing all models and data in a reproducibleway such that other researcher can use this setup to validate their methodologies.
Critical defects, also known as device killers, in wide bandgap semiconductors significantly affect the performance of power electronic devices. We used the methods imaging ellipsometry (IE) and white light interference microscopy (WLIM) in a hybrid optical metrology study for fast and non-destructive detection, classification, and characterisation of defects in 4H–SiC homoepitaxial layers on 4H–SiC substrates. Ellipsometry measurement results are confirmed by WLIM. They can be successfully applied for wafer characterisation already during production of SiC epilayers and for subsequent industrial quality control.
The damage mechanisms of metallic components produced by process laser powder bed fusion differ significantly from those typically observed in conventionally manufactured variants of the same alloy. This is due to the unique microstructures of additively manufactured materials. Herein, the focus is on the study of the evolution of creep damage in stainless steel 316L specimens produced by laser powder bed fusion. X-ray computed tomography is used to unravel the influence of the process-specific microstructure from the influence of the initial void distribution on creep damage mechanisms. The void distribution of two specimens tested at 600 °C and 650 °C is analyzed before a creep test, after an interruption, and after fracture. The results indicate that the formation of damage is not connected to the initial void distribution. Instead, damage accumulation at grain boundaries resulting from intergranular cracking is observed.
Ergot alkaloids are a group of mycotoxins occurring in products derived from various grasses (e.g., rye) and have been regulated in the EU recently. The new maximum levels refer to the sum of the six most common ergot alkaloids in their two stereoisomeric forms in different food matrices. Typically, these twelve compounds are individually quantified via HPLC-MS/MS or -FLD and subsequently summed up to evaluate food safety in a time-consuming process. Since all these structures share the same ergoline backbone, we developed a novel sum parameter method (SPM) targeting all ergot alkaloids simultaneously via lysergic acid hydrazide. After extraction and clean-up, in analogy to the current European standard method EN 17425 (ESM) for ergot alkaloid quantitation, the samples were derivatized by an optimized hydrazinolysis protocol, which allowed quantitative conversion after 20 min at 100 °C. The new SPM was evaluated against another established HPLC-FLD-based method (LFGB) and the HPLC-MS/MS-based ESM using six naturally contaminated rye and wheat matrix reference materials. While the SPM provided comparable values to the ESM, LFGB showed deviating results. Determined recovery rates, limits of detection and quantification of all three employed methods confirm that the new SPM is a promising alternative to the classical approaches for ergot alkaloid screening in food.
problem. One reason is the sensitivity to stress corrosion cracking of the prestressing steel. Failure of prestressing wires can result in collapse of the entire structure without premature indication by transverse bending cracks or considerable deformation. The response of a structure to significant number of prestressing wire breaks was studied on a bridge in Brandenburg, Germany. Two thirds of the prestressing wires in concentrated tendons of two girders were cut before the bridge was demolished. Acoustic Emission Analysis was used to detect the wire breaks. Thus, the number of wire breaks was correlated with results of other measurement techniques, in particular strain measurements on the girders. In preparation of the measurements, the acoustic properties of the bridge were determined and the suitability of Schmidt hammer impacts as an acoustic reference source was validated.
Ein großer Teil unserer Brücken wurden in den 1950er bis 1970er Jahren als Spannbetonbrücken gebaut. Mit der damals noch relativ jungen Technologie entstanden elegante, teilweise gewagte Bauwerke mit großen Spannweiten, welche die Vorteile der Materialien Stahl und Beton geschickt kombinieren. Die Standsicherheit einiger dieser Brücken ist heute gefährdet. Die Ursachen liegen in der enorm gewachsenen Belastung durch Schwerverkehr, teilweise ungenügender Wartung und in konstruktiven und Materialschwächen, die der mangelnden Erfahrung mit der Technologie in der Bauzeit geschuldet sind. Ein neuralgischer Punkt der Bauwerke sind die in den Beton integrierten Spannglieder.
Infolge von Korrosion und Ermüdung können Elemente der Spannglieder reißen, wodurch die für das Tragwerk notwendige Spannung und somit die Tragfähigkeit reduziert werden. Nicht bei allen Brücken kündigen sichtbare Risse im Beton oder auffällige Verformungen den Tragfähigkeitsverlust bzw. das finale Versagen rechtzeitig an.
Die Schallemissionsanalyse ist die derzeit einzige Methode, das Reißen einzelner Spannstähle zuverlässig und mit wirtschaftlich vertretbarem Aufwand zu detektieren. Trotzdem es schon einige Spannbetonbauwerke gibt, die mit Schallemissionsanalyse überwacht werden, ist das Verfahren noch wenig bekannt.
Außerdem fehlen technische Richtlinien, was die Ausschreibung und Vergabe von entsprechenden Aufträgen und die Bewertung der Angebote sehr erschwert. Um sowohl Baulastträger als auch Dienstleistungsanbieter in den Vergabeverfahren und im Betrieb der Monitoringsysteme zu unterstützen, hat sich eine Gruppe von Experten aus den Bereichen Bauingenieurwesen und Schallemission zum Entwurf einer Richtlinie „Detektion von Spanndrahtbrüchen mit Schallemission“ zusammengefunden. Mit diesem Beitrag wird die Richtlinie vorgestellt, deren Bearbeitung bis zur SCHALL 23 abgeschlossen sein soll.
NMR is becoming increasingly popular for the investigation of building materials as it is a non-invasive technology that does not require any sample preparation nor causes damage to the material. Depending on the specific application it can offer insights into properties like porosity and spatial saturation degree as well as pore structure. Moreover it enables the determination of moisture transport properties and the (re-)distribution of internal moisture into different reservoirs or chemical phases upon damage and curing. However, as yet most investigations were carried out using devices originally either designed for geophysical applications or the analysis of rather homogeneous small scale (< 10 mL) samples. This paper describes the capabilities of an NMR tomograph, which has been specifically optimized for the investigation of larger, heterogeneous building material samples (diameters of up to 72 mm, length of up to 700 mm) with a high flexibility due to interchangeable coils allowing for a high SNR and short echo times (50 - 80 m s).
Recovery is an important measure for seal applications representing to which extent the elastomer regains its initial shape after deformation and release of an applied force. Compression set (CS) indicates the degree of recovery. Ethylene propylene diene rubber (EPDM) was aged at 75 ◦C, 100 ◦C, 125 ◦C and 150 ◦C for different ageing times up to five years and compression set measurements were performed at different times after disassembly and after additional tempering. Short- and long-term recovery up to one year after release for samples aged at 125 ◦C and 150 ◦C was also studied. To assess the curvature in the Arrhenius diagram that may occur due to non-sufficiently aged specimens, a degradation-rate based model was fitted to the CS data after tempering. For each ageing temperature, two decay fit functions were proposed, each with an activation energy and a corresponding degradative process. The influence of ageing on the leak-tightness after fast small partial release is investigated and estimated through the analysis of the shift factors from time temperature superposition (TTS) of CS measurements at different times after disassembly. Shift factors of CS measurement after 1 s and after additional tempering are in good agreement.
Comparing the performance of molecular and nanoscale luminophores and luminescent microand nanoparticles and estimating achievable signal amplitudes and limits of detection requires a standardizable intensity scale. This initiated the development of the relative MESF (number of molecules of equivalent soluble fluorochromes) and ERF (equivalent reference fluorophores) scales for flow cytometry and fluorescence microscopy. Both intensity scales rely on fluorescence intensity values assigned to fluorescent calibration beads by an intensity comparison to spectrally closely matching fluorophore solutions of known concentration using a spectrofluorometer. Alternatively, the luminophore or bead brightness (B) can be determined that equals the product of the absorption cross section (σa) at the excitation wavelength (σa(λex)) and the photoluminescence quantum yield (Φpl).
Thereby, an absolute scale based on fundamental and measurable spectroscopic properties can be realized which is independent of particle size, material, and luminophore staining or labeling density and considers the sensitivity of the optical properties of luminophores to their environment. Aiming for establishing such a brightness scale for light-scattering dispersions of luminescent particles with sizes exceeding a few ten nanometers, we demonstrate how the brightness of quasi-monodisperse 25 nm, 100 nm, and 1 μm sized polystyrene particles (PSP), loaded with two different dyes in varying concentrations, can be obtained with a single custom-designed integrating sphere setup that enables the absolute determination of Φpl and transmittance and diffuse reflectance measurements. The resulting Φpl, σa(λex), imaginary parts of the refractive index, and calculated B values of these samples are given in dependence of the number of incorporated dye molecule per particle. Finally, a unitless luminescence efficiency (LE) is defined allowing for the direct comparison of luminescence efficiencies of particles with different sizes.
Photodynamic therapy (PDT) used for treating cancer relies on the generation of highly reactive oxygen species, for example, singlet oxygen 1O2, by light-induced excitation of a photosensitizer (PS) in the presence of molecular oxygen, inducing DNA damage in close proximity of the PS. Although many precious metal complexes have been explored as PS for PDT and received clinical approval, only recently, the potential of photoactive complexes of nonnoble metals as PS has been discovered. Using the DNA origami technology that can absolutely quantify DNA strand break cross sections, we assessed the potential of the luminescent transition metal complex [Cr(ddpd)2]3+ (ddpd=N,N’-dimethyl-N,N’-dipyridine-2-ylpyridine-2,6-diamine) to damage DNA in an air-saturated aqueous environment upon UV/Vis illumination. The quantum yield for strand breakage, that is, the ratio of DNA strand breaks to the number of absorbed photons, was determined to 1–4%, indicating efficient transformation of photons into DNA strand breaks by [Cr(ddpd)2]3+.
The embrittlement of metallic alloys by liquid metals leads to catastrophic material failure and severely impacts their structural integrity. The weakening of grain boundaries by the ingress of liquid metal and preceding segregation in the solid are thought to promote early fracture. However, the potential of balancing between the segregation of cohesion-enhancing interstitial solutes and embrittling elements inducing grain boundary decohesion is not understood. Here, we unveil the mechanisms of how boron segregation mitigates the detrimental effects of the prime embrittler, zinc, in a Σ5 [0 0 1] tilt grain boundary in α −Fe (4 at.% Al). Zinc forms nanoscale segregation patterns inducing structurally and compositionally complex grain boundary states. Ab-initio simulations reveal that boron hinders zinc segregation and compensates for the zinc induced loss in grain boundary cohesion. Our work sheds new light on how interstitial solutes intimately modify grain boundaries, thereby opening pathways to use them as dopants for preventing disastrous material failure.