Specific heat spectroscopy in the frequency range typically from 1 Hz to 1 kHz with a sensitivity of pJ/K was employed to study the glass transition behavior of ultrathin poly(vinyl methyl ether) (PVME) films with thicknesses ranging from 218 nm down to 12 nm. The amplitude and the phase angle of the complex differential voltage as a measure of the complex heat capacity were obtained as a function of temperature at a given frequency simultaneously. Both spectra are used to determine the dynamic glass transition temperature as a function of both the frequency and the film thickness. As main result no thickness dependence of the dynamic glass transition temperature was observed down to a film thickness of 12 nm within the experimental uncertainty of ±2 K. Further the width of the glass transition is independent of the film thickness which indicates that the extent of the cooperativity is essentially smaller than 12 nm.
Aerosol-based DBD - A simple way to provide polymers with functional groups for adhesion promotion
(2013)
Polypropylene (PP) foils were exposed to the plasma of an atmospheric dielectric barrier discharge (DBD) in presence of different aerosols. Pure liquids such as water, ethanol, and 1/1 mixtures ethanol/water (v/v) or aqueous Solutions of acetic acid, poly(acrylic acid), poly(vinyl alcohol), and ethylene glycolpoly(vinyl alcohol) copolymer were introduced into the DBD. Surface composition, the number of functional groups per 100 C atoms, and water contact angles were correlated with the energy density of DBD plasma exposure.
The wettability of the treated surfaces was investigated for different storage times. Peel strength of the thermally deposited aluminum layer to modified polymer surfaces revealed that the aerosol introduction strongly improves the adhesion between aluminum and polypropylene.
Polar groups were introduced on polypropylene surfaces for increasing the surface energy and the peel strength to evaporated aluminium layers. Three kinds of plasma processes were used for introducing such functional groups to polyolefin surfaces: low-pressure radio-frequency (RF) O2 plasma exposure, atmospheric-pressure dielectric-barrier discharge (DBD) treatment in air, and the deposition of allylamine plasma polymer. The amino groups of the allylamine plasma polymer were also used as anchoring points for chemical introduction of covalently bonded spacer molecules equipped with reactive endgroups. Thus, silanol endgroups of a covalently bonded spacer were able to interact with the evaporated metal layer. The Al-PP composites achieved a maximal peel strength of 470 N/m by exposing the polymer to the lowpressure O2 plasma and 500 N/m on exposure to the atmospheric DBD plasma. After allylamine plasma polymerization and grafting of spacers, the peel strength was usually higher than 1500 N/m and the composites could not be peeled.