Flame retarded polymeric materials are used in various applications in which a certain fire behavior is demanded. Protection goals are defined, such as limited flammability in terms of hindered sustained ignition or limited contribution to a fire, and these protection levels are tested with defined specimens or components in defined fire scenarios, that is to say, different fire tests. Passing a specific fire test by meeting whatever its demands is often the most important development goal, so the parameters of the different fire tests vary widely to emphasize different fire properties. Some fire tests are used to screen or provide a general assessment of flame retardant polymers during development, while other fire tests and tailored experiments are performed to address special phenomena or understand the flame retardancy modes of action. For all fire testing, the devil is in the details – demanding know-how and crucial efforts to manage the quality of investigations and advanced interpretation. This chapter aims to offer a structured overview of all these aspects.
Zur Charakterisierung von Brandschutzbeschichtungssystemen für Gas-
Lagertanks ist ein Großbrandversuch erforderlich. Zur Ermittlung der produktspezifischen Beschichtungsdicke sind Plattenbrandversuche notwendig. Für Brandprüfungen existieren verschiedene Brandkurven (z.B. ETK, Hydrocarbonkurve, Schwelbrandkurve, BAM-Kurve) um Prüfmuster je nach Anwendungsfall zu zertifizieren. Diese Brandkurven unterscheiden sich hinsichtlich des Temperaturgradienten. Zur Gewährleistung der Übertragbarkeit der BAM-Prüföfen (Kleinprüfstand DIN 4102-8 (Klep) und 1-m³ Ofen) auf die NORM ISO 21843 (2018-09) ist es erforderlich einen Wärmeintrag von 90 – 120 kW/m² in das Prüfmuster zu garantieren.
In order to investigate the heat fluxes over a wide range of surface temperatures during a propane gas fire test and to get information about local fire impact a fire reference package, representing the outer geometry of a specific type of transport cask for radioactive waste, was designed. A closed steel sheet cylinder with a wall thickness of 10 mm was chosen as fire reference package. The cylinder was filled with refractory insulation material and instrumented with thermocouples distributed all over the cylinder. The local steel sheet temperatures measured allow the determination of local as well as global heat fluxes as a function of time and surface temperature.
With this fire reference package three open-air propane gas fire tests were performed at BAM’s open air fire test stand. The flame exposure time period was changed for the different fire tests. Furthermore, the wind conditions changed between and during the tests. Test stand parameters like wind shield location and propane gas volume flow were chosen constant for the three tests. The test results were used to determine the changes of heat flux into the fire reference package in relation to the package surface temperature. This data also allows the calculation of local characteristics of the propane gas fire as there are the flame temperature, the fire convection coefficient and the radiation exchange coefficient in a first approach. The recently conducted tests provide an initial picture of local fire characteristics of the propane gas fire test facility. The test shows that the propane gas fire covers the IAEA-fire over a wide range of surface temperatures with the chosen test stand parameters.
The presentation gives an overview of actual research adtivities in the field of flame retardant polymers. Details are selected illuminating the scientific topic beyond the state of the art. Different concepts are illustrated with own results obtained in different Research projects over the last 15 years.
This presentation focusses on the thermal test of a typical storage container design for the German final storage repository KONRAD. The preparation of the container, the conduction of the fire test itself and results like the temperature evolution and as-sumptions for thermal material properties are shown.
As thermal test final storage containers have to be exposed to a fire of 800 °C (1472 °F) for 1 hour according to the final storage conditions provided by the federal com-pany for radioactive waste disposal (BGE). The here discussed cask contains a steel covered concrete layer of a thickness of 100/150 mm. Heating up concrete is a highly nonlinear process since the vaporization of residual water consumes high amounts of thermal energy and produce vast amounts of steam.
The constantly measured temperatures provide the basis to adjust common models of thermal properties for concrete esp. for FEAs. Finally in a later step this will allow predictions of similar designed container with different sizes.
Accident safe packages for the transport of spent nuclear fuel and high-level waste shall fulfil international IAEA safety requirements. Compliance is shown by consecutive mechanical and thermal testing. Additional numerical analysis are usually part of the safety evaluation. For damage protection some package designs are equipped with wood filled impact limiters encapsulated by steel sheets. The safety of these packages is established in compliance with IAEA regulations. Cumulative mechanical and fire tests are conducted to achieve safety standards and to prevent loss of containment. Mechanical reliability is proven by drop tests. Drop testing might cause significant damage of the impact limiter steel sheets and might enable sufficient oxygen supply to the impact limiter during the fire test to ignite the wood filling. The boundary conditions of the fire test are precisely described in the IAEA regulatory. During the test the impact limiter will be subjected to a 30 minute enduring fire phase. Subsequent to the fire phase any burning of the specimen has to extinguish naturally and no artificial cooling is allowed. At BAM a large-scale fire test with a real size impact limiter and a wood volume of about 3m³ was conducted to investigate the burning behaviour of wood filled impact limiters in steel sheet encapsulation. The impact limiter was equipped with extensive temperature monitoring equipment. Until today burning of such impact limiters is not sufficiently considered in transport package design and more investigation is necessary to explore the consequences of the impacting fire. The objective of the large scale test was to find out whether a self-sustaining smouldering or even a flaming fire inside the impact limiter was initiated and what impact on the cask is resulting. The amount of energy, transferred from the impact limiter into the cask is of particular importance for the safety of heavy weight packages. With the intention of heat flux quantification a new approach was made and a test bench was designed.
The vessel wall response shows a good agreement between the numerical predictions of and experimental data using the limit load approach. Further work is continuing to understand the thermohydraulic response and the boundary conditions for material modelling. As shown in figure 2 there was one BLEVE of a bare tank containing a PRV, highlighting the risk of serious consequences if models are inaccurate. The behavior of partly coated tanks were similar to the bare tank.
The rapid mass calorimeter based on reduced‐size specimens is proposed for accelerated fire
testing and put up for discussion, particularly for flame retarded polymeric materials. A mass loss
calorimeter is combined with a semiautomatic sample changer. Experiments on specimens of
reduced size were conducted on poly(methyl methacrylate), poly(propylene), polyamide 66,
poly(ether ether ketone), and pine sapwood square samples with edge lengths of 100, 75, 50,
25, 20, and 10 mm. Specimens of 20 × 20 mm2 were selected to achieve a crucial reduction in
specimen size and a measuring protocol developed. A total of 71 different polymeric materials
were investigated in the rapid mass calorimeter and cone calorimeter for comparison and several
materials with different heat release rate characteristics in the pyrolysis combustion flow calorimeter to test this additional screening method as well. The important fire properties obtained in the rapid mass calorimeter show reasonable correlation with the cone calorimeter results but also with the oxygen index. All in all, the rapid mass calorimeter produces reliable and meaningful results and, despite acceleration and size reduction, still allows for a certain degree of burning behavior interpretation. Material savings of 96% and time savings of around 60%‐70% are achieved compared to measure cone calorimeter.
In North America certain hazardous materials are transported in rail tank cars that must be able to survive an engulfing liquid hydrocarbon pool fire for 100 minutes without rupture. To meet this requirement these tanks are normally equipped with pressure relief valves (PRV) and some form of thermal insulation or thermal protection (TP).
These tanks sometimes have non-accident releases (NAR) due to unwanted activation of, or leakage from the pressure relief valves (PRV). These NARs are a nuisance for Industry and for this reason, the industry now wants to remove the PRVs from certain tanks. This is known as total containment and is common practice in Europe. However, Europe does not have a 100 minute fire survival requirement. This paper is about a series of fire tests of 1/3 rd linear scale US DOT 111 Tanks cars. The 2.4 m3 vessels were subjected to fully engulfing fires generated by liquid propane fueled burners.
Dripping and melt flow of the pyrolysing polymer melt can be both a benefit and a detriment during a fire. Well-adjusted melt flow and dripping are regularly beneficial to pass small-scale fire tests. Flame retardants often significantly change the melt viscosity of polymeric materials. The influence of certain flame retardants on the dripping behaviour of four commercial polymers is analysed based on experimental monitoring of the mass loss due to dripping, drop size and drop temperature as a function of the furnace temperature applied to a rod-shaped specimen. Investigating the thermal transition, thermal and thermo-oxidative decomposition, as well as the viscosity of the polymer and collected drops accomplish the work and connects dripping and melt flow with physical and chemical processes. Various flame retardant mechanisms affect the dripping behaviour in the UL 94 test. A changed viscosity and reduction in decomposition temperature also play a major role.