Wissenschaftliche Artikel der BAM
Filtern
Dokumenttyp
Schlagworte
- Laser beam welding (25)
- Additive manufacturing (22)
- Welding (14)
- Microstructure (11)
- Additive Manufacturing (10)
- Hydrogen (10)
- Mechanical properties (10)
- Laser powder bed fusion (9)
- Residual stress (9)
- Residual stresses (9)
- Solidification cracking (8)
- Friction (7)
- Tribology (7)
- Ultrasonic-assisted milling (7)
- Wear (7)
- Creep-resistant steel (6)
- Laser metal deposition (6)
- Process monitoring (6)
- Thermography (6)
- Fatigue (5)
- Resistance spot welding (5)
- Surface integrity (5)
- TIG welding (5)
- AFM (4)
- AISI 316L (4)
- Diffusible hydrogen (4)
- Hardness (4)
- High-strength steel (4)
- Hybrid laser arc welding (4)
- Hybrid laser-arc welding (4)
- L-PBF (4)
- Laser Powder Bed Fusion (4)
- Neutron diffraction (4)
- Numerical modeling (4)
- Selective laser melting (SLM) (4)
- Stress relief cracking (4)
- Thick-walled steel (4)
- AGIL (3)
- Alloy 36 (3)
- Artificial neural network (3)
- Atomic force microscopy (3)
- DED (3)
- Deep penetration (3)
- Fatigue crack propagation threshold (3)
- Fatigue tests (3)
- Heat accumulation (3)
- Heat treatment (3)
- High entropy alloy (3)
- In situ measurement (3)
- Inconel 718 (3)
- Infrared thermography (3)
- LIBS (3)
- Laser powder bed fusion (L-PBF) (3)
- Mechanical Engineering (3)
- Numerical modelling (3)
- Polymers (3)
- Post weld heat treatment (3)
- Quality assurance (3)
- Steel (3)
- Submerged arc welding (3)
- Ti-6Al-4V (3)
- Tubular X-joints (3)
- Varestraint test (3)
- Weld pool shape (3)
- 316L (2)
- AISI 304L (2)
- Additive manufacturing (AM) (2)
- Alloy modification (2)
- Austenite-to-martensite transformation (2)
- Bragg-edge imaging (2)
- Bulge effect (2)
- Chemical composition (2)
- Computed Tomography (2)
- Computed tomography (2)
- Contact resonance (2)
- Crack (2)
- Cracking (2)
- Critical strain (2)
- Crystallographic texture (2)
- Cyclic R-curve (2)
- Data preparation (2)
- Debye–Waller factor (2)
- Deuterium (2)
- Diffusion (2)
- Directed Energy Deposition (2)
- Distortion (2)
- EBSD (2)
- Electron backscattered diffraction (2)
- Finite element simulation (2)
- Force-distance curves (2)
- Fracture (2)
- Full penetration (2)
- GMA welding (2)
- Gap bridgeability (2)
- Gas metal arc welding (2)
- Gas tungsten arc welding (GTAW) (2)
- Grain refinement (2)
- Hardmetal (2)
- Heat control (2)
- High strength steels (2)
- High-entropy alloy (2)
- High-power laser beam welding (2)
- High-strength structural steel (2)
- Hot cracking (2)
- Hot stamping (2)
- Hydrogen Embrittlement (2)
- Hydrogen assisted cracking (2)
- Hydrogen embrittlement (2)
- Hydrogen-assisted cracking (2)
- Implant test (2)
- In situ monitoring (2)
- Inter layer time (2)
- LPBF (2)
- Laser beam melting (LBM) (2)
- Laser energy distribution (2)
- Laser hybrid welding (2)
- Laser-metal-deposition (2)
- Liquid metal embrittlement (2)
- Low transformation temperature (LTT) steel (2)
- Lubricants (2)
- Machining (2)
- Mechanics of Materials (2)
- Medium entropy alloy (2)
- Metals and Alloys (2)
- Microstructure characterization (2)
- Neutron imaging (2)
- Neutron radiography (2)
- Niobium carbide (2)
- Niobium carbide (NbC) (2)
- Numerical process simulation (2)
- Numerical simulation (2)
- Offshore (2)
- Optical flow (2)
- Plasma-transferred arc welding (2)
- Porosity (2)
- Post-weld heat treatment (2)
- Preheating (2)
- Ray tracing (2)
- Refill friction stir spot welding (2)
- Residual Stress (2)
- Residual stress analysis (2)
- Selective Laser Melting (2)
- Selective Laser Melting (SLM) (2)
- Simulation (2)
- Single pass welding (2)
- Software (2)
- Surface modification (2)
- Technical crack detection (2)
- Tensile properties (2)
- Texture (2)
- ToF-SIMS (2)
- Tool wear (2)
- Tribologie (2)
- WAAM (2)
- Weld pool dynamics (2)
- Wire arc additive manufacturing (2)
- X-ray diffraction (2)
- i-TRIBOMAT (2)
- 100Cr6 (AISI 52100) steel (1)
- 2101 duplex stainless steel (1)
- 3D Scanning (1)
- 3D printing (1)
- 9% Ni Steel (1)
- 9%Ni steel (1)
- AC magnetic field (1)
- AHSS (1)
- AM feature integration (1)
- ASTM E647 (1)
- Abdichtbauwerk (1)
- Accoustic emission (1)
- Additive Manufacturing (AM) (1)
- Additives (1)
- Advanced high strength steels (1)
- Advanced high-strength steel (1)
- Aging (1)
- AlMg0.7SiTiB filler wire (1)
- AlSi10Mg (1)
- AlSi10Mg alloy (1)
- Alite (1)
- Alkyd resin-based coating (1)
- Aluminum alloys (1)
- Aluminum bronze (1)
- Analytical calculation (1)
- Applications (1)
- Artificial Intelligence (1)
- Artificial intelligence (1)
- As-built LPBF IN718 alloy (1)
- Atomic force microscope (1)
- Austenitic stainless steels (1)
- Automated arc welding (1)
- Automated manufacturing (1)
- Automotive (1)
- Backlight (1)
- Bainitischer Schmiedestahl (1)
- Bauteilauslegung (1)
- Bayesian technique (1)
- Bead-on-plate welds (1)
- Beam oscillation (1)
- Bending test (1)
- Betriebsfestigkeit (1)
- Binders (1)
- Bismuth titanates (1)
- Bohrlochsonde (1)
- Bruchmechanik (1)
- Bulge formation (1)
- Bulging (1)
- Bulging effects (1)
- CFD model (1)
- Cantilever microprobe (1)
- Carbide (1)
- Carbon (1)
- Carbon dioxide footprint (1)
- Carbon steel (1)
- Catalysis (1)
- Cellular substructure (1)
- Cermet (1)
- Characterisation (1)
- Characterization (1)
- Characterization of corrosion layers (1)
- Charakterisierung (1)
- Charpy impact toughness (1)
- Chunky graphite (1)
- Cimensional Accuracy (1)
- Circumferential weld (1)
- Clinker substitute (1)
- Clustering (1)
- Co-Cr-alloy (1)
- Cobalt-chromium alloy (1)
- Cold cracking (1)
- Cold cracking safety (1)
- Columnar crystal growth (1)
- Component test (1)
- Component-like test (1)
- Composites (1)
- Computed tomography (CT) (1)
- Computer vision (1)
- Condensed Matter Physics (1)
- Condition monitoring (1)
- Convolutional neural network (1)
- Convolutional neural networks (CNN) (1)
- Core-shell structures (1)
- Corrosion (1)
- Crack closure effect (1)
- Crack-tip constraint (1)
- Creep (1)
- Creep behavior (1)
- Creep-resisting materials (1)
- Critical strain rate (1)
- Cryogenic steel (1)
- Cryogenic temperature (1)
- Crystal branch development (1)
- Crystal plasticity (1)
- Cutting forces (1)
- Cutting tool (1)
- Cyclic loading (1)
- Cylindrical turning (1)
- DED-EB (1)
- DED-arc (1)
- Damage prediction (1)
- Damage tolerance (1)
- Data evaluation methods (1)
- Data fusion (1)
- Data-driven quality assurance (1)
- Debye-Waller-Faktor (1)
- Deep learning (1)
- Deep penetration laser beam welding (1)
- Defect detection (1)
- Defects (1)
- Dental materials (1)
- Dichtungen (1)
- Diffraction (1)
- Diffraction-elastic constants (1)
- Diffusion/diffusivity (1)
- Digital Image Correlation (1)
- Digital image correlation (1)
- Digitalisation (1)
- Digitalization (1)
- Direct laser deposition (1)
- Directed energy deposition (1)
- Dislocation density (1)
- Dispersive XAS (1)
- Displacement (1)
- Dissimilar joints (1)
- Dissimilar materials (1)
- Dissimilar metal weld (1)
- Distortion upon baseplate removal (1)
- Ditigtal image correlation (1)
- Dual phase steel (1)
- Duplex AISI 2205 (1)
- Duplex stainless steel (1)
- Duplex stainless steels (1)
- Duplex steels (1)
- Dwell-time (1)
- EBAM (1)
- Edge quality (1)
- Effect of scanning strategies (1)
- Elastic modulus (1)
- Elastomers (1)
- Electrochemical permeation (1)
- Electromagnetic backing (1)
- Electromagnetic field (1)
- Electromagnetic forces (1)
- Electromagnetic stirring (1)
- Electromagnetic weld pool support (1)
- Electromagnetic weld pool support system (1)
- Electron backscatter diffraction (1)
- Electron beam welding (1)
- Electron microscopy (1)
- Element transport (1)
- Embedded electronics (1)
- Emisssivity (1)
- End crater (1)
- Endurance limit (1)
- Energy Engineering and Power Technology (1)
- Environmental conditions (1)
- Environmental impact categories (1)
- Error sources analysis (1)
- Evaporation (1)
- Experimental determination (1)
- Experimental procedure (1)
- FAIR data (1)
- FAT class (1)
- FEM (1)
- Fatigue Strength (1)
- Fatigue damage (1)
- Fatigue life (1)
- Fatigue limit (1)
- Fatigue properties (1)
- Femtosecond laser (1)
- Femtosecond laser processing (1)
- Ferritic spheroidal graphite cast iron (1)
- Ferroelectricity/ferroelectric materials (1)
- Filler material distribution (1)
- Filler wire (1)
- Filler wire mixing (1)
- Finish milling (1)
- Finite Element Method (1)
- Finite element (FE) (1)
- Finite element analysis (1)
- Finite element method (1)
- Finite element method (FEM) (1)
- Flange width (1)
- Flaw detection (1)
- Flüssigmetallinduzierte Rissbildung (1)
- Formation (1)
- Fractography (1)
- Fracture Mechanics (1)
- Frequency domain (1)
- Frequenzanalyse (1)
- Friction stir welding (1)
- Fuel Technology (1)
- Fusion zone size (1)
- Galvanized steel (1)
- General analytical solutions (1)
- Geteilte Infrastruktur (1)
- Green Deal (1)
- HAZ-softening (1)
- HCF (1)
- HSLA steel (1)
- Hard metals (1)
- Hardly separable problem (1)
- Harmonisation (1)
- Hastelloy X (1)
- Heat Treatment (1)
- Heat source models (1)
- Heat-affected zone (1)
- High power laser beam welding (1)
- High process speeds (1)
- High strength steel (1)
- High-entropy alloys (1)
- High-pressure hydrogen environment (1)
- High-strength filler metals (1)
- High-strength steel filler metal (1)
- High-strength steels (1)
- Hochfester Stahl (1)
- Hollow Specimen Technique (1)
- Hollow specimen (1)
- Hot Cracks (1)
- Hot cracking test (1)
- Hot tensile test (1)
- Hot working tool steel (1)
- Hybrid Laser arc Welding (1)
- Hybrid repair (1)
- Hydraulic reactivity (1)
- Hydrogen Transfer Film (1)
- Hydrogen diffusion (1)
- Hydrogen measurement (1)
- IBESS (1)
- IBESS Approach (1)
- IN 718 (1)
- IN725 (1)
- ISO 12108 (1)
- Image processing (1)
- Image registration (1)
- Impact Absorbed Energy (1)
- Implants (1)
- In situ (1)
- In-situ process monitoring (1)
- In-situ tensile test (1)
- Inconel 625 (1)
- Industrial and Manufacturing Engineering (1)
- Instumented indentation test (1)
- Integrated alignment features (1)
- Intelligent tribological material characterization (1)
- Intelligente tribologische Werkstoffcharakterisierung (1)
- Inter-layer time (1)
- Interoperability (1)
- Iron aluminide (1)
- Joining dissimilar materials (1)
- Joining technology (1)
- Kernel average misorientation (1)
- Keyhole collapse (1)
- Keyhole dynamics (1)
- Kitagawa-Takahashi diagram (1)
- L-PBF IN718 material (1)
- LCF (1)
- LIBS TIG welding (1)
- LMD (1)
- LTT Weld Filler Materials (1)
- LTT filler metal (1)
- LTT weld filler materials (1)
- Lab-to-field up-scaling (1)
- Lab-to-field upscaling (1)
- Lack-of-fusion (1)
- Lamé curves (1)
- Large-scale test (1)
- Laser Metal Deposition (LMD) (1)
- Laser Powder Bed Fusion (L-PBF) (1)
- Laser Powder Bed Fusion (LPBF) (1)
- Laser Powder Bed Fusion (PBF-LB/M, L-PBF) (1)
- Laser Welding (1)
- Laser beam melting (1)
- Laser cutting (1)
- Laser energy absorption (1)
- Laser implantation (1)
- Laser metal deposition (LMD) (1)
- Laser powder-based directed energy deposition (1)
- Laser welding (1)
- Laser-based additive manufacturing (1)
- Laser-induced oxide layer (1)
- Laser-induced periodic surface strctures (LIPSS) (1)
- Laser-induced periodic surface structures (LIPSS) (1)
- Laser-plasma hybrid (1)
- Lead-free ceramics (1)
- Life cycle assessment (1)
- Lifetime (1)
- Liquid Metal Embrittlement (1)
- Liquid phase sintering (1)
- Local Weld Geometry (1)
- Local critical strain (1)
- Local fatigue approaches (1)
- Local fatigue spproaches (1)
- Localized laser dispersing (1)
- Lorentz force (1)
- Lorentz forces (1)
- Low-cycle fatigue (1)
- L‐PBF (1)
- MVT (1)
- MWIR (1)
- Machine learning (1)
- Machine vision (1)
- Magnesium Alloy (1)
- Magnesium alloy (1)
- Magnetic bath support (1)
- Magnetic field (1)
- Martensite (1)
- Matching ferritic filler metal (1)
- Materials database (1)
- Mechanical anisotropy (1)
- Mechanical mismatching (1)
- Mechanical property (1)
- Melt pool depth (1)
- Melt pool dynamics (1)
- Metal (1)
- Metal mixing (1)
- Microalloying influences (1)
- Microbiologically influenced corrosion (1)
- Microcracking (1)
- Microfocus X-ray computer tomography (μCT) (1)
- Mild steels (1)
- Minimum Waiting Time (1)
- Mining head gear (1)
- Misalignment of edges (1)
- Model calibration (1)
- Model order reduction (1)
- Modellierung (1)
- Modelling studies (1)
- Modification of structural morphology (1)
- Molten pool (1)
- Multi-materials joining (1)
- Multi-physical modelling (1)
- Multi-principal element alloy (1)
- Multi-principal element alloys (1)
- Multiple principal element alloy (1)
- Multiple reflections (1)
- NIR (1)
- Nanotribology (1)
- Nanowear (1)
- Natural silver wires (1)
- Near-surface X-ray diffraction (1)
- Neutron Diffraction (1)
- Neutron and X-ray diffraction (1)
- Ni alloy (1)
- Ni-based austenitic filler metal (1)
- Nickel (1)
- Notch stress approach (1)
- Novel metrology (1)
- Numerical Simulation (1)
- Numerical investigation (1)
- Numerical welding simulations (1)
- Offshore steel grade (1)
- Online Process Monitoring (1)
- Online monitoring (1)
- Open science (1)
- Open source (1)
- Optical Tomography (1)
- Optical tomography (1)
- Oscillating ball-on-disc test (1)
- Oscillating magnetic field (1)
- Oscillating vapor plume (1)
- Oxidation (1)
- PBF-LB/M (1)
- PBF-LB/M/316L (1)
- Parabolic flight (1)
- Partial penetration (1)
- Particle transfer (1)
- Path planning (1)
- Peak stress method (1)
- Peak stress method (PSM) (1)
- Penetration depth (1)
- Periodic solidification pattern (1)
- Piezoresistive (1)
- Piezoresistive cantilever (1)
- Pipe weld preparation (1)
- Pipeline steel (1)
- Plasma cutting (1)
- Plasma-cut samples (1)
- Plasma-transferred-arc (1)
- Plastic deformation (1)
- Polymer (1)
- Polymere (1)
- Polyurethan (1)
- Position detection (1)
- Post Weld Heat Treatment (PWHT) (1)
- Potential drop technique (1)
- Potentiodynamic measurements (1)
- Ppreheating temperature (1)
- Precipitation hardening aluminum alloys (1)
- Pressure-dependent solubility (1)
- Prevention (1)
- Probabilistic assessment (1)
- Process chain (1)
- Projekt AGIL - Alterung additiv gefertigter metallischer Materialien und Komponenten (1)
- Proper generalized decomposition (1)
- Properties (1)
- Prostheses (1)
- Pulsed laser beam welding (1)
- Quality monitoring (1)
- Ray teacing (1)
- Ray-tracing methods (1)
- Reactor conditions (1)
- Reference data (1)
- Reference standards (1)
- Refraction (1)
- Renewable Energy, Sustainability and the Environment (1)
- Repair welding (1)
- Repair-welding (1)
- Representative specimens (1)
- Research data management (1)
- Residual Stresses (1)
- Residual stress in AM (1)
- Residual stress state (1)
- Ripples (1)
- Rissbildung in Stahl (1)
- Roughness (1)
- S-N curve (1)
- S-Phase (1)
- SEM (1)
- SIMS (1)
- SLM printed plasma torch (1)
- SSRT (1)
- SWIR (1)
- SWIR thermography (1)
- Sample random results (1)
- Scan strategy influence (1)
- Scanning kelvin probe force microscopy (1)
- Scattering (1)
- Schallemission (1)
- Seam geometry (1)
- Selective laser beam melting (1)
- Selektive-laser-melting (1)
- Shared infrastruture (1)
- Shear modulus (1)
- Ship building (1)
- Shipbuilding steel (1)
- Sicherheit (1)
- Single asperity (1)
- Single asperity contact (1)
- Single-pass welding (1)
- Sliding wear (1)
- Small-scale specimens (1)
- Solidification (1)
- Solubility (1)
- Spark plasma sintering (1)
- Stainless Steel (1)
- Stainless steel (1)
- Stainless steels (1)
- Staircase method (1)
- Statistical analysis (1)
- Steel and aluminium (1)
- Steelmaking slag (1)
- Stochastic sample functions (1)
- Strain fields prediction (1)
- Strain measurement (1)
- Strain-free lattice references (1)
- Strain-free lattice spacing (1)
- Stress Relief Cracking (SRC) (1)
- Stress balance (1)
- Stress balance condition (1)
- Structural stress approach (1)
- Structure analysis (1)
- Sub-oxide (1)
- Supermartensitic steel (1)
- Surface Integrity (1)
- Surface preparation (1)
- Surface processing (1)
- Surface structures (1)
- Synchrotron radiation (1)
- TEKKEN (1)
- Temperature (1)
- Temperature dependence (1)
- Tensile Strength (1)
- Tensile loading (1)
- Tensile resistance spot welding experiment (1)
- Tensile strength (1)
- Tensile testing (1)
- Thermal analysis (1)
- Thermal cycles (1)
- Thermal history (1)
- Thermodynamic modelling (1)
- Thermodynamic simulation (1)
- Thick materials (1)
- Thick plate welding (1)
- Thick-plate welding (1)
- Thick-walled (1)
- Titanium (1)
- Trapping (1)
- Tribo-Analytik (1)
- Tribo-analytics (1)
- Tungsten carbide (WC) (1)
- Two-dimensional solidification (1)
- Two-run welding technique (1)
- UV-blocker addition (1)
- Ultraschall-Echoverfahren (1)
- Ultraschall-Messtechnik (1)
- Ultrasonic Assisted Machining (1)
- Ultrasonic machining (1)
- Upscaling (1)
- V-notch impact toughness (1)
- Vaporization (1)
- Varestraint testing (1)
- Verschlussbauwerk (1)
- WRC 1992 diagram (1)
- Wear particles (1)
- Weathering tests (1)
- Weld metal cracking (1)
- Weld pool (1)
- Weldability (1)
- Welded Joints (1)
- Welded joint (1)
- Welded joints (1)
- Welding Simulation (1)
- Welding simulation (1)
- Welding thermal cycle (1)
- Weldx (1)
- Werkstoffdatenbank (1)
- White light interferometry (1)
- Widerstandspunktschweißen (1)
- Wind energy (1)
- Wire electron beam additive manufacturing (1)
- Wire feed laser beam welding (1)
- Wire-based additive manufacturing (1)
- X-ray Diffraction (1)
- X-ray and Neutron Diffraction (1)
- X-ray and neutron diffraction (1)
- X-ray computed tomography (XCT) (1)
- X-ray refraction (1)
- Young's modulus (1)
- Zero wear (1)
- Zerstörungsfreie Prüfung (1)
- Zink (1)
- contact resonance (1)
- infrared Thermography (1)
- µ-gravity (1)
- µCT (1)
- µCT-analysis (1)
- μCT-analysis (1)
Organisationseinheit der BAM
- 9 Komponentensicherheit (213) (entfernen)
Paper des Monats
- ja (9)
AbstractPowder Bed Fusion with Laser Beam of Metals (PBF-LB/M) has gained more industrial relevance and already demonstrated applications at a small series scale. However, its widespread adoption in various use cases faces challenges due to the absence of interfaces to established Manufacturing Execution Systems (MES) that support customers in the predominantly data-driven quality assurance. Current state-of-the-art PBF-LB/M machines utilize communication architectures, such as OPC Unified Architecture (OPC UA), Message Queuing Telemetry Transport (MQTT) and Representational State Transfer Application Programming Interface (REST API). In the context of the Reference Architecture Model Industry 4.0 (RAMI 4.0) and the Internet of Things (IoT), the assets, particularly the physical PBF-LB/M machines, already have an integration layer implemented to communicate data such as process states or sensor values. Missing is an MES component acting as a communication and information layer. To address this gap, the proposed Extract Transform Load (ETL) pipeline aims to extract relevant data from the fabrication of each build cycle down to the level of scan vectors and additionally to register process signals. The suggested data schema for archiving each build cycle adheres to all terms defined by ISO/TC 261—Additive Manufacturing (AM). In relation to the measurement frequency, all data are reorganized into entities, such as the AM machine, build cycle, part, layer, and scan vector. These scan vectors are stored in a runtime-independent format, including all metadata, to be valid and traceable. The resulting machine log represents a comprehensive documentation of each build cycle, enabling data-driven quality assurance at process level.
In this contribution, we present a physically motivated heat source model for the numerical modeling of laser beam welding processes. Since the calibration of existing heat source models, such as the conic or Goldak model, is difficult, the representation of the heat source using so-called Lamé curves has been established, relying on prior Computational Fluid Dynamics (CFD) simulations.
Lamé curves, which describe the melting isotherm, are used in a subsequent finite-element (FE) simulation to define a moving Dirichlet boundary condition, which prescribes a constant temperature in the melt pool. As an alternative to this approach, we developed a physically motivated heat source model, which prescribes the heat input as a body load directly. The new model also relies on prior CFD simulations to identify the melting isotherm. We demonstrate numerical results of the new heat source model on boundary-value problems from the field of laser beam welding and compare it with the prior CFD simulation and the results of the Lamé curve model and experimental data.
This study investigates the room‐ and high‐temperature (650 °C) tensile and low‐cycle‐fatigue behavior of Inconel 718 produced by laser powder bed fusion (PBF‐LB/M) with a four‐step heat treatment and compares the results to the conventional wrought material. The microstructure after heat treatment is characterized on different length scales. Compared to the wrought variant, the elastic and yield properties are comparable at both test temperatures while tensile strength, ductility, and strain hardening capacity are lower. The fatigue life of the PBF‐LB/M variant at room temperature is slightly lower than that of the wrought material, while at 650 °C, it is vice versa. The cyclic stress response for both material variants is characterized by cyclic softening, which is more pronounced at the higher test temperature. High strain amplitudes (≥0.7%) at room temperature and especially a high testing temperature result in the formation of multiple secondary cracks at the transitions of regions comprising predominantly elongated grain morphology and columns of stacked grains with ripple patterns in the PBF‐LB/M material. This observation and pronounced crack branching and deflection indicate that the cracks are controlled by sharp micromechanical gradients and local crystallite clusters.
The development of hydrogen technologies entails high safety requirements in distribution and dispensing infrastructure. Therefore, it is necessary to pursue research on material compatibility in hydrogen, especially for critical parts with tribological issues.
The focus of this study is to evaluate the influence of hydrogen on a wider range of commercially available polymer materials. Thereby, the friction and wear behavior of different grades of TPE, POM, PA66, PA12, PPA, PEEK, PPS, PTFE, PAI, PI and PBI were investigated against a rotating steel disk (AISI 304). Filled and unfilled polymers from different suppliers were evaluated at room temperature in air, vacuum and hydrogen gas (H2) as well as in liquid hydrogen at - 253°C (LH2).
The sliding behavior of the polymer materials is discussed by means of surface analyses, whereby special attention is paid to the formation of a transfer film.
According to the results at ambient temperature, the effect of hydrogen environment on the tribological behavior of neat polymers may be related to lack of moisture, but also to saturated hydrocarbons in gaseous hydrogen. In liquid hydrogen, the best tribological performances were achieved with neat PA polymers as well as PPS and PI composites.
Effect of high-pressure hydrogen environment on the physical and mechanical properties of elastomers
(2024)
This study presents the influence of high-pressure hydrogen environment on the physical and mechanical properties of two types of cross-linked hydrogenated acrylonitrile butadiene rubbers. Based on the CSA/ANSI standard, static exposures in hydrogen experiments were performed up to 100 MPa at 120 °C. Characterization before and after exposure was conducted by means of density and hardness measurements, dynamic mechanical analysis (DMA), tensile tests, compression set, FT-IR and AFM analyses to assess effects after decompression. While the effect of high-pressure exposure is significant immediately after exposure, most of the physical and mechanical properties recover after 48 hours. FT-IR, AFM, SEM and compression set results indicate, however, permanent effects.
Despite the advances in hardware and software techniques, standard numerical methods fail in providing real-time simulations, especially for complex processes such as additive manufacturing applications. A real-time simulation enables process control through the combination of process monitoring and automated feedback, which increases the flexibility and quality of a process. Typically, before producing a whole additive manufacturing structure, a simplified experiment in the form of a beadon-plate experiment is performed to get a first insight into the process and to set parameters suitably. In this work, a reduced order model for the transient thermal problem of the bead-on-plate weld simulation is developed, allowing an efficient model calibration and control of the process. The proposed approach applies the proper generalized decomposition (PGD) method, a popular model order reduction technique, to decrease the computational effort of each model evaluation required multiple times in parameter estimation, control, and optimization. The welding torch is modeled by a moving heat source, which leads to difficulties separating space and time, a key ingredient in PGD simulations. A novel approach for separating space and time is applied and extended to 3D problems allowing the derivation of an efficient separated representation of the temperature.
The results are verified against a standard finite element model showing excellent agreement. The reduced order model is also leveraged in a Bayesian model parameter estimation setup, speeding up calibrations and ultimately leading to an optimized real-time simulation approach for welding experiment using synthetic as well as real measurement data.
Hydrogen has great potential on the path towards decarbonization of the energy and transport sectors and can mitigate the urgent issue of global warming. It can be sustainably produced through water electrolysis with potentially zero emissions, and efficiently used (e.g., in fuel cell systems). Despite its environmental advantages, hydrogen-metal interactions could result in the degradation of the mechanical properties of several structural materials. In order to determine the magnitude of the material degradation in relation to hydrogen exposure, extensive material testing is required. The standardized procedure for in-situ testing for the quantification of the impact of compressed gaseous hydrogen (CGH2) relies on the utilization of an autoclave around the tested specimen. Such test set-up is complex, expensive, time-consuming and requires special equipment, trained personnel, and strict safety procedures. A relatively recent method to circumvent these issues and provide affordable results consists of using hollow specimens, thus applying the hydrogen pressure inside rather than outside the specimen. It allows to reduce the volume of hydrogen by several orders of magnitude and to perform the tests more efficiently and in a safer manner. This study focuses on evaluating the tensile properties of X65 vintage pipeline steel tested in a high-pressure hydrogen environment using hollow specimens. Tests are performed in 6 MPa H2 and Ar at the nominal strain rate of 10−6 s−1 to evaluate the reduced area at fracture and the elongation loss. The effect of surface finishing on crack initiation and propagation is investigated by comparing two different manufacturing techniques. In this way, this study provides insights into the applicability of a novel, reliable, and safe testing method which can be used to assess the hydrogen-assisted ductility loss in metallic materials.
Multiple principal element alloys encompass the well-known high entropy alloys (HEA). The alloy system represents a new class of materials consisting of at least three alloying elements, each containing 5 to 35 at.%. Thus, this alloying concept differs fundamentally from conventional materials such as steel or nickel alloys. For this purpose, the alloying elements are specifically selected, the microstructures are adjusted in a single-phase and, in some cases, multi-phase manner. In particular, conflicting goals, such as the trade-off between strength and ductility in conventional steels, are overcome. However, in the last 20 years, the focus has been on material synthesis. With the increase in available material quantities, the focus is now on processing issues such as joining and welding processes. The weldability of HEAs has received very little attention so far. The experience with dissimilar metal welds is completely lacking but is essential for the application of these materials in combination with conventional materials. The present study presents comprehensive experimental results on the weldability of an equimolar CoCrFeMnNi-HEA in cold-rolled and heat-treated condition, which was joined by tungsten inert gas welding to an austenitic steel AISI 304. The mechanical properties of the dissimilar metal welds were characterized by cross-weld tensile samples, whereas the local deformation in the weld of the different welding zones was measured by digital image correlation. In accordance with the respective initial HEA condition (cold-rolled vs. heat-treated), the local strain behavior was divergent and influenced the global mechanical properties of both DMW types. Nonetheless, the experiments provided proof in principle of the weldability for dissimilar joints of the CoCrFeMnNi-HEA welded to conventional materials like austenitic stainless steels ensuring a corresponding capability for mechanical loading. This allows further considerations on the application of these innovative materials.
AbstractThe sustainable and resource-efficient production of wind energy plants requires the use of modern high-strength fine-grain structural steels. This applies to both foundation and erection structures, like mobile or ship cranes. During the assembly of steel structures, unacceptable defects can occasionally be found in the weld area. In most cases, the economical solution would be local thermal gouging of the affected areas and re-welding. Due to the high shrinkage restraint of the joint groove in the overall structure, the superposition of global and local welding-induced stresses may lead to crack formation and component failure, particularly in interaction with the degradation of the microstructure and mechanical properties of high-strength steels during the repair process. However, manufacturers hardly have any information about these issues and there is a lack of recommendations and guidelines to take these safety-relevant aspects into account in adequate repair concepts. The aim of this research is to derive recommendations for repair concepts appropriate to the stresses and materials involved providing a basis for standards and guidelines to avoid cold cracking, damage and expensive reworking especially for high-strength steels. Part 1 of this study involves systematic investigations of influences of shrinkage restraint during repair welding of two high-strength steels S500MLO for offshore application and S960QL for mobile crane structures. The quantification of the shrinkage restraint of repair weld joints was achieved by means of experimental and numerical restraint intensity analysis. In welding experiments with self-restrained slot specimens, restraint intensity and introduction of hydrogen via the welding arc using anti spatter spray were varied systematically to analyse the effect on welding result, residual stresses and cold cracking. It could be shown that increasing restraint intensities result in significantly higher transverse residual stress levels. In the case of hydrogen introduction S500MLO showed no cold cracking independent of the restraint conditions. However, S960QL was found to be considerably cold cracking sensitive if hydrogen is introduced. With increasing restraint intensity length and number of cold cracks increases significantly. Part 2 [1] of this study is focussed on microstructure and residual stresses due to gouging and stress optimization via adequate heat control parameters in repair welding.
The Varestraint test and its variant Transvarestraint are one of the most widely used techniques for evaluating a material solidification cracking sensitivity during welding. The result of such tests is a crack length which is proportional to the material’s cracking susceptibility. Nevertheless, the welding and load parameters can unintentionally influence the crack length, which in some cases can distort the material evaluation. An approach is described as to how these effects can be assessed with the aid of a digital crack analysis. The crack lengths are compared position-dependently with their possible propagation due to the weld pool movement during continuous loading. The index derived from this can be used by the operator to evaluate his test parameters. In addition, a comparison of the results of different Varestraint setups is made possible. Alongside experimental results, a numerical sensitivity analysis is presented on how individual welding and loading parameters can affect the crack lengths.
The high potential of hydrogen as a key factor on the pathway towards a climate neutral economy, leads to rising demand in technical applications, where gaseous hydrogen is used. For several metals, hydrogen-metal interactions could cause a degradation of the material properties. This is especially valid for low carbon and highstrength structural steels, as they are commonly used in natural gas pipelines and analyzed in this work.
This work provides an insight to the impact of hydrogen on the mechanical properties of an API 5L X65 pipeline steel tested in 60 bar gaseous hydrogen atmosphere. The analyses were performed using the hollow specimen technique with slow strain rate testing (SSRT). The nature of the crack was visualized thereafter utilizing μCT imaging of the sample pressurized with gaseous hydrogen in comparison to one tested in an inert atmosphere.
The combination of the results from non-conventional mechanical testing procedures and nondestructive imaging techniques has shown unambiguously how the exposure to hydrogen under realistic service pressure influences the mechanical properties of the material and the appearance of failure.
Numerical and experimental assessment of liquid metal embrittlement in externally loaded spot welds
(2024)
Zinc-based surface coatings are widely applied with high-strength steels in automotive industry. Some of these base materials show an increased brittle cracking risk during loading. It is necessary to examine electrogalvanized and uncoated samples of a high strength steel susceptible to liquid metal embrittlement during spot welding with applied external load. Therefore, a newly developed tensile test method with a simultaneously applied spot weld is conducted. A fully coupled 3D electrical, thermal, metallurgical and mechanical finite element model depicting the resistant spot welding process combined with the tensile test conducted is mandatory to correct geometric influences of the sample geometry and provides insights into the sample’s time dependent local loading. With increasing external loads, the morphology of the brittle cracks formed is affected more than the crack depth. The validated finite element model applies newly developed damage indicators to predict and explain the liquid metal embrittlement cracking onset and development as well as even ductile failure.
Abstract
In the post-processing of large maritime components, a considerable amount of waste in the form of milling and grinding chips is produced. At the same time, additive manufacturing technologies have shown great potential in producing high-volume parts for maritime applications, allowing novel design approaches and short lead times. In this context, this study presents a sustainable approach to recycle and use aluminium bronze waste material, generated during post-processing of large cast ship propellers, as feedstock for laser-powder directed energy deposition. The recycling technology used to produce powder batches is inductive re-melting in combination with ultrasonic atomization. The derived metal powders are characterized using digital image analysis, powder flowability tests, scanning electron microscopy as well as energy dispersive X-ray spectroscopy. Compared to conventional metal powders produced by gas atomization, the recycled material shows excellent sphericity and a powder size distribution with a higher content of finer and coarser particles. Metallographic sections of deposited additively produced specimens show an increased hardness and reduced ductility, but also competitive densities and higher yield and ultimate tensile strength compared to cast material. The process chain shows high potential for the maritime sector to enable circular and sustainable manufacturing.
Die neue Generation von bainitischen Schmiedestählen bietet auf der einen Seite ein erhebliches Festigkeitspotenzial, das es im Sinne des Leichtbaus auch für zyklisch belastete Sicherheitsbauteile zu heben gilt. Auf der anderen Seite geht mit dieser Festigkeitssteigerung im Vergleich zu Vergütungsstählen ein Verlust an Duktilität und Zähigkeit einher. Am Beispiel des Demonstratorbauteils Achsschenkel ging das Forschungsvorhaben der Frage nach, wie ein Freigabeprozess zu gestalten ist, damit das Festigkeitspotenzial der neuen Stähle zuverlässig ausgenutzt werden kann. Als Ergebnis wird eine Vorgehensweise dargestellt, die den Eigenschaften der neuen Generation von Schmiedestählen Rechnung trägt, um den sicheren Betrieb der Komponenten zu gewährleisten.
The ISO 3690 standard “Determination of hydrogen content in arc weld metal” requires a thermal activation of the diffusible hydrogen in a piece of weld metal for the subsequent ex situ concentration measurement by carrier gas hot extraction CGHE or thermal desorption spectroscopy (TCD). Laser-induced breakdown spectroscopy (LIBS) offers a time and spatially resolved, almost non-destructive, in situ measurement of hydrogen at surfaces without sample preparation. We measured hydrogen in steels, which were charged either electrochemically or by high-pressure hydrogen gas, and compared the results. Further, the feasibility of quantitative hydrogen line scan measurements with LIBS was demonstrated by measuring hydrogen at water jet cut surfaces. The hydrogen concentrations measured with the help of LIBS were compared with CGHE measurements. It was observed that hydrogen can be reliably measured with LIBS for concentrations larger than 2 wt.-ppm. The maximum hydrogen concentration achieved using electrochemical charging was 85.1 ppm. The results show that LIBS is a promising technique for time- and spatially resolved measurements of hydrogen in steels.
High-strength steels offer potential for weight optimization due to reduced wall thicknesses in modern constructions. Additive manufacturing processes such as Wire Arc Additive Manufacturing (WAAM) enable the resource-efficient production of structures. In the case of defects occurring in weld seams orWAAM components due to unstable process conditions, the economical solution is local gouging or machining and repair welding. It is important to understand the effects of machining steps on the multiaxial stress state in conjunction with the design-related shrinkage restraints. Research into how welding and slot milling of welds andWAAM structures affects residual stresses is still lacking. For this reason, component-related investigations with high-strength steels with yield strengths ≥790 MPa are carried out in our research. In-situ digital image correlation (DIC) and ex-situ X-ray diffraction (XRD) were used to analyze the stresses and strains induced on specimens during and after milling. The systematic analyses revealed a significant interaction of the stiffness and microstructure of the specimens with the initial residual stresses induced by welding. Subsequent repair welds can result in significantly higher residual stresses.
Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods, or jackets. These components are typically constructed using submerged arc welding (SAW) with high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen-assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicates the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam/layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with over 20 passes and a seam length of 1000 mm. Additional welded stiffeners simulated the effect of a high restraint, to achieve critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of up to 48 h after the completion welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modeling allowed the qualitative estimation of the hydrogen diffusion in the weld. No noticeable HAC occurrence was identified and confirms the high cracking resistance of the investigated material. Finally, the applicability of the MWT concept should be critically discussed.
Steelmaking slag is a by-product of steel production, of which 4.5 Mt were produced in 2020 in Germany alone. It is mainly used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical cycle, used as fertiliser or landfilled.
With this use, iron oxides still contained in steelmaking slag are lost. In addition, the possibility of producing higher-grade products from steelmaking slag is foregone. In recent decades, many researchers have investigated the production of Portland cement clinker and crude iron from basic oxygen furnace slags (BOFS) via a reductive treatment. Carbothermal treatment of liquid BOFS causes a reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. Simultaneously, the chemical composition of the reduced slag is adapted to that of Portland cement clinker.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as a reducing agent. The resulting low-iron mineral product has a similar chemical composition to Portland cement clinker and was rich in the tricalcium silicate solid solution alite (Ca3SiO5). Based on its chemical and mineralogical composition, similar to that of Portland cement clinker, the reduced BOFS has the potential to react comparably. In our study, the reduced BOFS produced less hydration heat than OPC, and its hydraulic reaction was delayed. However, adding gypsum has shown to accelerate the hydration rate of the reduced BOFS compared to that known from the calcium silicates of Portland cement clinker.
Further research to improve the hydraulic properties of the reduced slag is essential. If successful, producing a hydraulic binder and crude iron from BOFS has economic and ecological benefits for both the cement and steel industries.
The effect of the oscillating metal vapor plume on the keyhole and molten pool behavior during the laser beam welding of AlMg3 aluminum alloys is investigated by experimental and numerical methods. The real-time height of the metal vapor plume is measured by high-speed camera observation. The obtained experimental results are used to evaluate the additional heating source and laser beam attenuation caused by the scattering and absorption based on the Beer–Lambert theory. Furthermore, the dynamic behavior of the metal vapor plume is incorporated into a 3D transient heat transfer and fluid flow model, coupled with the ray tracing method, for the laser beam welding of the AlMg3 alloy. It is found that additional heating resulting from the scattered and absorbed laser beam energy by the metal vapor plume significantly expands the shape of the molten pool on the top region. Moreover, the oscillating metal vapor plume caused the fluctuation of the high-temperature region in the molten pool. The probability of keyhole collapse at the bottom increases 17% due to the oscillating laser power induced by the laser beam attenuation. The internal interplay between the metal vapor plume, molten pool shape, and keyhole collapse is obtained. The developed model has been validated by experiments, which shows a good agreement.