Two fly ash-based geopolymer concretes with quartz aggregates or with expanded clay (lightweight) aggregates were exposed to the ISO 834-1 standard fire curve in a small-scale fire test set-up. Acoustic emission measurements during fire exposure and subsequent cooling were employed to study spalling events and cracking during the tests. Optical microscopy and additional acoustic measurements were conducted after the testing to better understand the crack propagation in the samples. The testing revealed that neither of the concretes were susceptible to spalling, which is particularly notable for the concrete with quartz aggregates, as it is a high-strength concrete. This behavior is attributed to the relatively high permeability of the concretes and their low amount of chemically bound water. Significant crack formation was detected only around the temperature of the alpha–beta quartz transition (573 °C) and on cooling. Because of aggregate deformations at the quartz transition temperature, deterioration after heating was more significant in the geopolymer concrete with quartz aggregates. Crack formation also occurred in the concrete with expanded clay aggregates, caused by shrinkage of the geopolymer paste on cooling. Acoustic emission measurements proved to be a valuable tool to investigate processes during high temperature exposure.
Thermo-mechanical and spalling behavior of normal weight and lightweight geopolymer concretes
(2016)
The mechanical and microstructural properties of two geopolymer concretes, produced with either quartz aggregate or expanded clay aggregate, were assessed before, during and after high-temperature exposure up to 750 °C in order to better understand the engineering properties of the material. SEM investigations were also undertaken to better understand the observed changes in the mechanical properties. It was found that dehydration of capillary water caused micro-cracking and strength losses at temperatures ≤ 300 °C. At higher temperatures (T ≥ 500 °C) sintering promoted strength increases, leading significant strength advantages over conventional concretes. Stress-mechanical strain curves, which are the basis of the fire design of concrete structures, were determined. In addition, the two geopolymer concretes where exposed to the ISO 834-1 standard fire curve in a small-scale spalling test set-up. Acoustic emission measurements during, and acoustic measurements and optical microscopy after heat exposure were employed to investigate crack formation during the tests. Both concretes did not spall, which is attributed to their comparatively high permeability and their low amount of chemically bound water. Significant crack formation was detected only around the temperature of the α–β quartz transition (573 °C) and on cooling. Because of aggregate deformations at the quartz transition temperature, deterioration after heating was more significant in the geopolymer concrete with quartz aggregates. Crack formation occurred also in the concrete with expanded clay aggregates, presumably caused by shrinkage of the geopolymer paste on cooling.