- Clay (3)
- Epoxy resin (3)
- Low-melting glass (3)
- Flame retardancy (2)
- Nanocomposites (1)
- Organic-inorganic polymer (1)
New low-melting organic–inorganic glassy polymers containing phosphorus and silicon are synthesized by the reaction between phenylphosphonic acid and methyltrichlorosilane or methyltriethoxysilane. They possess both low-softening points and high onset decomposition temperatures, which are favorable for preparing flame retardant composites. Although the glass by itself is sensitive to water, the composites are not significantly affected in that way. For glass/clay/epoxy composites glass transition temperature (Tg) as well as storage modulus increase with the glass amount. The glasses improve flame retardancy significantly due to flame inhibition and the formation of fire residue working as protection layer during burning. The total heat evolved is reduced by 23–28% for using 5–15 wt.% glass and the maximum HRR even by 5848%. The latter effect decreases with increasing glass amount due to an adulterate residue deformation. The combination of glass and clay is proposed as a possible route to enhance flame retardancy.
Due to optimised processing of epoxy based composite materials containing a low-melting organic–inorganic glass together with an organo clay, the size of the glass particles could be successfully reduced. Thus truly nano-dispersed composites were obtained, with glass particles in the range of 10 nm to 200 nm. The small particle size allowed efficient interaction of glass particles and organo clay layers. The flame retardancy as well as the thermo-mechanical properties were tested, and the results showed that the low-melting glass led to a remarkable reduction of peak heat release rate by forming an enhanced barrier layer. Nevertheless no further improvement could be achieved by lowering the particle size to the nanometre region. For good flame retardancy a microdispersion of the low-melting glass was already sufficient.
A low melting organic-inorganic glass and its effect on flame retardancy of clay/epoxy composites
(2011)
A low-melting organic-inorganic glass with a high molecular weight soluble in solvents was synthesized by hydrolytic polycondensation of phenyltriethoxysilane followed by a subsequent heat treatment. Softening point and thermostability were strongly increased after heat treatment. The composites of glass/epoxy and glass/clay/epoxy were studied with respect to their thermal properties, fire behavior and mechanical properties. Heat release rate as measured by cone calorimetry was remarkably reduced in the presence of glass, relative to neat epoxy resin and polymer/clay composites. The combination of glass and clay is a promising approach. It showed mainly superposition and even synergistic effects in some fire properties for higher filler concentrations due to the formation of an enhanced barrier. The structure of residue was investigated by transmission electron microscopy (TEM).