Acrylic acid-styrene copolymer films were deposited plasma-chemically more gently using the pulsed plasma mode instead of the continuous mode, with linear and some slightly branched chains and marginal crosslinking.
Then, the styrene unit of copolymers was wet-chemically sulfonated by chlorosulfuric acid. On exposure to air, the formed 4-chlorosulfonic acid groups hydrolyze to sulfonic acid groups (-SO3H).
FTIR, XPS and broadband dielectric spectroscopy were employed to characterize the composition, the structure, the functional groups, and the electrochemical performance for the copolymers. A high concentration of sulfonic acid-containing groups was obtained in the sulfonated PS sample. The values of the DC conductivity DC for the sulfonated sample of the AA/S copolymer are ca. five orders of magnitude higher than that of the not-sulfonated copolymer materials.
Decolorization of Acid Orange 142 (AO142) as important water pollutant was observed on the exposure of the dye solutions to an atmospheric non-thermal gas plasma. Aresponse Surface methodology (RSM) combined with a central composite design (CCD) was utilized to optimize the main factors (variables) affecting the degradation efficiency (response) of AO142, such as the applied voltage, the gap distance between the high voltage electrode and the surface of the solution. The regression analysis showed that a first-order polynomial model well fits the experimental data with a coefficient of determination R2=0.96. FT-IR, UV-vis,TOCand GC-MS measurements were used to investigate the decolorization of the dye on exposure to the plasma discharges. A possible Degradation pathway was postulated. Additionally, the conductivity and pH changes during the treatment were also evaluated. The plasma treatment combined with Fe2+ (plasma Fenton reaction) exhibited a higher degradation efficiency, higher energy yield connected with lower energy consumption in comparison to the plasma treatment without Fe2+ addition.
Tetraethyl orthosilicate (TEOS) was used as a chemical precursor to deposit ultra-thin SiO x C y plasma polymer films onto mild steel surfaces for preventing the corrosion process. The structure–property relationships of the coatings were evaluated by X-ray Photo Spectroscopy (XPS), X-Ray Diffraction (XRD), Fourier Transform InfraRed spectroscopy (ATR-FTIR) and Energy Dispersive X-ray spectroscopy (EDX) completed with Scanning Electron Microscopy (SEM). The SEM micrographs confirmed a pinhole-free surface morphology of the low-pressure deposited plasma polymer films. The TEOS molecules become fragmented in the plasma by numerous collisions with energy-rich electrons and heavier particles. Recombination of fragments and condensation onto the steel substrate is responsible for the formation of organic SiO containing plasma polymer layers. Such thin layers consist of predominantly SiO x structures. Their properties are determined largely by the gap distance between the two samples used as electrodes in the plasma. The efficiency of the corrosion-protecting coating was compared with uncoated samples. The corrosion protection was determined by exposure of samples to 3.5% NaCl aqueous solutions. For this purpose, polarization and Electrochemical Impedance Spectroscopy (EIS) were used to monitor the corrosion. The optimal gap distance between the electrodes was determined for corrosion protection. The best protective efficiency reached more than 97% of the total protection as measured at room temperature.