Präsentation
Filtern
Dokumenttyp
- Vortrag (46)
- Posterpräsentation (21)
Referierte Publikation
- nein (67)
Schlagworte
- Nanoparticles (67) (entfernen)
Organisationseinheit der BAM
- 6 Materialchemie (47)
- 6.1 Oberflächen- und Dünnschichtanalyse (47)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 1.0 Abteilungsleitung und andere (1)
- 1.2 Biophotonik (1)
- 4 Material und Umwelt (1)
- 4.2 Material-Mikrobiom Wechselwirkungen (1)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 6.3 Strukturanalytik (1)
This contributions shows the first results of the ongoing interlaboratory comparisons under VAMAS/TWA 34 Nanoparticle populations related on the determination of pasrticle size distribution and relative concentration of nanoparticles and an example of an ILC running under VAMAS/TWA 41 Graphene and Related 2D Materials on the determination of the lateral diemsnions of graphene oxide flakes by Scanning Electron Microscopy. The link to related standardisation projects at ISO/TC Nanotechnologies are explained.
In the present paper we show an approach of measuring large numbers of nanoparticles in a single scan TKD. TiO2 anatase nanoparticles (NP) of bipyramidal shape were deposited on standard carbon grid used for TEM. The procedure used promoted formation of NP ‘monolayer’ islands with uniform distribution of NPs on the carbon surface which allowed mapping of large number of nanoparticles in the single island.
Collection of whole map covering ~2800 nanoparticles took nearly 20 minutes. Inverse pole figure color coded map indicates that the NPs are either lying on a {101} facet (within 10° range around perfect {101} parallel to the carbon surface orientation) on the carbon film or are lying on a {100} facet (within 10° range around the perfect {100} parallel to the carbon surface orientation). Very unlikely was the NP orientation standing on a {001} face. The NPs size distribution described as equivalent circle diameter (ECD) has been also evaluated and the mean NP ECD was 59 nm with standard deviation of 15 nm, i.e. in good agreement with electron microscopy or AFM results.
This study shows high potential of the technique for crystalline NPs analysis with respect to geometrical orientation of the particles on the substrate. With known orientation, the 3D dimensional characterisation of such non-spherical NPs becomes possible from 2D projection electron micrographs. Moreover, the NP size distribution can be easily extracted. Superior accuracies down to 1-2 nm are achievable. The approach is applicable also on thin lamellae extracted from particulate (or mesoporous) layers.
Following points are presented and discussed: i) nPSize as an EMPIR project on the nanoparticle size and shape distribution of (more) complex particles including sample preparation and machine learning approaches; ii) parallel development of ISO 21363 (PSSD by TEM), ISO 19749 (PSSD by SEM), ISO 22292 (3D TEM), ISO 52408 (NP Prep for AFM and EM), iii) VAMAS and pre-standardisation, TWA 34 „Nanoparticle Populations“ with two nPSize ILC projects P15 & P16 – results to be published and integrated in ISO 21363 (PSSD by TEM); iv) Remaining challenges: platelets, 2D materials (TiO2 and GR2M); v) Reference data sets as part of a complete Characterisation Workflow.
Die Bestimmung der Nanopartikelgrößen- und -formverteilung nach OECD TG 125 mit der Transmission and Scanning Electron Microscopy (SEM/TEM) wird punktuell vorgestellt:
- Generelles Messprinzip
- Beispiele
- Korrelative Mikroskopie
- Welchen Durchmesser misst die Methode?
- Welche Partikel kann diese Methode messen?
- Welche Informationen kann diese Methode liefern?
- Wo stößt die Methode an ihre Grenzen?
- Implementierung und Datenauswertung,
- Reporting.
Anschließend wurde eine Q&A-Session für die Imaging-Methoden organisiert.
The progress in the VAMAS Project #15" Measurement of particle size and shape distribution of bipyramidal titania including deposition from liquid suspension" within TWA 34 Nanoparticle Populations is presented with highlight of the following points:
- Determine and compare particle size and shape distribution by means of:
• electron microscopy (SEM, TEM, STEM-in-SEM)
• atomic force microscopy (AFM)
• small angle X-ray scattering (SAXS)
- Determine uncertainty induced by deposition protocol from liquid suspension with comparison to known values from a prior ILC with already deposited nanoparticles on TEM grids.
- Provide comparative validation of protocols for the techniques other than TEM.
The progress of the VAMAS Project 16 "Measurement of (relative) number concentration of bimodal silica nanoparticles including deposition from liquid suspension" in TWA 34 Nanoparticle Populations is presented. Follwowing points are discusssed:
- Validate the performance of imaging methods to measure the relative number concentration
• electron microscopy (SEM, TEM) and atomic force microscopy (AFM)
• two modes of bimodal (30 and 60 nm) silica nanoparticles
- Validate the performance of small angle X-ray scattering (SAXS) for the traceable measurement of the number concentration of the two modes.
Nanoparticle Populations
(2022)
Two new projects P15 Measurement of particle size and shape distribution of bipyramidal titania including deposition from liquid suspension and P16 Measurement of (relative) number concentration of bimodal silica nanoparticles including deposition from liquid suspension have been started at VAMAS/TWA 34 under the lead of BAM. First results are presented and discussed.
The main outcomes of the EMPIR project nPSize are presented and the suitability of the new capabilities, e.g. reference materials, sample preparation protocols, measurement procedures, and data analysis, to be standardized and implemented in accredited analytical laboratories is discussed. Complementation and/or filling gaps of published and ongoing standardisation projects on size, shape and number concentration measurements under ISO/TC 229/JWG 2 are offered.
The two VAMAS inter-laboratory comparisons resulted from the nSPize project and just started under TWA 34 Nanoparticle Populations (Projects #15 and #16) of bipyramidal TiO2 anatase and bimodal SiO2 nanoparticles are presented in detail.
Both essential aspects of the surface of solid matter, its morphology and chemistry, are studied traditionally at BAM starting in the 60’s with different cyclical research focus areas, mostly related either to applicative research or method development. In the recent years, the focus has shifted almost exclusively to the nano-analytics of advanced materials such as complex nanoparticles, (ultra)thin films/coatings, nanocomposites, 2D materials, energy materials, etc. This is also the reason why BAM has established recently the new Competence Center nano@BAM (www.bam.de/Navigation/DE/Themen/Material/Nanotechnologie/sichere-nanomaterialien.html) with the five sub-fields nanoCharacterisation, nanoMaterial, nanoSafety, nanoData and nanoTechnology. The link to the BAM central guidelines to the safety in technology and chemistry is given by the development of reference products such as reference measurement procedures, reference (nano)materials, and newly reference data sets. Thus, an internationally well-networked group in surface analysis has been established @BAM, with regular contributions to integral analytical characterization with metrological and standardization background.
Examples of newly developed methodical approaches will be given with an emphasis on correlative nano-analysis of morphology and chemistry of nanomaterials. Correlative imaging by STEM-in-SEM with high-resolution SEM and EDX, and further with AFM or the new technique TKD (Transmission Kikuchi Diffraction) will be explained on various examples of nanostructures, both as starting materials and embedded/functionalized nanoparticles in products. The unique analytical benefits of the Auger electron probe as a veritable nano-tool for surface chemistry will be highlighted. The panoply of advanced surface characterization methods @BAM is completed by discussing examples of hybrid analysis of the bulk of nanomaterials by X-ray Spectroscopy with the highest surface-sensitive methods X-ray Photoelectron Spectroscopy (XPS) and Time-of-Flight Secondary Ion Mass Spectrometry (ToF-SIMS). Particularly for the analysis of the surface chemistry of nanostructures, such as the completeness of the shells of core-shell nanoparticles or in-depth and lateral gradients of chemistry within mesoporous thin layers, the latter methods are inherent.
Other special developments like approaches for the quantitative determination of the roughness of particle surface by electron microscopy or for the quantitative determination of the porosity of thin mesoporous layers by electron probe microanalysis (EPMA) with SEM will be presented.
Water splitting using semiconductor photo-catalysts is considered a sustainable method to produce clean hydrogen fuel. Nevertheless, H2 photo-production efficiency remains still low, although extensive research works to understand better the mechanisms of the Hydrogen Evolution Reaction (HER) and the Oxygen Evolution Reaction (OER) are being carried out. In this respect, TiO2 is a key photoactive material, usually employed with a co-catalyst deposited onto the surface to enhance charge carriers’ separation and catalyze surface charge transfer reactions. The deposition of a co-catalyst on the TiO2 nanoparticle surface represents one successful way to enhance the activity of the photocatalyst through a modification of its surface and redox properties. In this context, high-resolution scanning electron microscopy (SEM) coupled with elemental analysis by energy-dispersive X-ray spectroscopy (EDS) is fundamental for studying and understanding the effect of the nanoparticle morphology on the functional properties of shape-controlled TiO2 crystals (bipyramides, platelets, and elongated particles). Different types of metal-semiconductor combinations, TiO2 shapes and dopant metals (Ag, Pt, Au, Rh, Pd) and metal concentrations are discussed.
Both essential aspects of the surface of solid matter, its morphology and chemistry, are studied traditionally at BAM starting in the 60’s with different cyclical research focus areas, mostly related either to applicative research or method development. In the recent years, the focus has shifted almost exclusively to the nano-analytics of advanced materials such as complex nanoparticles, (ultra)thin films/coatings, nanocomposites, 2D materials, energy materials, etc. This is also the reason why BAM has established recently the new Competence Center nano@BAM (www.bam.de/Navigation/DE/Themen/Material/Nanotechnologie/sichere-nanomaterialien.html) with the five sub-fields nanoCharacterisation, nanoMaterial, nanoSafety, nanoData and nanoTechnology. The link to the BAM central guidelines to the safety in technology and chemistry is given by the development of reference products such as reference measurement procedures, reference (nano)materials, and newly reference data sets. Thus, an internationally well-networked group in surface analysis has been established @BAM, with regular contributions to integral analytical characterization with metrological and standardization background.
Examples of newly developed methodical approaches will be given with an emphasis on correlative nano-analysis of morphology and chemistry of nanomaterials. Correlative imaging by STEM-in-SEM with high-resolution SEM and EDX, and further with AFM or the new technique TKD (Transmission Kikuchi Diffraction) will be explained on various examples of nanostructures, both as starting materials and embedded/functionalized nanoparticles in products. The unique analytical benefits of the Auger electron probe as a veritable nano-tool for surface chemistry will be highlighted. The panoply of advanced surface characterization methods @BAM is completed by discussing examples of hybrid analysis of the bulk of nanomaterials by X-ray Spectroscopy with the highest surface-sensitive methods X-ray Photoelectron Spectroscopy (XPS) and Time-of-Flight Secondary Ion Mass Spectrometry (ToF-SIMS). Particularly for the analysis of the surface chemistry of nanostructures, such as the completeness of the shells of core-shell nanoparticles or in-depth and lateral gradients of chemistry within mesoporous thin layers, the latter methods are inherent.
Other special developments like approaches for the quantitative determination of the roughness of particle surface by electron microscopy or for the quantitative determination of the porosity of thin mesoporous layers by electron probe microanalysis (EPMA) with SEM will be presented in conjunction with the corresponding advanced materials studied.
Current research projects, promising ideas, including ongoing (pre-)standardization activities in the field of the challenging nano/surface analysis will be touched systematically, with the open goal of identifying future bilateral cooperation possibilities between EMPA and BAM.
In order to assess new nanomaterials and nanoparticles for potential risks to health and the environment, they need to be well-characterised. The measurement of constituent nanoparticle size, shape, and size distribution are important factors for the risk evaluation process.
EMPIR project Improved traceability chain of nanoparticle size measurements (17NRM04, nPSize) is working to assess a range of traceable nanoparticle measurement approaches, including Electron Microscopy (SEM, TEM, STEM-in-SEM), Atomic Force Microscopy and Small Angle X-ray Scattering, and deliver improved calibration methods to users. For the techniques under investigation, physical models of their response to a range of nanoparticle types are developed. Validated reference materials are also used for inter-comparisons of measurement systems, with an evaluation of the associated measurement uncertainty. With project contributions to standards development work, manufacturers will be better placed to assess the human and environmental risks posed by nanomaterials across a whole range of products.
A case study on the TEM analysis of the size and shape distribution of TiO2 bipyramidal nanoparticles prepared on TEM grids was included in the recently published ISO standard ISO 21363. It was agreed to organize at a later stage a second inter-lab comparison with the nanoparticles distributed to the participants as a liquid suspension. Protocols for uniform nanoparticle deposition on suited supports developed and optimized within the EMPIR nPSize project are also prepared to be distributed. For this, we have chosen the VAMAS platform (www.vamas.org) which offers an excellent international infrastructure of laboratories with high competence in nanoparticle measurement. The VAMAS technical working area dedicated to nanoparticle measurement is TWA 34 ‘Nanoparticle populations’. For this type of nanoparticles, the size and shape distributions are the primary parameters to be reported. Due to the good deposition protocols developed, an automated image analysis is enabled (in contrast to the manual analysis of irregular TiO2 nanoparticles.
In parallel with the TiO2 nanoparticle exercise, two spherical SiO2 nanoparticle samples with bi-modal size distributions (nominal relative number concentrations of 1:1 and 10:1) are prepared for a second VAMAS inter-lab comparison. Here, the nanoparticle concentration is the primary parameter to be measured. For the imaging methods it is targeted to measure the relative nanoparticle concentrations of the two modes. For the absolute nanoparticle concentration to be measured by imaging methods it is necessary to control the volume of the liquid suspension deposited on the substrate and to obtain such a homogeneous nanoparticle deposition on the substrate which allows to count (or extrapolate) all the deposited particles.
The progress in activities on Microbeam Analysis under VAMAS/TWA 37 is reviewed. Particularly the liaison with the new projects within the ISO technical committee TC 202 is presented and discussed with respect to the possibility of identifying and launching related VAMAS projects. Need of more promotion for the engagement of more participants from industry and academia at national, European and international level is highlighted. Also, the competition with the other technical working areas (on 'nano' or materials-related) is critically discussed. Further, a short overview of the VAMAS areas of activities is given where Germany is involved.
By far most of the current nanoparticle (NP) research is dealing with (quasi-) spherical and/or monodisperse particles. However, many NPs used in industrial applications are rather aspherical and polydisperse. This inhomogeneity considerably hampers their characterization and, particularly, the accurate determination of the nanoparticle size. In order to overcome this problem and to promote the availability of standardized size measurement methods, it is crucial to develop and establish (candidate) reference materials with inhomogeneous size (distribution), aspherical shape as well as agglomerated or aggregated particles.
Therefore, a new set of NPs including Au-, SiO2 , and TiO2-particles is investigated. The range of properties comprises polydisperse spherical, bimodal spherical, rod-like, acicular, bipyramidal, sheet-like as well as cubic NPs. With respect to a good traceability of the measurements, size and size distributions of the candidate reference materials are determined using microscopic methods like scanning electron microscopy (SEM), transmission electron microscopy (TEM), scanning electron microscopy in transmission mode (STEM-in-SEM), atomic force microscopy (AFM) as well as small angle X-ray scattering (SAXS) as an ensemble technique. The development of protocols for sample preparation is of particular importance to obtain a homogeneous dispersion of the NPs on a substrate. Further, approaches for signal modelling for all the methods above are being developed. The initiation of two VAMAS (www.vamas.org/twa34/index.html) inter-laboratory comparisons on bipyramidal titania and bimodal silica with different modal concentration ratios will be also highlighted.
It sounds like being a simple analytical task, it is definitely not. The way toward accurate measurement of the size distribution of nanoparticles (NPs) with complex shape, having a broad size polydispersity, with inhomogeneous chemistry, and with a high degree of agglomeration/aggregation is very challenging for all available analytical methods. Particularly for the NPs with complex shape, the access to the smallest dimension (as e.g. required for regulatory purposes) can be enabled only by using imaging techniques with spatial resolution at the nanoscale. Moreover, the full 3D-chacterisation of the NP shape can be provided either by advanced characterization techniques like 3D-TEM tomography or by correlative analysis, i. e. synergetic/complementary measurement of the same field-of-view of the sample with different probes. Examples of the latter type of analysis are: i) electron microscopy for the lateral dimensions and AFM for the height of the NPs, ii) SEM with STEM-in-SEM (also called T-SEM), iii) Electron Microscopy with TKD (Transmission Kikuchi Diffraction) for determination of the geometrical orientation of crystalline NPs, iv) Raman and SEM for e.g. thickness of graphen flakes, or v) Electron Microscopy for descriptive NP shape and SAXS for the NP concentration, the latter as a NP property able to be measured with higher and higher accuracy. For all these types of measurement, reference NPs are necessary for the validation of the measured size. Particularly non-spherical reference NPs are still missing. Examples of such new reference NPs as characterized by the correlative analyses enumerated above will be presented in detail in the contribution.
The main outcomes of the EMPIR project nPSize are presented and the suitability of the new capabilities (e.g. reference materials, measurement procedures, inter-laboratory comparisons) as pertinent contributions to normative projects within CEN/TC 352 Nanotechnologies are discussed. E.g. the first technical report of nPSize on full algorithm sequences for nanoparticle detection and size measurement as developed on both a physical basis (SEM, TSEM, AFM and SAXS) and by machine learning is put at disposal.
The present study addresses the capability of measurement of relative particle number concentration by scanning electron microscopy for model bimodal silica and gold samples prepared in the frame of the European research project “nPSize - Improved traceability chain of nanoparticle size measurements” as candidate reference nanoparticles.
In this paper one refined approach is applied to determine the exact orientation of bipyramidal TiO2 nanoparticles prepared with good dispersion as almost isolated particles on a carbon TEM grid. The advantages of the recently developed high-throughput Transmission Kikuchi Diffraction (TKD) are used to identify quickly and reliably the geometrical orientation of the crystalline TiO2 nanoparticle bipyramids (anatase) on a statistically relevant number of particles.
In this contribution different ways are explored with the aim to generate suitable training data for ‘non-ideal’ samples using various approaches, e.g., computer-generated images or unsupervised learning algorithms such as generative adversarial networks (GANs). We used these data to train simple CNNs to produce segmentation masks of SEM images and tested the trained networks on real SEM images of complex nanoparticle samples. The novel use of CNN for the automated analysis of the size of nanoparticles of complex shape and with a high degree of agglomeration has proved to be a promising tool for the evaluation of particle size distribution on a large number of constituent particles. Further development and validation of the preliminary model, respectively larger training and validation data sets are necessary.
Based on practical examples of analysis with Electron Microscopy and Energy-Dispersive X-ray Spectroscopy, the minimum information requirements for reliable and reproducible nanomaterial characterization data such as particle size and shape distribution and elemental analysis are presented and discussed.
This presentation is structured in two parts: i) Hybrid metrology by combining SEM with AFM (N. Feltin) and ii) hybridization and corelative microscopy by SEM, STEM-in-SEM, TEM, EDS, Auger Electron Microscopy, TKD and more (D. Hodoroaba).
The first part is focused on the metrological part of the hybrid measurement SEM-AFM, the second part offers some further possibilities of correlative microscopy of nanoparticles based on practical examples.
The main outcomes of the EMPIR project nPSize are presented and the suitability of the new capabilities (e.g. reference materials, measurement procedures, VAMAS inter-laboratory comparisons) to be standardized and implemented in accredited analytical laboratories is discussed. Complementation and/or filling gaps of published and ongoing standardisation projects on size, shape and number concentration measurements under ISO/TC 229/JWG 2 are offered.
The 44th Meeting of the Versailles Project on Advanced Materials and Standards (VAMAS) Steering Committee has just taken place at NIST in Boulder (CO, USA). BAM participates with significant contributions in Technical Working Areas on nanoparticle and surface chemistry characterization, but also has positioned itself to new global material challenges and trends in the developement of advanced materials and their characterization, such as thermal properties, self-healing materials, and micro- and nanoplastic.
New reference material candidates for traceable size measurement of nonspherical nanoparticles
(2019)
Size measurement of nanoparticles (NP) becomes a challenging analytical problem when non-spherical shapes must be traceably measured. However, most industrial NPs have irregular shapes and broad size distribution making it often more complex to follow European regulatory to identify a material as a nanomaterial according to which accurate measurement of the smallest dimension and its size Distribution is necessary.
The European research project nPSize - Improved traceability chain of nanoparticle size measurements aims to fill this gap by developing potential non-spherical reference nanoparticles, measurement procedures and physical modelling to improve the traceability chain, comparability and compatibility for NP size measurements between different methods. Therefore, new model NP with well-controlled shape has been synthesized and are supposed to be systematically characterized using the traceable methods scanning/transmission electron microscopy, atomic force microscopy and small angle X-ray scattering.
Following NP candidates are under investigation with respect to their homogeneity and stability: (i) titania nanoplatelets (10-15 nm thickness x 50-100 nm lateral), (ii) titania bipyramides (~60 nm length x 40 nm width), (iii) titania acicular particles (100 nm length x 15-20 nm width; aspect ratio 5.5/6), (iv) gold nanorods (~10 nm width x 30 nm length), and (v) gold nanocubes (~55 nm x 55 nm x 55 nm). In addition, sample preparation procedures as well as measurement analysis procedures with evaluation of appropriate measurands and descriptors for each material class and method are being developed to support standardization. To underpin the traceability of the size measurement of nonspherical NP, physical modelling of the signals in e.g. electron microscopy techniques will be used and in combination, the implementation of machine learning is aimed to facilitate measurement Analysis procedures, especially regarding the accurate thresholding/segmentation of the NPs.
New reference material candidates for traceable size measurement of non-spherical nanoparticles
(2019)
New model nanoparticles with well-controlled shape were synthesized within the EMPIR project nPSize - Improved traceability chain of nanoparticle size measurements. Their systematic characterization takes place by the traceable methods scanning/transmission electron microscopy, atomic force microscopy and small angle X-ray scattering. Following reference nanoparticle candidates are under investigation with respect to their homogeneity and stability: titania nanoplatelets (10-15 nm x 50-100 nm), titania bipyramides (~60 nm x 40 nm), titania acicular particles (100 nm x 15-20 nm; aspect ratio 5.5/6), gold nanorods (~10 nm x 30 nm), and gold nanocubes (~55 nm x 55 nm x 55 nm).
Challenges in Traceable Size Measurement of Non-Spherical, Non-Monodisperse Nanoparticles - nPSize
(2019)
Size measurement of nanoparticles (NP) becomes a challenging analytical problem when non-spherical shapes must be traceably measured. However, most industrial NPs have irregular shapes and broad size distribution making it often more complex to follow European regulatory to identify a material as a nanomaterial according to which accurate measurement of the smallest dimension and its size Distribution is necessary.
The European research project nPSize - Improved traceability chain of nanoparticle size measurements aims to fill this gap by developing potential non-spherical reference nanoparticles, measurement procedures and physical modelling to improve the traceability chain, comparability and compatibility for NP size measurements between different methods. Therefore, new model NP with well-controlled shape has been synthesized and are supposed to be systematically characterized using the traceable methods scanning/transmission electron microscopy, atomic force microscopy and small angle X-ray scattering.
Following NP candidates are under investigation with respect to their homogeneity and stability: (i) titania nanoplatelets (10-15 nm thickness x 50-100 nm lateral), (ii) titania bipyramides (~60 nm length x 40 nm width), (iii) titania acicular particles (100 nm length x 15-20 nm width; aspect ratio 5.5/6), (iv) gold nanorods (~10 nm width x 30 nm length), and (v) gold nanocubes (~55 nm x 55 nm x 55 nm). In addition, sample preparation procedures as well as measurement analysis procedures with evaluation of appropriate measurands and descriptors for each material class and method are being developed to support standardization. To underpin the traceability of the size measurement of nonspherical NP, physical modelling of the signals in e.g. electron microscopy techniques will be used and in combination, the implementation of machine learning is aimed to facilitate measurement Analysis procedures, especially regarding the accurate thresholding/segmentation of the NPs.zeige mehr
Measurement of nanoparticle size (distribution) becomes a challenging analytical problem when non-spherical nanoparticles must be accurately measured. Most industrial nanoparticles have not only non-spherical shapes but also possess polydisperse size distributions, and due to their agglomeration/aggregation state are difficult (or even impossible) to be addressed individually. Moreover, driven by regulatory purposes related to the identification of a material as a nanomaterial, the accurate measurement of the smallest dimension of a (nano)particulate material makes the analysis even more complex.
In the first phase of the EU Project nPSize - Improved traceability chain of nanoparticle size measurements (https://www.bam.de/Content/DE/Projekte/laufend/nPSize/npsize.html), the efforts are focused on synthesis of nanoparticles of well-defined, non-spherical shape. Following candidates of reference materials (CRM) with certifiable particle size (distribution) are under characterization with respect to their homogeneity and stability: (i) titania nanoplatelets (10-15 nm thickness x 50-60 nm lateral), (ii) titania bipyramides (~60 nm length x 40 nm width), (iii) titania acicular particles (100 nm length x 15-20 nm width; aspect ratio 5.5/6), (iv) gold nanorods (~10 nm width x 30 nm length), and (v) gold nanocubes (~55 nm x 55 nm x 55 nm).
Das EMPIR-Förderprogramm wird kurz erläutert und laufende Projekte aus der Nanotechnologie werden vorgestellt. Der Schwerpunkt liegt auf Standardisierungsprojekten, die gemeinsam mit ISO/TC 229 'Nanotechnologies' und CEN/TC 352 'Nanotechnologies' zu neuen Normen führen sollten. Als Beispiel für laufende Nanotechnologie-Projekte mit Koordination aus Deutschland werden MagNaStand (PTB) und nPSize (BAM) gegeben.
An overview of the activities in the field of surface and microbeam analysis at BAM-6.1 is given with focus on physico-chemical characterization at the nanoscale. Ideas of potential joint activities are presented: structural and chemical analysis of graphene, deposition techniques for nanoparticles, EBSD on steel for a broader range of methods, instruments and types of steel, soft X-ray Analysis of low-Z materials, analysis of mesoporous thin films, etc.
Controlled deposition of nanoparticles by electrospray for improved analysis by imaging techniques
(2018)
Of many experimental techniques for measuring particle sizes and size distributions, electron microscopy (EM) is still considered as the gold standard, especially in the nano range (1–100 nm).
Furthermore, high-resolution X-ray spectroscopy (EDX) in conjunction with EM can be applied to individual NPs. Preparation of an EM sample for generic particulate materials is a difficult task. Usually the particles in a suspension are deposited on a support. However, this procedure includes the drying of larger solvent amounts on the substrate itself, and this can affect the spatial distribution of the deposited particles. One possibility to overcome this is the use of an electrospray system, where the suspension of particles is sprayed onto the substrate in charged droplets that are so small that they either dry off on the substrate immediately without affecting the position of particles, or even already during their flight time to the substrate. Additionally, the charging of particles minimizes agglomeration and aggregation, maximizing the collection of the EM grids. The prototype of an electrospray deposition system from RAMEM under its trademark IONER (www.ioner.eu) was tested. Electrospray is theoretically described since a long time, but no dedicated commercial instruments are available for the preparation of TEM grids yet, apart from electrostatic deposition of aerosols.2 Several materials have been sprayed onto TEM grids and the resulting particle distributions were evaluated. Operation parameters such as the sample flow-rate, capillary – substrate distance, electric field strength and sampling period length have been optimized. It was found that the particles deposited by electrospray generally show a much more homogeneous spatial distribution on the substrate and a substantial increase of the number of single particles (suited to automatic analysis).
The EC Recommendation on the definition of nanomaterial1, based solely on size of the constituent particles, foresees development of harmonised measurement methods ensuring ‘consistent results across materials and over time’. The EU/FP7 large research project NanoDefine (http://www.nanodefine.eu) has been exclusively dedicated to support the implementation of this EC Recommendation for the European Union’s legislation. For the first time, measurement techniques able to determine the size of nanoparticles have been evaluated systematically on a well-defined set of quality control materials (spherical, monodisperse) as well as industrial materials of complex shapes and considerable polydispersity. Particularly based on the analytical performance of the measurement techniques as tested on the challenging real-world particulate materials, it was possible to formulate recommendations for use of a new tiered approach consisting of screening and confirmatory techniques. Thus, a consistent framework of guidance for nanomaterial identification according to the EC Definition has been issued in form of the NanoDefiner e-tool (https://labs.inf.fh-dortmund.de/NanoDefiner), with a transparent decision flow scheme and an extensive user manual. Selected examples of analysis and classification as nano-/non-nanomaterials will be given, highlighting the limits of applicability of the available measurement techniques in dependence on sample properties. On some recent relevant developments in sample preparation – as a crucial part for an accurate analysis - will be also reported.
Controlled electrospray deposition of nanoparticles for improved analysis by electron microscopy
(2018)
Of many experimental techniques for measuring particle sizes and size distributions, electron microscopy (EM) is considered as the gold standard, especially in the nano range (1–100 nm). Furthermore, high-resolution X-ray spectroscopy (EDX) in conjunction with EM can be applied to individual NPs. Preparation of an EM sample for generic particulate materials is a difficult task. Usually, the particles in a suspension are deposited on a support. However, this procedure includes the drying of larger solvent amounts on the substrate itself, and this can affect the spatial distribution of the deposited particles. One possibility to overcome this is the use of an electrospray system, where the suspension of particles is sprayed onto the substrate in charged droplets that are so small that they either dry off on the substrate immediately without affecting the position of particles, or even already during their flight time to the substrate. Additionally, the charging of particles minimizes agglomeration and aggregation, maximizing the collection of the EM grids. The prototype of an electrospray deposition system from RAMEM under its trademark IONER (www.ioner.eu) was tested.
Electrospray is theoretically described since a long time, but no dedicated commercial instruments are available for the preparation of TEM grids yet, apart from electrostatic deposition of aerosols. Several materials have been sprayed onto TEM grids and the resulting particle distributions were evaluated. Operation parameters such as the sample flow-rate, capillary – substrate distance, electric field strength and sampling period length have been optimized. It was found that the particles deposited by electrospray generally show a much more homogeneous spatial distribution on the substrate and a substantial increase of the number of single particles (suited to automatic analysis).
The project has received funding from the European Union’s Seventh Programme for research, technological development and demonstration under grant agreement No 604347.
Coming as response to the needs expressed by The European Commission mandating CEN, CENELEC and ETSI to develop European standards for methods that can characterize reliably manufactured nanomaterials, a new European metrology research project ‘nPSize - Improved traceability chain of nanoparticle size measurements’ has received funding for the next three years. The project will develop methods, reference materials and modelling to improve the traceability chain, comparability and compatibility for nanoparticle size measurements to support standardization.
nPSize has selected only those nanoparticle sizing techniques which are able to provide traceable results: electron microscopy (SEM, TSEM and TEM), AFM and SAXS. Metrologists from national metrological or designated institutes (PTB, LNE, LGC, VSL, SMD and BAM) will work together with scientists with know-how in development of new nano reference nanoparticles (CEA, University of Turin, LGC, BAM) and with experts in advanced data processing, e.g. by machine learning (POLLEN). With the support of DIN, the project outcomes will be channelized to standardization bodies such as ISO/TC 229 ‘Nanotechnologies’/JWG 2 ‘Nanoparticle Measurement and Characterization’ (SEM, TSEM and TEM), CEN/TC 352 ‘Nanotechnologies’ (SEM, TSEM and TEM), ISO/TC 201/SC 9 (AFM), ISO/TC 24/SC 4 (SAXS).
Three technical work packages will ensure input for impact to standardization community, nanoparticle manufacturers, instrument manufacturers, and (accredited) service laboratories:
- WP1 Performance and traceability of characterization methods
- WP2 Reference materials - Preparation and Characterization
- WP3 Modelling and development of measurement procedures
Well-defined non-spherical nanoparticles shapes such as cubes, platelets, bipyramids, rods/acicular will be developed, with mono- and polydisperse size distribution, as well as with accurate particle number concentration (by SAXS and isotopically enrichment for ICP-MS).
Physical modelling of the signal for TSEM, SEM, 3D-AFM and SAXS will be used to feed machine learning modeling from a-priori measurement data. Further, data fusion will be developed for hybrid sizing techniques: SEM with TSEM/TEM, SEM/TSEM with AFM, SEM/TSEM with SAXS with the final aim of improving the true shape and size of non-spherical nanoparticles by a better estimation of the measurement uncertainties.
In the second half-time of the project dedicated workshops (focused on method improvement and reference materials development) will be organized to disseminate the gained knowledge to end-users. Further, a data library with relevant tagged measurement data is planned to be organized and made publicly available. Inter-laboratory comparisons based on the newly developed multi-modal nano reference materials will be organized preferably within VAMAS/TWA 34 ‘Nanoparticle populations’.
Extraction of true, 3D shape (and size) of non-spherical nanoparticles (NPs) is associated with errors by conventional 2D electron microscopy using projection images. Significant efforts within the ISO technical committee TC 229 ‘Nanotechnologies’ are aimed at establishing accurate TEM and SEM measurement of NP size and shape as robust, standard procedures. Study groups have been organizing inter-laboratory comparisons on well-selected NP systems according to the market needs, such as aggregated titania nano-powder for which size and shape distribution of primary crystallites of irregular shape must be measured accurately. To be noticed is e. g. the fact that the measurement procedure allows only manual selection of the particles clearly distinguishable for analysis as well as manual definition of the contour of the imaged NPs.
An inter-laboratory exercise on titania NPs (pure anatase, grown by hydrothermal synthesis) of well-defined non-spherical shape, i.e. bipyramidal has been recently started within ISO/TC 229 under similar conditions as for the irregular shaped titania. Overlapped particles were allowed to be considered, as long as they are clearly distinguishable. One decisive NP selection criterion was to analyze only those NPs with a roundness value below 0.7, i.e. the NPs laying on the support foil and, hence, with projection areas clearly deviating from perfect circles (R=1). The overall evaluation (for 15 labs) of the size descriptors (area, Feret, minFeret, perimeter) and shape descriptors (aspect ratio, roundness, compactness, extent) by analysis of variance is just to be finished and included in ISO/WD 21363 Nanotechnologies -- Protocol for particle size distribution by transmission electron microscopy.
The EC Recommendation on the definition of nanomaterial, based solely on size of the constituent particles, foresees development of harmonised measurement methods ensuring ‘consistent results across materials and over time’. The EU/FP7 research project NanoDefine has been exclusively dedicated to support the implementation of this EC Recommendation for the European Union’s legislation. For the first time, measurement techniques able to determine the size of nanoparticles have been evaluated systematically on a well-defined set of quality control materials (spherical, monodisperse) as well as industrial materials of complex shapes and considerable polydispersity.
Particularly based on the analytical performance of the measurement techniques as tested on the challenging real-world particulate materials, it was possible to formulate recommendations for use of a new tiered approach consisting of screening and confirmatory techniques. Thus, a consistent framework of guidance for nanomaterial identification according to the EC Definition has been issued in form of the NanoDefiner e-tool, with a transparent decision flow scheme and an extensive user manual. Selected examples of analysis and classification as nano-/non-nanomaterials will be given, highlighting the limits of applicability of the available measurement techniques in dependence on sample properties. On some recent relevant developments in sample preparation – as a crucial part for an accurate analysis - will be also reported. Further, ISO/TC 229 ‘Nanotechnologies’ activities aiming at establishing accurate TEM and SEM measurement of NP size and shape as robust, traceable, standard procedures are highlighted. With participation of BAM, study groups have been organizing inter-laboratory comparisons on well-selected NP systems according to the market needs, such as aggregated or shape-controlled titania nano-powder for which size and shape distribution of primary particles must be measured accurately.
Many techniques are available for measuring particle size distribution. For ideal materials (spherical particles, well dispersed) it is possible to evaluate the Performance of These methods. The performance of the analytical instrumentation for the purpose of classifying materials according to EC Definition is unknown. In this work the performance of commercially available particle sizing techniques on representative NanoDefine set of real-world testing materials (RTM) and quality control materials (QCM) for the implementation of the Definition is evaluated.
The overall objective of project Improved traceability chain of nanoparticle size measurements is to improve the traceability chain for nanoparticle size measurements. The main impact will be achieved by manifold contributions to standard documents for CEN/TC 352 “Nanotechnologies”, which directly addresses the research needs of CEN, CENELEC and ETSI mandated by EC to develop standards for methods and reference materials to accurately measure the size and size distribution of nanoparticles. This will take place in collaboration with ISO/TC229 ‘Nanotechnologies’, ISO/TC24/SC4 ‘Particle characterization’ and ISO/TC201 ‘Surface analysis’/ SC9 ‘Scanning probe microscopy’.
We discuss the role of the volume specific surface area (VSSA) as determined from the specific surface area measured by the (extended) Brunauer-Emmett-Teller (BET) technique, in the identification process of powdered nano- and non-nanomaterials in line with the EU definition of nanomaterial. Results obtained in the NanoDefine project demonstrate that under appropriate conditions, VSSA can be used as proxy to the number-based particle size distribution. The extent of agreement between nano/non-nano classification by electron microscopy (EM) and classification by VSSA is investigated systematically on a large set of diverse particulate substances, representing most of the cases expected in regulatory practice. Thus, parameters such as particle shape, size polydispersity/multi-modality, and particle (inner or coating) porosity are evaluated. Based on these results, we derive a tiered screening strategy for powders, involving the use of VSSA for the purpose of implementing the definition of nanomaterial, and recommend it for inclusion in a technical guidance for the implementation of the definition.
Extraction of true, 3D shape (and size) of non-spherical nanoparticles (NPs) is associated with errors by conventional 2D electron microscopy using projection images. Significant efforts within the ISO technical committee TC 229 ‘Nanotechnologies’ are aimed at establishing accurate TEM and SEM measurement of NP size and shape as robust, standard procedures. Study groups have been organizing inter-laboratory comparisons on well-selected NP systems according to the market needs, such as aggregated titania nano-powder for which size and shape distribution of primary crystallites of irregular shape must be measured accurately. To be noticed is e. g. the fact that the measurement procedure allows only manual selection of the particles clearly distinguishable for analysis as well as manual definition of the contour of the imaged NPs.
An inter-laboratory exercise on titania NPs (pure anatase, grown by hydrothermal synthesis) of well-defined non-spherical shape, i.e. bipyramidal has been recently started within ISO/TC 229 under similar conditions as for the irregular shaped titania. Overlapped particles were allowed to be considered, as long as they are clearly distinguishable. One decisive NP selection criterion was to analyze only those NPs with a roundness value below 0.7, i.e. the NPs laying on the support foil and, hence, with projection areas clearly deviating from perfect circles (R=1). The overall evaluation (for 15 labs) of the size descriptors (area, Feret, minFeret, perimeter) and shape descriptors (aspect ratio, roundness, compactness, extent) by analysis of variance is just to be finished and included in ISO/WD 21363 Nanotechnologies -- Protocol for particle size distribution by transmission electron microscopy.
Titanium dioxide is one of the most studied metal oxides due to its chemical, surface, electronic and (photo)catalytic properties, providing this material of multisectorial applications ranging from healthcare, photocatalysis, smart materials with self cleaning and self sterilizing properties and solar energy harvesting. However it is difficult to correlate the functional properties of TiO2 nanomaterials to the properties at single nanoparticle level due to the high polydispersity in shape, size and surface features of the currently available TiO2 nanoparticles (NPs). Although intensive experimental and theoretical studies have been conducted on the reactivity of different surfaces of metal oxides such as TiO2 much less attention is paid on the dependence of functional properties, like photocatalytic activity, dye adsorption, open circuit potential and fill factor in dye sensitized solar cells, on crystal facets in different orientations. One of the goal of SETNanoMetro project was the development of design rules to tune crystal facets of TiO2 NPs in order to optimize and control functional properties. In the present work we have developed a series of design rules in order to obtain sets of anatase TiO2 NPs with low polydispersity and to tune their shape and size by hydrothermal processing of Ti(IV)-Triethanolamine complex in presence of different shape controllers. Through a careful experimental design, a predictive soft model was developed. The model is able to predict the synthesis outcome allowing to tune the shape factor from 5 (prisms) to 1.5 (bipyramids) to 0.2 (platelets). This allows to control the main crystal facets exposed ranging from (100) to (001). Due to the dependence of functional properties of nanomaterials on shape distribution and not only size, the availability of NPs sets with uniform and well defined and tunable shapes can be of paramount relevance in order to produce reference nanomaterials for shape measurement.
The EC Recommendation on the definition of nanomaterial, based solely on size of the constituent particles, foresees development of harmonised measurement methods ensuring ‘consistent results across materials and over time’. The EU/FP7 research project NanoDefine has been exclusively dedicated to support the implementation of this EC Recommendation for the European Union’s legislation. For the first time, measurement techniques able to determine the size of nanoparticles have been evaluated systematically on a well-defined set of quality control materials (spherical, monodisperse) as well as industrial materials of complex shapes and considerable polydispersity.
Particularly based on the analytical performance of the measurement techniques as tested on the challenging real-world particulate materials, it was possible to formulate recommendations for use of a new tiered approach consisting of screening and confirmatory techniques. Thus, a consistent framework of guidance for nanomaterial identification according to the EC Definition has been issued in form of the NanoDefiner e-tool, with a transparent decision flow scheme and an extensive user manual. Selected examples of analysis and classification as nano-/non-nanomaterials will be given, highlighting the limits of applicability of the available measurement techniques in dependence on sample properties. On some recent relevant developments in sample preparation – as a crucial part for an accurate analysis - will be also reported.
The main objectives of the new EMPIR project nPSize are to establish EU capability of traceable measurement of NP size and shape, lower uncertainties of NP size measurement by developement of new nano-CRMs, new models (physical and machine learning), 3D method combination, and also by new ISO and CEN standards on accurate NP size measurement and guidance and knowledge transfer. The envisaged outcomes of the project will be presented and their suitability will be discussed to be taken over as pertinent contributions to normative projects within CEN/TC 352 Nanotechnologies.
A femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated by XRD and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation.
Although there are many experimental techniques for measuring particle sizes and size distributions, electron microscopy (EM) is still considered as the gold standard in this field, especially when it comes to particle sizes in the nanorange (1 nm – 100 nm). Furthermore, high-resolution X-ray spectroscopy (EDS) can be applied to individual nanoparticles. To be able to extract accurate information from the EM micrographs and EDS elemental maps that are representative for the material under investigation, one needs to assure the representativity of the particles as sampled on the substrate and their homogeneous spatial distribution, to avoid operator bias when selecting the imaged area. Furthermore, agglomeration should be avoided as far as possible. Several sample preparation techniques exist since a long time, the most common way being suspending the particles in a liquid and depositing them on the grid. However, this procedure includes the drying of larger solvent amounts on the substrate itself, which can affect the spatial distribution of the deposited particles. One possibility to overcome this problem is the use of an electrospray system, where the suspension of particles is sprayed onto the substrate in charged droplets that are so small that they either dry off on the substrate immediately without affecting the position of particles, or even already during their flight time to the substrate. No dedicated commercial instruments are available for the preparation of TEM grids yet, only electrostatic deposition of aerosols on TEM grids has been reported so far. To test the prototype and assess its performance, several materials have been sprayed onto TEM grids and the resulting particle distributions were compared to more traditional sample preparation strategies like the “drop on grid” method. Operation parameters such as the sample flow-rate, capillary – substrate distance, electric field strength and sampling period length have been optimised. It was found that the particles deposited by electrospray generally show a much more homogeneous spatial distribution on the substrate and a substantial increase of the number of single particles, which are much better suited to an automatic image evaluation procedure than the agglomerated particles observed otherwise. The applicability of the technique to a broad range of materials is demonstrated by various examples, but also the influence of the substrate, the choice of the particular TEM grid, on the obtained spatial particle distribution is assessed.
The overall objective of project Improved traceability chain of nanoparticle size measurements is to improve the traceability chain for nanoparticle size measurements. The main impact will be achieved by manifold contributions to standard documents for CEN/TC 352 “Nanotechnologies”, which directly addresses the research needs of CEN, CENELEC and ETSI mandated by EC to develop standards for methods and reference materials to accurately measure the size and size distribution of nanoparticles. This will take place in collaboration with ISO/TC229 ‘Nanotechnologies’, ISO/TC24/SC4 ‘Particle characterization’ and ISO/TC201 ‘Surface analysis’/ SC9 ‘Scanning probe microscopy’.
The presentation goes into the characterization of TiO2 engineered nanoparticles within EU/FP7 SETNanoMetro Project and the nanomaterial classification according to the EC definition tested within EU/FP7 NanoDefine Project. Further, ISO/TC 229/JWG 2 activities related on ISO standards in development and inter-laboratory comparisons on measurement of nanoparticle size and shape distribution by SEM and TEM are discussed.
The capability of currently available particle sizing techniques for reliable classification of materials that potentially fall under the EU Definition of a nanomaterial is discussed. A systematic quantitative evaluation of the sizing techniques is presented together with representative case studies of analysis of industrially relevant materials.
Recommendations on the most appropriate and efficient use of techniques for different types of material are given.
The large European nanometrology Project NanoDefine is presented briefly with respect to the challenges of measurement of particle size distribution for complex nanoparticulate materials.
The methods chosen for a tiered approach for the classification of a nanomaterial are discussed with regard to their peformance. Representative resuls on real life, complex shaped nanoparticulate materials are shown.
The recently initiated VAMAS inter-laboratory comparisons to determine the reproducibility necessary for international standardisation have been also presented.
The press conference on the results of the European Project FP7 constitutes a dissemination event dedicated to the production and characterization of "Shape-engineered TiO2 nanoparticles for metrology of functional properties: setting design rules from material synthesis to nanostructured devices" with the main large-scale applications in the three reference sectors: energy, health and environment.
At the Final Outreach Event of the European FP7 NanoDefine project the results achieved during 4 years of intensive research and development work (2013-2017) with relevant stakeholders and wider community, and their practical implications and impact are presented and discussed. The newly developed particle-size related measurement tools and their practical suitability and applicability to classify materials, formulations and products according to the EC recommendation on the definition of a nanomaterial (2011/696/EU) are demonstrated.
Of many experimental techniques for measuring particle sizes and size distributions, electron microscopy (EM) is still considered as the gold standard, especially in the nano range (1–100 nm). Furthermore, high-resolution X-ray spectroscopy (EDX) in conjunction with EM can be applied to individul NPs.
Preparation of an EM sample for generic particulate materials is a difficult task. Usually, the particles in a suspension are deposited on a support. However, this procedure includes the drying of larger solvent amounts on the substrate itself, and this can affect the spatial distribution of the deposited particles. One possibility to overcome this is the use of an electrospray system, where the suspension of particles is sprayed onto the substrate in charged droplets that are so small that they either dry off on the substrate immediately without affecting the position of particles, or even already during their flight time to the substrate. Additionally, the charging of particles minimizes agglomeration and aggregation, maximizing the collection of the EM grids.
The prototype of an electrospray deposition System was tested. Electrospray is theoretically described since a long time, but no dedicated commercial instruments are available for the preparation of TEM grids yet, apart from electrostatic deposition of aerosols.
Several materials have been sprayed onto TEM grids and the resulting particle distributions were evaluated. Operation parameters such as the sample flow-rate, capillary – substrate distance, electric field strength and sampling period length have been optimized. It was found that the particles deposited by electrospray generally show a much more homogeneous spatial distribution on the substrate and a substantial increase of the number of single particles (suited to automatic analysis).
The synthesis of TiO2 nanoplatelets with fluorine-containing reactants is carried out using Ti (IV) butoxide as precursor and concentrated HF as shape controller, the final product requires a working up in order to eliminate or at least to reduce the amount of residual fluorides, which is realized here by well-defined thermal treatment.
Qualitative investigation of the bulk elemental composition by means of EDX of TiO2 nanoparticles (NPs) has identified fluorine in case of the as-synthesized samples. EDX spectra of thermally treated products exhibit either a fluorine content close to the limit of detection. The latter holds also true for the reference sample, TiO2 NPs of bipyramidal shape and prepared by a different synthesis route. For differentiation whether fluorine is present in the bulk or at the surface of the TiO2 nanoplatelets, top-surface sensitive AES and ToF-SIMS has been applied. Secondary ions of fluorine are detected in ToF-SIMS spectra of all samples, but could be roughly quantified by measurement of same reference sample as for EDX, namely TiO2 nano-bipyramids. This revealed that the amount of fluorine within1 nm depth beneath the surface is reduced in the thermally treated specimen compared to the raw product down to a content about as low as in the reference sample. AES allows analyzing analysis of the first few nanometers from the top-surface of individual NPs by point analysis. An F KLL peak has been detected at the surface of samples of as-prepared TiO2 nanoplatelets under optimized measurement conditions, but was not detectable after their calcination, which is in agreement with ToF-SIMS results. Moreover, high resolution AES on single TiO2 nanoplatelets elucidated that the surface atomic layers surrounding the TiO2 nanopaltelet contain fluorides before thermal treatment of the NPs.
Self-assembly of TiO2 nanoparticles in multiple layers by layer-by-layer deposition has been selected of different deposition procedures usually applied for fabrication of TiO2 thin films with defined and homogeneous thickness on supports of interest for the large-scale applications. The substrates tested were: conductive (FTO) glass, silica glass and titanium alloy. The selected film fabrication technique consists of the deposition of alternating layers of oppositely charged, i.e. functionalized, TiO2 nanoparticle layers with wash steps in between. The controlled assembly of TiO2 nanoparticles on the supports surface requires both a proper functionalization of the supports to promote the adhesion of the TiO2 film to the substrates and proper functionalization of TiO2 nanoparticles to allow attachment to substrate and subsequent reaction between different NP layers. The current study focusses on the analytical control of the functionalization of the substrates with 3-Aminopropyltriethoxysilane (APTS) and glutaraldehyde (GA) by means of surface sensitive methods, XPS, Auger Electron Spectroscopy (AES) and ToF-SIMS. Chemical composition of surface of functionalized substrates shows differences in the degree and type of modification in dependence on substrate.
Evaluation of particle sizing techniques for implementation of the EC Definition of a nanomaterial
(2017)
Many techniques are available for measuring particle size distribution. For ideal materials (spherical particles, well dispersed) it is possible to evaluate the Performance of these methods. The performance of the analytical instrumentation for the purpose of classifying materials according to EC Definition is unknown. In this work the performance of commercially available particle sizing techniques on representative NanoDefine set of real-world testing materials (RTM) and quality control materials (QCM) for the implementation of the Definition is evaluated.
Electrospray ionization constitutes a promising deposition technique for high-resolution imaging. Particle distribution on TEM grids takes place homogeneously and no losses occur. Suspension must be appropriate (stabilizer may induce artefacts). ESI parameters need to be optimized for each material.
Volume specific surface area (VSSA) by BET: concept and demonstration on industrial materials
(2017)
Volume specific surface area (VSSA) as measured by BET constituites a simple and reliable solution to (most) powders. Porous, coated, polydisperse/multimodal materials are to be treated with care, i.e. doubled by analysis with electron microscopy or more advanced BET analysis (e.g. t-plot)for each material in part.
The potential of electrospray deposition, for the controlled preparation of particles for imaging in electron microscopes, is evaluated on various materials: from mono-modal suspensions of spherical particles to multimodal suspensions and to real-world industrial materials. It is shown that agglomeration is reduced substantially on the sample carrier, compared with conventional sample preparation techniques. For the first time, it is possible to assess the number concentration of a tri-modal polystyrene suspension by electron microscopy, due to the high Deposition efficiency of the electrospray. We discovered that some suspension stabilizing surfactants form artifact particles during electrospraying. These can be avoided by optimizing the sprayed suspension.
Loss in efficiency of perovskite solar cells may be caused by structural and/or chemical alterations of the complex layered system. As these changes might take place either in the bulk and/or on the surface of the stratified material, analytical tools addressing both key issues are selected and combined. SEM/EDX combined with XPS were chosen as appropriate methodical approach to characterise perovskite laboratory cells in depth and complementary on top, before and after light exposure. The layered perovskite system investigated here is based on glass covered with fluorine doped tin oxide (FTO), followed by three porous thin films of TiO2, ZrO2 and a thick monolithic carbon. The TiO2 film is subdivided into a dense layer covered by a porous one constituted of nanoparticles with a truncated bipyramidal shape. This layered system serves as the matrix for the perovskite. After infiltration of perovskite solution and annealing, EDX
spectral maps on cross-sections of the specimen have been measured. The distribution of relevant
elements – Si, Sn, Ti, Zr and C – correlates conclusively with layers visible in the acquired SEM images. Lead and iodine are distributed throughout the porous layers C, ZrO2 and TiO2. In a SEM micrograph taken of the cross-section of a sample after illumination, the glass substrate and all layers FTO, TiO2, ZrO2 as well as C are clearly identified. By EDX it was found that several weeks of ambient daylight did not change significantly the qualitative elemental composition of lead and iodine throughout the solar cell system. It was confirmed with EDX that nanoparticles identified in high-resolution SEM micrographs contain mainly Pb and I, indicating these to be the perovskite
crystals. However, a time-dependent compositional and chemical altering was observed with XPS for the near-surface region of the outermost ~10 nm after two months of illumination.
A combined methodical approach is tested with respect to the characterization of the inner structure of porous TiO2 layers as typically used in modern dye sensitized solar cells (DSSC). Their performance is directly linked to the surface area of the pore network. The micrometer thick layer employed was manufactured by screen-printing of a starting TiO2 powder constituted of shape-controlled, bipyramidal anatase nanoparticles on FTO/glass substrates. The analytical methods exploited in our study are Focused Ion Beam (FIB) slicing followed by 3D reconstruction as well as the new approach transmission Kikuchi diffraction (TKD) technology in the scanning electron microscope (SEM). Size and shape distribution of the TiO2 NPs within the layer can be extracted. SEM in transmission mode and atomic force microscopy (AFM) have been used to verify the dimensional data obtained by the new combined methodical approach. Its analytical benefits but also the challenges and limitations are highlighted.
Organic surface modification and analysis of TiO2 nanoparticles for self-assembly in multiple layers
(2017)
Parameters of TiO2 coatings can greatly influence their final performance in largescale applications such as photocatalytic measurements, orthopedic and/or dental prostheses, cell cultures, and dye-sensitized solar cells. From different film deposition procedures, self-assembly of TiO2 NPs in multiple layers was selected for systematic characterization. EDX, AES and ToF-SIMS analysis have been carried out in order to evaluate the functionalization of several types of TiO2 NPs differing in size, shape and surface area.
Scanning Electron Microscopy (SEM) represents the mostly widespread method available in analytical laboratories dedicated to the characterization of physical properties such as morphology of various solid materials from ‘micro-’ down to the nanometre scale. The use of secondary electrons excited by a sharply, nm-focussed primary electron beam enables at any modern SEM to image objects with high in-depth and lateral sensitivity, i.e. with high spatial resolution. Hence, e. g. nanoparticles (NPs) are able to be easily characterized with respect to their individual size and shape, but also to the morphology of their surface.
By preparing the nano-objects on thin membranes as electron transparent samples it is possible to perform electron microscopy in the transmission mode (TEM and TSEM). The corresponding transmission (i.e. mass-thickness) contrast reveals in-depth information, but is also well suited for dimensional measurements in the 2D projection image. Both the surface sensitive mode and the transmission one are meanwhile available at any modern SEM. If an X-ray spectrometer is attached to an electron microscope, it is possible to analyse the characteristic X-rays induced by electron bombardment. Most electron microscopes have attached an energy dispersive X-ray spectrometer (EDX) so that EDX elemental maps can be carried out. Recent technological developments of high throughput EDS detectors and their advantages regarding high-resolution X-ray analysis down to the nm range are reviewed.
High-resolution micrographs (SEM, TSEM, TEM) and corresponding X-ray elemental maps on various representative nanoparticles, but also layered samples prepared in cross-section, will be presented and discussed. The importance of selecting the best suited analysis conditions will be highlighted. Also other, often challenging, topics such as sample preparation and image data processing will be critically addressed by practical examples. Further analytical techniques able to be employed at an electron microscope, like cathodoluminescence (CL) or micro-X-ray fluorescence (µXRF) will be briefly surveyed.
The TiO2 material selected for the present inter-laboratory comparison (ILC) was the bipyramidal anatase UT001 batch synthesized hydrothermally by University of Turin in the frame of the EU/FP7 Project SETNanoMetro and carefully prepared on TEM grids by BAM to be distributed to the ILC participants. A clear measurement protocol including data analysis and reporting (including an xls reporting template) has been also prepared by BAM. 14 of 18 participants have measured and reported results which have been already checked by BAM as being conform to the agreed protocol. After receiving the last results (of 4 participants) the ILC data evaluation will be carried out by BAM in line with agreed ISO/TC229 procedures as for the other case sudies.
A proposal of an inter-laboratory study (ILC) on determination of size and shape distribution of TiO2 nanoparticles (NPs) by transmission electron microscopy is presented. The anatase NPs synthesized in a controllable fashion within the EU/FP7 project SETNanoMetro can be considered as shape-defined (bipyramidal) and are offered to complete the list of case studies already in progress within ISO/TC229/JWG2. The main points of the measurement procedure are presented as well as a proposed procedure to evaluate the size and shape according to the standard operation procedure already developed within SETNanoMetro is discussed. Potential ILC participants and a plan with next step to be carried out are proposed.