- 2022 (56) (entfernen)
Dokumenttyp
- Vortrag (54)
- Posterpräsentation (2)
Referierte Publikation
- nein (56)
Schlagworte
- Korrosion (35)
- Corrosion (17)
- Potentialfeldmessung (9)
- Atmosphärische Korrosion (5)
- Geothermal (5)
- Spannungsrisskorrosion (5)
- Trinkwasser (5)
- KorroPad (4)
- Korrosionsprüfung (4)
- Hydrogen (3)
Organisationseinheit der BAM
- 7.6 Korrosion und Korrosionsschutz (56) (entfernen)
Eingeladener Vortrag
- nein (54)
Surface applied corrosion inhibitors (SACI) are widely used to mitigate corrosion process of steel reinforcement in concrete. But they remain controversial as to their effectiveness and the ability to compare materials from different manufacturers
and technologies. They are applied onto the surface of
hardened concrete and penetrate towards steel reinforcement. This paper discusses the corrosion inhibition performances of
dual-phase surface applied corrosion inhibitor and the efficiency of the corrosion inhibitor is assessed by selected testing procedures in BAM laboratories.
Due to the corrosion resistance of carbon steel, bridge constructions are currently protected against corrosion by applied coating systems. These coating systems need to be renewed after approximately 25 50 years. Galvanized constructions without any welding areas at the construction site could be prepared as grouted joints and can be used without any renewing for about 100 years.
Unter Passivität versteht man den Korrosionsschutz durch dünne, festhaftende Schichten aus Korrosionsprodukten. Für den schadensfreien Einsatz nichtrostender Stähle ergeben sich daraus zwei grundsätzliche Anforderungen.
Erstens muss sich die Passivschicht vollständig ausbilden können. Dabei sind die Oberflächenausführung, die mechanische Bearbeitung, die Elementverteilung, Ausscheidungen, die Wärmeeinbringung z.B. bei der schweißtechnischen Verarbeitung, Anlauffarben, sowie die chemische Nachbehandlung bzw. Konditionierung der Oberflächen von großer Bedeutung. Zweitens muss die Repassivierung von Defektstellen unter den Einsatzbedingungen möglich sein. Für das Repassivierungsvermögen sind die Legierungszusammensetzung, mögliche kritische Betriebszustände, prozessbedingte Besonderheiten, wie etwa Stagnationsbedingungen und Reinigungsprozesse von Bedeutung.
Durch das alkalische Porenwassermilieu ist Stahl im Beton vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich korrosionsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz
The presentation shows systematic investigations to describe the corrosion and corrosion product formation processes of pure zinc under the climatic conditions currently prevailing in the Federal Republic of Germany. The investigations in their entirety aim at questioning current and establishing new ways of looking at the formation of corrosion products of pure zinc under atmospheric corrosion conditions. Thus, they make a significant contribution in understanding corrosion protection by zinc and zinc coatings. In particular, the focus is placed on the initial stage of the corrosion product formation. A systematic investigation of this time range, which is characterized by very reactive corrosion products, is only made possible by using gel-type electrolytes. The short periods of time at the beginning of weathering is now measurable and their influence on the formation of corrosion products and the kinetics of layer formation describable. By combining the new electrochemical approach with gravimetric, microscopic and analytical methods, new insights could be gained both on a methodic and scientific level.
Prüfung von Spannstählen
(2022)
Ein Stand zum WIPANO-Projekt Spannstahlsicherheit wurde auf Anfrage in einer Gemeinschaftssitzung des AK "Eisen und Stahl" sowie des AK "Korrosionsuntersuchung und -überwachung" der Gesellschaft für Korrosionsschutz e.V. (GfKORR) präsentiert. Das Projekt hat die Verbesserung der produktspezifischen Prüfnorm ISO 15630-3 als Ziel. Vorgestellt wurden die Wahl der neu entwickelten Wasserstoffbeladung mit galvanostatischer kathodischer Polarisation und die Frage, ob die Prüfung an Lieferoberflächen sinnvoll ist.
Grundlagen der Korrosion
(2022)
Darstellung der Grundlagen der elektrochemischen Korrosion von metallenen Werkstoffen im Bauwesen. Dabei liegt das Hauptaugenmerk auf dem Zusammenhang zwischen Energieaufwand für den Herstellungsprozess und daraus resultierendem thermodynamisch instabilen Zustand und Korrosionsneigung. Der Einfluss der Deckschicht- Oxidschichtbildung wird ebenfalls behandelt.
Elektrochemische Messungen
(2022)
Elektrochemische Messungen könne, richtig angewandt, dazu dienen ein Korrosionssystem ausreichend gut zu beschreiben. Im Bauwesen, speziell bei Stahl in Beton, ist es jedoch ohne Kenntnis der korrodierenden Flächen oft nur möglich zwischen aktiv korrodierenden Bereichen und passiven, als Kathode wirksamen, Bereichen zu differenzieren.
Durch das alkalische Porenwassermilieu ist Stahl im Beton vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich korrosionsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz.
Erörterung des Messprotoklls
(2022)
Das für die Potentialfeldmessung in der neusten Ausgabe des Merkblattes B03 der DGZfP erarbeitete Messprotokoll berücksichtigt sowohl en Einsatz, von Stab-, Einrad- oder Vierradelektroden. In diesem Vortrag wird auf alle varianten des Gegenmessen von Bezugselektroden im Einsatz eingegangen, ebenso wie auf das Erfassen der notwendigen Randparameter.
Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz. Bei der Durchführung dieser Messung gibt es jedoch messtechnikspezifische Fehlerquellen und äußere Einflüsse aus dem zu untersuchenden Bauwerk die eine Interpretation der Messergebnisse signifikant beeinflussen können.
Wasserstoffinduzierte Spannungsrisskorrosion an hochfesten und hochempfindlichen Spannstählen führt an bestehenden Brückenbauwerken nach Jahren der Rissinitiierung zu Trag- und Standsicherheitsverlusten. Anhand des Beispiels der Brücke am Altstädter Bahnhof gibt es eine bauartbedingte Schadensinitiierung die über den gesamten Spannkanalquerschnitt zu Spannungsrisskorrosion führen kann.
In diesem Vortrag werden die Hintergründe, Ziele und ausgewählte Ergebnisse aus dem IGF-Vorhaben zu Korrosionsuntersuchungen an alternativen nichtrostenden Stählen vorgestellt. Weiterhin werden die Vorteile dieser Stähle hinsichtlich mechanisch -technologischer Eigenschaften sowie deren Kosten gegenüber den klassischen austenitischen nichtrostenden Stählen aufgezeigt.
Dieser Vortrag stellt die technologischen und industriellen Meilensteine bei der Etablierung von Lean Duplex Stählen im Bereich des Bauwesens vor. Ein weiterer Blick geht auf die weiteren Entwicklungen an der BAM hinsichtlich der Ausweitung der Kapazitäten und Standorte atmosphärischer Bewitterungsstände der BAM.
Diese Präsentation stellt die Ergebnisse des abgeschlossenen WIPANO Vorhabens "Spannstahlsicherheit" vor, welches von der BAM in Kooperation mit dem Stahlwerks Annahütte und der Max Aicher GmbH bearbeitet wird. Es werden die Projektziele näher beleuchtet und verschiedentliche Highlights der erzielten Untersuchungsergebnisse vorgestellt.
A conclusion on the WIPANO research project "Safety of Prestressing Steel" was presented in the final committee meeting at the end of the project. The project's exciting findings and recommendations for a new method were discussed with the audience of national and international stakeholders of the prestressing steel industry and representatives of inspection bodies and standardization.
The screening of coatings shows that the modification by adding individual pigment was not sufficient to protect carbon steel even during a short-term exposure, indicated by the discoloration after only seven days of exposure.
Electrochemical tests indicated that the coating cathodically protects carbon steel or slows down the corrosion reaction.
A long-term exposure test confirmed that the PANI/SiO2 modified coating successfully protects the carbon steel in the Sibayak artificial geothermal water at 150 °C for 6 months.
In dem Vortrag werden die Highlights und Ergebnisse des abgeschlossenen Wipano Forschungsprojekts "Spannstahlsicherheit" berichtet. In dem Vorhaben wurde das Projektziel ein neues Prüfverfahren für die Prüfung von Spannstählen auf Spannungsrisskorrosionsempfindlichkeit zu entwickeln erfolgreich abgeschossen. Weiterhin wurden neue Erkenntnisse zu den Ursachen der Ergebnisstreuung der bisherigen Prüfung gemäß ISO 15630-3 gewonnen. Das neue Prüfverfahren soll bei der nächsten Überarbeitungsrunde der ISO 15630-3 als Verfahren zunächst in den informativen Anhang aufgenommen werden.
Ein Umlaufkühler ist im Betrieb explodiert. Splitter des zerborstenen Gehäuses aus Kunststoff wurden mit dem Kühlwasser in die Umgebung geschleudert, am Betriebsort entstand Personenschaden. Bei Funktionsprüfungen am beschädigten Gerät traten unerwartet - aber reproduzierbar - Knalleffekte bei Berührung der Außenoberfläche der Kupfer-Kühlschlange auf. Ein möglicher Mechanismus konnte im Labor durch Synthese von Kupferazid auf Kupferproben und Auslösung vergleichbarer Knalleffekte nachgestellt werden. Damit ist die Plausibilität des beschriebenen Schadensereignisses mit diesem oder einem ähnlich reagierenden Stoff belegt. Ein eindeutiger Nachweis darüber, dass bei dem aufgetretenen Schadensfall dieselbe chemische Reaktion stattgefunden hat, war nicht möglich, da die Belag-Überreste aus dem explodierten Kühlgerät für eine Analyse nicht mehr in ausreichender Menge verfügbar gewesen sind.
Bei Betrachtungen zur Lebensdauer von Metallbauteilen im Bauwesen müssen Korrosions- und Runoff-Vorgänge an der Atmosphäre als verschiedene Reaktionen unterschieden werden. Korrosion ist der Prozess, der von elektrochemischen Reaktionen an der Grenzfläche Metall/Patina kontrolliert wird. Runoff dagegen wird durch chemische Reaktionen an der Grenzfläche Patina/Atmosphäre begünstigt. Mit zunehmender Bewitterungszeit nimmt die Korrosionsgeschwindigkeit stetig ab, während postuliert wird, dass die Geschwindigkeit des Runoffs über die gesamte Zeit konstant bleibt. Dieses Verhalten des Runoffs muss aber zunehmend bezweifelt werden. Die Gesamtmenge an abgezehrtem Metall beinhaltet zwei Bestandteile. Ein Teil wird in die Schicht aus Korrosionsprodukten eingebaut, der andere wird aufgrund von Niederschlägen aus der Patina gelöst. Aus diesem Grund ist die Menge an Zink-Runoff stark abhängig von den Eigenschaften der Korrosionsprodukt- bzw. Patinaschicht und nicht anhand der Zusammensetzung des Metalls abschätzbar. Vorhandene Modelle können die Menge an Runoff, und damit verbunden die Abzehrung einer Schicht aus Zink und Kupfer, sowie den resultierenden Eintrag von Schwermetallionen in die Umwelt nicht mehr darstellen und erklären. Um den Korrosionsschutz an Bauwerken zum einen dauerhaft unter Beachtung von Kostenaspekten und Ressourcenschonung und zum anderen unter ökologischen Gesichtspunkten auslegen zu können, müssen deshalb neue wissenschaftliche Grundlagen erarbeitet und die Mechanismen beschrieben werden.
Das BAM-Forschungsvorhaben RUNOFF widmet sich den Fragestellungen. Der Vortrag gibt einen kurzen Überblick zum Forschungsvorhaben.
Elektrochemische Messungen zur hygienischen Bewertung additiv gefertigter Bauteile werden diskutiert. Die Bewertung und Details des Werkstoffs werden beschrieben, Anwendungsbeispiele gezeigt.
Evaluation of corrosion resistance of metallic materials is essential to assure safe and reliable operation of geothermal sites. One need to be aware that corrosion is not a material's but a system property, determined by medium, material and construction aspects. Various corrosion types have to be evaluated. Conditions in laboratory shall reflect on-site reality. Depending on brine composition and temperature suitability of metallic materials can be ranked. Most important outcome of the research is that highly saline geothermal brines require high alloyed materials, for safe long-term operation.
Integrated Coating System for Corrosion Protection of Carbon Steel in Artificial Geothermal Brine
(2022)
Corrosive geothermal brines are a major challenge to geothermal power-plants. For cost reasons, plant designers prefer to use carbon and low alloyed steels, which are susceptible to uniform and localized corrosion when exposed to geothermal brines having acidic and saline properties. To solve such problem, coatings or inhibitors would be a protective solution as an alternative to the use of high alloyed materials.
This study investigated a coating system consisting of polyaniline/silicon dioxide based on resources locally available in Indonesia. Protection against corrosion of carbon steel was shown by long-term (28 day) exposure and electrochemical tests of coated carbon steels, performed in an artificial acidic and saline geothermal brine, comparable to the conditions encountered at a site in Indonesia.
Therefore, an integrated coating system is proposed for corrosion protection, combining the electrochemical functionality of polyaniline and the physical advantages of silica.
In order to obtain a statement on the corrosion resistance of stainless steel against pitting corrosion, a well-tested measuring arrangement is required. For this purpose, the so-called ECISS test can be used to determine the critical chloride content. This makes it possible to assess the corrosion resistance of various stainless steels that have different chromium contents.
Durch Fortführung der Untersuchungen aus einem Forschungsvorhaben wurden neun verschiedene Stahllegierungen unter maritimen Umgebungsbedingungen über zehn Jahre ausgelagert und deren Korrosionsverhalten untereinander verglichen und bewertet. Anhand der Ergebnisse der Auslagerungsprüfungen konnten Rückschlüsse auf die Einflüsse der Legierungszusammensetzung, der Oberfächenausführung und der Auslagerungszeit unter maritimen Auslagerungsbedingungen gewonnen werden. Die Proben der drei untersuchten Duplexwerkstoffe zeigten über den Auslagerungszeitraum von zehn Jahren sowohl mit als auch ohne Spaltgeometrie die beste Korrosionsbeständigkeit. Ebenso konnte der molybdänlegierte Ferrit 1.4521 eine vergleichbar gute Korrosonsbeständigkeit erzielen, wie die klassischen austenitischen Werkstoffe 1.4301 und 1.4404.
In the course of the deconstruction of the "Bridge of the 20th anniversary of the GDR" at the Altstädter Bahnhof in Brandenburg a. d. Havel, new information on the initiation of hydrogen-induced stress cracks was obtained. BAM was commissioned by the Brandenburg State Road Administration to participate in a corresponding joint project which is financed by the Federal Ministry for Digital and Transport. The added value of the new information gained in this project goes beyond the specific structure. It describes unexpected new damage patterns that can be transferred to other structures with concentrated tendons (tendon block method and Baur-Leonhardt method) and were previously unknown in this form. These should be made known to other developers to enable them to initiate any necessary actions.
Due to the high corrosivity that are present in road tunnel structures, cleaning and maintenance work on stainless steel components in the tunnels is carried out at regular intervals in the tunnels, which means that parts of the lanes or the whole tunnel have to be temporarily closed. To reduce these traffic disruptions and maintenance costs, it is important to reduce the work that is needed for cleaning and maintenance of stainless steel components in road tunnels. One possibility is the identification and utilization of better suited alternatives to the commonly used austenitic stainless steels AISI 316L and AISI 316Ti. Thus, a field exposure study was carried out in different road tunnels throughout Germany to qualify different duplex and lean duplex stainless steels for tunnel constructions.
The proposed scientific poster gives an overview of results after the first three years of exposure in three different road tunnels. Samples of different stainless steels were placed in different areas of the tunnel – at lane height and at the ceiling. Some samples were exposed under sheltered conditions. Pit depths were evaluated on the free surface and in crevice areas after each year of exposure. The investigations show that duplex stainless steels have a comparable or even better corrosion resistance than austenitic steels in tunnel atmospheres.
A series of field exposure tests according to ISO 9223 up to 9226 was carried out at different locations to determine the corrosivity and the corrosion progress of different test sites throughout northern and eastern Germany. Standard test specimens of steel, zinc, copper and aluminium were exposed to rural, city and marine atmosphere at test sites of the Bundesanstalt für Materialforschung und -prüfung (BAM). Test sites at city atmosphere comprised exposure on a rooftop, next to a highly frequented road and directly at a motorway. Exposure under marine conditions was carried out at Heligoland in the North Sea. The specimens were stored under sheltered and unsheltered conditions on each test site, respectively. Corrosion rates after the first year of field exposure were determined and used for the classification of the atmospheres and the test sites regarding the corrosivity category.
Results after the first year of exposure were presented at the EUROCORR 2018 in Cracow. The current presentation will present an update of results of the systematic study after five years of exposure. The corrosion progress and the mass loss of the standard metals steel, zinc, copper and aluminium will be presented and discussed with respect to the atmospheric conditions and the time of wetness at the test sites. In addition, the difference between sheltered and unsheltered conditions will be discussed.
Potential Mapping - What could we measure and what should we able to detect – guideline B03 of DGZfP
(2022)
“Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Non-Destructive Testing) is a recognized technique for the localization of corroding reinforcing steels.
Areas of corroding reinforcement steel can be located in a non-destructive manner by means of this procedure. Half‐cell potential measurements are used in order to detect chloride‐induced corrosion. However, it is not recommended in order to assess the risk of carbonation‐induced corrosion. For this purpose, determining the carbonation depth and the concrete cover appears more appropriate. The content of this specification exclusively refers to the application of mobile, local variable reference electrodes, which are only placed on the concrete surface while measuring. The technique distinguishes itself thereby from the range of corrosion monitoring systems with stationary installed reference electrodes and sensor systems, respectively, whereby it is possible to continuously track measurements within the area of the installed electrodes. However, these methods are not dealt with in this specification.”
Recently, non-destructive testing in civil engineering (NDT-CE), in particular of concrete components, has successfully mastered the leap from research to practice. Several methods have been established for field inspections to determine the concrete cover of reinforcement or to estimate the compressive strength as well as other parameters related to the concrete material. In addition, the application of non-destructive testing is indispensable, if information about the inner structure - such as the location of rebars and tendon ducts or the damage-related condition assessment to detect grouting defects, honeycombs, delamination, or corrosion - is required. Besides the selection of a suitable NDT method and an appropriate inspection system, the reliability of the results depends largely on the person who applies the non-destructive inspection technique and evaluates the inspection results. To ensure a high quality of non-destructive concrete evaluation as well as to keep the uncertainty caused by the inspection personnel to a minimum, structured, consistent, and regulated theoretical as well as practical training of inspection personnel is essential. To close this gap, the subcommittee of education and training (UA-A) within the committee for NDT-CE of the German Society for Non-Destructive Testing (DGZfP) has been reactivated in 2018 to establish uniform training standards for non-destructive concrete inspections in the long term. The subcommittee consists of scientists, practitioners, authorities, and clients. So far, the national standard DIN 4871 “Non-destructive testing - Qualification of NDT personnel in Civil Engineering (NDT-CE)” was developed. This standard considers the civil-industry-specifics, for example, that standards for NDT of concrete, as well as related product standards with a few exceptions, still do not exist at the moment. Within this presentation, the concept, the connection to ISO 9712 and other standards as well as an overview of the recently developed German standard DIN 4871 will be presented.
Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV. The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-anode) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkolleit.
Significant Cu-deposition and ‑precipitation only occurred in combination with carbon steel. High-alloyed materials prevent the disturbing Cu-agglomeration. Pb-deposition and ‑precipitation only occurred in combination with carbon steel. No negative Pb-effect could be observed in combination with high-alloyed steels. High alloyed corrosion resistant alloys are suitable and shall be chosen for future design of the piping system, either in massive or in cladded form, if formation of crevices with non-metallic materials can be excluded!
This talk reports the findings of the WIPANO "Knowledge and Technology Transfer via Patents and Standards" research project "Safety of Prestressing Steels," founded by the German Ministry of Economic Affairs and Climate Action (BMWK). A new test method for assessing the susceptibility of prestressing steels to hydrogen-induced stress corrosion cracking (SCC) is presented, which serves the demands of a lower scattering compared with the present standard. Moreover, the ability to differentiate between high susceptible and low susceptible prestressed wires is possible, modifying the method by hydrogen charging and surface preparation.
Brückenbauwerke, die im Spannblockverfahren hergestellt wurden, können bauartbedingt wasserstoffinduzierte Spannungsrisse über den gesamten Querschnitt eines Spannkanals aufweisen. Das Risswachstum kann infolge dynamischer Beanspruchung über die Nutzungsdauer fortschreiten und zu Spanndrahtbrüchen führen.
Corrosion testing in a laboratory container: Corrosion testing with artificial seawater and sediment
(2022)
Electricity generation by offshore wind turbine generators (WTG) is an important pillar of the energy transition. Corrosion processes on WTGs pose a particular challenge with regard to safe operation over longer periods of time due to the highly corrosive conditions in the offshore area. BAM is therefore conducting research to ensure a safe operation of the turbines over their intended service life to protect people and the environment.
In a joint research project, different corrosion-relevant areas of a WTG foundation structure were specifically simulated in test basins within a laboratory container. The aim of the work was, on the one hand, the gravimetric and electrochemical determination of corrosion rates in the different areas of an WTG that are relevant for cathodic corrosion protection (CCP): Underwater and sediment zone as well as the transition area between these two zones. Also, targeted tests were carried out under CCP. In addition, investigations regarding calcareous deposition during CCP were carried out on idealized specimens under laboratory conditions to better assess its influence on the protection process. The investigations were carried out in a laboratory container with different basins, which were filled with sand as sediment and artificial seawater according to ISO 15711and connected via a closed water circuit.
The poster at EURCORR 2022 provides an overview of the investigations and the most important results. It will be evaluated, if a simulation of offshore corrosion conditions is possible to a certain extent in an idealized system with artificial seawater and sediment.
Determination of the corrosion product layer resistance on zinc samples by using gel electrolytes
(2022)
Crash barriers, railings, lamp posts, waste glass containers - these are just a few of the many examples of galvanized surfaces. They withstand wind and weather for decades, which is possible thanks to a protective layer made of corrosion products. When designing the atmospheric durability of galvanized components, a linear corrosion loss is assumed. In the past 30 years, however, the surrounding atmosphere has changed a lot. Due to the restriction of sulfur exhaust air, acid rain completely disappeared in Europe and Germany, which has a direct influence on the type and protective effect of the corrosion products. Under the influence of current atmospheric conditions, zinc layers are significantly more resistant and no longer show any linear corrosion loss. The established test methods cannot correctly map this change in neither short-term nor long-term tests and thus provide incorrect results. In order to solve this problem, a new measurement method was developed at BAM that can assess the protective effect of the formed surface layers in a minimally invasive manner without damaging the sample and in short test times. For this new method, gel electrolytes are used and the so-called corrosion product layer resistance RL, which is made up of various surface resistances, is measured electrochemically. As a single measurement, the surface layer resistance can provide information about the existing corrosion protection, while time-dependent measurements assess the stability of the layer. Thus, it is possible again to evaluate the corrosion protection layer. Furthermore, this method can also be used for field measurements on real components.
Der Vortrag wurde im Rahmen der konstituierenden Sitzung des Arbeitskreises "Atmosphärische Korrosion" der GfKORR - Gesellschaft für Korrosionsschutz e.V. gehalten. Er stellt die zur Diskussion stehenden Fragestellungen und Herausforderungen im Bereich der atmosphärischen Korrosion zusammen, denen sich der neue Arbeitskreis widmen wird.
Commercially available carbon steels are suitable for compression and pipelines as long as moisture content and impurities are limited. (water 50 to 100 ppmv, SO2 and NO2 ca. 100 ppmv) Corrosion rates increase with increasing water content. (0.2 – 20 mm/a) Condensation of acids and therefore droplet formation is always possible, even at low water contents. A low SO2 content within the CO2-stream might be more important than a low water content. Cr13-steels showed a general susceptibility to shallow pitting and pitting. So, they seem to be not suitable for CCUS applications. Low alloyed steels showed better corrosion behavior (predictable uniform corrosion). For direct contact with saline aquifer fluids only high alloyed steels shall be used.
To reveal the corrosion resistance of casing steel/mortar interface in CO2 injection condition, sandwich samples were prepared and exposed up to 20 weeks in aquifer fluid under 10 MPa and 60 °C.
Cross section analysis revealed the crevice corrosion as main mechanism instead of pitting corrosion despite very high concentration of Cl in NGB.
EDS element line scan analysis of the 20-week-exposed metal/mortar coupon showed Chloride distribution, which still not reached the metal/mortar interface, explaining no pitting was observed.
It was confirmed that FeCO3 cannot protect the steel surface in CO2 saturated NGB.
To verify the protective possibility of passivation happened on casing steel/mortar interface, simulated pore solution was synthesized and used to passivate the steel for 42 days. OCP and EIS confirmed the formation of passive layer.
The 42 day passivated layer was broken during the first minute of exposure in CO2 saturated NGB.
However, due to high concentration of Ca2+, a new carbonate CaCO3 dense layer was formed, increased the corrosion resistance of steel surface.