Datei im Netzwerk der BAM verfügbar ("Closed Access")
Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (19)
- Beitrag zu einem Tagungsband (19)
- Vortrag (8)
- Posterpräsentation (3)
- Buchkapitel (2)
- Sonstiges (1)
Schlagworte
- Friction (17)
- Wear (10)
- Hydrogen (9)
- Vacuum (7)
- Tribologie (6)
- Tribology (6)
- PEEK (5)
- Graphite (4)
- Hydrogen environment (4)
- Polymer composites (4)
Organisationseinheit der BAM
- 9 Komponentensicherheit (26)
- 9.5 Tribologie und Verschleißschutz (26)
- 3 Gefahrgutumschließungen; Energiespeicher (3)
- 3.3 Sicherheit von Transportbehältern (2)
- 8 Zerstörungsfreie Prüfung (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.4 Prozessanalytik (1)
- 2 Prozess- und Anlagensicherheit (1)
- 2.0 Abteilungsleitung und andere (1)
- 2.1 Sicherheit von Energieträgern (1)
Eingeladener Vortrag
- nein (8)
Friction coefficients for wood-wood and wood-steel interfaces in impact limiters for transport casks
(2023)
Wood is widely used in impact limiters of transport casks for radioactive material. Encapsulated by an outer and inner steel structure, spruce wood is often applied in layers of alternating direction. The friction at the interfaces between these layers is of crucial importance for the impact and energy absorption e.g., at an accidental impact of a cask against a hard target. In order to get detailed information for corresponding numerical calculations, in this study the friction coefficient for the combinations wood-wood and wood-steel was measured in the temperature range between -40°C and 90°C according to the relevant stress conditions for such casks. Results show decreasing friction with increasing temperature, ranging from 0.43 at -40°C to 0.22 for 90°C for wood-steel combinations and from 0.3 at -40°C to 0.24 at 90°C to for a wood-wood combination.
Wood is widely used in impact limiters of Transport casks for radioactive material. Encapsulated by an outer and inner Steel structure, spruce wood is offen applied in layers of altemating direction. The friction at the interfaces between these layers is of crucial importance for the impact and energy absorption e.g., at an accidental impact of a cask against a hard component.
In order to get detailed Information for corresponding numerical calculations, in this study the friction coefficient for the combinations wood-wood and wood-steel was measured in the temperature ränge between -40 °C and 90 °C according to the relevant stress conditions for such casks. Results show decreasing friction with increasing temperature, ranging from 0.43 at -40 °C to 0.22 for 90 °C for wood-steel combinations and from 0.3 at -40 °C to 0.24 at 90 °C to for a wood-wood combination.
Holz wird vielfach in Stoßdämpfern von Transportbehältern für radioaktives Material eingsetzt. Dafür wird oftmals Fichtenholz verwendet. Die Reibung zwischen den dabei entstehenden Grenzflächen ist von entscheidender Bedeutung. Die Ergebnisse hierzu zeigen eine gleichmäßige, mit steigender Temperatur abfallende Reibung.
Holz wird vielfach in Stoßdämpfern von Transportbehältern für radioaktives Material eingesetzt. Dafür wird oftmals Fichtenholz verwendet, das in mehreren Lagen und senkrecht zueinander liegender Faserrichtung zwischen einer inneren und einer äußeren Stahlhülle eingebaut wird. Die Reibung zwischen den dabei entstehenden Grenzflächen ist von entscheidender Bedeutung für die Stoß- und Energieabsorption, z. B. bei einem Aufprall des Behälters auf eine harte Unterlage. Um detaillierte Informationen für entsprechende numerische Simulationen zu bekommen, wurden in dieser Arbeit die Reibungszahlen von Holz-Holz- und Holz-Stahl-Paarungen bei für derartige Behälter relevanten Beanspruchungsbedingungen im Temperaturbereich zwischen -40°C und 90°C gemessen. Die Ergebnisse zeigen eine gleichmäßige, mit steigender Temperatur abfallende Reibung, wobei die Werte für Holz-Stahl-Paarungen zwischen 0,43 bei -40°C und 0,22 bei 90°C sowie für Holz-Holz-Kontakte zwischen 0,3 bei -40°C und 0,24 bei 90°C liegen.
Verschleißfeste Kohlenstoffschichten mit niedriger Reibung sind hervorragend für Anwendungen in der Erdgas- und Wasserstofftechnologie geeignet. Einige Varianten versagen jedoch in inerter Umgebung, was für die praktische Anwendung sehr nachteilig ist. Im Vortrag werden Beispiele aus Modellversuchen für verschiedene Varianten, auch für Flüssigmethan-Umgebung gezeigt.
In this presentation tribological investigations on steels, polymers and coatings in gaseous and liquid hydrogen are shown. For steels the results of show that although martensitic steel may suffer from hydrogen embrittlement, application e.g. in roller bearings is possible. On the other hand, martensitic transformation of austenitic steels may cause problems in the application of these materials. Furthermore, the tribological performance of polymer composites with and without solid lubricant fillers in gaseous and liquid hydrogen was investigated. In particular, PEEK- and PTFE-matrix compounds showed low friction and sufficient low wear under these conditions. Among the solid lubricants, carbon-based materials are appropriate for hydrogen applications. Several variants of DLC and ta-C materials were tested. Beside the results for hydrogen, also a comparison with CH4-environment is shown.
Anerkannte Institutionen stellen ihre Kompetenzen auf dem Gebiet tribologischer Charakterisierungen Industrie und Forschung zur Verfügung (https://www.i-tribomat.eu/). Ein Aspekt hierbei ist eine tribologische Datenbank. Um die nötige Qualität der Daten sicherzustellen, sind vereinheitlichte Prozeduren erforderlich, in deren Auswirkungen dieser Vortrag einen Einblick gibt.
The focus of this study is to evaluate the influence of hydrogen on the friction and wear behavior of a wide range of polymer materials. Thereby, the tribological performance of filled und unfilled polymers from different suppliers were compared at room temperature in air and hydrogen gas (H2) as well as in liquid hydrogen at -235°C (LH2).
Increasing demand for alternatives to tungsten carbide (WC) cemented carbides as cutting tools, due to the health risks of their wear products WO3 and Co3O4. Niobium carbide (NbC) has a high potential, due to its high wear resitance, high hot hardness and melting point (3520°C), and low solubility in iron alloys.
The development of hydrogen technologies is a key strategy to reduce greenhouse gas emission worldwide. Power-to-Gas is a challenging solution, in which hydrogen and methane can be used in mobility, industry, heat supply and electricity generation applications. This presentation deals with the tribological behaviour of polymer materials in hydrogen and methane, both in gas and in liquefied form.
Renowned institutions in the field of tribology combine their testing and analytical capabilities with experts in materials/process information management technology to provide the respective Services in Europe (i-TRIBOMAT). This requires a centralized materials information management system or the standardised capture, consolidation and harmonization of tribological information.
In special cases of angle beam ultrasonic measurement – e.g. defect detection in hot solids as well as flow measurement of liquid gases or energy storage mediums – the applied transducer has to withstand extreme temperatures. Since the irradiation angle into the specific material is determined not only by wedge design, but also by the speed of sound in both the wedge material and the tested object, the developer must take into account the speed of the wave propagation in a wedge material over the whole temperature range of transducers application.
In this study we investigate the temperature dependence of the speed of longitudinal wave propagation in 10 different materials in the range from -200 °C to 400 °C. The investigated materials belong to different material classes (ceramics, glass, as well as ferrous and non-ferrous metals) and are all temperature-resistant up to at least 600 °C, and therefore applicable as wedge materials in an ultrasonic transducer for use at extreme temperatures.
The talk gives a historical introduction and introduces some of the biggest and most important research institutes in Germany dealing with tribology at Universities, scientific societies and companies. Some examples for research projects and focus areas are given. As an example for a research institute with a long history in tribological research the activities of BAM in Berlin are presented.
The tribological behavior of neat and filled PEEK and PEKK composites were compared in air and vacuum conditions. Very low friction and wear coefficient were obtained at low sliding speed while severe wear occurred at high speed. Experimental results are discussed by analysing the transfer film and wear debris.
Die BAM ist nahezu über die gesamte Wertschöpfungskette hinweg wissenschaftlich tätig. Von der sicheren und effizienten Wasserstofferzeugung (POWER-to-GAS), über die (Zwischen-)Speicherung von Wasserstoff in Druckgasspeichern bis hin zum Transport bspw. mittels Trailerfahrzeug zum Endverbraucher.
Komplettiert werden die Aktivitäten der BAM durch die sicherheitstechnische Beurteilung von wasserstoffhaltigen Gasgemischen, die Verträglichkeitsbewertung von Werkstoffen bis hin zur Detektion von Wasserstoffkonzentrationen über geeignete Sensorik, auch mittels ferngesteuerter Messdrohnen (sog. UAV-Drohnen).
Zudem untersucht die BAM proaktiv Schadensrisiken und Unfallszenarien für die Sicherheitsbetrachtung, um mögliche Schwachstellen aufzeigen und potenzielle Gefährdungen erkennen zu können.
In a first test series, the friction and wear properties of 6 polymeric candidate materials for application in LNG tribosystems were tested. The most favorable properties showed PTFE composite, filled with carbon fibers and PEEK, which showed low and stable friction and a wear coefficient in the order of 10-7 mm3N-1m-1. PTFE containing PEEK composites seem to be also appropriate for LNG applications. Admixtures of graphite as solid lubricant result in lower wear. Contrary, a lubricating mechanism of MoS2 was not observed. The PI-materials showed comparatively high friction and medium wear.
In a first test series, the friction and wear properties of 6 polymeric candidate materials for application in LNG tribosystems were tested. The most favorable properties showed PTFE composite, filled with carbon fibers and PEEK, which showed low and stable friction and a wear coefficient in the order of 10-7 mm3N-1m-1. PTFE containing PEEK composites seem to be also appropriate for LNG applications. Admixtures of graphite as solid lubricant result in lower wear. Contrary, a lubricating mechanism of MoS2 was not observed. The PI-materials showed comparatively high friction and medium wear.
The tribological characteristics of pure and graphite filled polymers were investigated in gaseous hydrogen at ambient temperatures and in LH2 at -253°C. It could be shown that the tribological properties of PI and PEEK materials is related to the formation of a transfer film. The influence of both hydrogen and cryogenic temperatures will be discussed in the presentation.
Copper, magnetite and graphite particles were mixed in order to observe their impact on the coefficient of friction (CoF) during pin-on-disc tests and on the tribofilm formation after testing. Pure magnetite powder provided a value of CoF of 0.4. Magnetite-copper mixtures tested at 400 °C revealed lower CoF values (~0.4) than those at room temperature (~0.6). Magnetite-graphite and magnetite-graphite-copper mixtures presented lower CoF values (~0.3). All systems formed a magnetite-based tribofilm and patches of metallic copper were found on the tribosurfaces of the mixtures containing copper. Carbon layers and graphite nanoinclusions were observed in the graphite mixtures. The incorporation of zirconia particles, a by-product of ball milling mixing, prevented the selective transfer of graphite and copper to the tribosurfaces of some of the samples.
Besides carbon, metal sulphides are used in every standard brake pad formulation as friction stabilisers. In order to investigate their impact, various powder mixtures were tribologically stressed in a pin-on-disc device in order to produce and test artificial third bodies. containing the three main components of a real friction film, namely magnetite, graphite and a metal sulphide of interest. Since the sliding behaviour is influenced by the relative humidity the powder mixtures are tested at low, medium and high moisture levels. The tests revealed that the presence of graphite dominates the friction behaviour as well as the humidity sensitivity.
The powders were prepared by either manual mixing or high energy ball-milling. Interestingly, all ball-milled blends provided coefficients of friction within the desired range for braking, which was attributed to the effect of zirconia particles from wear debris of the milling balls. The zirconia particles prevent the formation of solid lubricant films on the surfaces and support a homogeneous mixture of all constituents of the powder. Optimum brake performance is gained by an optimum combination of solid lubricants and abrasives.
Die Reibeigenschaften von PEEK-Materialien gegen Stahlscheiben wurden in Luft, Vakuum und Wasserstoffumgebung untersucht. Die Ergebnisse zeigen, dass reines PEEK umgebungsabhängig ist und die Desorption von Gasen im Vakuum zu hohen Verschleißraten führt. Die niedrigsten Verschleißraten sowohl in Vakuum als auch in einer Wasserstoffumgebung erzielen TiO2-Partikel. Ferner treten chemische Prozesse in den Materialien und im Tribokontakt auf und interagieren miteinander.
The magnetic plasma confinement system of the nuclear fusion experiment “Wendelstein 7-X”, which recently produced the first plasma, consists of 20 planar and 50 non-planar superconducting coils. To keep them precisely in position, these coils contact each other at special support elements. The supports are operated in high vacuum at a temperature of about 4 K, and when the magnetic field is ramped up, forces up to 1500 kN and sliding motion of some mm occurs. Because mechanical disturbances may cause severe failures, only low friction without any stick-slip behaviour is tolerable. In pre-tests a PVD-MoS2-coating had proven to be the optimum solution. It was tested with downsized samples in reciprocating motion in liquid nitrogen (T = 77 K) and liquid helium (T = 4,2 K). In long-term tests in liquid nitrogen this coating showed stable sliding for up to 14.900 friction cycles without coating failure. However, in liquid helium an unexpected stick-slip effect occurred, whose origin could not be clarified so far.
Sliding wear of martensitic steels in hydrogen – X30CrMoN15-1 and 100Cr6 – the role of water traces
(2016)
Initially the primary objective of the project has been the investigation of the influence of gaseous hydrogen on the wear of martensitic steels under heavy tribological stress. As a counter body an Al2O3 ball has been used because the material is inert and hard so that a low amount of wear was expected. If only the gas pressure is responsible for the absorption of hydrogen from the gas to pure α-iron it would require 15·105 MPa (~15 Mbar) to press 1 ppm into the material.
In the test series the Al2O3 balls showed in N2 and H2 atmosphere a higher wear compared to aerial experiments which showed a smaller wear track and a severer wear for the disc. Because of scattering and thereof following investigations it was shown that hydrogen has no noticeable influence but water traces in the gas are manipulating the outcome of the tests distinctly.
The composition and nanostructure of a beneficial tribofilm formed during sliding of a hybrid nanocomposite against steel were characterized comprehensively. A similar nanostructure was produced by high energy ball milling of the three identified tribofilm constituents: silica, hematite and graphite. By supplying powders to a pin-on-disc test it has been shown that neither silica, nor hematite, nor a mixture of both provide the low coefficient of friction (COF) observed for the hybrid composite. Only if graphite was blended with the oxides, the low COF was obtained. Thus, a film of finely dispersed stable inorganic wear products containing 15 vol% graphite provides low friction and wear in the considered case.
We applied a combination of Raman spectroscopy (RS) and cross-sectional transmission electron microscopy (X-TEM) to identify silicone oil residues and tribofilms at steel disc surfaces after tribological testing. Neither chemical cleaning nor mechanical removal of a 50 µm thick surface layer produced a surface without any silicone residue. Nevertheless, long-term tribological properties are not affected due to silicone degradation which has been proved by Raman spectroscopy. Excellent anti-wear and anti-friction properties of a nanocomposite at severe stressing conditions correlated with the formation of a silica-based tribofilm containing amorphous and graphite-like carbon nanoparticles. Since reliable carbon quantification by analytical TEM is difficult, RS is a useful complementary method for carbon identification at wear scars.
High performance polymer composites have been intensively investigated for tribological applications in air, but rarely in hydrogen environment. Author's previous benchmark of composites in liquid hydrogen (LH2) showed that graphite filled polymers have beneficial friction behaviour in this extreme condition. Therefore, further investigations have been undertaken in hydrogen environment. This paper presents first results obtained with polyimide composites filled with different types (natural, synthetic) and amounts of graphite in air, vacuum and hydrogen environments. A particular attention is taken to the influence of hydrogen on graphite as well as on the polymer matrix.
The influence of hydrogen environment on the friction and wear behavior of polyimide (PI) composites was investigated for two different PI-types (PI1 and PI2) filled with natural or synthetic graphite. Sliding tests were run against AISI 52100 steel and the worn surfaces as well as the transfer film were analyzed by means of SEM, EDX and Infrared Spectroscopy. Results indicate that the chemical structure of the polyimide has a major influence on the tribological behavior. While the friction of PI2 remains rather stable in all environments, PI1 showed very low friction in hydrogen without any lubricant. The lubricity of graphite was found to be more effective in hydrogen than in moist air.
Die tribologischen Eigenschaften von graphitgefüllten Polyimiden gegen Stahl 100Cr6 wurden an Luft, im Hochvakuum (l0⁻ ³ Pa) und in Wasserstoffumgebung bei verschiedenen Drücken (10³ Pa, 10⁴ Pa und 10⁵ Pa) untersucht. Zwei unterschiedliche Polyimid-Typen wurden eingesetzt, wobei Typ und Menge des Graphits variiert wurden.
Die Experimente wurden bei 3,1 MPa Kontaktdruck und einer Gleitgeschwindigkeit von 0,2 m/s bzw. 1 m/s durchgeführt. Die verschlissenen Oberflächen und die Morphologie des Materialübertrags auf die Stahl-Gegenfläche wurden mittels Lichtmikroskopie, REM, TEM und FTIR untersucht. Die Untersuchung zeigt, dass sowohl die Matrix als auch der Graphitanteil einen deutlichen Einfluss auf das Reibverhalten von Verbundwerkstoffen in Wasserstoffumgehungen haben können.
A modified pin-on-disc test was applied to determine tribological properties of typical brake pad constituents. Ball-milling of these ingredients together with iron oxide and graphite provided model materials displaying the main features of real third bodies. Solid lubricants like graphite affected the friction and wear behaviour of Fe3O4 powders considerably whereas further addition of hard nanoparticles induced only minor effects. This was corroborated by comparison with modelling results. MoS2 played a dual role. Depending on special conditions, this ingredient either reduced or increased friction. The latter could be explained, after nanoscopic characterization, by oxidation and destruction of the wear-protecting tribofilm.
Starke Magnetfelder, wie sie z.B. für die Magnetresonanztomografie (MRT) notwendig sind, werden durch supraleitende Spulen erzeugt, die mit Flüssighelium auf eine Temperatur von -269°C gekühlt werden. Die Reibungswärme, die z.B. bei kleinsten Bewegungen zwischen der Spule und deren Stützstruktur entsteht, kann bewirken, dass die kritische Temperatur des Supraleiters lokal überschritten wird und ein normalleitender Bereich entsteht. Aufgrund der bei Normalleitung entstehenden jouleschen Wärme kann sich dieser Bereich weiter erwärmen und schnell ausbreiten. Dieser Vorgang wird als Quench bezeichnet und führt zum schlagartigen Verdampfen des extrem teuren Kältemittels und zu Betriebsunterbrechungen von mehreren Tagen.
Da diese Quenche durch Reibungswärme verursacht werden, ist es notwendig, das Reibverhalten der beteiligten Werkstoffe so zu optimieren, dass kein kritischer Betriebszustand erreicht wird. Dies betrifft in erster Linie Polymerfolien, die zur elektrischen Isolierung zwischen der Spule und der Stützstruktur notwendig sind. Neben zu hoher Reibung allgemein müssen ausgeprägte Haftreibungsspitzen und StickSlip-Effekte vermieden werden. Mit
diesem Ziel wurde das Reibverhalten von PTFE-, PET- und Pl-Folien bei tiefen Temperaturen und den für diese Anwendung typischen niedrigen Gleitgeschwindigkeiten untersucht. Es zeigte sich, dass die Reibung zwischen Polymeroberflächen in Flüssighelium allgemein höher, aber stabiler als in Flüssigstickstoff ist. Allerdings hängt das Reibverhalten erheblich von der Werkstoffpaarung ab. Der Stick-Slip-Effekt nimmt bei allen untersuchten Polymer-Polymer-Paarungen mit wachsender Kontaktpressung zu. PET gegen PET hat das ungünstigste Reibverhalten und sollte bei hohen Pressungen vermieden werden. Zum Vergleich getestete Paarungen von Polymeren gegen Aluminium zeigten deutlich günstigeres Reibverhalten ohne signifikanten Stick-Slip. Deshalb sollte bei derartigen Anwendungen sichergestellt werden, dass die Gleitebene zwischen Polymer- und Metalloberfläche liegt.
In order to obtain a better understanding of the role of tribofilms during automotive braking, their structures were investigated and the essential features identified.
Next, different ingredient combinations were studied by preparing some model materials with simpler compositions than real tribofilms. A test method was developed for verifying the tribological properties of the model materials and for comparison with results obtained with numerical sliding simulations of such structures. Prerequisites of good brake Performance properties were identified. Although the coefficient of friction could be varied in a wide ränge, smooth sliding conditions could only be achieved with values smaller than 0.4. Tests with artificial third body powders turned out to be useful as screening method for the selection of raw materials for brake pad formulations.
The tribological behaviour of MoS2/ta-C double layer coatings deposited by Laser-Arc technology was investigated in vacuum and air. In vacuum environment, the friction coefficient against steel balls varies between 0.005 and 0.02 depending on the contact pressure. At high contact pressures, the friction coefficient is as low as 0.005 and the life time between 340,000 and 500,000 cycles. Furthermore, it is shown that a ta-C base layer improves the performance of MoS2 coating.
Surface analyses were performed before and after the tribological tests by means of SEM, EDX, XRD, and TEM. They show that in the top layer beneath the sliding surface crystallization of the initially quasi-amorphous MoS2 took place. TEM images also verified an orientation of the basal MoS2-lattice planes parallel to the surface.
MoS2 is a suitable solid lubricant for environments free of oxygen or water vapor (i.e. vacuum). Humid air degrades film properties due to oxidation accompanied by high wear and increasing coefficients of friction. The present study aims at the further development of sputtered pure MoS2 coatings, extending their applicability to varying environmental conditions by increasing the resistance against humidity. The systematic coating development process is supported by using an experimental Box–Behnken design with variations of the deposition parameters cathode voltage, target/substrate distance, temperature and argon gas pressure. In contrast to common one-factor-at-a-time (OFAT) studies, this approach enables a determination of interactions between deposition process parameters and tribological–mechanical MoS2 film properties. The tribological improvement focuses on a maximization of wear resistance in air and vacuum measured in ball-on-disk experiments. The evaluated mechanical properties are hardness, elastic modulus and residual stresses. These stresses were determined by the substrate curvature method. The study reveals that the residual stress state in the films and the hardness-to-modulus ratio are crucial for their tribological performance in humid air and vacuum environments. After a detailed determination of the relationships between deposition conditions and film properties, some selected microstructural analyses are presented which show that a substantially basal orientation of the lattice has positive effects on wear but also causes anisotropic film properties which result in fissile fracture of the coating if strong shock or point loads occur.
Der Festschmierstoff Molybdändisulfid ist insbesondere für Extremanwendungen ein gerne eingesetzter Werkstoff, problematisch ist jedoch der negative Einfluss von Feuchtigkeit. Bei mittels PVD-Verfahren abgeschiedenen MoS2-Schichten ergibt sich jedoch die Möglichkeit, durch Anpassung der Beschichtungsparameter vorwiegend basal ausgerichtete Schichten herzustellen, die auch an Luft ein verbessertes tribologisches Verhalten zeigen.
Superconducting magnets are susceptible to quenching, even with the smallest amounts of energy disturbances due to the extremely low thermal capacity of materials at 4.2 K. Hence, small mechanical disturbances resulting in frictional heating can be sufficient to exceed the wire’s critical temperature, causing it to quench. Unfortunately, relative motion between surfaces in the magnet System is inevitable due to various forces present in the System, including winding pretension, differences in material thermal contraction and the large electromagnetic forces. Typically insulating polymers are present at this interface to achieve the required electrical insulation requirements.
Ensuring a sustainable energy supply is currently one of the most important areas for industry and research institutions. Hydrogen technology is a promising candidate, but its broad extension requires extremely high reliability and safety in all areas for common applications as automobiles and stationary fuel cells. Particularly components containing tribosystems are critical parts.
Polymers are extensively used for sliding systems in cryogenic applications because of their favourable friction and wear behaviour in the absence of external lubrication. Since important new technologies are based on applications under extreme conditions, such as at low temperatures, new requirements on material properties, in particular regarding their operability and reliability, must be met. Up to now, most tribological investigations have been carried out in inert cryogens or cryogenic gas (He, N2). Few experiments have been performed in vacuum environment at cryogenic temperatures. Rarely were testing in reactive media, such as LH2 or LOX. Due to the wide range of operating conditions in cryogenic applications, it is difficult to state general rules. Therefore, this chapter tends to give an overview on theories and experimental studies on polymer tribology at cryogenic temperatures.
The solid lubricant molybdenum disulfide is a well known material for extreme conditions where conventional oil or grease lubrication is not feasible (vacuum, high pressures). However, under reactive environments e.g. high humidity or hydrogen MoS2 is prone to premature failure. By using a PVD process, deposition parameters can be optimized to gain coatings with a more textured structure orienting the basal planes parallel to the Substrate surface, A similar concept has been used by Koch et al. for coatings developed to withstand the extreme operational conditions of the WENDELSTEIN W7-X fusion experiment. Therefore, an improved tribological behavior even under adverse conditions can be achieved.
In a future energy supply system based on renewable sources hydrogen technology will play a key role. Because the amount of energy from renewable sources, such as wind or solar power, differs seasonally and regionally, an energy storage method is necessary.
Hydrogen, as an environmentally friendly energy carrier, can fill this gap in an ideal way, in particular for mobile applications (Wurster et al., 2009). Already today, in Germany the amount of hydrogen as a byproduct in chemical industry is enough for fuelling about 1 Mio passenger cars1. Excess electrical power can be used to produce hydrogen by electrolysis. On demand, this hydrogen can be used for mobile or stationary fuel cells. Beside this new developing technology, hydrogen is used as fuel for rocket engines and in chemical industry since a long time. Table 1 comprises some physical parameters of hydrogen. It can be seen that hydrogen gas has a very low density which makes storage at high pressure or in liquid form (LH2) necessary.