Kerntechnische Entsorgung
Filtern
Dokumenttyp
- Vortrag (120)
- Beitrag zu einem Tagungsband (72)
- Posterpräsentation (30)
- Zeitschriftenartikel (21)
- Buchkapitel (7)
- Monografie (1)
- Beitrag zu einem Sammelband (1)
- Amtliche Bekanntmachung (1)
- Forschungsbericht (1)
Sprache
- Englisch (254) (entfernen)
Schlagworte
- Ageing (28)
- Ring Compression Test (18)
- Spent Nuclear Fuel (18)
- Drop test (17)
- Metal seal (17)
- Transport (17)
- Cladding Embrittlement (16)
- Ageing Management (15)
- IAEA (15)
- Compression set (13)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (254) (entfernen)
Paper des Monats
- ja (2)
Eingeladener Vortrag
- nein (120)
Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. The cladding is the first barrier for the spent fuel pellets. An established method for characterising the cladding material is the ring compression test (RCT), in which a small, cylindrical sample of the cladding tube is subjected to a compressive load. Radial hydrides may precipitate in zirconium-based alloys (Zircaloy) under pre-storage drying and during slow cooling, which result in embrittlement of the cladding material and eventually a possible sudden failure of cladding integrity under additional mechanical loads. The focus of the presented research is on the development of appropriate nu-merical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. A modelling approach based on cohesive zones is ex-plained which is able to reproduce the propagation of cracks initiated at radial hydrides in the zir-conium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hy-drides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. Based on the developed fracture mechanics approach, not only the deformation behaviour but also the fail-ure behaviour of irradiated as well as unirradiated Zircaloy claddings with radial hydrides under RCT loading conditions can be adequately described.
Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. The cladding is the first barrier for the spent fuel pellets. An established method for characterising the cladding material is the ring compression test (RCT), in which a small, cylindrical sample of the cladding tube is subjected to a compressive load. Radial hydrides may precipitate in zirconium-based alloys (Zircaloy) under pre-storage drying and during slow cooling, which result in embrittlement of the cladding material and eventually a possible sudden failure of cladding integrity under additional mechanical loads. The focus of the presented research is on the development of appropriate nu-merical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. A modelling approach based on cohesive zones is ex-plained which is able to reproduce the propagation of cracks initiated at radial hydrides in the zir-conium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hy-drides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. Based on the developed fracture mechanics approach, not only the deformation behaviour but also the fail-ure behaviour of irradiated as well as unirradiated Zircaloy claddings with radial hydrides under RCT loading conditions can be adequately described.
The European Joint Programme on Radioactive Waste Management (EURAD) is working on Spent Fuel Characterization (SFC) in its work package (WP) 8. Inspired by the EURAD activities, the International Atomic Energy Agency (IAEA) established an international Coordinated Research Project (CRP) on SFC. The EURAD WP SFC participants are collaborating as a team on the IAEA CRP on SFC. The EURAD WP SFC project consists of four tasks. Task 3 investigates the behaviour of nuclear fuel and cladding after discharge. The aim of these activities is to understand and describe the evolution of the cladding-pellet system and its ageing under conditions of extended interim storage, transportation and emplacement in a final disposal system. At the Third Research Coordination Meeting on Spent Fuel Characterization, BAM as contributor to Task 3 reported on the activities and status of its research work.
The investigation of the long-term performance of sealing systems employed in containers for radioactive waste and spent nuclear fuel is one research focus area for division 3.4 “Safety of Storage Containers” at the Bundesanstalt für Materialforschung und -prüfung. Metallic seals are in use in interim storage casks for used fuel and high active waste. Their change in performance over time is of high importance for maintaining safe enclosure. Therefore, investigations on these systems were started at BAM to get a general understanding of the relevant processes. Our investigations comprise investigations on different parameters which influence the seal performance and the main part is focussed on the time and temperature dependent behaviour.
In this contribution an update on the performed tests and their respective results will be given in respect to the overview presented in 2020.
The understanding of the long-term behaviour of the sealing systems and the performance evaluation during interim storage and subsequent transportation are our goals.
A new hydrogen-based test rig is being developed for a feasibility study on the use of hydrogen as an energy source for thermal testing in accordance with the IAEA SSR-6 guidelines for transport packages containing radioactive materials.
The test rig will be capable of combusting hydrogen for a wide range of different burner geometries, mass flows and if necessary hydrogen blends. As this type of fire test according to the IAEA boundary conditions (SSR-6 & SSG-26) does not yet exist, a large number of preliminary investigations, safety assessments and calculations must be carried out in order to develop a viable concept for hydrogen fires.
A new hydrogen-based test rig is being developed for a feasibility study on the use of hydrogen as an energy source for thermal testing in accordance with the IAEA SSR-6 guidelines for transport packages containing radioactive materials.
The test rig will be capable of combusting hydrogen for a wide range of different burner geometries, mass flows and if necessary hydrogen blends. As this type of fire test according to the IAEA boundary conditions (SSR-6 & SSG-26) does not yet exist, a large number of preliminary investigations, safety assessments and calculations must be carried out in order to develop a viable concept for hydrogen fires.
Hydrogen Fire Testing
(2024)
In this presentation we present a new hydrogen-based test rig for an ongoing feasibility study of using hydrogen as an energy source for the thermal testing of transport packages containing radioactive materials. The test rig will be capable of combusting hydrogen for a wide range of different burner geometries, mass flows and if necessary hydrogen blends. As this type of fire test according to the IAEA boundary conditions does not yet exist, a large number of preliminary investigations, safety assessments and calculations must be carried out in order to develop a viable concept for hydrogen fires. In the first step of the feasibility study, the temperature, structure, and radiation of various hydrogen flames are surveyed. In future works, the results will make it possible to design burner frames that are suitable for fire reference tests in order to make comparisons with pool and propane fires used in assessment procedures today. In parallel comparative numerical simulations are conducted to model the thermal behaviour of hydrogen flames using the software package Ansys®. On the one hand, the numerical simulations support the experiments by providing an overview of numerous parameters and the measuring range; on the other hand, they will help with the design of the burner frame in future work. This paper gives an overview in the design and capabilities of the test rig. Furthermore, the results of the parameter studies show that burner geometry and mass flow provide a significant design margin for the thermal shape of the hydrogen flames. In addition, the results of the initial numerical calculations will be used to determine the necessary sensors, the positions, and their operating range. Only the optimal interaction allows a controlled system that permits user-defined hydrogen fires.
Introduction and Necessity of the Investigation
The IAEA regulations for the safe transport of radioactive material (IAEA SSR-6) define the safety requirements for different package types and consider different transport conditions. The accident conditions of transport specify different mechanical and thermal tests based on investigations of real accident scenarios.
Considering the rapid development of new boundary conditions of transport such as electric mobility and the use of hydrogen as energy source for trucks and other kind of vehicles, potential effects of battery and hydrogen fires in transport accidents should be investigated. The aim is to evaluate the existing test requirements developed and derived decades ago, whether they are covering the current transport situation.
This concept paper will briefly present the reasons for detailed investigations as bases for a coordinated research project under the roof of the IAEA.
Brittle Failure Limits of Spent Fuel Claddings Subjected to Long-Term Dry Interim Storage Conditions
(2024)
The mechanical properties of spent fuel claddings can be adversely affected under the conditions of long-term dry interim storage, so that the failure limits may be reached in case of mechanical loads during handling or transport after storage. Pre-storage drying and the early stage of interim storage can expose the cladding to higher temperatures and higher tensile hoop stresses than those associated with in-reactor operation and pool storage. During slow cooling of a cladding tube under internal pressure, radial hydrides may precipitate in zirconium-based cladding alloys. This can lead to embrittlement of the material and sudden failure of the cladding integrity under mechanical stress. In order to prevent brittle failure, numerical methods are being developed to predict the mechanical behaviour and identify limiting conditions. Experimental investigations, numerical analyses and evaluation methods are discussed.
An established experimental method for characterising cladding materials is the Ring Compression Test (RCT). Some test results on irradiated cladding tubes after operation in pressure water reactors are publicly available. However, it is helpful to carry out studies on unirradiated surrogate claddings with similar material properties to reduce the effort associated with irradiated samples in hot cells and to perform material tests with a wider range of parameters. On the basis of such experimental data, load-displacement curves have been numerically analysed for a selection of cladding materials.
Radial hydrides can cause a sample to break suddenly due to fracture even at low deformation. Noticeable load drops in the RCT are caused by unstable crack propagation through the radial hydride network. The failure mechanism is quasi-cleavage in the hydrides and micro-void nucleation, growth, and coalescence in the zirconium matrix, with ductile tearing patches connecting adjacent hydrides. The cohesive zone approach was used to simulate the failure process taking into account the radial hydride morphology.
The developed method can adequately describe both the deformation and failure behaviour of irradiated as well as unirradiated claddings of zirconium-based alloys with radial hydrides under RCT conditions. Limiting conditions can be expressed in terms of fracture energy and cohesive strength.
Brittle Failure Limits of Spent Fuel Claddings Subjected to Long-Term Dry Interim Storage Conditions
(2024)
The mechanical properties of spent fuel claddings can be adversely affected under the conditions of long-term dry interim storage, so that the failure limits may be reached in case of mechanical loads during handling or transport after storage. Pre-storage drying and the early stage of interim storage can expose the cladding to higher temperatures and higher tensile hoop stresses than those associated with in-reactor operation and pool storage. During slow cooling of a cladding tube under internal pressure, radial hydrides may precipitate in zirconium-based cladding alloys. This can lead to embrittlement of the material and sudden failure of the cladding integrity under mechanical stress. In order to prevent brittle failure, numerical methods are being developed to predict the mechanical behaviour and identify limiting conditions. Experimental investigations, numerical analyses and evaluation methods are discussed.
An established experimental method for characterising cladding materials is the Ring Compression Test (RCT). Some test results on irradiated cladding tubes after operation in pressure water reactors are publicly available. However, it is helpful to carry out studies on unirradiated surrogate claddings with similar material properties to reduce the effort associated with irradiated samples in hot cells and to perform material tests with a wider range of parameters. On the basis of such experimental data, load-displacement curves have been numerically analysed for a selection of cladding materials.
Radial hydrides can cause a sample to break suddenly due to fracture even at low deformation. Noticeable load drops in the RCT are caused by unstable crack propagation through the radial hydride network. The failure mechanism is quasi-cleavage in the hydrides and micro-void nucleation, growth, and coalescence in the zirconium matrix, with ductile tearing patches connecting adjacent hydrides. The cohesive zone approach was used to simulate the failure process taking into account the radial hydride morphology.
The developed method can adequately describe both the deformation and failure behaviour of irradiated as well as unirradiated claddings of zirconium-based alloys with radial hydrides under RCT conditions. Limiting conditions can be expressed in terms of fracture energy and cohesive strength.
Packages for the transport of spent nuclear fuel are designed to endure severe accidents. To obtain approval, these transport packages must adhere to the specification-based criteria of the international transport regulations SSR-6 of the International Atomic Energy Agency (IAEA). To ensure compliance with these requirements, specific mechanical and thermal tests need to be addressed with respect to the package type. Typically, SSR-6 prescribes a mechanical test followed by a thermal fire test as part of different testing scenarios. To approve the latter test of the sequence, BAM performs calorimeter tests in advance with so-called fire reference packages for characterizing the actual fire and its impact on the package to be tested. Packages are designed with different geometry sizes depending on their purpose. For previous tests, the implemented test setups in the fire test stand were sufficiently dimensioned and could cover all requirements in this respect. However, to cover additional testing needs in the future, BAM is expanding the test setup for the purpose of testing significantly larger packages.
In previous test setups one ring burner for propane surrounding the test specimen was sufficient. The limiting size in this configuration was the design height of the transport package to be tested. According to the thermal test of the IAEA-Regulations [1], a 30-minute fully engulfing 800°C pool fire or an equally severe fire, e.g., propane gas fire, must be applied to the transport package. Possible adjustments such as nozzle cross-section and propane mass flow can be adjusted to a certain extent. Further modifications, to cover significantly higher and larger packages all-around with a fully engulfing fire, must be accomplished with an additional, second burner ring. Both burner rings had the same dimensions and were mounted on top of each other at different heights to create a significantly larger volume of fire that completely engulfs the package including its impact limiter.
To meet the IAEA regulatory boundary conditions, the enhanced fire test stand with the second burner ring is tested with a large fire reference package and will then be used for real-size transport packages after all parameters are successfully met. This fire reference package represents the external geometry of a generic transport cask for radioactive material and is equipped with numerous temperature sensors to record temperature curves at the interior wall surfaces.
Packages for the transport of spent nuclear fuel are designed to endure severe accidents. To obtain approval, these transport packages must adhere to the specification-based criteria of the international transport regulations SSR-6 of the International Atomic Energy Agency (IAEA). To ensure compliance with these requirements, specific mechanical and thermal tests need to be addressed with respect to the package type. Typically, SSR-6 prescribes a mechanical test followed by a thermal fire test as part of different testing scenarios. To approve the latter test of the sequence, BAM performs calorimeter tests in advance with so-called fire reference packages for characterizing the actual fire and its impact on the package to be tested. Packages are designed with different geometry sizes depending on their purpose. For previous tests, the implemented test setups in the fire test stand were sufficiently dimensioned and could cover all requirements in this respect. However, to cover additional testing needs in the future, BAM is expanding the test setup for the purpose of testing significantly larger packages.
In previous test setups one ring burner for propane surrounding the test specimen was sufficient. The limiting size in this configuration was the design height of the transport package to be tested. According to the thermal test of the IAEA-Regulations [1], a 30-minute fully engulfing 800°C pool fire or an equally severe fire, e.g., propane gas fire, must be applied to the transport package. Possible adjustments such as nozzle cross-section and propane mass flow can be adjusted to a certain extent. Further modifications, to cover significantly higher and larger packages all-around with a fully engulfing fire, must be accomplished with an additional, second burner ring. Both burner rings had the same dimensions and were mounted on top of each other at different heights to create a significantly larger volume of fire that completely engulfs the package including its impact limiter.
To meet the IAEA regulatory boundary conditions, the enhanced fire test stand with the second burner ring is tested with a large fire reference package and will then be used for real-size transport packages after all parameters are successfully met. This fire reference package represents the external geometry of a generic transport cask for radioactive material and is equipped with numerous temperature sensors to record temperature curves at the interior wall surfaces.
eavy-weight packages for the safe transport of radioactive material are equippedwith impact limiters often built ofwood-filled steel sheet structures to fulfil the requirements of the International Atomic Energy Agency (IAEA) regulations. The requirements definemechanical tests followed by a thermal test, including criteria ensuring the package design’s ability to withstand severe accidents and provide a high level of technical safety. Impact limiters are a package component mainly designed for the packages to withstand severe mechanical accident scenarios. In drop tests the impact limiters absorb the kinetic energy during impact of the package. The package must then - with its pre-damaged impact limiters - endure a thermal test defined precisely in the IAEA regulations as a 30-min fully engulfing 800 °C-fire. After the fire, a wood-filled impact limiter may continue to release thermal energy from an ongoing combustion process, defining relevant package temperatures. The energy flow from a possible burning impact limiter to the package is important for the safety evaluation of transport packages. To investigate the combustion behaviour of densely packed layers of spruce wood, encapsulated in pre-damaged cylindrical metal enclosures, a test set-up has been realised. The set-up consists of a combustion chamber to perform these tests under defined boundary conditions. The temperature development of the test specimens will be observed fromoutside with a thermographic imager, with HD-Cameras, and the mass loss will be measured during the entire test. Airflow conditions in the combustion chamber are analysed using Computational Fluid Dynamics (CFD) calculations in OpenFOAM. The planned combustion test setup is described.
Heavy-weight packages for the safe transport of radioactive material are equippedwith impact limiters often built ofwood-filled steel sheet structures to fulfil the requirements of the International Atomic Energy Agency (IAEA) regulations. The requirements definemechanical tests followed by a thermal test, including criteria ensuring the package design’s ability to withstand severe accidents and provide a high level of technical safety.
Impact limiters are a package component mainly designed for the packages to withstand severe mechanical accident scenarios. In drop tests the impact limiters absorb the kinetic energy during impact of the package. The package must then - with its pre-damaged impact limiters - endure a thermal test defined precisely in the IAEA regulations as a 30-min fully engulfing 800 °C-fire. After the fire, a wood-filled impact limiter may continue to release thermal energy from an ongoing combustion process, defining relevant package temperatures. The energy flow from a possible burning impact limiter to the package is important for the safety evaluation of transport packages. To investigate the combustion behaviour of densely packed layers of spruce wood, encapsulated in pre-damaged cylindrical metal enclosures, a test set-up has been realised. The set-up consists of a combustion chamber to perform these tests under defined boundary conditions. The temperature development of the test specimens will be observed fromoutside with a thermographic imager, with HD-Cameras, and the mass loss will be measured during the entire test. Airflow conditions in the combustion chamber are analysed using Computational Fluid Dynamics (CFD) calculations in OpenFOAM. The planned combustion test setup is described.
The consideration of ageing mechanisms is with integration into the IAEA-requirements now obligatory for the design of transport packages. For packages intended to be used for shipment after storage the consideration of the effects of ageing mechanisms during storage in safety analyses and the implementation of corresponding instructions for operation and maintenance are required. Therefore, these packages have been maintained during storage in a manner that all requirements specified in the IAEA-requirements and in the applicable certificates of approval have been fulfilled.
BAM is the competent authority in Germany for evaluating the thermal and mechanical design of packages for the transport of radioactive materials. In this context, BAM also evaluates the aging mechanisms and aging effects occurring during the long-term storage period of such transport packages. BAM has developed a guideline for the implementation of ageing assessment and of the measures for ageing management into the approval procedure based on IAEA-requirements.
The goal of the presented paper is to introduce this guideline and the general approach for ageing management requirements and to describe the application to a specific package design. The type and amount of the ageing management not only depend on the use of the packaging, but also on the accessibility of the components that are considered in the ageing assessment. The different operating phases of a packaging are considered for the ageing assessment, such as loading, interim storage or transport.
The implementation of measures for ageing management is divided into three levels – systemic measures, package design related measures and documentation. The systemic measures are attributed to the general management system and define the whole activities for organization of ageing management like structure, responsibilities, documentation, reports and evaluation. The package design related measures are defined in an ageing management plan. These measures shall ensure that the anticipated changes of the package design under consideration of ageing effects still complies with the design approval specification. Therefore, an ageing surveillance program and, if necessary, a gap analysis program shall be developed. The ageing management documentation ensures the continuous documentation of the compliance of a specific package to the approved package design, comprising mainly records resulting from operation and surveillance.
The consideration of ageing mechanisms is with integration into the IAEA-requirements now obligatory for the design of transport packages. For packages intended to be used for shipment after storage the consideration of the effects of ageing mechanisms during storage in safety analyses and the implementation of corresponding instructions for operation and maintenance are required. Therefore, these packages have been maintained during storage in a manner that all requirements specified in the IAEA-requirements and in the applicable certificates of approval have been fulfilled.
BAM is the competent authority in Germany for evaluating the thermal and mechanical design of packages for the transport of radioactive materials. In this context, BAM also evaluates the aging mechanisms and aging effects occurring during the long-term storage period of such transport packages. BAM has developed a guideline for the implementation of ageing assessment and of the measures for ageing management into the approval procedure based on IAEA-requirements.
The goal of the presented paper is to introduce this guideline and the general approach for ageing management requirements and to describe the application to a specific package design. The type and amount of the ageing management not only depend on the use of the packaging, but also on the accessibility of the components that are considered in the ageing assessment. The different operating phases of a packaging are considered for the ageing assessment, such as loading, interim storage or transport.
The implementation of measures for ageing management is divided into three levels – systemic measures, package design related measures and documentation. The systemic measures are attributed to the general management system and define the whole activities for organization of ageing management like structure, responsibilities, documentation, reports and evaluation. The package design related measures are defined in an ageing management plan. These measures shall ensure that the anticipated changes of the package design under consideration of ageing effects still complies with the design approval specification. Therefore, an ageing surveillance program and, if necessary, a gap analysis program shall be developed. The ageing management documentation ensures the continuous documentation of the compliance of a specific package to the approved package design, comprising mainly records resulting from operation and surveillance.
In 2007 the license for the German Konrad repository for low and intermediate level radioactive waste was finally confirmed. Since then, the site is improved, prepared and equipped for the currently planned start of waste package emplacement in 2029. Bundesanstalt fuer Materialforschung und -pruefung is regularly contracted by the Bundesgesellschaft für Endlagerung as the responsible authority for waste product control, waste container design testing, and waste package acceptance. In this context BAM is mainly responsible for design testing of various container types including the evaluation of quality assurance measures for container manufacturing.
In addition to general requirements concerning container design, the casks have to withstand specific mechanical load scenarios. Drop tests from different heights under consideration of the most damaging drop orientation and a stacking test are two examples for necessary safety demonstrations.
If the containers are made from concrete the reinforcement has the function to absorb tensile forces the concrete is not able to withstand by its own. Because of manufacturing imperfections of cylindrical concrete containers manufactured already decades ago, the reinforcement cages are not always exactly, asymmetrically positioned when they were poured. This inspired BAM to perform various ABAQUS® finite-element (FE) simulations by using the example of a simplified cylindrical container design with generic dimensions. On the basis of the calculated tensile and compressive stress distributions suggestions are derived on how a cylindrical concrete container with an imperfectly placed reinforcement cage has to be oriented for a drop or stacking test to ensure the most damaging test scenario.
Packages for the transport of radioactive material are designed to en-dure severe accidents. Packages for the transportation of radioactive material must demonstrate that the package can withstand certain prescribed tests from the IAEA Regulations [1]. In addition to mechanical tests, a thermal test in form of a fire test must be carried out. As packages to be tested at BAM are signifi-cantly larger than previous package designs, BAM has expanded an existing fire test stand. A modular concept is chosen, which means that the arrangement of the burner nozzles can be adapted to the test specimen. The dimensions of the burner rings, the type, the orientation and the number of burner nozzles can be varied depending on the test specimen. In addition, various pumps can be used to set the corresponding mass flow. With the help of a calorimeter test, the fire test stand can be qualified for a specific size of packages regarding the boundary conditions of the IAEA Regulations [1]. Due to the typically wood filled impact limiters in German package designs, a fire test is necessary, as experiments have shown that possible openings that occurred during a mechanical test contributed to the igni-tion of the wood filled impact limiters within the prescribed 30 minutes of the IAEA Regulations [1]. From a series of experiments, two experiments are pre-sented to show the possibilities to obtain different temperatures and temperature rates in the test specimen. In addition to sensor data, the heat flux into the package is calculated to verify that the IAEA boundary conditions are satisfied. In addition to the temperature data, other data such as wind speed and wind direction are also recorded to explain subsequent effects in the measurement data in a comprehen-sible manner.
Acceptable limits for activity release from transport casks for high-level radioactive material specified in the IAEA regulations must be kept by the integrity of cask body and the cask sealing system. BAM as the German competent authority for mechanical, thermal and containment assessment of packages liable for approval verifies the activity release compliance with the regulatory limits. The specification of conservative package design leakage rates is one of the most important aspects in assessment.
Metal seals of the Helicoflex® Type are usually used to ensure the required package tightness for both, storage, and transport of the cask before and after storage. Due to the long-term use the seal behavior is influenced by temperature and time. The mechanical and thermal loadings associated with the routine, normal and accident conditions of transport specified in the regulations can have a significant effect on the leak tightness of the sealing system. Whereas the safety for application of new, non- aged Helicoflex® seals is verified sufficiently, there are still technical data gaps concerning the efficiency of aged Helicoflex® seals.
BAM performed experiments to learn more about the sealing efficiency of aged Helicoflex® seals with Aluminum and Silver outer jackets. The seals were compressed in test-flanges and for artificial ageing the complete flange systems were stored in an oven for several month at a high temperature. After this ageing procedure the flanges were opened completely, the seals were moved a little to vary the contact area, and the flanges were compressed again. During the compression and decompression tests after the aging, load-deformation characteristics of the seals, and leakage rates were measured.
With these tests a load situation was simulated, which can occur in the regulatory drop test of the cask: Under high impact loads the bolted lid can lift a little for a short moment, allowing a little movement of the seal, so that the contact area can change before compressing again.
Details about test conditions and first results will be presented in the poster.
Packages for the transport of radioactive material are designed to en-dure severe accidents. Packages for the transportation of radioactive material must demonstrate that the package can withstand certain prescribed tests from the IAEA Regulations [1]. In addition to mechanical tests, a thermal test in form of a fire test must be carried out. As packages to be tested at BAM are signifi-cantly larger than previous package designs, BAM has expanded an existing fire test stand. A modular concept is chosen, which means that the arrangement of the burner nozzles can be adapted to the test specimen. The dimensions of the burner rings, the type, the orientation and the number of burner nozzles can be varied depending on the test specimen. In addition, various pumps can be used to set the corresponding mass flow. With the help of a calorimeter test, the fire test stand can be qualified for a specific size of packages regarding the boundary conditions of the IAEA Regulations [1]. Due to the typically wood filled impact limiters in German package designs, a fire test is necessary, as experiments have shown that possible openings that occurred during a mechanical test contributed to the igni-tion of the wood filled impact limiters within the prescribed 30 minutes of the IAEA Regulations [1]. From a series of experiments, two experiments are pre-sented to show the possibilities to obtain different temperatures and temperature rates in the test specimen. In addition to sensor data, the heat flux into the package is calculated to verify that the IAEA boundary conditions are satisfied. In addition to the temperature data, other data such as wind speed and wind direction are also recorded to explain subsequent effects in the measurement data in a comprehen-sible manner.