Datei im Netzwerk der BAM verfügbar ("Closed Access")
Filtern
Dokumenttyp
- Zeitschriftenartikel (5)
- Beitrag zu einem Tagungsband (5)
- Vortrag (5)
- Sonstiges (1)
- Posterpräsentation (1)
Schlagworte
- AKR (7)
- ASR (6)
- Degradation (5)
- Fatigue (5)
- Baustoffe (4)
- Pavement (4)
- Ermüdung (3)
- Alkali-Kieselsäure-Reaktion (2)
- Building Materials (2)
- Concrete (2)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (10)
- 7.1 Baustoffe (10)
Eingeladener Vortrag
- nein (5)
ln most of the ASR-test procedures, the expansion of concrete or mortar specimens is used as an indicator to assess the ASR-potential of an aggregate or a specific concrete mix. For these tests, the specimens are stored in an ASR-provoking environment, where the reaction is accelerated by elevated temperature and humidity. To measure the length change, the storage must be interrupted for at least a few minutes. Düring the 60 °C Concrete Prism Test (60 °C-CPT), the specimens are cooled down to 20 °C for 24 hours, to ensure the same hygrothermal conditions for every measurement. This limits the number of measurements during the test period and may lead to additional effects, that probably influence the expansion development.
With a recently developed device, it is possible to continuously monitor the expansion ofprisms without interrupting the ASR-provoking storage. Due to the dense database of this automated test, the results can contribute to a better understanding of the ASR-process. This study compares results of the automated and conventional 60 °C-CPT. Tests of different aggregates showed, that the results of the automated and conventional test are consistent, but the expansions during the conventional test are generally higher. Preliminary results led to the conclusion, that the cooling for the measurements leads to additional expansions. Therefore, a modified threshold should be discussed for the automated 60 °C-CPT.
Einfluss einer druckschwellinduzierten Degradation von Fahrbahndeckenbeton auf die schädigende AKR
(2020)
In den letzten Jahren sind im deutschen Bundesautobahnnetz verstärkt Schäden an vor 2005 errichteten Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden. Neben dem AKR-fördernden Einfluss von alkalihaltigen Taumitteln werden Fahrbahndecken zyklischen mechanischen Belastungen infolge des Verkehrs und Zwangsspannungen durch klimatische Einwirkungen ausgesetzt. Solche mechanischen Belastungen werden bisher in keinem AKR-Prüfverfahren berücksichtigt. Die zyklischen Belastungen können zu einer Degradation des Betongefüges führen, die ggf. einen AKR-fördernden Einfluss hat. Dieser Beitrag stellt Untersuchungen vor, die zur Beantwortung der Frage nach dem Einfluss einer zyklischen mechanischen Belastung auf den AKR-Schadensprozess beitragen. Dabei wird der Hypothese nachgegangen, dass die ermüdungsinduzierte Degradation zu einer Erhöhung des Stofftransports führt.
Dieser hat einen Einfluss auf die AKR-Schadensentwicklung, da die Reaktionspartner zunächst zum Reaktionsort transportiert werden müssen. Daher wird angenommen, dass sich mit dem Stofftransport auch die AKR-Schädigung verstärkt. Es werden Betonproben aus typischen Fahrbahndeckenbetonen einer vorgeschalteten zyklischen Druckschwellbelastung ausgesetzt.
Die Degradation infolge der Vorbelastung wird simultan mittels ZfP-Verfahren charakterisiert. Anschließend werden die Auswirkungen der zyklischen Vorschädigung auf den Stofftransport sowie auf die AKR vergleichend an Prüfkörpern ohne und mit Vorschädigung untersucht. Die Ergebnisse lassen den Schluss zu, dass die zyklische Vorschädigung sowohl den Stofftransport als auch die AKR fördert.
Alkali-Kieselsäure-Reaktion in Betonfahrbahndecken unter Berücksichtigung von Verkehr und Taumitteln
(2019)
In Betonfahrbahndecken treten häufig Schäden auf, welche mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden. Obwohl die Hintergründe einer solchen AKR intensiv untersucht wurden, gibt es bei Betonfahrbahndecken besondere Randbedingungen, welche die Schadreaktion signifikant erhöhen können. Diese sind vor allem die Überlagerung der mikrostrukturellen Degradation durch Verkehrsbeanspruchung mit externer Alkali-Zufuhr durch Taumittel. Bisherige Untersuchungen der AKR beschränkten sich auf die Ausgangsstoffe (Gesteinskörnung, Zement, Bewertung des Betons), wobei die besonderen Randbedingungen außer Acht gelassen wurden. Betonfahrbahndecken sind zyklischen Belastungen aus Verkehr und Witterungsbedingungen ausgesetzt.
In einem gemeinschaftlichen Forschungsprojekt wurden die verschiedenen, gegenseitig voneinander abhängigen, Einflussfaktoren auf eine schädigende AKR in Betonfahrbahndecken sowohl experimentell untersucht als auch numerisch modelliert. Auf Mikro-Ebene wurden die AKR-bezogenen Transportprozesse innerhalb der Gesteinskörnung, sowie die Gelbildung und der Ionen-Transport, untersucht. Auf Meso-Ebene fokussierte das Projekt auf die Charakterisierung der durch zyklische Belastung induzierten Schädigung im Mikrogefüge des Betons. Des Weiteren wurde das Transportverhalten in ein derart geschädigtes Betongefüge mit und ohne Berücksichtigung des zusätzlichen Einflusses überrollender Reifen beschrieben und dessen Auswirkung auf eine AKR analysiert. Schließlich wurde auf Makro-Ebene das Risiko eines AKR-bedingten Schadens bewertet. Einige ausgewählte Ergebnisse werden in diesem Beitrag dargestellt.
Der 60 °C-Betonversuch ist eine in Deutschland und international verbreitete Methode um die Empfindlichkeit von Gesteinskörnungen und Betonen hinsichtlich einer Alkali-Kieselsäure Reaktion (AKR) zu prüfen. Dieser Beitrag stellt eine neuentwickelte automatisierte Variante der Prüfmethode in einem Minireaktor vor. Dabei werden die Dehnungen von Betonprismen nicht, wie beim konventionellen Test manuell, sondern automatisch in entsprechend ausgerüsteten Prüfbehältern gemessen. Neben einer Reduzierung des Messaufwands bringt die automatisierte Prüfung im Minireaktor weitere Vorteile. Die Dehnungssignale werden, anders als bei der konventionellen Messung, quasi-kontinuierlich aufgezeichnet und bilden das Expansionsverhalten der Prismen detailliert ab. Außerdem bleiben Unterbrechungen der AKR-provozierenden Lagerung aus, die bei der konventionellen Prüfung notwendig sind. Im Beitrag werden die automatisierte und konventionelle Prüfung anhand der Dehnungen von Prismen zweier Gesteinskörnungen verglichen. In Übereinstimmung mit vorhergehenden Untersuchungen sind im Minireaktor gemessene Dehnungen systematisch kleiner als manuell gemessene. Als mögliche Ursache werden Unterschiede im Auslaugverhalten experimentell untersucht. Zur Überprüfung der Einstufung der zwei Gesteinskörnungen erfolgen außerdem Referenzprüfungen in der Nebelkammerlagerung bei 40 °C.
In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces that can be attributed to the alkali-silica reaction (ASR). The effects of mechanically-induced damage resulting from cyclic traffic and climatic loading have previously not been taken into consideration while developing ASR test procedures. Therefore this contribution investigates the influence of fatigue mechanical loading on the ASR.
The susceptibility of concrete structures due to alkali–silica reaction (ASR) can be assessed by means of ASR concrete prism testing at 60 °C, according to RILEM AAR 4.1. There, expansion of concrete prisms indicates alkali-reactivity of the examined concrete mix. This work applies in situ expansion measurement to accelerated concrete prism testing. Automated measuring facilitates both storage without the usually necessary interruptions for manual measurement and acquisition of quasi-continuous expansion data. A comparative experimental programme showed that conventional testing resulted in stronger expansion and leaching of alkalis than automated testing. Experimental simulation of interruptions, typically associated with manual measurements in conventional testing, could prove the influence of these cooling–heating cycles. Auxiliary measurement of acoustic emissions and ultrasonic velocity helped characterising mechanisms such as hydration and cracking, which also influence prism expansion. The proposed modification of the measurement procedure provides an extended basis to analyse expansion mechanisms.
In concrete pavements, damages occurred which are related to an Alkali-Silica-Reaction (ASR). Although the background for such an ASR has been studied extensively, special conditions in pavements increase this reaction significantly. These are especially the superposition of microstructural degradation caused by cyclic loading with an external alkali supply. Previous investigations of ASR focused mainly on the material itself (aggregates, cements, assessment of the concrete) while these special circumstances have not been considered. Concrete pavements are subjected to cyclic loadings by traffic and climate changes.
Within cooperative research projects the different interdependent influencing factors for a damaging ASR in concrete pavements are studied by experiments as well as by numeric modelling. On the micro-level the ASR-related processes within the aggregate, such as gel-formation or ion-transport, are investigated. On the meso-level, the project focuses on the characterization of degradation effects in the concrete microstructure due to cyclic loading. Further, special attention is paid to the transport behavior of fluids in such pre-damaged concrete structures with and without the effect of overrunning tires as well as the impact on the ASR itself. Finally, on the macro-level the risk of an ASR-damage is assessed.
Die vorstehend dargestellten Untersuchungen lassen sich wie folgt zusammenfassen:
• Mit dem für die mechanische Vorschädigung entwickelten Versuchsstand und gewählten Prüfregime können die für die ermüdungsinduzierte Schadensevolution typische stabilisierende und stabile Phase in der auf Zug beanspruchten Betonrandzone gut abgebildet werden. So wurde dort zum Beispiel, ausgehend von dem hier gewählten praxisnahen Belastungsregime, mit Ultraschall in der Ruhephase durch das Trockenschwingen ein maximaler Abfall des relativen dynamischen E-Moduls von ca. 8 - 10 % ermittelt.
• Mit aufbauenden kapillaren Aufsaugversuchen wurde gezeigt, dass die erzeugte Betondegradation zu einer moderaten Erhöhung der Aufnahme des Prüfmediums führt.
• Zur Bewertung der Auswirkungen einer alleinigen Vorschädigung (Trockenschwingen) auf die schädigende AKR mittels Performance-Prüfung ist die Klimawechsellagerung aufgrund der einseitigen Tausalzbeaufschlagung am besten geeignet. Die hier ermittelten Dehnungsverläufe lassen auf einen moderaten Einfluss der mechanischen Vorschädigung auf die AKR schließen.
• Die zusätzlich im Kontext der Nasschwingversuche durchgeführten 60°C Betonversuche zeigen, dass die zyklische Beanspruchung vor und nach dem Aufbringen der Tausalzlösung die schädigende AKR gleichfalls moderat erhöht.
In derzeit laufenden ergänzenden Untersuchungen wird der separate Einfluss der ermüdungsinduzierten Rissbildung auf die schädigende AKR an homogen, stärker geschädigten Prüfkörpern mit einem hohen inneren AKR-Schädigungspotenzial im 60°C Betonversuch grundhaft analysiert. Zusätzlich wird gegenwärtig der Einfluss der degradierten Betonrandzone auf die Dehnungsverteilung an großformatigen Prüfkörpern
über die Höhe im 40°C Betonversuch vertiefend für die makroskopische Modellierung untersucht.
Fatigue induced degradation in pavement concrete and its effect on the alkali-silica reaction
(2018)
In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces that can be attributed to the alkali-silica reaction (ASR). In view of the often drastically reduced service life of road surfaces due to ASR, research activity in this field has notably increased. Alongside preventative measures in concrete technology i.e. the usage of low-alkali cements, the main research focus up to now has been on the development of performance-oriented testing procedures for ASR prevention. The effects of mechanicallyinduced damage resulting from cyclic traffic and climatic loading have previously not been taken into consideration.
The assessment of the myriad degradation and transport processes necessary for an understanding of these effects requires close interaction between experiments and corresponding multi-scale models. This contribution is focused on the experiments utilizing innovative testing techniques. The research is founded on a series of fatigue tests performed on large-scale beams with simultaneous tracking of the degradation process using non-destructive evaluation methods. Subsequently, smaller test specimens were extracted from the predamaged beams for further experiments. These experiments included investigation of the influence of fatigue-induced cracks on moisture and alkali transport. Subsequent storage of the small-scale test specimens, with and without cyclic pre-damage, in an ASR-conducive environment then provided initial findings on the influence of fatigue-induced degradation on the ASR.
The results show that the degradation process can be well observed with the test Setup developed for the fatigue experiments. Further, a small but noticeable increase of mass Transport due to fatigue-induced degradation was measured, which correspondingly indicated an increased ASR damage potential.
Fatigue induced degradation in pavement concrete and its effect on the alkali-silica-reaction
(2018)
In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces that can be attributed to the alkali-silica reaction (ASR). In view of the often drastically reduced service life of road surfaces due to ASR, research activity in this field has notably increased. Alongside preventative measures in concrete technology i.e. the usage of low-alkali cements, the main research focus up to now has been on the development of performance-oriented testing procedures for ASR prevention. The effects of mechanicallyinduced damage resulting from cyclic traffic and climatic loading have previously not been taken into consideration.
The assessment of the myriad degradation and transport processes necessary for an understanding of these effects requires close interaction between experiments and corresponding multi-scale models. This contribution is focused on the experiments utilizing innovative testing techniques. The research is founded on a series of fatigue tests performed on large-scale beams with simultaneous tracking of the degradation process using non-destructive evaluation methods. Subsequently, smaller test specimens were extracted from the predamaged beams for further experiments. These experiments included investigation of the influence of fatigue-induced cracks on moisture and alkali transport. Subsequent storage of the small-scale test specimens, with and without cyclic pre-damage, in an ASR-conducive environment then provided initial findings on the influence of fatigue-induced degradation on the ASR.
The results show that the degradation process can be well observed with the test Setup developed for the fatigue experiments. Further, a small but noticeable increase of mass Transport due to fatigue-induced degradation was measured, which correspondingly indicated an increased ASR damage potential.