Innovative low transformation temperature (LTT) welding filler materials are featuring a characteristic chemical composition which favors the formation of martensite at comparatively low temperatures. This permits deliberate adjustment of welding residual stresses. Even though numerous investigations can be found in the literature on this issue, they provide only little insight into the interaction between phase transformation and resulting welding residual stresses. For this purpose, a component weld test was performed in a special large-scale testing facility. The results illustrate that the desired residual stress control by using LTT alloys is actually feasible. With increasing shrinkage restraint, however, higher tensile residual stresses are formed in transverse direction of the weld. By contrast, the residual stress level in longitudinal weld direction is nearly independent of the restraint conditions. On-line stress analysis revealed that the amount of stress reduction during cooling of the individual weld runs is dependent on the weld volume undergoing phase transformation. Overall, evidence was furnished that the approach of residual stress engineering by LTT alloys is suitable even in the case of large-scale multilayer welding.
Low Transformation Temperature (LTT) alloys were developed in order to control the residual stress development by the martensitic phase transformation already during cooling of the weld metal. The positive effect of such LTT alloys on the mitigation of detrimental tensile residual stresses during welding has already been confirmed on the basis of individual laboratory tests. Within the current project it was experimentally investigated whether the phase transformation mechanisms are effective under increased restraint due to multi-pass welding of thicker specimens. The local residual stress depth distribution was analyzed non-destructively for V-type welds processed by arc welding using energy dispersive synchrotron X-ray diffraction (EDXRD). The use of high energy (20 keV to 150 keV) EDXRD allowed for the evaluation of diffraction spectra containing information of all contributing phases. As the investigated LTT alloy contains retained austenite after welding, this phase was also considered for stress analysis. The results show in particular how the constraining effect of increased thickness of the welded plates and additional deposited weld metal influences the level of the residual stresses in near weld surface areas. While the longitudinal residual stresses were reduced in general, in the transition zone from the weld to the heat-affected zone (HAZ) compressive residual stresses were found.