The detection and characterization of surface breaking cracks in steel prior to damage is a technologically as well as economically important task especially for safety-relevant structures. Detection of small cracks already during the steel production process might significantly reduce the risk of failure and reduce production costs due to an obsolete post-processing.
However, the hostile environmental conditions (high temperature specimens) together with very strict requirements in current steel production (production speeds, in-line testing and evaluation) are challenging and render many well-established NDE techniques hardly applicable.
We present an approach to use laser thermographic testing as a fast, remote and contactless NDE method, that addresses these challenges and might ultimately allow for online crack detection.
The basic idea of laser thermographic testing, introduced by Kubiak in 1968, is the monitoring of the heat flow as induced by local heating. Disturbances within the heat flow generated by the presence of surface cracks can then be analyzed by image processing algorithms, as we have shown in previous work.
The aim of the presented work is to advance laser thermographic testing to be applicable to the specific conditions of steel production environments. This purpose was met by the development of a laboratory setup that allows us to simulate production conditions, as rolling speed, specimen temperature, laser heating power and study their influence on crack detection performance. This parametric study enabled us to develop and improve data processing and crack detection algorithms with the final goal of providing optimized in-line crack detection. The studies were accompanied by comprehensive FEM simulations to intensify the understanding of the contrast formation as well as the crucial parameters influencing the performance of the method.
At present, Wind Turbine Generators (WTGs) operating in onshore and offshore wind farms are primary sources of renewable energy around the world. Cylindrical grouted sleeve connections are usually adopted in these WTG structures to connect the upper structure and foundation for ease of installation. These structures including grouted connections experience considerable adverse loading during their lifetimes. Settlements were reported inside similar connections used in energy structures especially oil and gas platforms, which were installed in last three decades. Thus, repair and rehabilitation of such connections in existing wind structures should also be planned ahead to keep them operating in the future. The nature of failure and crack generation in grouted connections are crucial prior to adopt a strengthening strategy. This pilot study is carried out to actualize the failure mechanism in the grouted connection, when subjected to axial loading. A novel reusable scaled cylindrical grouted connection with shear keys was designed and tested for its load bearing behaviour. The mechanical test was accompanied by classical measuring techniques (e.g. displacement transducer) as well as non-destructive measuring techniques (e.g. digital image correlation (DIC), acoustic emission analysis (AE)). The failure mechanism incorporating slippage of the shear keys and cracking of the grout was investigated. The capacity and applicability of such test mould were also discussed. The knowledge is expected to pave way towards repair of deteriorated grouted connections with similar geometry and failure pattern.
X-ray refraction techniques represent a very promising, yet not so wide-spread, set of X-ray techniques
based on refraction effects. They allow determining internal specific surface (surface per unit volume) in a non-destructive fashion, position and orientation sensitive, and with nanometric detectability. While they are limited by the X-ray absorption of the material under investigation, we demonstrate showcases of ceramics and composite materials, where understanding of microstructural features could be achieved in a way unrivalled even by high-resolution techniques such as electron microscopy or computed tomography.