The realistic description of plastic deformation caused by dislocations demands the representative measurement of their features, e.g., Burgers vector, slip plane, line direction and density. In the case of bulk deformation of technical alloys, reliable data must be ensured for large regions. Nonetheless, the (thin) filiform nature of dislocations and also the heterogeneity in some microstructures additionally require flexible analysis techniques that resolve the details of their interactions. Strong and clear channeling contrasts, faint extinction contours and the absence of chromatic aberration make scanning transmission electron microscopy (STEM) an ideal imaging mode in wide and thick regions of TEM foils, as opposed to conventional (C)TEM. It is the purpose of this contribution to show how STEM can be applied for quantitative measurement of dislocation features. Furthermore, a new tool will be presented, which enables the three-dimensional (3D) reconstruction, visualization and quantification of dislocation densities and directions from stereo-pairs. The application of these techniques will be shown on a monocrystalline Ni-base superalloy, an important class of structural materials that has been implemented in the first row blades of gas turbines. The examples are extracted from specimens subjected to creep deformation at high temperature and low stress under various macroscopic deformation geometries. The spacial and angular accuracy are discussed as well as possible sources of error.
The demand for improved castability and low angle grain boundary (LAGB) resistance has led to the addition of low contents of e.g., B, Hf, Zr or C, into large industrial gas turbine components made of Ni-base superalloy single crystals (SXs). Due to the long-term application of Ni-base superalloy SX components in the temperature regime > 1000 °C, the formation of carbides is highly probable, which could jeopardize mechanical properties, such as high cycle fatigue. In the present contribution, the effect of internal and external stresses on the nucleation and growth characteristics of M23C6 carbides is investigated. Creep experiments are performed on the Ni-base superalloy SX LEK 94, which shows a low C concentration (= 0.1 at. %), at 1020 °C under parallel and circularly notched tensile specimens at a nominal stress of 160 MPa in the crystallographic direction [001]. The carbides are then characterized via scanning (S) and transmission (T) electron microscopy (EM). Nucleation is enhanced in the dendritic cores, often as coalesced colonies, extending over micrometers within M-rich (M: Cr, Re, W, Mo) γ channels. Lath shapes with facets on {100} (parallel to growth direction) and {111} are common. These facets exist since early stages (Fig.1a) and later develop misfit dislocations (Fig.1b), preserving the orientation relationship {100}γ || {100}M23C6. Fig. 1c shows a region from the creep gage, where carbides interact with superdislocations in the γ’ phase. Possible mechanisms are discussed.