In geothermal power plants materials e.g. pumps are exposed to extremely corrosive thermal water. This results in corrosion fatigue and so inevitably the reduction of the lifetime of these components. Also in the field of the carbon dioxide storage technology (carbon capture and storage CCS) components are exposed to a corrosive environment and mechanical stress. In order to gain knowledge upon the corrosion fatigue strength of materials a corrosion chamber for "in situ" conditions was designed and successfully applied.Two different steels X46Cr13 and X5CrNiCuNb16-4 have been tested and their corrosion fatigue behavior was compared. To simulate the frequency of operating pumps (30 – 40 Hz) a resonant testing machine was used. In addition technical CO2 was introduced into the closed system at a rate close to 9 L/h to keep stable environmental conditions. The samples have a surface roughness of Rz = 4 to simulate technical machined surfaces. The calculated tensile strength of X46Cr13 with soft annealed microstructure (coagulated cementite in ferrite-perlite matrix) is about 680 MPa and the yield strength is about 345 MPa. The tensile strength of X5CrNiCuNb16-4 is about 1078 MPa and the yield strength about 928 MPa. Testing parameters are: corrosion media: saline aquifer water (Stuttgart Aquifer) temperature of the brine at 60 °C and load ratio of R=-1. For X46Cr13 a stress amplitude between 160 MPa to 270 MPa and for X5CrNiCuNb16-4 a stress amplitude between 150 to 500 was chosen. Cycles until crack initiation differ strongly and were found to start at 5 x 104 up to 12.5 x 106 cycles.X46Cr13 has reached a maximum number of cycles (12.5 x 106) at a stress amplitude of 173 MPa. X5CrNiCuNb16-4 has reached the maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa. The range of scatter for X5CrNiCuNb16-4 is very high (1:34) in comparison the range of scatter for X46Cr13 (1:3.5).
Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are due to the chemical composition of hydrothermal waters and temperatures, in many cases, extreme in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities.
This contribution deals with the evaluation of the corrosion behavior of different steels in flowing low saline, slightly alkaline, artificial geothermal water simulating the conditions in the Molasse-Basin, a location with geothermal potential in Germany.
Test results for steels UNS S31603 and UNS S31803 exposed to this geothermal water obtained by electrochemical measurements and exposure tests are presented. Results obtained in static and flowing water condition show good performance of both alloys with a possible onset of localized corrosion at UNS S31603 in static conditions.
This contribution provides current findings regarding materials susceptibility for carbon capture, utilization and storage (CCUS) applications. Basing on results gathered in 2 German long-term projects (COORAL and CLUSTER) suitable materials are introduced as well as dominating impurities of the CO2-stream and corrosion mechanisms. Investigations cover the whole CCUS process chain and provide material recommendations for certain parts.
Many technologies have been developed to take advantage of geothermal energy, which became a feasible energy source to replace fossil fliel supply. Nevertheless, Service conditions in geothermal facilities are due to the Chemical composition of hydrothermal fluids and involved high temperatures, in many cases, extreme in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable Operation ofthe facilities.
This contribution deals with the evaluation of the corrosion behavior of two high-alloyed metallic materials and a-A1203 in an artificial geothermal fluid simulating the conditions in the Northern German Basin, a location with high geothermal potential. The suitability of the super austenitic stainless Steel, alloy 31, and the nickel base alloy 59 in this geothermal fluid obtained by electrochemical measurements and exposure tests is addressed. As an alternative to the suitable but costly alloy 59 that showed excelient corrosion resistance against pitting corrosion, ceramic made of a-A1203 represents an interesting possibility for selected components to be used in the construction of geothermal facilities.
Influence of Precipitating Brine Components on Materials Selection for Geothermal Applications
(2021)
Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are in many cases extreme in terms of corrosion due to the chemical composition of hydrothermal fluids and temperatures. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. During operation of a geothermal research facility in Groß Schönebeck copper and lead effects have been found downhole. Occurring mechanisms and measures to prevent precipitation or scaling needed to be investigated as well as potential influences of such precipitates on corrosion resistance of metallic materials used for equipment.
This contribution deals with the evaluation of the corrosion behavior of carbon steel and corrosion resistant alloys in copper and/or lead containing artificial geothermal water, simulating the conditions in the Northern German Basin.
The behavior of these materials in an artificial geothermal water obtained by electrochemical measurements and exposure tests are presented. While carbon steel exhibits precipitation and deposition, higher alloyed material shows different response to such species and a higher resistance in saline geothermal water.
Basing on these results the suitability of the investigated corrosion resistant alloy is given for use in such conditions, whereas carbon steel creates difficulties due to its susceptibility to Cu- and Pb-precipitation.
By exposure and electrochemical tests in the laboratory the Cu-effect on corrosion behavior of carbon steel, high-alloyed steels and Ti-alloy can be assessed.
Critical materials specific properties were determined by static exposure and electrochemical tests in an artificial geothermal water with high salinity and low pH, containing Cu. Conclusions were drawn using characteristic potential values.
It could be shown that significant Cu-deposition and -precipitation only occurred in combination with carbon steel. High-alloyed materials (S31603, S31653, S31700, S31703, S31803 and N08904) prevent the disturbing Cu-agglomeration. Therefore, they are suitable to be chosen for future design of the piping system, either in massive or in cladded form, if formation of crevices with non-metallic materials can be excluded.
From the interactions and pitting corrosion point of view, R50400 seems to be most favorable.
In Germany the “BAM-List - Requirements for Tanks for the Transport of Dangerous Goods” is the basis for substance-related prototype approvals for tank Containers undertaken by the BAM1 - Federal Institute for Materials Research and Testing. Compatibility evaluations of selected metallic materials as well as of polymeric gasket and lining materials under the influence of approximately 7200 dangerous goods have been published in the BAM-List since 1989.
The ferritic Steel UNS S44400 (X2CrMoTil8-10, 1.4521) was originally developed as alternative for the austenitic grade AISI316L (X2CrNiMo 17-12-2, 1.4404). Due to its characteristic profile this Steel was qualified for applications requiring high strength values at concomitant adequate corrosion resistance. Because of the lack of Nickel this Steel is a cost-efficient alternative to the Ni-containing austenites. No corrosion test results of UNS S44400 under the influence of dangerous goods were published in the BAM-List so far. Only data on the behavior of AISI 316L are listed. Therefore test specimens of this Steel were exposed to selected corrosive substances in order to compare both steels.
Due to the reduced alloy content a reduced corrosion resistance of the Steel UNS S44400 in acidic substances, such as formic acid, acetic acid and sulfuric acid, in comparison to the austenitic CrNiMosteels was expected but not observed. Tests in an alkaline medium showed sufficient resistance.
Carbon Capture Utilization and Storage (CCUS) is a promising technology to reach the target for reduction of CO2 emissions, e.g. from fossil-fuel operated power plants or cement mills. Crucial points for a sustainable and future-proof CCUS procedure are reliability and cost efficiency of the whole process chain, including separation of CO2 from the source, compression of CO2, its subsequent transportation to the injection site and injection into geological formations, e.g. aquifers.
Most components that are in contact with CO2-stream consist of steel. Depending on the operating conditions (e.g. temperature, pressure, and CO2-stream composition) specific suitable steels should be used. The compressed CO2-stream is likely to contain process specific impurities; small amounts of SO2 and NO2 in combination with oxygen and water are most harmful.
One approach, as currently preferred by pipeline operators, is to clean the CO2-stream to such levels, acceptable for carbon steel, commonly used as pipeline material. Another consideration would be, to use more corrosion resistant alloys for CO2-streams with higher amounts of impurities.
Due to the absence of certified benchmarks for upper limits, systematic experiments with impurities in the CO2-stream were carried out reflecting mainly transport and injection conditions.
Within the COORAL project (German acronym for “CO2 purity for capture and storage”) levels of impurities in the CO2-stream, being acceptable when using specific steels, were evaluated. Material exposure to dense or multiphase carbon dioxide (CO2) containing specific amounts of water vapor, oxygen (O2) sulfur dioxide (SO2), nitrogen dioxide (NO2), carbon monoxide (CO) can be a challenge to steels. In some situations, condensation of impurities and reaction products from the CO2 stream can occur.
CO2 saturated brine is supposed to rise in the well when the injection process is interrupted. The material selection shall ensure that neither CO2 nor brine or a combination of both will leak out of the inner tubing.
This COORAL-work was extended by a follow-up project, called CLUSTER. Here the additional influence of impurities was investigated when merging CO2 streams from different sources, combined within a “so-called” cluster.
Results are summarized within the following table regarding suitability for different parts of the process chain.
Intumescent coatings are used in civil engineering to improve the fire resistance of steel constructions. Due to the thin coating thickness and the profile-following application, the architectural appearance of the steel structure can be preserved. EN 13381-8 provides regulations to determine the contribution to the fire resistance of intumescent coatings applied to steel beams and columns. The scope of this standard excludes tension members and steel members with solid sections. For products that have already been successfully tested and assessed on beams and columns, EN 13381-10 offers the possibility based on unloaded fire tests to extend the scope of application of intumescent coatings to tension bars with solid sections. This approach contradicts the national safety level in Germany, where mechanically loaded testing is mandatory. Therefore, a new part of the test standard series EN 13381 is currently developed to enable the application of intumescent coatings on steel tension bars with solid section based on mechanically loaded fire tests. BAM has already carried out numerous fire tests on loaded steel tension members with intumescent coatings. Currently, in the BAM research project FIRESTEMIC, the influence of the steel bar orientation and the profile type on the thermal performance of intumescent coatings are investigated. Both questions concerning the thermal protection ability of intumescent coatings were analysed based on three different test sets, which were carried out in the tension furnace (Fig. 1a). The fire exposure corresponds to the standard temperature-time curve according to EN 1363-1.
This paper summarises the main findings from the fire tests conducted in the FIRESTEMIC project. The results serve as an experimental background for the proposal of the new standard. Regarding the bar orientation, a new test setup was developed and proposed for the new standard. The two tested commercial water-based intumescent coatings with applied dry film thickness from 1.5 mm to 2.5 mm showed only a slight dependence on the bar orientation. In terms of the steel profile type, circular and rectangular solid sections with identical section factor and applied dry film thickness were tested. It was observed that the circular solid bars with diameter 30 mm heat up faster compared to the solid rectangular bars with dimension 30×30 mm (Fig. 1b). Also at larger steel bars, i.e. diameter 40 mm and dimension 40×40 mm, the same trend occurred. Thus, it is recommended for the new test standard to allow a transfer of the test results from circular to rectangular solid sections. In addition, the paper will describe and explain the test and assessment procedure proposed for the newly developed standard.
Revealing hydrogen embrittlement mechanisms in steels is of great interest to scientists and engineers. Neutron radiography makes it possible to measure in-situ hydrogen diffusion with high spatial and temporal resolution at concentrations as low as 20 ppm. We compare hydrogen-charged specimens with hydrogen-free reference specimens and use calibration standards to normalize the hydrogen concentrations. This allows quantitative tracking of the hydrogen concentration evolution as a function of time, space and temperature. Furthermore, a view into the material with 'neutron eyes' facilitates the detection of cavities that contain molecular hydrogen.