Wissenschaftliche Artikel der BAM
Filtern
Dokumenttyp
- Zeitschriftenartikel (21) (entfernen)
Sprache
- Englisch (21) (entfernen)
Schlagworte
- Corrosion (14)
- Carbon steel (4)
- Corrosion testing (3)
- Impurities (3)
- Aluminium (2)
- CCUS (2)
- Corrosion resistance (2)
- Gel electrolytes (2)
- Geothermal (2)
- Agar (1)
Organisationseinheit der BAM
- 7.6 Korrosion und Korrosionsschutz (21) (entfernen)
Paper des Monats
- ja (1)
The corrosion behavior of galvanized steels and zinc components under atmospheric exposure depends mostly on the corrosion product‐based cover layer formation under the prevailing conditions. The use of agar‐based gel electrolytes makes it possible to use electrochemical methods to obtain a characteristic value from these cover layers that describe their current and future protective capacity. It is shown here that different states of galvanized steel can be distinguished very well under laboratory conditions and that this method is also suitable for use under practical conditions. Based on the characteristic values and assuming future time of wetness, it is very easy to draw up a forecast for the future corrosion rate, which provides plausible values.
Tests for assessing prestressing steels' susceptibility to hydrogen‐induced stress corrosion cracking are essential for approvals, in‐house monitoring, and third‐party material testing. According to ISO 15630‐3, the time to brittle fracture by constant load under corrosive conditions in thiocyanate test solutions (A or B) at 50°C is measured. In the literature, a high scattering in stress corrosion tests is reported, which questions the integrity of the test procedure. This paper shows the results of studies about the influence of solution composition on hydrogen charging in electrochemical and permeation measurements. Electrochemical experiments show that polished steel surfaces without common drawing layers have more consistent free corrosion currents, polarization resistances, and B‐values in solution A with low scattering compared to the solution B experiments. The influence of temperature at 50°C and an ambient temperature of 22°C was also tested.
Corrosion monitoring of reinforced concrete structures:The DGZfP specification B12 Collaboration
(2023)
Corrosion monitoring of reinforced or prestressed concrete structures has becomeincreasingly important in recent years. Areas of application include componentsthat are no longer accessible after completion or where potential fieldmeasurements cannot be carried out due to existing coatings. Corrosion monitoringcan also be used to monitor the progress of corrosion in corroding systems, e.g. to prove the success of repair measures according to repair principle 8 in accordancewith EN 1504‐9 or repair method 8.3 in accordance with the DIBt repair guideline.It also could be used to prove the functionality of cathodic corrosion protectionsystems in accordance with ISO 12696. Despite the increasing importance ofcorrosion monitoring, no guidelines orrecommendations existed until 2018. Thisgap was closed by the English version of specification B12,“Corrosion Monitoringof Reinforced and Prestressed Concrete Structures,”of the German Society for Non‐Destructive Testing, which was published in 2021. This article introducesspecification B12 by explaining the basicmeasurement principles and illustratingthe potential of corrosion monitoring in new and existing buildings.
The corrosivity of atmospheres in Europe has changed significantly in recent decades. For the Federal Republic of Germany, no current values for the corrosion rate based on 1‐year atmospheric exposure of standard specimens can be found in the scientific literature after 2000. This paper presents results from a field exposure study in the Berlin metropolitan area and Helgoland in 2016. Based on standard specimens, values for the corrosion rate and the corresponding atmospheric corrosivity category are determined for open exposure and indirect weathering in a ventilated enclosure as sheltering after 1 year of exposure. The results prove that determined corrosivity categories are material‐specific. Sheltered exposure is a typical atmospheric situation for many building components. It allows statements on the effect of the concentration of airborne substances on the corrosivity beyond the normative requirements.
Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV.
The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-ANODE) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkollite.
A global transition towards more sustainable, affordable and reliable energy systems is being stimulated by the Paris Agreement and the United Nation's 2030 Agenda for Sustainable Development. This poses a challenge for the corrosion industry, as building climate‐resilient energy systems and infrastructures brings with it a long‐term direction, so as a result the long‐term behaviour of structural materials (mainly metals and alloys) becomes a major prospect. With this in mind “Corrosion Challenges Towards a Sustainable Society” presents a series of cases showing the importance of corrosion protection of metals and alloys in the development of energy production to further understand the science of corrosion, and bring the need for research and the consequences of corrosion into public and political focus. This includes emphasis on the limitation of greenhouse gas emissions, on the lifetime of infrastructures, implants, cultural heritage artefacts, and a variety of other topics.
In general, pH-sensitive colorants such as phenolphthalein are applied on freshly split surfaces of building structures to determine the state of carbonation. For years, it has been known that the aerosols of phenolphthalein are suspected of being carcinogenic. Hence, more work has currently being done on alternative indicators for the use in research and the use on construction sites. Over the past years, mainly pH indicators from other research areas and natural dyes were investigated for their usability to cementitious systems. This paper presents the experimental results of using phenolphthalein solution bound in agar-agar gel. This gel-bound indicator allows the future use of the already known phenolphthalein dye without the health hazards for the user. To demonstrate the flexibility of the gel-bound colorant, different application forms of the indicator were carried out and assessed. In addition, the results obtained by the different methods were statistically evaluated to ensure validity.
The accuracy of the results was confirmed by thermogravimetric analysis and IR spectroscopic studies as reference methods. It has also succeeded to demonstrate the comparability of the results achieved by the gel-bound colorant with the results of the common sprayed application method. As an additional gain in knowledge, comparative results of indicator tests, TGA analysis, and FTIR investigation are shown.
Novel agar-based test electrolytes are used to perform electrochemical corrosion investigations on ZnFe and ZnNi binary as well as ZnFeMo ternary zinc coatings. The objectives of the electrochemical investigations include the characterization of the corrosion behavior, the description of the protective effect of the coatings as well as the investigation of the layer formation and degradation under artificial aging. ZnFe and ZnFeMo coatings are applied with varying iron content as well as an additional passivation layer, respectively, to study the effect on corrosion resistance. The results show that the protective effect of the coatings is not negatively influenced by different iron contents or the addition of molybdenum. Additional passivation of the ZnFe-containing coatings by means of a passivating agent leads to a significant improvement in the protective effect. Artificial aging leads to slight degradation of the additional passivation layer whereas coatings without post-treatment enhance their protective effect by the formation of corrosion product layers.
To set up recommendations on how to define “reasonable minimum composition thresholds” for CO2 streams to access CO2 pipeline networks, we investigated potential impacts of CO2 streams with different and temporally variable compositions and mass flow rates along the CCS chain. All investigations were based on a generic “CCS cluster scenario” in which CO2 streams captured from a spatial cluster of eleven emitters (seven fossil-fired power plants, two cement plants, one refinery and one steel mill) are collected in a regional pipeline network. The resulting CO2 stream (19.78 Mio t impure CO2 per year) is transported in a trunk line (onshore and offshore) and injected into five generic replicate storage structures (Buntsandstein saline aquifers) offshore. Experimental investigations and modeling of selected impacts revealed beneficial as well as adverse impacts of different impurities and their combinations. Overall, no fundamental technical obstacles for transporting, injecting and storing CO2 streams of the considered variable compositions and mass flow rates were observed. We recommend to define minimum composition thresholds for each specific CCS project through limiting
i) the overall CO2 content,
ii) maximum contents of relevant impurities or elements,
iii) acceptable variability of concentrations of critical impurities, and defining impurity combinations to be avoided.
The critical chloride content C(crit) is an indicator for the corrosion resistance of reinforcing steels in concrete. In this article, several experimental methods for determining the critical chloride content C(crit) of mild and an alloyed (12% Cr) steel in cementitious materials are compared. The methods used include accelerated polarization tests and tests using more natural (unpolarized) conditions in which chloride ingress occurs by diffusion and capillary uptake. The advantages and disadvantages of the methods are discussed, in particular, with the objective of reaching a compromise between applicability to practice and feasibility in laboratory testing.