Kerntechnische Entsorgung
Filtern
Dokumenttyp
- Vortrag (16)
- Beitrag zu einem Tagungsband (10)
- Zeitschriftenartikel (3)
- Posterpräsentation (1)
- Forschungsbericht (1)
Sprache
- Englisch (31) (entfernen)
Schlagworte
- Ring Compression Test (11)
- Cladding Embrittlement (9)
- Spent Nuclear Fuel (8)
- Cladding (7)
- Ageing Management (6)
- Extended Storage (6)
- Discharge (4)
- Extended Interim Storage (4)
- Nuclear fuel (4)
- Spent Fuel Characterization (4)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (31) (entfernen)
Eingeladener Vortrag
- nein (16)
The European Joint Programme on Radioactive Waste Management (EURAD) is working on Spent Fuel Characterization (SFC) in its work package (WP) 8. Inspired by the EURAD activities, the International Atomic Energy Agency (IAEA) established an international Coordinated Research Project (CRP) on SFC. The EURAD WP SFC
participants are collaborating as a team on the IAEA CRP on SFC. The EURAD WP SFC project consists of four tasks. Task 3 investigates the behaviour of nuclear fuel and cladding after discharge. The aim of these activities is to understand and describe the evolution of the cladding-pellet system and its ageing under conditions of extended interim storage, transportation and emplacement in a final disposal system. At a Consultancy Meeting, BAM as contributor to Task 3 presented current results of the failure analysis of irradiated ZIRLO® claddings under conditions of the Ring Compression Test.
SFC is a work package in Eurad that investigates issues related to the properties of the spent nuclear fuel in the back-end of the nuclear fuel cycle. Decay heat, nuclide inventory, and fuel integrity (mechanical and otherwise), and not least the related uncertainties, are among the primary focal points of SFC. These have very significant importance for the safety and operational aspect of the back-end. One consequence is the operation economy of the back-end, where deeper understanding and quantification allow for significant optimization, meaning that significant parts of the costs can be reduced. In this paper, SFC is described, and examples of results are presented at about half-time of the work package, which will finish in 2024. The DisCo project started in 2017 and finished in November 2021 and was funded under the Horizon 2020 Euratom program. It investigated if the properties of modern fuel types, namely doped fuel, and MOX, cause any significant difference in the dissolution behavior of the fuel matrix compared with standard fuels. Spent nuclear fuel experiments were complemented with studies on model materials as well as the development of models describing the solid state, the dissolution process, and reactive transport in the near field. This research has improved the understanding of processes occurring at the interface between spent nuclear fuel and aqueous solution, such as redox reactions. Overall, the results show that from a long-term fuel matrix dissolution point of view, there is no significant difference between MOX fuel, Cr+Al-doped fuel, and standard fuels.
The European Joint Programme on Radioactive Waste Management (EURAD) is working on Spent Fuel Characterization (SFC) in its work package (WP) 8. Inspired by the EURAD activities, the International Atomic Energy Agency (IAEA) established an international Coordinated Research Project (CRP) on SFC. The EURAD WP SFC participants are collaborating as a team on the IAEA CRP on SFC. The EURAD WP SFC project consists of four tasks. Task 3 investigates the behaviour of nuclear fuel and cladding after discharge. The aim of these activities is to understand and describe the evolution of the cladding-pellet system and its ageing under conditions of extended interim storage, transportation and emplacement in a final disposal system. At the Second Research Coordination Meeting on Spent Fuel Characterization, BAM as leader of Task 3 reported on the status of the research work.
Task 3 of Work package 8 (Spent Fuel Characterization) of the European Joint Programme on Radioactive Waste Management (EURAD) investigates the behaviour of nuclear fuel and cladding after discharge. The aim of the work is to understand and describe the behaviour of spent nuclear fuel (SNF), irradiated cladding, fuel/cladding chemical interaction (FCCI) and ageing under conditions of extended interim storage, transportation and emplacement in a final disposal system. BAM contributes to the project as partner and leads Task 3. The presentation gives an overview of the project status, main achievements in experimental work and modelling studies, deviations from the plan, delays and challenges ahead.
In order to demonstrate the safety of both spent fuel and the storage system, a good understanding of the processes that might cause deterioration is required. The International Atomic Energy Agency (IAEA) continued the coordinated research on Spent Fuel Performance Assessment and Research (SPAR) into a fourth phase starting in 2015 to evaluate fuel and materials performance under wet and dry storage and to assess the impact of interim storage on associated spent fuel management activities (such as handling and transport). BAM’s understanding and experiences in the field of long-term storage of spent fuel and especially spent fuel characterization are presented to assist the preparation of the final project report.
Embrittlement of spent fuel claddings during long-term dry interim storage - Current approach at BAM
(2019)
The integrity of fuel rods and cladding tubes must be demonstrated throughout the dry interim storage of spent nuclear fuel in Germany. For at least a relevant number of casks, an extension of interim storage between 40 and 100 years is foreseeable. The drying procedure for the fuel rods in conjunction with the thermomechanical storage conditions may change the microstructure of the cladding tubes and lead to their possible embrittlement. The failure probability might increase under mechanical load by handling procedures (transport after storage) on potentially embrittled cladding tubes of fuel rods especially at low temperatures after long-term storage. Results of ring compression tests on unirradiated pre-hydrided as well as irradiated samples with radial hydrides are investigated by finite element analyses to be able to describe the failure process and to identify failure criteria.
A Memorandum of Understanding (MOU) between Argonne National Laboratory (Argonne) and the German Bundesanstalt für Materialforschung und -prüfung (BAM) was signed in October 2014. Its objectives are to promote cooperation among scientists and specialists at Argonne and BAM and establish a framework for collaboration in advanced technologies associated with the back end of the nuclear fuel cycle. Collaborative activities involving Argonne and BAM may be implemented through the promotion of joint research activities and scientific workshops and conferences; exchange of technical information; and visits by scientists, specialists, and graduate, postgraduate, and Ph.D. students. The MOU was renewed in January 2020 for another five years. Highlights of the progress and achievements are provided in identified topical areas for collaboration on ageing management guidance, storage, transportation and disposal R&D, joint conference activities, and conclude with the benefits of the MOU in fostering Argonne and BAM collaboration.
The characterization of spent fuel and radioactive waste is essential in the evaluation of the ability of these materials to meet acceptance criteria. Prior to determining a method for spent fuel characterization, it is necessary to identify the type of data required to support safety and other analyses for the storage, transportation and final disposal of spent fuel. BAM’s understanding and capabilities in the field of spent fuel characterization are presented for the scope of a coordinated research project on the topic.
The European Joint Programme on Radioactive Waste Management (EURAD) deals in work package (WP) 8 with Spent Fuel Characterization (SFC). Inspired by the EURAD activities, an international Coordinated Research Project (CRP) on SFC was established by the International Atomic Energy Agency (IAEA). The EURAD WP SFC participants are collaborating as a team on the IAEA CRP on SFC. The EURAD WP SFC project is divided into four tasks. Task 3 investigates the behaviour of nuclear fuel and cladding after discharge. The aim of these activities is to understand and describe the evolution of the cladding-pellet system and its ageing under conditions of extended interim storage, transportation and emplacement in a final disposal system. During an IAEA consultancy meeting, BAM as leader of Task 3 reported on the current status of the research work.
The purpose of this paper is to investigate the relationship between hydride morphology, in particular the presence of radial hydrides (RHs), stress state and failure mechanisms associated with the ring compression test (RCT). Samples of ZIRLO®cladding were pre-hydrided and subjected to thermo-mechanical treatments to precipitate long radial hydrides. The results show that the reorientation treatment was very successful. A considerable fraction of RHs was generated, the radial hydride continuity factor being around 80 to 90% of the wall thickness. The samples with reoriented hydrides were tested using the RCT at room temperature. Macroscopic brittle failure was observed with sudden load drops for displacements around 0.5 mm, with a calculated “offset strain”between 0.5 and 1%. Crack nucleation occurs in RHs located in regions with the highest values of hoop stress. These locations are the inner diameter of cladding at the vertical plane of the sample (12 and 6 o’clock positions) and the outer diameter at the horizontal plane (3 and 9 o’clock positions). Noticeable load drops in the RCT are associated with unstable crack propagation events through the radial hydride network, the crack front reaching up to 90% of the wall thickness in some cases. The failure micro-mechanism is quasi-cleavage in the hydrides and micro-void nucleation, growth and coalescence in the Zr matrix, with ductile tearing patches connecting neighboring hydrides. The main conclusion is that radial hydride metrics is not the only parameter that determines cladding failure in the presence of RHs, but the interaction between the location and continuity of RHs and the stress normal to the hydride (the hoop stress in this case). Consequently, if a radial hydride is located at a position within the cladding where the hoop stress is small, a crack will not be initiated easily in the RCT.